JP2023543922A - コーティング組成物特性又は濡れフィルム特性を用いたスクリーニング方法 - Google Patents
コーティング組成物特性又は濡れフィルム特性を用いたスクリーニング方法 Download PDFInfo
- Publication number
- JP2023543922A JP2023543922A JP2023520457A JP2023520457A JP2023543922A JP 2023543922 A JP2023543922 A JP 2023543922A JP 2023520457 A JP2023520457 A JP 2023520457A JP 2023520457 A JP2023520457 A JP 2023520457A JP 2023543922 A JP2023543922 A JP 2023543922A
- Authority
- JP
- Japan
- Prior art keywords
- coating material
- material composition
- optionally
- polymer
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1) 第1のコーティング材料組成物F1を提供する工程であって、
その第1のコーティング材料組成物F1が、
(i) 架橋性官能基を有する、少なくとも1つのフィルム形成ポリマーP1、
(ii) 少なくともポリマーP1の架橋性官能基に対して反応性である官能基を有する、少なくとも1つの架橋剤CA1、
(iii) 水及び/又は少なくとも1つの有機溶媒、
(iv) 任意に、少なくとも1つの相溶化ポリマーPMP、
(v) 任意に、少なくとも1つの添加剤A、好ましくは、ポリマーP1の架橋性官能基と架橋触媒CA1の官能基との架橋反応を触媒することができる、添加剤Aとしての少なくとも1つの架橋触媒CLC1、及び
(vi) 任意に、少なくとも1つの顔料PI1及び/又はフィラーFI1
を含み、
ここで、構成成分(i)、(ii)、(iii)及び(iv)、及び(v)及び(vi)は、それぞれ互いに異なる、提供する工程、
(2) 第1のコーティング材料組成物F1を、基材の少なくとも1つの任意に事前に被覆された表面上に任意に適用して、基材の前記表面上に濡れたコーティングフィルムを形成する工程、
(3) 工程(2)の後に得られた濡れたコーティングフィルムを任意に乾燥させて、基材の表面に部分的に乾燥したコーティングフィルムを形成する工程、
(4) 工程(1)で提供されたコーティング材料組成物、及び/又は工程(2)を行った場合は濡れたコーティングフィルム、及び/又は工程(3)を行った場合は部分的に乾燥したコーティングフィルムの、少なくとも1つの特性を測定する工程、
(5) 第1のコーティング材料組成物F1とは正確に1つ又は多くても2つ、好ましくは正確に1つのパラメータ(複数可)が異なる、少なくとも1つのさらなるコーティング材料組成物を提供する工程であって、
前記パラメータ(複数可)が、(a)ポリマーP1と、ポリマーP1とは異なり且つ少なくとも架橋剤CA1の官能基に対して反応性である架橋性官能基を有するさらなるポリマーとの、部分的又は完全な交換、(b)架橋剤CA1と、架橋剤CA1とは異なり且つ少なくともポリマーP1の架橋性官能基に対して反応性である官能基を有するさらなる架橋剤との、部分的又は完全な交換、(c)ポリマーP1及び/又はさらなるコーティング材料組成物中の(a)で定義したポリマーP1の部分的又は完全な交換に使用されたポリマーP1とは異なるポリマーの量の低下又は増加、(d)架橋剤CA1及び/又はさらなるコーティング材料組成物中の(b)で定義したCA1の部分的又は完全な交換に使用されたCA1とは異なる架橋剤の量の低下又は増加、(e)存在する場合に添加剤A、例えば架橋触媒CLC1と、添加剤Aとは異なるさらなる添加剤、例えば架橋触媒CLC1とは異なる架橋触媒との部分的又は完全な交換、(f)存在する場合に添加剤A、例えば架橋触媒CLC1、及び/又はさらなるコーティング材料組成物中の(e)で定義した添加剤A、例えば架橋触媒CLC1の部分的又は完全な交換に使用された添加剤Aとは異なる添加剤、例えばCLC1とは異なる架橋触媒の量の低下又は増加、(g)存在する場合に顔料PI1及び/又はフィラーFI1と、顔料PI1及び/又はフィラーFI1とは異なるさらなる顔料及び/又はフィラーとの部分的又は完全な交換、及び(h)存在する場合に顔料PI1及び/又はフィラーFI1及び/又は存在する場合にさらなるコーティング材料組成物中の(g)で定義した顔料PI1及び/又はフィラーFI1の部分的又は完全に交換に使用された顔料PI1及び/又はフィラーFI1とは異なる顔料の量の低下又は増加、からなる群から選択される、提供する工程、
