JP2020158372A - 高耐久性グラウト組成物 - Google Patents
高耐久性グラウト組成物 Download PDFInfo
- Publication number
- JP2020158372A JP2020158372A JP2019061963A JP2019061963A JP2020158372A JP 2020158372 A JP2020158372 A JP 2020158372A JP 2019061963 A JP2019061963 A JP 2019061963A JP 2019061963 A JP2019061963 A JP 2019061963A JP 2020158372 A JP2020158372 A JP 2020158372A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- aggregate
- cement
- powder
- grout composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)粒径1.2〜3.0mmの骨材を25〜35質量%、粒径0.6〜1.2mmの骨材を10〜14質量%、粒径0.6mm以下の骨材を20〜30質量%含有し、更に、セメント、減水剤、増粘剤及びポリマーディスパージョンを含有し、骨材セメント比が1:2.6〜3.4であり、液体の質量が粉体質量の10〜12質量%であ、且つポリマーディスパージョンの含有割合が105℃における不揮発性分換算で粉体質量の0.2〜0.8質量%である高耐久性グラウト組成物。
(2)更に、粉体中にフライアッシュを5〜11質量%含有する上記(1)の高耐久性グラウト組成物。
(3)更に、尿素、膨張材、石膏、アルカリ金属硫酸塩から選ばれる1種又は2種以上を含有する上記(1)又は(2)の高耐久性グラウト組成物。
以下に示す使用材料を用い、表1〜表4に示す配合割合で各水準6kgのグラウト組成物を作製した。グラウト組成物の作製方法は、予め粉体(固形物)のセメント、骨材、混和材料を乾式混合しておき、ミキサにより水及び水にポリマーが分散しているポリマーディスパージョンとともに混合することでグラウト組成物(グラウト材)を作製した。作製したグラウト材の品質試験として、以下に示す通り、ポンプ圧送試験、充填性試験、乾燥収縮試験、付着試験、強度試験、モルタル作業性試験、中性化抵抗性試験、及び遮塩性試験を行い、その結果を配合とともに表1〜表4に示した。
・セメント: 普通ポルトランドセメント(太平洋セメント社製)、記号:OPC
・フライアッシュ: 常磐火力産業社製フライアッシュ(JIS II種相当)、記号:FA
・減水剤: ポリカルボン酸系高性能減水剤「NF−200」(製品名)(粉末、太平洋マテリアル社製)、記号:SP
・膨張材: 石灰系膨張材「太平洋N−EX」(製品名)(太平洋マテリアル社製)、記号:EX
・骨材:
(1)骨材1: 珪砂(粒径1.2〜3.0mm、岐阜県土岐産、絶乾状態)、記号:S1
(2)骨材2: 珪砂(粒径0.6〜1.2mm、岐阜県土岐産、絶乾状態)、記号:S2
(3)骨材3: 珪砂(粒径0.15〜0.6mm、愛知県三河産、絶乾状態)、記号:S3
・増粘剤
(1)増粘剤1:水溶性セルロース「マーポローズ90MP-30000」(製品名)(松本油脂社製)、記号:MC
(2)増粘剤2:スターチエーテル「Starvis SE25F」(製品名)(BASF社製)、記号:SE
・アルカリ金属硫酸塩: 硫酸ナトリウム(Na2SO4)、1級試薬、記号:Na2SO4
・石膏: II型無水石膏(CaSO4)、ブレーン比表面積7000cm2/g、記号:CaSO4
・尿素: 尿素(CO(NH2)2)、1級試薬、記号:CO(NH2)2
・ポリマーディスパージョン: スチレン・ブタジエン共重合体合成ゴム(SBR)系ポリマーエマルション、固形分含有率50質量%
・ポンプ圧送試験
スクイズポンプにより内径50mm・長さ80mホースを用いてグラウト材を15分間圧送し、脈動及び詰まりが何れも発生しなかったものを「良好」(記号:○)、それ以外を「問題あり」(記号:×)とした。
・充填性試験
NEXCO試験方法「試験法432−2006」に規定されている「鉄筋背面への充填性試験」により、目視にて空隙を確認した。評価は、鉄筋付近に空隙が見られなかったものを「良好」(記号:○)とし、鉄筋付近に空隙が見られたものを「不良」(記号:×)とした。
・乾燥収縮試験
温度20℃、湿度80%の恒温恒湿槽でモルタルを内径4×4×16cmの型枠に充填し、24時間養生した後脱型・基長し、その後材齢91日まで20℃相対湿度60%で養生し、JIS A112 9−3「モルタル及びコンクリートの長さ変化試験方法」に準じて測定し、長さ変化率を算出し、収縮率を求めた。評価は、収縮率が500μ以下であるものを「良好」(記号:○)、500μを超えるものを「不良」(記号:×)とした。
・付着試験
JIS A 1171に規定される「接着強さ試験」に準拠して材齢28日における付着強さを測定した。評価は、材齢28日における付着強さが、1.0N/mm2以上のものを「良好」(記号:○)とし、それ以外を「不足」(記号:×)とした。
・強度試験
JIS A 1171に規定される「圧縮強さ試験」準拠して材齢28日における圧縮強さを測定した。評価は、材齢28日における圧縮強さが、40N/mm2以上のものを「良好」(記号:○)とし、それ以外を「不足」(記号:×)とした。
・モルタル作業性試験
JIS A 1171に規定される「フロー試験」に準拠してフロー値を測定した。評価は、フロー値が210〜270mmのものを「良好」(記号:○)とし、それ以外を「不良」(記号:×)とした。フロー値が210mm以下の場合は流動性(コンシステンシー)が不足しており充填作業が行い難く、270mmを超える場合は流動性が過剰で材料分離が生じ易くポンプ詰まりも生じ易いという問題がある。
・中性化抵抗性試験
JIS R 5201に準じて作製したモルタル(JISモルタル)との比較するように、JIS A 1153に規定される促進中性化試験を実施した。評価は、材齢91日における中性化深さがJISモルタルの80%以下のものを「良好」(記号:○)、60%以下のものを「優良」(記号:◎)とし、JISモルタルよりも少ないがJISモルタルの80%を超えているものを「不足」(記号:△)、JISモルタルと同じ又は大きき場合を「不良」(記号:×)とした。
・遮塩性試験
JIS R 5201に準じて作製したモルタル(JISモルタル)との比較するように、10%塩化ナトリウム水溶液による浸漬試験を実施し、材齢91日における塩化物イオン浸透深さをJIS A 1171に規定される「塩化物イオン浸透深さ試験」 により測定し、JISモルタルの60%以下のものを「良好」(記号:○)とし、それ以外を「不足」(記号:×)とした。
Claims (3)
- 粒径1.2〜3.0mmの骨材を25〜35質量%、粒径0.6〜1.2mmの骨材を10〜14質量%、粒径0.6mm以下の骨材を20〜30質量%含有し、更に、セメント、減水剤、増粘剤及びポリマーディスパージョンを含有し、骨材セメント比が2.6〜3.4であり、液体の質量が粉体質量の10〜12%であり、且つポリマーディスパージョンの含有割合が105℃における不揮発性分換算で粉体質量の0.2〜0.8質量%である高耐久性グラウト組成物。
- 更に、粉体中にフライアッシュを5〜11質量%含有する請求項1に記載する高耐久性グラウト組成物。
- 更に、尿素、膨張材、石膏、アルカリ金属硫酸塩から選ばれる1種又は2種以上を含有する請求項1又は2の何れかに記載する高耐久性グラウト組成物。