JP2585130B2 - 合成樹脂製パレットの製造方法 - Google Patents

合成樹脂製パレットの製造方法

Info

Publication number
JP2585130B2
JP2585130B2 JP18466090A JP18466090A JP2585130B2 JP 2585130 B2 JP2585130 B2 JP 2585130B2 JP 18466090 A JP18466090 A JP 18466090A JP 18466090 A JP18466090 A JP 18466090A JP 2585130 B2 JP2585130 B2 JP 2585130B2
Authority
JP
Japan
Prior art keywords
leg
heating
pallet
synthetic resin
surface side
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP18466090A
Other languages
English (en)
Other versions
JPH0469230A (ja
Inventor
照一 森
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daifuku Co Ltd
Original Assignee
Daifuku Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daifuku Co Ltd filed Critical Daifuku Co Ltd
Priority to JP18466090A priority Critical patent/JP2585130B2/ja
Publication of JPH0469230A publication Critical patent/JPH0469230A/ja
Application granted granted Critical
Publication of JP2585130B2 publication Critical patent/JP2585130B2/ja
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は合成樹脂製パレットの製造方法に関し、更に
詳しくは、矩形板状の荷載置部の一方の面に脚部を突出
させた形状に合成樹脂を一体成形してなるパレット構成
体の２個を、それらの脚部の先端部を加熱した上で突き
合わせた後にアプセットして前記脚部同士を熱溶着し、
前記パレット構成体の２個を接合する合成樹脂製パレッ
トの製造方法に関する。
〔従来の技術〕
かかる方法を用いて合成樹脂製パレットを製造する場
合、第７図（イ）に示すように、パレット構成体（Ａ）
の脚部（２）を加熱源（Ｈ）を用いて加熱した後（加熱
後は、前記加熱源（Ｈ）を除去する）、前記脚部（２）
の突き合わせ・アプセットを行って前記脚部（２）同士
を熱溶着し、もって前記パレット構成体（Ａ）の接合を
行う。かくして製造されたパレットにおいては、通常、
前記脚部（２）同士が熱溶着された部分に、第７図
（ロ）に示すようにバリ（Ｂ）が発生する。
そして、フォーク（フォークリフト等のフォーク）に
よってパレット操作が行われる場合、前記バリ（Ｂ）が
発生した部分にフォークが挿入されると、該フォークが
前記バリ（Ｂ）を引っ掛けてパレットの姿勢を乱すこと
になる等、フォークによるパレット操作に不都合を来す
虞れがある。
また、前記バリ（Ｂ）にフォークが繰り返して引っ掛
かると、前記脚部（２）の熱溶着部が離脱する虞れもあ
る。
また、前記バリ（Ｂ）がフォークに引っ掛けられて落
下すると、その落下したバリ（Ｂ）が不良異物となり、
パレットの使用場所次第では種々の問題が生じる。例え
ば、パレットの使用場所が食品を取り扱う場所である場
合には、食品衛生上の問題が生じることになる。
なお、フォークがバリに引っ掛かって生じる上述の諸
問題は、フォーク以外の物体（前記パレットの近傍の人
・物等）がバリに引っ掛かるような場合にも同様に生じ
る。
そこで従来は、第８図（イ）に示すように、前記パレ
ットを製造するに際して、パレット構成体（Ａ）の脚部
（２）の突き合わせ面の外面側の部分（具体的には、フ
ォーク差込口側の部分やパレットの外周側の部分）を切
り欠いてその部分に、熱溶着時に発生するバリ（Ｂ）が
収まるスペース（Ｓ）を熱溶着に先立って形成してお
き、前記脚部（２）が熱溶着されるときに発生するバリ
（Ｂ）を第８図（ロ）に示すように前記スペース（Ｓ）
内に収めるようにし、もって前記バリ（Ｂ）の外方への
突出を回避するということが行われている。なお、前記
脚部（２）の熱溶着に際しては、前記脚部（２）の先端
部は前記加熱源（Ｈ）によって均一に加熱される。
〔発明が解決しようとする課題〕
然るに、第８図に示す方法によって前記バリ（Ｂ）の
外方への突出を回避するように対策した場合、フォーク
によるパレット操作に不都合を来す虞れがあるという問
題、フォーク以外の人体・物体がバリに引っ掛かる虞れ
があるという問題、前記脚部の熱溶着部が離脱する虞れ
があるという問題、落下したバリが不良異物となる虞れ
があるという問題等は解消されるものの、前記脚部
（２）の熱溶着部の接合強度は、前記スペース（Ｓ）を
形成することによる接合面積の大幅な減少に起因して低
下してしまうという別の問題が生じる。
本発明は、かかる事情に鑑みてなされたものであり、
上述したような諸問題を解消すると共に、前記熱溶着部
の接合強度の問題をも解消し得る手段を提供することを
目的としている。
〔課題を解決するための手段〕
本発明による合成樹脂製パレットの製造方法の特徴構
成は、前記脚部の先端部におけるアプセットに先立つ加