(6) さらなるコーティング材料組成物を、基材の少なくとも1つの任意に事前に被覆された表面に任意に適用して、基材の前記表面上に濡れたコーティングフィルムを形成する工程、
(7) 工程(6)の後に得られた濡れたコーティングフィルムを任意に乾燥させて、基材の表面に部分的に乾燥したコーティングフィルムを形成する工程、
(8) 工程(5)で提供されたコーティング材料組成物、及び/又は工程(6)を行った場合は濡れたコーティングフィルム、及び/又は工程(7)を行った場合は部分的に乾燥したコーティングフィルムの少なくとも1つの特性を測定する工程であって、前記少なくとも1つの特性が工程(4)で測定したものと同じ特性である、測定する工程、
(9) 任意に、工程(5)及び(8)及び任意に工程(6)及び/又は工程(7)を少なくとも1回繰り返す工程であって、提供されたさらなるコーティング組成物の各々が、互いに異なり、そしてコーティング材料組成物F1とは異なる、繰り返す工程、
(10) 工程(4)及び(8)で測定された特性の結果、及び任意に工程(9)で定義した少なくとも1回の繰り返しの場合に測定された特性の結果を、好ましくは電子データベースに組み込む工程、
(11) 組み込む工程(10)により好ましくは電子データベースに存在する測定された特性の少なくとも1つを選択する工程、
(12) 工程(4)及び(8)により、及び任意に工程(9)で定義した少なくとも1回の繰り返しの後に測定された少なくとも1つの選択された特性の結果を、評価及び互いに比較する工程、及び
(13) 第1のコーティング材料組成物F1、及び工程(5)の後に得られたさらなるコーティング材料組成物の各々、及び工程(9)で定義した少なくとも1回の繰り返しの後に任意に得られた任意のコーティング材料組成物とは異なる、少なくとも1つの新規コーティング配合物を配合及び提供するために、評価及び比較工程(12)から得られた情報を使用する工程であって、少なくとも1つの新規コーティング配合物それ自体、及び/又はそれから得られた濡れた又は部分的に乾燥したコーティングフィルムが、工程(4)及び/又は(8)で定義した通り測定した場合に、工程(11)で選択された少なくとも1つの特性の改善を示す、使用する工程
を含む。
工程(1)
本発明の方法の工程(1)において、第1のコーティング材料組成物F1が提供される。第1のコーティング材料組成物F1は、少なくとも構成成分(i)、(ii)及び(iii)及び任意に(iv)及び/又は(v)及び/又は(vi)を含む。構成成分(i)、(ii)、(iii)、(iv)及び(v)及び(vi)は、互いに異なる。
好ましくは、構成成分(i)~(iii)及び任意に(iv)及び/又は(v)及び/又は(vi)は、第1のコーティング材料組成物F1の唯一の構成成分である。よって好ましくは、第1のコーティング材料組成物F1は、構成成分(i)~(iii)、及び任意に(iv)及び/又は(v)及び/又は(vi)からなる。好ましくは、構成成分(iv)は、第1のコーティング材料組成物F1中に存在する。F1とは異なるさらなるコーティング材料組成物の各々についても好ましくは同様である。
第1のコーティング材料組成物F1は、構成成分(i)として少なくとも1つのフィルム形成ポリマーP1を含み、該ポリマーP1は、架橋性官能基を有する。第1のコーティング材料組成物F1は、構成成分(ii)として少なくともポリマーP1の架橋性官能基に対して反応性である官能基を有する少なくとも1つの架橋剤CA1をさらに含む。ポリマーP1の架橋性官能基と架橋剤CA1の官能基との間で好ましくは生じる架橋反応は、少なくとも1つの架橋触媒(任意の構成成分(v))によって触媒できるが、必ずしも触媒される必要はない。そのような触媒作用が所望される場合、第1のコーティング材料組成物F1は、少なくとも1つの架橋触媒(v)をさらに含む。F1とは異なるさらなるコーティング材料組成物の各々についても好ましくは同様である。
