JPH0619854B2 - 光学的情報記憶媒体 - Google Patents

光学的情報記憶媒体

Info

Publication number
JPH0619854B2
JPH0619854B2 JP59209697A JP20969784A JPH0619854B2 JP H0619854 B2 JPH0619854 B2 JP H0619854B2 JP 59209697 A JP59209697 A JP 59209697A JP 20969784 A JP20969784 A JP 20969784A JP H0619854 B2 JPH0619854 B2 JP H0619854B2
Authority
JP
Japan
Prior art keywords
dye
dye film
storage medium
film thickness
information storage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP59209697A
Other languages
English (en)
Other versions
JPS6190342A (ja
Inventor
通治 安倍
正彬 梅原
勉 佐藤
秀章 大庭
裕 上田
哲 山室
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ricoh Co Ltd
Original Assignee
Ricoh Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ricoh Co Ltd filed Critical Ricoh Co Ltd
Priority to JP59209697A priority Critical patent/JPH0619854B2/ja
Publication of JPS6190342A publication Critical patent/JPS6190342A/ja
Publication of JPH0619854B2 publication Critical patent/JPH0619854B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 〔技術分野〕 本発明は基板上の凸部に光吸収反射性色素膜を有する光
学的情報記憶媒体に関する。さらに詳しくは、本発明は
光デイスクメモリ装置に使用する光デイスクメモリ媒体
に関する。
〔従来技術〕
従来、色素薄膜を記録層として用いる光学的情報記憶媒
体が種々知られている。第２図に示すように、この種の
光学的情報記憶媒体１は透明基板２と色素膜３とから構
成されるものである。
光学的情報記憶媒体１として使用する場合には、レーザ
ビーム４を集光レンズ５により基板２側から集光照射し
て記録再生を行なう方法が知られており、基板２を透明
にする必要がある。情報の記録はレーザビーム４を大き
いパワーで照射し色素膜３は自ら吸収した光エネルギー
によつて熱的に変化し小孔（ピツト）が形成され小孔の
有無によつて行なわれる。一方、情報の再生は、色素膜
を破壊しない小さいパワーでレーザビームを照射し色素
膜からの反射光によつて小孔の有無を検出することによ
つて行なわれる。かかる構成の記憶媒体は塗布という極
めて生産性の高い方法によつて製造できるため低コスト
で工業生産できるという利点を有しているが、反面色素
膜を反射率が高くしかも均一性もよく形成することはか
なり困難である。
そこで、本発明者等は第３図に示すようにプレグルーブ
またはピツト６が色素膜３の面からみて凹みで形成され
るようにすることにより反射率が最大になるように色素
膜を厚く設定することを先に提案した。しかしながら、
色素塗布時に溶液が流動性のため凹み部分の色素膜厚が
周囲に比べて厚くなるという問題がある。通常、凹みの
深さは５００〜１５００Åであるが、色素膜厚が３００
〜１０００Åになるように塗布すると凹みの部分の厚さ
が周囲の部分の厚さよりも１０〜１００％程度厚くな
る。色素の厚さが厚くなると記録時にレーザビームの熱
により除去されにくくなり感度が低下したり、ノイズが
増加したり、波形干渉によりジツタが増加し再生信号に
エラーが発生し易くなる。一方、色素膜厚をうすくする
と凹み以外の部分の反射率が低下し、また色素膜厚のう
すいところと厚いところで反射率が異つてくるためプレ
グルーブまたはプレフオーマツトからの反射光がうまく
干渉しなくなりプレフオーマツト信号およびトラツキン
グエラー信号が弱くなるという欠点があつた。
〔目 的〕
本発明は上記現状に鑑みてなされたものであつてその目
的は光吸収反射性色素をプレグルーブまたはプレフオー
マツト付き基板上に塗布した光学的情報記憶媒体におい
て、プレフオーマツト信号の検出エラーの低減、情報記
録部分からの再生信号の品質向上およびエラー低減など
にある。
〔構 成〕
上記目的を達成するために、本発明は基板上に凸になる