熱を、前記脚部の外面側部分に供給される加熱エネルギ
ーよりもその内面側部分に供給される加熱エネルギーの
方が高くなるようにして不均一に行うことにある。
なお、前記加熱を不均一に行うには、例えば前記脚部
の先端部の外面側を面取りすることによって形状的に内
外不均一となった先端部を、前記脚部の先端側に配置し
た加熱源にて加熱すればよい。また、前記脚部の内面側
に配置した加熱源にて内外不均一に加熱することによっ
ても前記不均一加熱が可能となる。
〔作 用〕
かかる本発明方法のアプセットに先立つ加熱は、前記
脚部の外面側部分に供給される加熱エネルギーよりもそ
の内面側部分に供給される加熱エネルギーの方が高くな
るように行われるので、その加熱が実際に行われると、
前記脚部の先端部においては、脚部の外面側部分よりも
脚部の内面側部分の方が変形され易い状態となる。その
結果、アプセット後の状態では前記内面側部分の方が前
記外面側部分よりもバリが多量に発生し、前記外面側部
分へのバリの突出は可及的に少なく抑えられるようにな
る。
しかも、前記外面側部分へのバリの突出を可及的に少
なく抑えるのに、バリを収めるためのスペースを形成し
て前記外面側部分へのバリの突出を可及的に少なく抑え
るという従来方法の場合のような、熱溶着部への接合面
積の大幅な減少という現象も生じない。
〔発明の効果〕
かくして本発明方法によれば、前記脚部の内面側部分
にバリが多量に発生する一方、前記脚部の外面側部分に
殆どバリが発生しない状態となすことができるため、前
記外面側部分へのバリの突出が可及的に少なく抑えら
れ、もって外面側部分へのバリの突出に起因する従来の
諸問題はいずれも解消されるようになる。
しかも、熱溶着部の接合面積が減少することを抑制で
きるので、熱溶着部の接合強度の低下も抑えられるよう
になる。
その結果、外面側部分へのバリの突出に起因する従来
の問題、及び、熱溶着部の接合強度に関する従来の問題
は一挙に解消されることとなる。
〔実施例〕
以下、本発明の実施例を図面に基づいて説明する。
第２図及び第３図は本発明方法にて製造される合成樹
脂製パレットの一例を示しており、該合成樹脂製パレッ
トは、第４図及び第５図に示すパレット構成体（Ａ）の
２個を、上下逆姿勢で対をなすように配置し、それらの
脚部（２）同士を相互に接合することによって製造され
る。
前記パレット構成体（Ａ）は、具体的には、矩形板状
の荷載置部（１）の一方の面に脚部（２）を突出させた
形状に合成樹脂を一体成形することによって得られる。
なお、前記脚部（２）は、前記荷載置部（１）の四角部
及び各辺部中央に位置し補強部材（2a）にて補強された
筒状脚部（2A）、並びに、前記荷載置部（１）の下方周
縁を前記筒状脚部（2A）及びフォーク差込口（６）の部
分を除いて取り巻くように位置し補強部材（2b）にて補
強された壁状脚部（2B）に大別される。
前記パレット構成体（Ａ）同士の接合は、具体的に
は、それらの脚部（２）の先端部を加熱した上で突き合
わせた後にアプセットして前記脚部（２）同士を熱溶着
することによって行われる。
前記熱溶着に際し、本発明方法においては、前記脚部
（２）の先端部における前記アプセットに先立つ加熱
を、前記脚部（２）の外面側部分に供給される加熱エネ
ルギーよりもその内面側部分に供給される加熱エネルギ
ーの方が高くなるようにして不均一に行う。
上述の不均一な加熱は、具体的には、第１図（イ）に
示すように、前記脚部（２）（該脚部（２）としては、
第４図中の斜線にて示す前記筒状脚部（2A）及び前記壁
状脚部（2B）を含む）の先端部の外面側の角部分（具体
的には、前記フォーク差込口（６）側に当たる部分やパ
レットの外周側に当たる部分）を面取りすることによ
り、前記先端部を形状的に内外不均一な形状的となし、
その先端部を、前記脚部（２）の先端側に配置した加熱
源（Ｈ）にて加熱することによって行う。
かかる不均一な加熱が行われると、前記脚部（２）の
先端部においては、脚部（２）の外面側部分よりも脚部
（２）の内面側部分の方が高温に加熱され（等温線をと
れば、第１図（イ）中の破線にて示されるようにな
る）、前記内面側部分の方が変形され易い状態となる
（変形可能領域は、第１図（イ）中の斜線にて示された
領域となる）。その結果、アプセット後の状態では、第
１図（ロ）に示すように、前記内面側部分の方が前記外
面側部分よりもバリ（Ｂ）が多量に発生し、前記外面側
部分へのバリ（Ｂ）の突出は可及的に少なく抑えられる
ようになる。
しかも、前記外面側部分へのバリ（Ｂ）の突出を可及
的に少なく抑えるのに、従来方法の場合のように熱溶着
部の接合面積を犠牲にすることもない。
〔別実施例〕
上述した如き不均一な加熱は、第５図（イ），（ロ）
に示すように、前記脚部（２）の内面側に配置した加熱
源（Ｈ）（その外面側には加熱源（Ｈ）を配置しないよ
うする）にて内外不均一に加熱することによっても実現
が可能である。
なお、特許請求の範囲の項に図面との対照を便利にす
るために符号を記すが、この記入によって本発明方法は
添付図面によって示される方法に限定されるものではな
い。
【図面の簡単な説明】
第１図（イ），（ロ）は本発明に係る合成樹脂製パレッ
トの製造方法の主要工程を例示する説明図、第２図は本
発明方法にて製造される合成樹脂製パレットを示す平面
図、第３図はその正面図、第４図は前記合成樹脂製パレ
ットの組立素材となるパレット構成体を示す底面図、第
５図はその正面図、第６図（イ），（ロ）は本発明方法
の別実施例を示す説明図、第７図（イ），（ロ）及び第
８図（イ），（ロ）は従来の合成樹脂製パレット製造方
法の主要工程を示す説明図である。 （１）……荷載置部、（２）……脚部、（Ａ）……パレ
ット構成体、（Ｂ）……バリ、（Ｈ）……加熱源。