フィルム形成ポリマーP1は、バインダーを表す。本発明の目的では、用語「バインダー」は、DIN EN ISO4618(ドイツ版、日付:2007年3月)に準拠して、コーティング材料組成物の不揮発性(固体)構成成分であると理解され、フィルム形成に関与する。この用語には、架橋剤(crosslinking agent)(架橋物(crosslinkers))及び触媒などの添加剤が含まれる(これらが不揮発性構成成分を表す場合)。顔料及び/又はフィラーは、フィルム形成に関与しないので、用語「バインダー」に包含されない。しかしながら、好ましくは、顔料及び/又はフィラーは存在しない。好ましくは、構成成分(i)、(ii)、(iv)及び(v)の各々は、コーティング材料組成物F1の総バインダー固形分含量に寄与する。F1とは異なるさらなるコーティング材料組成物の各々についても好ましくは同様である。
あらゆる従来の架橋剤を使用することができる。これには、メラミン樹脂、好ましくはメラミンアルデヒド樹脂、より好ましくはメラミンホルムアルデヒド樹脂、ブロック化ポリイソシアネート、遊離(非ブロック化)イソシアネート基を有するポリイソシアネート、アミノ基、例えば第2級及び/又は第1級アミノ基を有する架橋剤、及びエポキシド基及び/又はヒドラジド基を有する架橋剤、及びカルボジイミド基を有する架橋剤が含まれる(特定の架橋剤の官能基が、架橋反応においてバインダーとして用いられるフィルム形成ポリマーの架橋性官能基と反応するのに好適である限り)。例えば、ブロックされた又は遊離イソシアネート基を有する架橋剤は、1K配合物の場合には高温で、2K配合物の場合には周囲温度で、架橋性OH基及び/又はアミノ基を有するフィルム形成ポリマーと反応させることができる。さらに可能な組み合わせは、例えばフィルム形成ポリマーのエポキシド基であり、これは架橋剤の酸及び/又はアミノ基と反応させることができ、又はその逆もまた可能である。さらに可能な組み合わせは、例えばフィルム形成ポリマーのケト基であり、これは架橋剤のヒドラジド基と反応させることができ、又はその逆も可能であり、又は例えば架橋剤のカルボジイミド基であり、これはフィルム形成ポリマーの酸基と反応させることができ、又はその逆も可能である。
第1のコーティング材料組成物F1は、構成成分(iii)として、水及び/又は少なくとも1つの有機溶媒を含む。
第1のコーティング材料組成物F1は、任意に及び好ましくは、構成成分(iv)として少なくとも1つの相溶化ポリマーPMPを含む。相溶化ポリマーPMPは、特に、水及び少なくとも1つの有機溶媒の両方が第1のコーティング材料組成物中に存在する場合に、相媒介剤及び/又は相促進剤として使用される。好ましくは、構成成分(iii)が少なくとも部分的に水を表す場合、構成成分(iv)は第1のコーティング材料組成物F1中に存在する。
第1のコーティング材料組成物F1は、任意に、構成成分(v)として少なくとも1つの添加剤A、例えばポリマーP1の架橋性官能基と架橋触媒CA1の官能基との架橋反応を触媒することができる、少なくとも1つの架橋触媒CLC1を含む。同様に、本発明の方法で提供されるさらなるコーティング材料組成物の各々は、任意に、添加剤A及び/又は添加剤Aと異なる少なくとも1つの添加剤を含んでよい。上記に概説した通り、例えば、添加剤(v)として架橋触媒が使用される場合、これらはその触媒活性以外にさらなる機能を示すことが可能である。例えば、ブロック化又は非ブロック化スルホン酸を架橋触媒として使用する場合、これらは界面活性剤としても機能し、ひいては測定される特性のさらなる例としての表面張力に影響を有することもある。この原則は、構成成分(v)として使用されるあらゆる添加剤に当てはまる。
第1のコーティング材料組成物F1は、構成成分(vi)として、少なくとも1つの顔料PI1及び/又は少なくとも1つのフィラーFI1を任意に含む。同様に、本発明の方法において提供されるさらなるコーティング材料組成物の各々は、顔料PI1及び/又はフィラーFI1、及び/又は顔料PI1とは異なる少なくとも1つの顔料及び/又はフィラーFI1とは異なる少なくともフィラーを任意に含んでよい。しかしながら、好ましくは、第1のコーティング材料組成物F1は、いかなる顔料及び/又はフィラーも含まない。
任意の工程(2)において、第1のコーティング材料組成物F1を、基材の少なくとも1つの任意に事前に被覆された表面上に適用して、基材の前記表面上に濡れたコーティングフィルムを形成する。この工程は、濡れたコーティングフィルムの特性を、工程(4)において測定することが意図されている場合に行われる。
