JP2699509B2 - 光学記録媒体の製造方法 - Google Patents

光学記録媒体の製造方法

Info

Publication number
JP2699509B2
JP2699509B2 JP1003101A JP310189A JP2699509B2 JP 2699509 B2 JP2699509 B2 JP 2699509B2 JP 1003101 A JP1003101 A JP 1003101A JP 310189 A JP310189 A JP 310189A JP 2699509 B2 JP2699509 B2 JP 2699509B2
Authority
JP
Japan
Prior art keywords
recording
recording medium
optical recording
layer
control layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP1003101A
Other languages
English (en)
Other versions
JPH02183448A (ja
Inventor
正明 鈴木
栄司 安藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Holdings Corp
Original Assignee
Matsushita Electric Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsushita Electric Industrial Co Ltd filed Critical Matsushita Electric Industrial Co Ltd
Priority to JP1003101A priority Critical patent/JP2699509B2/ja
Priority to US07/456,371 priority patent/US5110648A/en
Publication of JPH02183448A publication Critical patent/JPH02183448A/ja
Application granted granted Critical
Publication of JP2699509B2 publication Critical patent/JP2699509B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 産業上の利用分野 本発明は、情報記録用の光ディスクなどに利用される
光学記録媒体の製造方法、さらに波長多重光学記録媒体
に関する。
従来の技術 有機色素薄膜を記録媒体とした光記録の１方式とし
て、色素の会合状態の中で鋭い（ピーク波長半値幅の狭
い）吸収スペクトルを示すＪ会合体を利用した光学記録
媒体の製造方法が提案されている（例えば、特開昭61−
205187公報）。この記録方式は、ピーク吸収波長に対応
する発振波長のレーザ光を照射することによって、対応
するピークが熱モードで消失、あるいは低減する際の、
その吸光度の変化によって記録が行われる。さらに、光
学記録技術において情報の高密度記録を行うための方法
として、吸収極大波長の異なる色素を利用して１つの記
録ビットに複数ビットの情報を記録する波長多重記録方
式がある。
発明が解決しようとする課題 色素の会合体を利用した光学記録媒体は、記録感度が
良く、γ値が大きいため、小さい記録エネルギーでの記
録が可能である。しかし、記録エネルギーの変動に対し
て敏感であるため、記録時の吸光度の変化率にばらつき
を生じて記録状態が不安定になる。また、再生（記録の
読みだし）の際には、再生光の再生エネルギーによって
記録されて吸光度の減少を生じてしまい、記録状態の変
化や消失、すなわち情報の損失を生じてしまう。従来の
光学記録媒体では、記録感度特性は色素材料自体の選択
によって決定され、制御することができなかった。
課題を解決するための手段 本発明は、光学記録媒体の記録層上に可視光領域から
近赤外線領域に渡って吸収のない制御層を形成すること
によって、記録層の記録感度を制御する方法である。
作用 本発明の製造方法で作製した光学記録媒体は、照射光
の吸収による熱モードによって有機色素のＪ会合体が消
失する際に生じる、Ｊ会合体構造から色素単量体構造へ
の膜構造変化を、その上に形成した構造的に安定な制御
層によって制御する。それによって、記録層の記録エネ
ルギーに対する記録感度特性を制御してγ値を大きくす
ることができるため、記録エネルギーの変化に対する吸
光度の変化率のばらつきを小さくして記録を安定に行な
うことが可能となる。さらに、再生エネルギーによる記
録情報の読みだしの際に、情報の記録状態に対して影響
することなく再生することが可能となる。
実施例 以下に、本発明の実施例を図面を参照して説明する。
本発明で制御層形成に用いたラングミュアーブロジェ
ト（LB）法は低温プロセスの薄膜作製方法であり、膜厚
制御も単分子膜のオーダーで行え、制御性が高いため記
録層の作製にも有効である。
実施例１ 請求項１記載の発明について、第１図、第２図、およ
び第３図を用いて説明する。本発明の製造方法で作製し
た光学記録媒体の構成図を第１図に示す。また、従来例
の光学記録媒体の構成を第２図に示す。本発明の記録層
は、Ｊ会合体を形成する有機色素からなる累積膜であ
り、有機色素としては、シアニン、メロシアニン、スク
アリリウム系色素が用いられる。LB法によって形成され
る記録感度の制御層は、脂肪酸、脂肪酸エステル、脂肪
酸金属塩、脂肪族アミド、脂肪族アルコール、あるいは
アクリル系ポリマーが用いられる。
第２図に示すように、従来の構成の光学記録媒体は光
学基板３上にLB法を用いてＪ会合体の吸収波長が約700n
mであるシアニン色素累積膜10層の記録層２を形成した
ものである。このLB法による形成条件は、水温約16℃、
PH約５の水相上にシアニン色素単分子膜を形成し、単分
子膜の表面圧約35dyne/cm、累積速度約10mm/分で光学基
板３上に累積した。この光学記録媒体の記録特性を第３