ように形成されたプレグルーブまたはプレフオーマツト
用ピツト列の上に、光吸収反射性色素膜を塗布により凸
部と非凸部の反射率がほぼ等しくなるように設けると共
に凸部の色素膜厚を非凸部の色素膜厚よりも薄くした光
学的情報記憶媒体を提供することである。
プレグルーブはすでに知られているように記録あるいは
再生レーザビームを照射する際にトラツキング制御がで
きるようにするための信号検出を可能にするものであ
り、またプレフオーマツトはアドレスあるいはその他の
システム構成上必要な情報をあらかじめ形成しておくた
めに形成されるものである。プレグルーブあるいはプレ
フオーマツトは通常凸の高さが０．０５μｍ〜０．１５
μｍ程度、その幅０．３μｍ〜１．０μｍ程度に選択さ
れる。しかしながら、レーザビーム径および光波長をも
とにして既知の方法で設計されるのでこの数値に限定さ
れるものではない。
本発明において、凸部の光吸収性色素膜の膜厚を非凸部
の色素膜の膜厚よりも薄くしておくことが必要である。
このような構成にしておくと凸部と非凸部の反射率が同
程度になるためプレグルーブまたプレフオーマツトから
の反射光が適宜干渉し、プレフオーマツト信号およびト
ラッキングエラー信号が効果的に検知でき、また凸部７
の色素膜厚を記録感度の低下、波形干渉によるジツタの
増加が生じない程度にうすくできる。すなわち良好な記
録特性を保つことができると同時にプレフオーマツト信
号およびトラツキングエラー信号レベルを高くすること
ができる。
本発明における凸部の色素膜厚は通常４００〜１２００
Å好ましくは４５０〜１０００Åであり、非凸部の色素
膜厚を通常５００〜１５００Å好ましくは６００〜１３
００Åである。
本発明における光吸収反射性色素は特に制限されず２０
〜３０％の金属並みの高い反射率を与えるようなものを
適宜選択することができ、その代表的な例としてシアニ
ン色素またはメロシアニン色素をあげることができる。
また、本発明における色素膜は色素単独で構成される必
要はなく、他の色素との混合、ニツケル錯体などの安定
化剤との混合によつて形成されていてもよい。また、こ
のような色素膜にはこの他高分子物質、各種可塑剤、界
面活性剤、帯電防止剤、滑剤、難燃剤、分散剤などが含
有されていてもよい。色素膜の形成は色素の溶媒溶液を
基板上にスピンニング法、デイツプ法あるいはローラ法
などにより塗布することにより行なわれる。また、色素
膜の上には必要に応じ保護層を設けてもよいしあるいは
色素膜の下には必要に応じ下引層を設けてもよい。
本発明において色素膜を設ける基板の材質には特に制限
はなく各種プラスチツク、ガラス、セラミツクス、金属
などいずれであつてもよい。また、本発明の記憶媒体は
このような基板の一面上に上記の色素膜を有するもので
あつてもよくあるいはその両面に色素膜を有するもので
あつてもよい。さらに、基板の一面上に色素膜を設けた
ものを一対とし色素膜が対向するように配置したいわゆ
るサンドイツチ構造にすることもできる。
次に、本発明の好適な態様を第１図について説明する。
本発明の光学的情報記憶媒体１は基板２に色素膜３の面
からみて凸になるようにプレグルーブまたはプレフォー
マット用ピット７が形成されその上に色素膜３ａが、一
方非凸部には色素膜３ｂが反射率がほぼ等しくなるよう
に設けられ、かつ色素膜３ａが色素膜３ｂよりもその膜
厚が薄くなるように設けられたものである。このような
構成にするとプレグルーブまたはプレフォーマット用ピ
ットの部分で色素の膜厚が薄くなるように色素膜が形成
されるので凸部７の情報が記録される部分の色素膜厚３
ａを記録感度の低下、波形干渉によるジッタの増加を伴
うことなくプレフォーマット信号およびトラツキングエ
ラー信号レベルを高くすることができるので良好な記録
特性とトラッキング特性およびプレフォーマット信号を
両立させることができる。
〔実施例〕
以下に実施例とともに比較例をあげて本発明をさらに説
明するが、本発明はこれらに限定されるものではない。
実施例 １ 厚さ１．１５mmのアクリル板上にフオトポリマー法によ
りトラツクピツチ２．０μｍ、幅０．６μｍ、高さ７０
０Åの凸部を有するプレグルーブを形成した基板上に下
記式のシアニン色素（日本感光色素研究所ＮＫ２８８
３）をジクロルエタンに溶かして塗布して光学的情報記
憶媒体を作製した。この際、プレグルーブ上の色素膜厚
を５００Åとし、その他の部分の色素膜厚を７５０Åと
した。
実施例 ２ 厚さ１．１５mmのアクリル板上にフオトポリマー法によ
りトラツクビツチ２０μｍ、幅０．７μｍ、高さ９００
Åの凸部を有するプレグルーブを形成した基板上に実施
例１で用いたシアニン色素をジクロルエタンに溶かして
塗布して光学的情報記憶媒体を作製した。この際、プレ
グルーブ上の色素膜厚を５００Åとし、その他の部分の
色素膜厚を８００Åとした。
実施例 ３ 厚さ１．１５mmのアクリル板上にフオトポリマー法によ
りトラツクピツチ２．０μｍ、幅０．６μｍ、高さ５０
０Åの凸部を有するプレグルーブを形成した基板上に実