任意に、本発明の方法は、任意の工程(2)の後且つ工程(4)の前に実施される工程(3)をさらに含む。この工程は、部分的に乾燥したコーティングフィルムの特性を、工程(4)において測定することが意図されている場合に行われる。前記工程(3)において、工程(2)の後に得られた濡れたコーティングフィルムを任意に部分的に乾燥させて、部分的に乾燥したコーティングフィルムを基材の表面上に形成する。部分的な乾燥は、好ましくはフラッシュオフにより、好ましくは1~30分の期間、より好ましくは1.5~25分の期間、特に2~20分の期間、最も好ましくは3~15分の期間行う。好ましくは、工程(3)は、100℃を超えない温度、より好ましくは18~80℃の範囲の温度で行う。
工程(4)では、工程(1)で提供されたコーティング材料組成物、及び/又は工程(2)を行った場合は濡れたコーティングフィルム、及び/又は工程(3)を行った場合は部分的に乾燥したコーティングフィルムの、少なくとも1つの特性を測定する。
工程(5)において、第1のコーティング材料組成物F1とは正確に1つ又は多くても2つのパラメータが異なる、少なくとも1つ、好ましくは正確に1つのさらなるコーティング材料組成物が提供される。前記パラメータは、(a)ポリマーP1と、ポリマーP1とは異なり且つ少なくとも架橋剤CA1の官能基に対して反応性である架橋性官能基を有するさらなるポリマーとの、部分的又は完全な交換、(b)架橋剤CA1と、架橋剤CA1とは異なり且つ少なくともポリマーP1の架橋性官能基に対して反応性である官能基を有するさらなる架橋剤との、部分的又は完全な交換、(c)ポリマーP1及び/又はさらなるコーティング材料組成物中の(a)で定義したポリマーP1の部分的又は完全な交換に使用されたポリマーP1とは異なるポリマーの量の低下又は増加、(d)架橋剤CA1及び/又はさらなるコーティング材料組成物中の(b)で定義したCA1の部分的又は完全な交換に使用されたCA1とは異なる架橋剤の量の低下又は増加、(e)存在する場合に添加剤A、例えば架橋触媒CLC1と、添加剤Aとは異なるさらなる添加剤、例えば架橋触媒CLC1とは異なる架橋触媒との部分的又は完全な交換、及び(f)存在する場合に添加剤A、例えば架橋触媒CLC1、及び/又はさらなるコーティング材料組成物中の(e)で定義した添加剤A、例えば架橋触媒CLC1の部分的又は完全な交換に使用された添加剤Aとは異なる添加剤、例えばCLC1とは異なる架橋触媒の量の低下又は増加、(g)存在する場合に顔料PI1及び/又はフィラーFI1と、顔料PI1及び/又はフィラーFI1とは異なるさらなる顔料及び/又はフィラーとの部分的又は完全な交換、及び(h)存在する場合に顔料PI1及び/又はフィラーFI1及び/又は存在する場合にさらなるコーティング材料組成物中の(g)で定義した顔料PI1及び/又はフィラーFI1の部分的又は完全に交換に使用された顔料PI1及び/又はフィラーFI1とは異なる顔料の量の低下又は増加、からなる群から選択される。好ましくは、添加剤Aとして、及び添加剤Aとは異なる任意のさらなる添加剤として、架橋触媒が使用される。
第1のコーティング材料組成物F1中に構成成分(i)として存在するポリマーP1の架橋性官能基と、ポリマーP1とは異なり且つ工程(5)、及び任意に、工程(9)で定義した少なくとも1回の繰り返しの後に提供されたさらなるコーティング材料組成物のうちの任意に存在する各ポリマーの架橋性官能基とは、同一であり、好ましくは各場合ともヒドロキシル基及び/又は酸基から選択され、より好ましくは各場合とも少なくとも部分的にヒドロキシル基を表し、そして
第1のコーティング材料組成物F1中に構成成分(ii)として存在する架橋剤CA1の官能基と、架橋剤CA1とは異なり且つ工程(5)、及び任意に、工程(9)で定義した少なくとも1回の繰り返しの後に提供されたさらなるコーティング材料組成物のうちの任意に存在する各架橋剤の官能基とは、同一であり、好ましくは各場合ともイミノ基、アルキロール基、エーテル化アルキロール基、及び任意にブロック化イソシアネート基から選択され、より好ましくは各場合とも少なくとも部分的なエーテル化アルキロール基を表す。
任意の工程(6)において、工程(5)で提供されたさらなるコーティング材料組成物を、基材の少なくとも1つの任意に事前に被覆された表面上に任意に適用して、基材の前記表面上に濡れたコーティングフィルムを形成する。この工程は、濡れたコーティングフィルムの特性を、工程(8)において測定することが意図されている場合に行われる。上記で述べた同じ基材は、上述した同じ従来の適用手段によって工程(6)で使用することができる。
