JP2021154682A - チューブ容器用包材およびチューブ容器 - Google Patents
チューブ容器用包材およびチューブ容器 Download PDFInfo
- Publication number
- JP2021154682A JP2021154682A JP2020059765A JP2020059765A JP2021154682A JP 2021154682 A JP2021154682 A JP 2021154682A JP 2020059765 A JP2020059765 A JP 2020059765A JP 2020059765 A JP2020059765 A JP 2020059765A JP 2021154682 A JP2021154682 A JP 2021154682A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- tube container
- resin
- film
- packaging material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
一方、エンボスロールなどによって加圧あるいは熱圧により印刷表面に凹凸のあるマット加工を施す方法があるが、微細な凹凸形状を形成することが難しかった。
1官能性モノマーとしては、例えば、メチルアクリレート、メチルメタクリレート(以下、「メチルアクリレート」と「メチルメタクリレート」とを「(メタ)アクリレート」と表記する。)、エチル(メタ)アクリレート、n−ブチル(メタ)アクリレート、ヘキシル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、ラウリル(メタ)アクリレート、イソボニル(メタ)アクリレート、ジシクロペンテニル(メタ)アクリレート、N−ビニルピロリドン、スチレン等を使用できる。
2官能性モノマーとしては、例えば、エチレングリコールジ(メタ)アクリレート、プロピレングリコールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、トリエチレングリコールジ(メタ)アクリレート、ジプロピレングリコールジ(メタ)アクリレート等を使用できる。
3官能性モノマーとしては、例えば、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、トリス(アクリロキシエチル)イソシアヌレート等を使用できる。
ここで、はじくとは、第二表面層1bの濡れ性が悪く、第一表面層1aの上に第二表面層1bをコーティングできない状態をいう。
更に詳しくは、上記のPVD法においては、酸化アルミニウムからなる蒸着層の厚さは、20〜100nmが好ましく、30〜50nm位がより好ましい。
また、上記のCVD法においては、酸化珪素からなる蒸着層の厚さは、5〜50nmが好ましく、10〜30nmがより好ましい。
なお、上記において、総じて、金属酸化物、無機酸化物からなる蒸着層の場合は、蒸着層の厚さが200nmを超えると、蒸着層にクラック等が入りやすくなり、そりによりバリア性が低下するという危険性があると共に、材料コストが高くなるという問題点であるので好ましくない。また、10nm未満であると、酸素バリア性を奏することが困難になることから好ましくないものである。
樹脂フィルムが、蒸着膜を備える場合、前記バリアコート層は、上記蒸着膜上に設けられていても、蒸着膜下に設けられていてもよい。
また、上記蒸着膜が、無機酸化物から構成される場合、バリアコート層にポリビニルアルコールを含有させることにより、蒸着膜におけるクラックの発生を効果的に防止することができる。
バリアコート層の厚さを0.01μm以上とすることにより、チューブ容器の内容物の酸素バリア性および水蒸気バリア性をより向上することができる。
蒸着膜を支持するフィルムが、無機酸化物から構成される蒸着膜を備える場合、前記の形態のバリアコート層を、蒸着膜と隣接するように設けることにより、蒸着膜におけるクラックの発生を効果的に防止することができる。
R1 nM(OR2)m
(ただし、式中、R1、R2は、それぞれ、炭素数1〜8の有機基を表し、Mは金属原子を表し、nは0以上の整数を表し、mは1以上の整数を表し、n+mはMの原子価を表す。)
