JP2019154385A - 種子用光沢被覆材 - Google Patents
種子用光沢被覆材 Download PDFInfo
- Publication number
- JP2019154385A JP2019154385A JP2018048750A JP2018048750A JP2019154385A JP 2019154385 A JP2019154385 A JP 2019154385A JP 2018048750 A JP2018048750 A JP 2018048750A JP 2018048750 A JP2018048750 A JP 2018048750A JP 2019154385 A JP2019154385 A JP 2019154385A
- Authority
- JP
- Japan
- Prior art keywords
- seeds
- coating material
- seed
- coated
- glossy coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の光沢被覆材は原液のままで使用してもよいし、あるいは種子の種類や加工機によっては適宜希釈して使用してもよい。
本発明の光沢被覆材によって種子を被覆する方法としては、従来公知の加工方法、処理装置を用いることができる。加工方法としては種子との混合、機械的な塗布、噴霧、および浸漬等を使用できる。被覆に用いられる装置としては、例えば流動層乾燥式種子処理装置やroto−stat式種子処理装置等が好適に使用できる。
本発明の光沢被覆材で被覆可能な種子は、特に限定されるものではなく、例えば野菜種子、草花種子、牧草種子、野草種子、穀物種子及び工芸作物種子が挙げられ、詳しくは以下のものが挙げられる。
被覆対象の種子は、本発明の光沢被覆材で被覆される前に、予め、従来公知の方法によって被覆造粒されていてもよい。また、除菌、発芽改良等のための処理が施されていてもよい。あるいはまた、本発明の光沢被覆材によって被覆された後に、被覆造粒や除菌、発芽改良等のための処理が施されてもよい。
光沢被覆材を水で2倍に希釈し、アプリケーターを用いて厚さ50μmとなるように黒色のケント紙(厚み0.5mm、60°鏡面光沢度:4.6)に塗布し一晩乾燥させる。そしてさらに恒温恒湿室に1日静置する。その後、光源:ハロゲン電球、受光絞り:60°、測定角度:60°として、測定装置(デジタル光沢計GM-3D型(村上色彩技術研究所製))を用いて60°鏡面光沢度を測定する。
(光沢被覆材の作製)
75重量部の水にポリビニルアルコール25重量部を懸濁させ、95℃に加熱して溶解させ、濃度25%のポリビニルアルコール水溶液を得た。
また、1Lのビーカーに水26.4重量部を入れ、撹拌しながら非イオン系界面活性剤1.3重量部、陰イオン系界面活性剤0.3重量部を添加した。次いで、タルク(平均粒子径10μm)10重量部、酸化チタンで表面修飾された雲母(以下、「表面修飾雲母」と記すことがある。)(平均粒子径25μm)20重量部をさらに添加して10分間撹拌した。次に、前記作製した濃度25%のポリビニルアルコール水溶液を20重量部、エチレン酢酸ビニル共重合体の50%エマルジョンを4.0重量部、顔料としての水系分散体(フタロシアン系青色)18重量部を添加し、約30分間撹拌した。なお、すべての混合は室温で実施した。得られた光沢被覆材の沈殿性、再分散性及び60°鏡面光沢度を後述の方法で評価した。評価結果を表1に示す。
得られた光沢被覆材15mLに水10mLを加えて希釈液を作製した。そして、roto−stat式種子処理装置を用いてキャベツ種子200gを希釈液8mLで被覆した。
処理装置の内壁等への光沢被覆材の付着状態(加工性)を後述の方法で評価した。また、得られた被覆種子の外観(着色状態)、被覆層の種子からの剥離性、光沢感について後述の方法で評価した。評価結果を表1に合わせて示す。
(発芽試験)
ろ紙2枚を敷いた直径9cmのシャーレを用意し、そこに水4.5mLを滴下した後、被覆種子50粒をそれぞれ置床し、温度20℃で約2000ルクスの光条件下で保存して7日目の発芽率(%)を測定した。被覆種子の発芽率は、被覆していない種子の被覆率を同等であった。