図の４に示す。第１図に示す本発明の光学記録媒体は、
第２図の光学記録媒体上にLB法を用いて炭素数20の脂肪
酸であるアラキン酸のカドミウム塩累積膜20層（厚さ約
55nm）の制御層１を形成した構成である。このLB法によ
る形成条件は、水温約16℃、PH約6.5のカドミウムイオ
ンを溶解した水相上にアラキン酸単分子膜を展開、その
後アラキン酸カドミウム塩単分子膜となった単分子膜を
表面圧約35dyne/cm、累積速度約10mm/分で第２図の光学
記録媒体上に累積した。本発明の光学記録媒体の記録特
性を第３図の５に示す。制御層１の形成によって、Ｊ会
合体形成した有機色素記録層における記録光照射による
Ｊ会合体の消失に伴う構造変化が、制御層１によって抑
制されるため記録特性が変化する。そして、制御層１の
膜厚、制御層材料の種類、作製条件等によって、記録特
性を選択することが可能である。
第３図の４、５に示すように、これらの特性のγ値を
表わす曲線の傾きは本発明の構成を形成することによっ
て小さくなる。よって、第３図に示す記録時の吸光度変
化50％の許容変化率±３％に対する許容される照射光エ
ネルギー範囲は、従来の４では約1mJ/cm2・pulseであ
り、本発明の５では約4mJ/cm2・pulseとなる。したがっ
て、４で生じるような記録光エネルギーのわずかな変化
による吸光度の変化を緩和して、安定な記録を行なうこ
とができる。
また、第３図の４に示すように従来構成の光学記録媒
体では再生光のエネルギー６によって記録層の吸光度が
変化するために、情報の消失を生じてしまう。
また、制御層１の材質をアラキン酸カドミウム塩累積
膜５層（厚さ約13.8nm）にした場合には、記録特性の曲
線の傾きは従来の４とほとんど変わりなかった。そし
て、安定な記録を行うにはアラキン酸カドミウム塩累積
膜を制御層１として用いた場合には10層（厚さ約27.5n
m）以上必要であり、層数を増加するにつれて記録特性
の曲線の傾きは緩やかになるが30層（厚さ約82.5nm）以
上では効果が飽和する。
さらに、制御層１の材料として、アクリル系ポリマー
のポリ（アクリル酸ターシャルブチルエステル）を用い
た場合には、LB法による累積膜では10層（厚さ約10nm）
でアラキン酸カドミウム塩累積膜10層程度の効果が得ら
れた。そして、溶液塗布法であるスピンコーティングで
作製した場合にも記録特性の曲線の傾きを緩やかにする
ことができたが、膜厚100nmより薄い膜を均一に塗布す
ることは難しかしいため記録特性の変えることが十分に
できるが、制御性は低かった。
このように、本発明の製造方法による構成では、記録
感度５に示されるように再生光エネルギーによる吸光度
変化を防ぐことができ、安定な再生の可能な光学記録媒
体を提供できる。
実施例２ 次に請求項３に記載の発明について、第４図を用いて
説明する。
波長多重記録において、記録層間のクロストークが重
要な問題となっている。本発明では、第４図に示すよう
に、基板３上に、記録層10A、制御層9A、記録層8B、制
御層7Bの順に積層して構成される。記録層10Aに対する
制御層9Aにクロストークを防ぐための分離層としての働
きを行なわせている。なお、記録層10Aは実施例１と同
じＪ会合体の吸収波長約700nmのシアニン色素累積膜10
層、制御層9Aとしてはアラキン酸カドミウム塩累積膜20
層、記録層8BはＪ会合体吸収波長が約600nmのシアニン
色素来席膜８層、制御層7Bとしてアラキン酸カドミウム
塩累積膜10層を用い、累積条件は各シアニン色素、アラ
キン酸カドミウム塩ともそれぞれ実施例１と同じ条件で
形成した。用いた制御層は、記録層の吸収波長が存在す
る可視光領域から近赤外領域に渡って吸収を持たない
で、記録、または再生エネルギーを吸収しないために好
ましく用いられる。
このように、LB法によって順次記録層と制御層を作製
することによって形成した本発明の波長多重光学記録媒
体では、制御層の形成によって記録層への安定な記録が
行え、再生時の情報の消失を防ぐことができる。さら
に、この制御層を分離層として記録層間のクロストーク
を防ぐことが可能である。
発明の効果 以上述べたところから明らかなように、本発明によ
り、記録層の記録感度を制御することが可能となり、記
録情報の安定な記録、再生が行える。さら、本製造方法
で作製する制御層を分離層として利用して積層すること
によって、波長多重記録方式による高密度の波長多重光
学記録媒体を提供できる。
【図面の簡単な説明】
第１図は本発明の一実施例の製造方法で作製した光学記
録媒体の断面図、第２図は従来の光学記録媒体の断面
図、第３図は本発明の一実施例の光学記録媒体の記録特
性と従来の光学記録媒体の記録特性を示すグラフ、第４
図は本発明の一実施例の製造方法で作製された波長多重
光記録媒体の断面図である。 １……制御層、２……記録層、３……基板、４……従来
構成の記録特性、５……本発明での構成の記録特性、６
……再生光エネルギー、７……制御層Ｂ、８……記録層
Ｂ、９……制御層Ａ、10……記録層Ａ。

Claims (2)

    (57)【特許請求の範囲】
  1. 【請求項１】ラングミュアーブロジェット法により形成
    した有機色素累積膜を含む記録層上に、可視光領域およ
    び近赤外領域に渡って吸収を持たない制御層をラングミ
    ュアーブロジェット法を用いて作製することによって記
    録媒体の記録感度を制御することを特徴とする光学記録
    媒体の製造方法。
  2. 【請求項２】ラングミュアーブロジェット法により形成
    した有機色素累積膜を含む記録層上に、可視光領域およ
    び近赤外領域に渡って吸収を持たない制御層を作製する
    ことによって記録媒体の記録感度を制御した光学記録媒
    体の前記制御層が、異なる波長の記録光に対して独立に
    記録される波長多重光学記録媒体の分離層として使用さ
    れることを特徴とする光学記録媒体の製造方法。
JP1003101A 1989-01-10 1989-01-10 光学記録媒体の製造方法 Expired - Lifetime JP2699509B2 (ja)