また、R1およびR2で表される有機基としては、例えば、メチル基、エチル基、n−プロピル基、i−プロピル基、n−ブチル基およびi−ブチル基などのアルキル基を挙げることができる。
シランカップリング剤としては、既知の有機反応性基含有オルガノアルコキシシランを用いることができるが、特に、エポキシ基を有するオルガノアルコキシシランが好ましい。エポキシ基を有するオルガノアルコキシシランとしては、例えば、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルメチルジエトキシシランおよびβ−(3,4−エポキシシクロヘキシル)エチルトリメトキシシランなどが挙げられる。
バリア性塗布膜における水溶性高分子の含有量を、金属アルコキシド100質量部に対して5質量部以上とすることにより、チューブ容器20の内容物の油分バリア性、酸素バリア性および水蒸気バリア性をより向上することができる。また、バリア性塗布膜における水溶性高分子の含有量を、金属アルコキシド100質量部に対して500質量部以下とすることにより、バリア性塗布膜の製膜性を向上することができる。
バリア性塗布膜の厚さを0.01μm以上とすることにより、チューブ容器20の内容物の酸素バリア性および水蒸気バリア性を向上することができる。また、無機酸化物から構成される蒸着膜と隣接するように設けた場合に、蒸着膜におけるクラックの発生を防止することができる。
ゾルゲル法触媒としては、酸またはアミン系化合物が好適である。アミン系化合物としては、水に実質的に不溶であり、且つ有機溶媒に可溶な第3級アミンが好適であり、例えば、N,N−ジメチルベンジルアミン、トリプロピルアミン、トリブチルアミン、トリペンチルアミンなどが挙げられる。これらの中でも、N,N−ジメチルべンジルアミンが好ましい。
ゾルゲル法触媒は、金属アルコキシド100質量部当り、0.01質量部以上、1.0質量部以下の範囲で使用することが好ましく、0.03質量部以上、0.3質量部以下の範囲で使用することがより好ましい。
ゾルゲル法触媒の使用量を金属アルコキシド100質量部当り、0.01質量部以上とすることにより、その触媒効果を向上することができる。
また、ゾルゲル法触媒の使用量を金属アルコキシド100質量部当り、1.0質量部以下とすることにより、形成されるバリア性塗布膜の厚さを均一にすることができる。
酸としては、硫酸、塩酸、硝酸などの鉱酸、ならびに酢酸、酒石酸などの有機酸が用いられる。酸の使用量は、アルコキシドおよびシランカップリング剤のアルコキシド分(例えばシリケート部分)の総モル量に対して、0.001モル以上、0.05モル以下であることが好ましい。
酸の使用量をアルコキシドおよびシランカップリング剤のアルコキシド分(例えばシリケート部分)の総モル量に対して、0.001モル以上とすることにより、触媒効果を向上することができる。
また、アルコキシドおよびシランカップリング剤のアルコキシド分(例えばシリケート部分)の総モル量に対して、0.05モル以下とすることにより、形成されるガスバリア性塗布膜の厚さを均一にすることができる。
水の含有量をアルコキシドの合計モル量1モルに対して、0.1モル以上とすることにより、本発明のチューブ容器20の内容物の油分バリア性、酸素バリア性および水蒸気バリア性を向上することができる。
また、水の含有量をアルコキシドの合計モル量1モルに対して、100モル以上とすることにより、加水分解反応を速やかに行うことができる。
まず、金属アルコキシド、水溶性高分子、ゾルゲル法触媒、水、有機溶媒および必要に応じてシランカップリング剤などを混合し、組成物を調製する。前記の組成物中では次第に重縮合反応が進行する。
次いで、基材上に、上記従来公知の方法により、上記組成物を塗布、乾燥する。この乾燥により、アルコキシドおよび水溶性高分子(組成物が、シランカップリング剤を含む場合は、シランカップリング剤も)の重縮合反応がさらに進行し、複合ポリマーの層が形成される。
最後に、上記組成物を20〜250℃、好ましくは50〜220℃の温度で、1秒〜10分間加熱することにより、ガスバリア性塗布膜を形成することができる。
K=ρ40×t
ρ:樹脂フィルムの密度
t:樹脂フィルムの厚さ
