JP2022513989A - 合金コーティング鋼板およびその製造方法 - Google Patents
合金コーティング鋼板およびその製造方法 Download PDFInfo
- Publication number
- JP2022513989A JP2022513989A JP2021534754A JP2021534754A JP2022513989A JP 2022513989 A JP2022513989 A JP 2022513989A JP 2021534754 A JP2021534754 A JP 2021534754A JP 2021534754 A JP2021534754 A JP 2021534754A JP 2022513989 A JP2022513989 A JP 2022513989A
- Authority
- JP
- Japan
- Prior art keywords
- alloy
- steel sheet
- layer
- coated
- coated steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の一実施形態による合金コーティング鋼板の製造方法は、AlおよびSiを含むメッキ層が形成されたメッキ鋼板を用意する用意段階と、メッキ層上にMgが含まれているMgコーティング層を形成させる第1コーティング段階と、Mgコーティング層上にZnが含まれているZnコーティング層を形成させる第2コーティング段階と、Mgコーティング層およびZnコーティング層が形成されたメッキ鋼板を熱処理してMgおよびZnをメッキ層に拡散させる熱処理段階とを含む。
本発明の一実施形態による合金コーティング鋼板は、図2を参照するとき、鋼板および鋼板上に位置するAl-Mg-Si-Zn合金層を含み、Al-Mg-Si-Zn合金層は、Mg-Zn合金相を含み、Mg-Zn合金相は、MgZn2およびMg2Zn11を含み、MgZn、Mg21Zn25、Mg51Zn20およびMg2Zn3のうちの1種以上をさらに含む。
(1)合金コーティング鋼板の製造
[実施例1]AlおよびSiを含むメッキ層が形成された溶融アルミニウムメッキ鋼板上に、物理気相蒸着(PVD)を用いてMgコーティング層およびZnコーティング層を形成させた後、熱処理温度400℃を基準として300秒間熱処理を施した。Znは熱処理後、生成されたAl-Mg-Si-Zn合金層を基準として1.2重量%であった。
図3は、Zn含有量に応じたコーティング層の組成をグロー放電分光器で分析した結果である。図3(a)はZn含有量が1.2重量%、図3(b)はZn含有量が2.6重量%、図3(c)はZn含有量が7.9重量%であるコーティング鋼板のグロー放電分光分析の結果である。図3に示されているように、熱処理時間400℃で300秒間実施すれば、MgおよびZnの拡散が起きてアルミニウムメッキ層に拡散する。MgおよびZnの拡散深さは約3μmであった。
図5は、Znが含有されないAl-Mg-Si(比較例1)コーティング鋼板と、Znが1.2重量%含有されたAl-Mg-Si-Znコーティング鋼板(実施例1)の塩水噴霧試験の結果を示す。塩水噴霧試験はASTM B-117により実施した。
Claims (13)
- 鋼板;および
前記鋼板上に位置するAl-Mg-Si-Zn合金層;を含み、
前記Al-Mg-Si-Zn合金層は、Mg-Zn合金相を含み、
前記Mg-Zn合金相は、
MgZn2およびMg2Zn11を含み、
MgZn、Mg21Zn25、Mg51Zn20およびMg2Zn3のうちの1種以上をさらに含む合金コーティング鋼板。 - 前記Al-Mg-Si-Zn合金層は、
Al-Mg合金相およびMg-Si合金相のうちの1種以上をさらに含む、請求項1に記載の合金コーティング鋼板。 - 前記Al-Mg-Si-Zn合金層は、
全体100重量%に対して、1~45重量%のZnを含む、請求項1に記載の合金コーティング鋼板。 - 前記Al-Mg-Si-Zn合金層は、
全体100重量%に対して、5~30重量%のMgを含む、請求項1に記載の合金コーティング鋼板。 - 前記Al-Mg-Si-Zn合金層は、
Al-Mg合金相およびMg-Si合金相のうちの1種以上をさらに含む、請求項1に記載の合金コーティング鋼板。 - 前記Al-Mg合金相は、
Al3Mg2およびAl12Mg17のうちの1種以上を含む、請求項5に記載の合金コーティング鋼板。 - 前記Mg-Si合金相は、
Mg2Siを含む、請求項5に記載の合金コーティング鋼板。 - 前記鋼板および前記Al-Mg-Si-Zn合金層の間に位置するAl-Fe-Si合金層;をさらに含む、請求項1に記載の合金コーティング鋼板。
- AlおよびSiを含むメッキ層が形成されたメッキ鋼板を用意する用意段階;
前記メッキ層上にMgが含まれているMgコーティング層を形成させる第1コーティング段階;
前記Mgコーティング層上にZnが含まれているZnコーティング層を形成させる第2コーティング段階;および
前記Mgコーティング層およびZnコーティング層が形成されたメッキ鋼板を熱処理して前記Mgおよび前記Znを前記メッキ層に拡散させる熱処理段階;を含む合金コーティング鋼板の製造方法。 - 前記用意段階において、
前記メッキ鋼板は、溶融アルミニウムメッキ鋼板である、請求項9に記載の合金コーティング鋼板の製造方法。 - 前記第1コーティング段階および前記第2コーティング段階において、
物理気相蒸着(PVD)を用いて前記Mgコーティング層および前記Znコーティング層を形成させる、請求項9に記載の合金コーティング鋼板の製造方法。 - 前記熱処理段階において、
300~450℃の温度で熱処理する、請求項9に記載の合金コーティング鋼板の製造方法。 - 前記熱処理段階において、
5~600秒間熱処理する、請求項9に記載の合金コーティング鋼板の製造方法。