任意に、本発明の方法は、工程(6)の後且つ工程(8)の前に実施される工程(7)をさらに含む。この工程は、部分的に乾燥したコーティングフィルムの特性を、工程(8)において測定することが意図されている場合に行われる。前記工程(7)において、工程(6)の後に得られた濡れたコーティングフィルムを任意に部分的に乾燥させて、部分的に乾燥したコーティングフィルムを基材の表面上に形成する。部分的な乾燥は、好ましくはフラッシュオフにより、好ましくは1~30分の期間、より好ましくは1.5~25分の期間、特に2~20分の期間、最も好ましくは3~15分の期間行う。好ましくは、工程(7)は、100℃を超えない温度、より好ましくは18~80℃の範囲の温度で行う。
工程(8)では、工程(5)で提供されたコーティング材料組成物、及び/又は工程(6)を行った場合は濡れたコーティングフィルム、及び/又は工程(7)を行った場合は部分的に乾燥したコーティングフィルムの少なくとも1つの特性を測定する。少なくとも1つの特性は、工程(4)で測定されたものと同じ特性である。
任意の工程(9)において、工程(5)~(8)が任意に少なくとも1回繰り返され、このようにして提供されたさらなるコーティング組成物の各々は、互いに異なり、そしてコーティング材料組成物F1とは異なる。繰り返しの回数は限定されず、例えば、1~1000回の範囲、又は1~100回の範囲の繰り返しとすることができる。
工程(10)では、工程(4)及び(8)で測定された特性の結果、及び任意に工程(9)で定義した少なくとも1回の繰り返しの場合に測定された特性の結果が、好ましくは電子データベースに組み込まれる。好ましくは、工程(10)は、少なくとも1つのソフトウェアの支持により実行される。データベースは、本発明の方法を実行している間、常に更新することができる。
工程(11)では、組み込み工程(10)により好ましくは電子データベースに存在する測定された特性の少なくとも1つが選択される。
工程(12)において、工程(4)及び(8)により、及び任意に工程(9)で定義した少なくとも1回の繰り返しの後に測定された少なくとも1つの選択された特性の結果を、評価し、そして互いに比較する。好ましくは、これは少なくとも1つのソフトウェアによって実行される。
工程(13)において、評価及び比較工程(12)から得られた情報を、第1のコーティング材料組成物F1、及び工程(5)の後に得られたさらなるコーティング材料組成物の各々、及び工程(9)で定義した少なくとも1回の繰り返しの後に任意に得られた任意の追加のコーティング材料組成物とは異なる、少なくとも1つの新規コーティング配合物を配合及び提供するために使用する。ここで、少なくとも1つの新規コーティング配合物それ自体、及び/又はそれから得られた濡れた又は部分的に乾燥したコーティングフィルムは、工程(4)及び/又は工程(8)で定義した通り測定した場合に、工程(11)で選択された少なくとも1つの特性の改善を示す。
本発明のさらなる主題は、自動車分野における新規コーティング配合物を開発し提供するための本発明の方法の使用であり、前記新規コーティング配合物は、好ましくはベースコート組成物、特に水性ベースコート組成物である。
1. 不揮発性画分の決定
総固形分含量を含む固形分含量(不揮発分、固形画分)は、DIN EN ISO3251:2019-09を介して、110℃、60分間で測定した。
コーティング組成物から得られた濡れたコーティングフィルムのDMA(動的機械分析)IVデルタ測定を用いて、濡れたフィルムのオンセット温度(反応性に対応するE’進行[℃])及びオフセット時間(反応時間に対応する外挿されたもの[分])を測定した。オンセット温度の測定は、周波数1Hz(振幅:0.2%)及び25℃~200℃(2℃/分)の範囲で行った。オフセット時間測定は、周波数1Hz(振幅:0.2%)、及び25℃~120℃(24℃/分)の範囲、及びさらに25℃~120℃(6℃/分)の範囲で63分間(140℃で等温)で行った。次のパラメータを測定した:オンセット温度(E’進行度からのネットワーク構造の外挿されたオンセット温度及びtanδ進行度からのネットワーク構造の外挿されたオンセット温度)、オフセット時間(線形適用におけるE’進行度からのネットワーク構造の外挿されたオフセット時間[分]、70分後及び20分後の貯蔵弾性率の比を決定した。測定はISO11357:2018に準拠して行った。
1.1 いくつかのコーティング組成物(I1、I2及びI3)を調製した。表1aに列挙する構成成分を、当該表に示す順序でディゾルバー中攪拌下で混合して、コーティング組成物を調製した。
2.1 反応性及び反応時間に及ぼすバインダーの影響
コーティング組成物I1~I3の調製に使用したバインダーがオンセット温度及びオフセット時間に及ぼす影響を、「方法」のセクションで上記で特定した方法によるDMA IVデルタ測定によって調査した。結果を表2aにまとめる。