樹脂フィルムの密度(ρ)は、単位が「g/cm3」の場合の数値であり、樹脂フィルムの厚さ(t)は、単位が「μm」の場合の数値である。
基材層2として二軸延伸ポリエチレンテレフタレート(PET)フィルム(厚さ12μm)、意匠性向上層5としてアルミニウム蒸着膜(50nm)を有する2軸延伸ポリエチレンテレフタレートフィルム(厚さ12μm)、ガスバリア層3としてアルミニウム箔(厚さ10μm)を用いた。
次に、基材層2であるPETフィルムの印刷面側において、接着層8としてドライラミネート接着剤(三井武田ケミカル株式会社製 品名「XA−311/A−3」)を介して、意匠性向上層5となるVM−PETフィルム(厚さ12μm)を貼り合わせた。ここで、「VM−PETフィルム」は、アルミ蒸着層が設けられたPETフィルムをいう。
次に、意匠性向上層5のアルミ蒸着層が形成されていない面側にコロナ処理を施し、アンカーコート(AC)剤(東洋モートン株式会社製 品名「EL510/RT−80」)を塗布した。
次に、アンカーコート塗布面にEC(押出)ラミネーターを使用し、ポリエチレン押出樹脂(20μm)を介して中間層となる低密度ポリエチレン(LDPE)フィルム(厚さ130μm)を貼り合わせた。
次に、基材層の内面側にコロナ処理を施し、アンカーコート剤(DIC株式会社製 品名「AC−Q.ET.」)を塗布した。次に、アンカーコート塗布面にEC(押出)ラミネーターを使用し、接着層8としてエチレン−メタアクリル酸共重合体(EMAA)樹脂(厚さ20μm)を介してガスバリア層3となるアルミニウム箔(厚み10μm)を貼り合わせた。
さらに、アルミニウム箔の内面側に、エチレン−メタクリル酸共重合体(EMAA)樹脂((厚さ35μm)を押出しラミネートし、さらに、このエチレン−メタクリル酸共重合体樹脂面に、EC(押出)ラミネーターを使用し、2工程により内面シーラント層4となる低密度ポリエチレン(LDPE)樹脂層(厚み50μm)を形成した。
次に、印刷層が形成されていない基材層2の外面側にアンカーコート層を形成して、外面シーラント層1となるPE層を2工程の押出しラミネートにより、低密度ポリエチレン(LDPE)樹脂層(厚み60μm)を形成した。
東洋インキ社製 商品名:FD 剥離OPニス M
主成分として、紫外線硬化性モノマー50〜60質量%、合成樹脂10〜20質量%、光重合開始剤1〜20質量%、顔料5〜15質量%、助剤10〜20質量%、を含む混合物
東洋インキ社製、商品名:REXWIN
主成分として、紫外線硬化性樹脂およびモノマー80〜90質量%、光重合開始剤5〜15質量%、合成樹脂1質量%未満、助剤1〜10質量%を含む混合物
基材層2として厚み12μmのバイオマスPETフィルム(東洋紡社製 品名「DE024」)を用いた以外は、実施例1と同様にしてチューブ容器用包材10を得て、チューブ容器20を作製した。なお、チューブ容器用包材10の層構成は以下の通りである。
中間層として、バイオマスポリエチレンフィルム(3層構成)を下記のように設計した。まずは、第1層を構成する樹脂として、100質量部の化石燃料由来の中密度ポリエチレン((株)プライムポリマー社製、商品名:UZ3520L、密度:0.931g/cm3、MFR:2.1g/10分、バイオマス度:0%)を溶融した。
次いで、第2層を構成する樹脂として、70質量部の化石燃料由来の中密度ポリエチレン((株)プライムポリマー社製、商品名:UZ3520L、密度:0.931g/cm3、MFR:2.1g/10分、バイオマス度:0%)と、30質量部のバイオマス由来の直鎖状低密度ポリエチレン(ブラスケム社製、商品名:SLL−118、密度:0.916g/cm3、MFR:1.0g/10分、バイオマス度87%)とを別途溶融した。
次いで、第3層を構成する樹脂として、100質量部の化石燃料由来の中密度ポリエチレン((株)プライムポリマー社製、商品名:UZ3520L、密度:0.931g/cm3、MFR:2.1g/10分、バイオマス度:0%)を別途溶融した。
これらの溶融物を、第1層及び第3層が樹脂フィルムの最外層を構成するように、インフレーション成形にて共押出し、層厚比が1:3:1(第1層:第2層:第3層)の樹脂フィルムを作製した。樹脂フィルムの厚さは130μmであった。第2層の平均密度は0.927g/cm3であり、樹脂フィルムの平均密度は0.928g/cm3であった。樹脂フィルムのバイオマス度は16%であった。実施例3の樹脂フィルムの剛性パラメータ(K)は、6.04であった。