施例１で用いたシアニン色素をジクロルエタンに溶かし
て塗布して光学的情報記憶媒体を作製した。この際、プ
レグルーブ上の色素膜厚を５００Åとし、その他の部分
の色素膜厚を６８０Åとした。
実施例 ４ 厚さ１．１５mmのアクリル板上にフオトポリマー法によ
りトラツクピツチ２．０μｍ、幅０．６μｍ、高さ７０
０Åの凸部を有するプレグルーブを形成した基板上に下
記式のトリアリールメタン色素（保土谷化学アイゼンビ
クトリアブルーＢＨ）をエタノールに溶かして塗布して
光学的情報記憶媒体と作製した。この際、プレグルーブ
上の色素膜厚を５００Åとし、その他の部分の色素膜厚
を７５０Åとした。
比較例 １ 厚さ０．１５mmのアクリル板上にフオトポリマー法によ
りトラツクピツチ２．０μｍ、幅０．６μｍ、深さ７０
０Åの凹部を有するプレグルーブを形成した基板上に実
施例１と同様にしてシアニン色素を塗布して記憶媒体を
作製した。この際、プレグルーブ上の色素膜厚を５００
Åとし、その他の部分の色素膜厚を３００Åとした。
比較例 ２ 比較例１においてプレグルーブ上の色素膜厚を７５０Å
としその他の部分の色素膜厚を５００Åとした以外は比
較例１と同様にして記憶媒体を作製した。
比較例 ３ 厚さ１．１５mmのアクリル板上にフオトポリマー法によ
りトラツクピツチ２．０μｍ、幅０．７μｍ、深さ９０
０Åの凹部を有するプレグルーブを形成した基板上に実
施例２と同様にしてシアニン色素を塗布して記憶媒体を
作製した。この際、プレグルーブ上の色素膜厚を５００
Åとし、その他の部分の色素膜厚を２７０Åとした。
比較例 ４ 比較例３においてプレグルーブ上の色素膜厚を８００Å
としその他の部分の色素膜厚を５００Åとした以外は比
較例３と同様にして記憶媒体を作製した。
比較例 ５ 厚さ１．１５mmのアクリル板上にフオトポリマー法によ
りトラツクピツチ２．０μｍ、幅０．６μｍ、深さ５０
０Åの凹部を有するプレグルーブを形成した基板上に実
施例３と同様にしてシアニン色素を塗布して記憶媒体を
作製した。この際、プレグルーブ上の色素膜厚を５００
Åとし、その他の部分の色素膜厚を３７０Åとした。
比較例 ６ 比較例５においてプレグルーブ上の色素膜厚を６８０Å
としその他の部分の色素膜厚を５００Åとした以外は比
較例５と同様にして記憶媒体を作製した。
比較例 ７ 厚さ１．１５mmのアクリル板上にフオトポリマー法によ
りトラツクピツチ２．０μｍ、幅０．６μｍ、深さ７０
０Åの凹部を有するプレグルーブを形成した基板上に実
施例４と同様にしてアリアリールメタン色素を塗布して
記憶媒体を作製した。この際、プレグルーブ上の色素膜
厚を５００Åとし、その他の部分の色素膜厚を３００Å
とした。
比較例 ８ 比較例７においてプレグルーブ上の色素膜厚を７５０Å
としその他の部分の色素膜厚を５００Åとした以外は比
較例７と同様にして記憶媒体を作製した。
次に、実施例および比較例で作製した記憶媒体に実施例
１、比較例７および比較例８については波長６３３ｎｍ
のヘリウムネオンレーザを用いそしてその他の例につい
ては波長７９０ｎｍの半導体レーザを用い線速度１．２
４ｍ／ｓｅｃ、レーザビーム径０．９μｍ（半値幅）で
情報を記録しアイパターンの判定レベルがゼロになる記
録パワーとトラツキングエラー信号（相対値）を測定し
その結果を以下の表にまとめて示す。
〔効 果〕 本発明の光学的情報記憶媒体によれば、以下の利点が得
られる。
(1) 記録レーザパワーを低くできる（トラツキングエ
ラー信号を同一にしたとき）。
(2) トラツキングエラー信号を大きくできる（記録レ
ーザパワーが同じのとき）。
(3) 波形干渉が少なくなりエラーが減少する。
【図面の簡単な説明】
第１図は本発明に係る光学的情報記憶媒体の好適な例を
示す断面図であり、そして第２図および第３図は従来例
の光学的情報記憶媒体の構成を示す断面図である。 １……光学的情報記憶媒体、２……基板、３……色素
膜、４……レーザビーム、５……集光レンズ、６，７…
…プレグルーブまたはピツト。
フロントページの続き (72)発明者 大庭 秀章 東京都大田区中馬込１丁目３番６号 株式 会社リコー内 (72)発明者 上田 裕 東京都大田区中馬込１丁目３番６号 株式 会社リコー内 (72)発明者 山室 哲 東京都大田区中馬込１丁目３番６号 株式 会社リコー内 (56)参考文献 特開 昭55−97033（ＪＰ，Ａ)

Claims (1)

    【特許請求の範囲】
  1. 【請求項１】基板上に凸になるように形成されたプレグ
    ルーブまたはプレフォーマット用ピット列の上に光吸収
    反射性色素膜を塗布により凸部と非凸部の反射率がほぼ
    等しくなるように設けると共に該凸部の色素膜の膜厚を
    非凸部の色素膜の膜厚よりも薄くしたことを特徴とす
    る、光学的情報記憶媒体。
JP59209697A 1984-10-08 1984-10-08 光学的情報記憶媒体 Expired - Lifetime JPH0619854B2 (ja)