コーティング組成物I4~I6の調製用の触媒の影響を、「方法」のセクションで上記で特定した方法によるDMA IVデルタ測定によって調査した。結果を表2cにまとめる。
Claims (15)
- 自動車分野における新規コーティング配合物を開発するためのコーティング材料組成物をスクリーニングする方法であって、少なくとも工程(1)、(4)、(5)、(8)及び(10)~(13)及び任意の工程(2)、(3)、(6)、(7)及び(9)の少なくとも1つ、すなわち、
(1) 第1のコーティング材料組成物F1を提供する工程であって、
該第1のコーティング材料組成物F1が、
(i) 架橋性官能基を有する、少なくとも1つのフィルム形成ポリマーP1、
(ii) 少なくともポリマーP1の架橋性官能基に対して反応性である官能基を有する、少なくとも1つの架橋剤CA1、
(iii) 水及び/又は少なくとも1つの有機溶媒、
(iv) 任意に、少なくとも1つの相溶化ポリマーPMP、
(v) 任意に、少なくとも1つの添加剤A、及び
(vi) 任意に、少なくとも1つの顔料PI1及び/又は少なくとも1つのフィラーFI1
を含み、
ここで、構成成分(i)、(ii)、(iii)及び(iv)、及び(v)及び(vi)の各々が互いに異なる、提供する工程、
(2) 第1のコーティング材料組成物F1を、基材の少なくとも1つの任意に事前に被覆された表面上に任意に適用して、基材の前記表面上に濡れたコーティングフィルムを形成する工程、
(3) 工程(2)の後に得られた濡れたコーティングフィルムを任意に乾燥させて、基材の表面に部分的に乾燥したコーティングフィルムを形成する工程、
(4) 工程(1)で提供されたコーティング材料組成物、及び/又は工程(2)を行った場合は濡れたコーティングフィルム、及び/又は工程(3)を行った場合は部分的に乾燥したコーティングフィルムの、少なくとも1つの特性を測定する工程、
(5) 第1のコーティング材料組成物F1とは正確に1つ又は多くても2つのパラメータが異なる、少なくとも1つのさらなるコーティング材料組成物を提供する工程であって、
前記パラメータが、(a)ポリマーP1と、ポリマーP1とは異なり且つ少なくとも架橋剤CA1の官能基に対して反応性である架橋性官能基を有するさらなるポリマーとの、部分的又は完全な交換、(b)架橋剤CA1と、架橋剤CA1とは異なり且つ少なくともポリマーP1の架橋性官能基に対して反応性である官能基を有するさらなる架橋剤との、部分的又は完全な交換、(c)ポリマーP1及び/又はさらなるコーティング材料組成物中の(a)で定義したポリマーP1の部分的又は完全な交換に使用されたポリマーP1とは異なるポリマーの量の低下又は増加、(d)架橋剤CA1及び/又はさらなるコーティング材料組成物中の(b)で定義したCA1の部分的又は完全な交換に使用されたCA1とは異なる架橋剤の量の低下又は増加、(e)存在する場合に添加剤A、例えば架橋触媒CLC1と、添加剤Aとは異なるさらなる添加剤、例えば架橋触媒CLC1とは異なる架橋触媒との部分的又は完全な交換、及び(f)存在する場合に添加剤A、及び/又は存在する場合にさらなるコーティング材料組成物中の(e)で定義した添加剤Aの部分的又は完全な交換に使用された添加剤Aとは異なる添加剤の量の低下又は増加、(g)存在する場合に顔料PI1及び/又はフィラーFI1と、顔料PI1及び/又はフィラーFI1とは異なるさらなる顔料及び/又はフィラーとの部分的又は完全な交換、及び(h)存在する場合に顔料PI1及び/又はフィラーFI1及び/又は存在する場合にさらなるコーティング材料組成物中の(g)で定義した顔料PI1及び/又はフィラーFI1の部分的又は完全に交換に使用された顔料PI1及び/又はフィラーFI1とは異なる顔料の量の低下又は増加、からなる群から選択される、提供する工程、
(6) さらなるコーティング材料組成物を、基材の少なくとも1つの任意に事前に被覆された表面に任意に適用して、基材の前記表面上に濡れたコーティングフィルムを形成する工程、
(7) 工程(6)の後に得られた濡れたコーティングフィルムを任意に乾燥させて、基材の表面に部分的に乾燥したコーティングフィルムを形成する工程、
(8) 工程(5)で提供されたコーティング材料組成物、及び/又は工程(6)を行った場合は濡れたコーティングフィルム、及び/又は工程(7)を行った場合は部分的に乾燥したコーティングフィルムの少なくとも1つの特性を測定する工程であって、前記少なくとも1つの特性が工程(4)で測定したものと同じ特性である、測定する工程、