第二表面層1bおよび第一表面層1aを塗布しない以外は、実施例1と同様にしてチューブ容器用包材10を得て、チューブ容器20を作製した。なお、チューブ容器用包材10の層構成は以下の通りである。
上記で得られた実施例1〜3および比較例1における胴部チューブの積層シートに対して、表面の摩擦係数を測定した。その結果を表1に示す。測定機器は、株式会社東洋精機製作所製TR−2を使用し、JIS K−7125に準じて、静止摩擦係数と動摩擦係数の測定を行った。試験回数はn=3、試験速度は100mm/minであった。なお、胴部チューブの積層シートの表面は、同じ材質の組み合せで摩擦係数の測定を行っており、チューブ容器を輸送する際のチューブ同士の擦れを想定している。また、金属面は、チューブ容器の充填・包装作業時の搬送工程において、金属製部品との接触を想定している。摩擦測定に使用した金属面は、ステンレスであり、平面で表面が平滑性のあるミラーの性状をしているものを使用した。
上記で得られた実施例1〜3および比較例1における胴部チューブの積層シートに対して、表面の耐傷性を測定した。その結果を表2に示す。測定機器は、スガ試験機株式会社製 FR−2を使用し、JIS L−0849に準じて学振式摩擦試験を行った。なお、試験を行う際は、下側の試験片台に、短冊状(幅30mm)のチューブ容器の筒状胴部の積層体を固定し、上側の摩擦子に、同じ材質の胴部チューブの積層シートを短冊状(幅30mm)にして取り付けた。胴部チューブの積層シートと金属板との摩擦試験を行う際は、上側の摩擦子に金属板を取り付けて、この摩擦子を摺動させた。今回、学振式摩擦試験に使用した金属板は、ステンレスであり、表面が平滑性のあるミラーの性状をしているものを使用した。また、錘は200gのものを使用した。上記の学振式摩擦試験を100回および300回繰り返した。
胴部チューブの積層シートの表面に生じた傷の本数を目視にて数えた。1つのサンプル当たりの傷の本数が20本以上のものは試験の結果を×(不良)とし、傷の本数が10本以上20本未満のものは結果を△(やや不良)とし、傷の本数が10本未満のものは試験の結果を○(良好)とした。
上記で得られた実施例1〜3における胴部チューブの積層シートを水浸漬直後と24時間水漬のそれぞれを、印字部の表面にセロハンテープを貼り付けた後、セロハンテープを引き剥がし、目視にて剥がれ具合によりインキ密着性を確認した。結果を表3に示す。
インキ剥がれが全体の0%以上、25%以下のものを〇(良好)とし、インキ剥がれが全体の25%を超えるものを×(不良)とした。
1a 第一表面層
1b 第二表面層
2 基材層
2a 印刷層
3 ガスバリア層
4 内面シーラント層
5 意匠性向上層
8 接着層
10 チューブ容器用包材
11,11’ 一対の貼り合わせ端部
20 チューブ容器
20A 包装製品
21 筒状胴部(胴部)
40 頭部部材
71 金型
72 マンドレル
Claims (5)
- 一対の貼り合わせ端部を有するチューブ容器用包材において、
外面から内面に向かって順に配置された外面シーラント層と、基材層と、内面シーラント層とを少なくとも備え、
前記外面シーラント層の外面のうち、少なくとも一部の領域に微細な凹凸部が設けられ、
前記微細な凹凸部は、前記外面シーラント層の外面に第一表面層が部分的に形成され、前記第一表面層の形成されていない領域に紫外線硬化性樹脂を含有する第二表面層が形成され、
前記第二表面層の厚さが、前記第一表面層の厚さより厚いことを特徴とするチューブ容器用包材。 - 前記外面シーラント層の外面のうち、貼り合わせ端部以外の領域に前記微細な凹凸部が設けられている、請求項1記載のチューブ容器用包材。
- 前記基材層に印刷が施されている、請求項1または請求項2に記載のチューブ容器用包材。
- ガスバリア層を更に備えた、請求項1乃至3のいずれかにチューブ容器用包材。
- 請求項1乃至4のいずれかに記載のチューブ容器用包材の対向する端部同士を重ね合わせて互いに接合した筒状胴部と、
前記筒状胴部の一端に接合された頭部部材と、を備えることを特徴とするチューブ容器。