Claims (3)

    (57)【特許請求の範囲】
  1. 【請求項１】矩形板状の荷載置部（１）の一方の面に脚
    部（２）を突出させた形状に合成樹脂を一体成形してな
    るパレット構成体（Ａ）の２個を、それらの脚部（２）
    の先端部を加熱した上で突き合わせた後にアプセットし
    て前記脚部（２）同士を熱溶着し、前記パレット構成体
    （Ａ）の２個を接合する合成樹脂製パレットの製造方法
    であって、 前記脚部（２）の先端部における前記アプセットに先立
    つ加熱を、前記脚部（２）の外面側部分に供給される加
    熱エネルギーよりもその内面側部分に供給される加熱エ
    ネルギーの方が高くなるようにして不均一に行う合成樹
    脂製パレットの製造方法。
  2. 【請求項２】前記脚部（２）の先端部の外面側を面取り
    することにより、形状的に内外不均一となった先端部
    を、前記脚部（２）の先端側に配置した加熱源（Ｈ）に
    て加熱することにより、前記アプセットに先立つ加熱を
    不均一に行う請求項１記載の合成樹脂製パレットの製造
    方法。
  3. 【請求項３】前記脚部（２）の内面側に配置した加熱源
    （Ｈ）にて内外不均一に加熱することにより、前記アプ
    セットに先立つ加熱を不均一に行う請求項１記載の合成
    樹脂製パレットの製造方法。
JP18466090A 1990-07-11 1990-07-11 合成樹脂製パレットの製造方法 Expired - Fee Related JP2585130B2 (ja)