(9) 任意に、工程(5)及び(8)及び任意に工程(6)及び/又は工程(7)を少なくとも1回繰り返す工程であって、提供されたさらなるコーティング組成物の各々が、互いに異なり、そしてコーティング材料組成物F1とは異なる、繰り返す工程、
(10) 工程(4)及び(8)で測定された特性の結果、及び任意に工程(9)で定義した少なくとも1回の繰り返しの場合に測定された特性の結果を、電子データベースに組み込む工程、
(11) 組み込む工程(10)により電子データベースに存在する測定された特性の少なくとも1つを選択する工程、
(12) 工程(4)及び(8)により、及び任意に工程(9)で定義した少なくとも1回の繰り返しの後に測定された少なくとも1つの選択された特性の結果を、評価及び互いに比較する工程、及び
(13) 第1のコーティング材料組成物F1、及び工程(5)の後に得られたさらなるコーティング材料組成物の各々、及び工程(9)で定義した少なくとも1回の繰り返しの後に任意に得られた任意のコーティング材料組成物とは異なる、少なくとも1つの新規コーティング配合物を配合及び提供するために、評価及び比較工程(12)から得られた情報を使用する工程であって、少なくとも1つの新規コーティング配合物それ自体、及び/又はそれから得られた濡れた又は部分的に乾燥したコーティングフィルムが、工程(4)及び/又は(8)で定義した通り測定した場合に、工程(11)で選択された少なくとも1つの特性の改善を示す、使用する工程
を含む、方法。 - 第1のコーティング材料組成物F1中に構成成分(i)として存在するポリマーP1の架橋性官能基と、ポリマーP1とは異なり且つ工程(5)、及び任意に、工程(9)で定義した少なくとも1回の繰り返しの後に提供されたさらなるコーティング材料組成物のうちの任意に存在する各ポリマーの架橋性官能基とが、同一であり、好ましくは各場合ともヒドロキシル基及び/又は酸基から選択され、より好ましくは各場合とも少なくとも部分的にヒドロキシル基を表し、そして
第1のコーティング材料組成物F1中に構成成分(ii)として存在する架橋剤CA1の官能基と、架橋剤CA1とは異なり且つ工程(5)、及び任意に、工程(9)で定義した少なくとも1回の繰り返しの後に提供されたさらなるコーティング材料組成物のうちの任意に存在する各架橋剤の官能基とが、同一であり、好ましくは各場合ともイミノ基、アルキロール基、エーテル化アルキロール基、及び任意にブロック化イソシアネート基から選択され、より好ましくは各場合とも少なくとも部分的にイミノ基、アルキロール基及び/又はエーテル化アルキロール基を表すことを特徴とする、請求項1に記載の方法。 - 第1のコーティング材料組成物F1、及び工程(5)で提供され、そして任意に、工程(9)で定義した少なくとも1回の繰り返しの後に得られた、さらなるコーティング材料組成物のうちの任意が、1成分(1K)又は2成分(2K)コーティング材料組成物であり、好ましくはそれぞれ1成分(1K)コーティング材料組成物であり、より好ましくはベースコート材料組成物として使用するためのものであることを特徴とする、請求項1又は2に記載の方法。
- 第1のコーティング材料組成物F1中に構成成分(ii)として存在する少なくとも1つの架橋剤CA1、及び工程(5)で提供され、そして任意に、工程(9)で定義した少なくとも1回の繰り返しの後に得られた、さらなるコーティング材料組成物のうちの任意に存在する、任意のさらなる少なくとも1つの架橋剤が、メラミンアルデヒド樹脂、好ましくはメラミンホルムアルデヒド樹脂であることを特徴とする、請求項1から3のいずれか一項に記載の方法。
- 第1のコーティング材料組成物F1の構成成分(i)として存在する少なくとも1つのポリマーP1、及び工程(5)で提供され、そして任意に、工程(9)で定義した少なくとも1回の繰り返しの後に得られた、さらなるコーティング材料組成物のうちの任意に存在する、任意のさらなる少なくとも1つのフィルム形成ポリマーが、物理的乾燥性ポリマー、化学的架橋性ポリマー、放射線硬化性ポリマー、及びそれらの混合物からなる群から選択され、好ましくは、物理的乾燥性ポリマー、化学的自己架橋性ポリマー、化学的非自己架橋性ポリマー、放射線硬化性ポリマー、及びそれらの混合物からなる群から選択され、より好ましくは、化学的非自己架橋性ポリマーからなる群から選択されることを特徴とする、請求項1から4のいずれか一項に記載の方法。
- 第1のコーティング材料組成物F1の構成成分(i)として存在する少なくとも1つのポリマーP1、及び工程(5)で提供され、そして任意に、工程(9)で定義した少なくとも1回の繰り返しの後に得られた、さらなるコーティング材料組成物のうちの任意に存在する、任意のさらなる少なくとも1つのフィルム形成ポリマーが、ポリエステル、ポリ(メタ)アクリレート、ポリウレタン、ポリウレア、ポリアミド及びポリエーテルからなる群から選択され、好ましくは、ポリエステル、ポリ(メタ)アクリレート、ポリウレタン及びポリエーテルからなる群から選択されることを特徴とする、請求項1から5のいずれか一項に記載の方法。
- 構成成分(i)~(iii)及び任意に(iv)及び/又は(v)及び/又は(vi)が、第1のコーティング材料組成物F1の唯一の構成成分であることを特徴とする、請求項1から6のいずれか一項に記載の方法。
- 好ましくは構成成分(iii)が少なくとも部分的に水を表す場合、構成成分(iv)が第1のコーティング材料組成物F1中に存在することを特徴とする、請求項1から7のいずれか一項に記載の方法。
- 工程(5)、及び任意に工程(9)で定義した少なくとも1回の繰り返しの間に選択されたパラメータ(複数可)が、コーティング材料組成物の各々の総固形分含量に寄与する、好ましくは、コーティング材料組成物の各々の総バインダー固形分含量に寄与する、少なくとも1つの構成成分の量の、部分的又は完全な交換、及び/又は低下又は増加に関連していることを特徴とする、請求項1から8のいずれか一項に記載の方法。
- 工程(4)及び(8)で測定され、そして任意に工程(9)で定義した少なくとも1回の繰り返しの後に測定され、そして工程(11)で選択された少なくとも1つの特性が、オンセット温度、オフセット時間、収縮率、広がり、表面張力、粘度、特に高せん断粘度及び/又は低せん断粘度、特に粒度分布に関する分散安定性、膨張係数、及びゼータ電位からなる群から、好ましくはオンセット温度及びオフセット時間からなる群から選択される少なくとも1つの特性であることを特徴とする、請求項1から9のいずれか一項に記載の方法。
- 工程(4)及び(8)で測定され、そして任意に工程(9)で定義した少なくとも1回の繰り返しの後に測定され、そして工程(11)で選択された少なくとも1つの特性が、コーティング材料組成物及び/又はそれから得られた濡れた又は部分的に乾燥したコーティングフィルムの少なくとも1つの特性と相関し、好ましくは反応性、反応時間、特に架橋反応時間、外観、色安定性及びフロップ、レベリング、濡れ性、付着性、凝集性、霧化性、貯蔵安定性及びリング循環安定性からなる群から選択される特性の少なくとも1つと相関することを特徴とする、請求項1から10のいずれか一項に記載の方法。
- 評価及び比較工程(12)及び工程(13)が、好ましくは電子データベースに存在する、工程(11)で選択された少なくとも1つの特性のあらゆる結果を利用することを特徴とする、請求項1から12のいずれか一項に記載の方法。
- 工程(13)で提供された少なくとも1つの新規コーティング配合物が、請求項1の工程(5)内で定義されたパラメータの少なくとも1つにおいて、第1のコーティング材料組成物F1とは異なり、そして工程(5)の後に得られたさらなるコーティング材料組成物のうちの任意とも異なり、そして任意に工程(9)で定義した少なくとも1回の繰り返しの後に得られたコーティング材料組成物のうちの任意とも異なることを特徴とする、請求項1から12のいずれか一項に記載の方法。
- 工程(13)で提供された少なくとも1つの新規コーティング配合物それ自体が、工程(4)及び/又は(8)で定義した通り測定した場合に、工程(11)で選択された少なくとも1つの特性、好ましくは請求項10で定義した少なくとも1つの特性の改善を示すだけでなく、コーティング配合物それ自体及び/又はそれから得られた濡れた又は部分的に乾燥したコーティングフィルムの少なくとも1つの特性の改善も示し、前記特性は、好ましくは請求項11で定義した特性であり、且つ前記少なくとも1つの特性と相関することを特徴とする、請求項1から13のいずれか一項に記載の方法。
- 請求項1から14のいずれか一項に記載の方法の使用であって、架橋性官能基を有するフィルム形成ポリマー(i)、及び/又は少なくとも前記ポリマーの前記架橋性官能基に対して反応性である官能基を有する架橋剤(ii)、及び/又は添加剤(v)、好ましくは(i)と(ii)との間の架橋反応を触媒する架橋触媒、及び/又は顔料及び/又はフィラー(vi)が、少なくとも構成成分(i)及び(ii)及び任意に(v)及び/又は(vi)を含有するコーティング材料組成物それ自体、及び/又はそれから得られた濡れた又は部分的に乾燥したコーティングフィルムの特性に及ぼす影響を調査するための、使用。