水を27.1重量部、濃度25%のポリビニルアルコール水溶液を20重量部、エチレン酢酸ビニル共重合体の50%エマルジョンを3.3重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を28.9重量部、濃度25%のポリビニルアルコール水溶液を16重量部、エチレン酢酸ビニル共重合体の50%エマルジョンを5.5重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を26.9重量部、濃度25%のポリビニルアルコール水溶液を16重量部、エチレン酢酸ビニル共重合体の50%エマルジョンを7.5重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を28.4重量部、濃度25%のポリビニルアルコール水溶液を12重量部、エチレン酢酸ビニル共重合体の50%エマルジョンを10重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を26.4重量部、タルク(平均粒子径10μm)を6.7重量部、表面修飾雲母(平均粒子径25μm)を23.3重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を26.4重量部、タルク(平均粒子径10μm)を7.5重量部、表面修飾雲母(平均粒子径25μm)を22.5重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を26.4重量部、タルク(平均粒子径10μm)を15重量部、表面修飾雲母(平均粒子径25μm)を15重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を23.1重量部、表面修飾雲母(平均粒子径25μm)を22.3重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を33.1重量部、表面修飾雲母(平均粒子径25μm)を13.3重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を27.9重量部、濃度25%のポリビニルアルコール水溶液を20重量部、エチレン酢酸ビニル共重合体の50%エマルジョンを2.5重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
タルク(平均粒子径10μm)を5重量部、表面修飾雲母(平均粒子径25μm)を25重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
タルク(平均粒子径10μm)を20重量部、表面修飾雲母(平均粒子径25μm)を10重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
水を39.8重量部、表面修飾雲母(平均粒子径25μm)を6.6重量部とした以外は実施例1と同様にして光沢被覆材を作製し、そして作製した光沢被覆材で種子を被覆した。光沢被覆材の沈殿性、再分散性、60°鏡面光沢度、加工性、被覆種子の外観、被覆層の剥離性及び光沢感を実施例1と同様にして評価した。評価結果を表1に合わせて示す。
実施例1で作製した光沢被覆材20mLに水20mLを加えて希釈液を作製した。roto−stat式種子処理装置を用いて、トマト種子200gを希釈液32mLで被覆した。得られた被覆種子の外観、剥離性及び光沢感について下記の方法で評価した。評価結果を表3に示す。また、得られた被覆種子の発芽率を下記の方法で測定した。測定結果を表3に合わせて示す。
(発芽試験)
ろ紙2枚を敷いた直径9cmのシャーレを用意し、そこに水4.5mLを滴下した後、被覆種子50粒をそれぞれ置床し、温度20℃で約2000ルクスの光条件下で保存して7日目の発芽率(%)を測定した。
実施例11と同様にしてホウレンソウ種子200gを希釈液16mLで被覆した。
得られた被覆種子の外観、剥離性及び光沢感について下記の方法で測定した。評価結果を表3に示す。また、得られた被覆種子の発芽率を下記の方法で測定した。測定結果を表3に合わせて示す。
(発芽試験)
長さ60cm、2.5cm幅で蛇腹状に折ったろ紙に5粒×10列になるように被覆種子を挟み込み、そこに水15mLを滴下した後、温度25℃で約2000ルクスの光条件下で保存して7日目の発芽率(%)を測定した。
実施例11と同様にしてカボチャ種子200gを、希釈液16mLで被覆した。
得られた被覆種子の外観、剥離性及び光沢感について下記の方法で測定した。評価結果を表3に示す。また、得られた被覆種子の発芽率を下記の方法で測定した。測定結果を表3に合わせて示す。
(発芽試験)
長さ60cm、2.5cm幅で蛇腹状に折ったろ紙に1粒×5列、2粒×5列を交互となるように種子を挟み込み、そこに水15mLを滴下した後、温度25℃で約900ルクスの光条件下で保存して7日目の発芽率(%)を測定した。
実施例11と同様にしてメロン種子200gを、希釈液16mLで被覆した。
得られた被覆種子の外観、剥離性及び光沢感について下記の方法で測定した。
評価結果を表3に示す。また、得られた被覆種子の発芽率を下記の方法で測定した。測定結果を表3に合わせて示す。
(発芽試験)
長さ60cm、2.5cm幅で蛇腹状に折ったろ紙に2粒×5列、3粒×5列を交互となるように種子を挟み込み、そこに水15mLを滴下した後、温度25℃で約900ルクスの光条件下で保存して7日目の発芽率(%)を測定した。
実施例11と同様にしてエダマメ種子200gを、希釈液16mLで被覆した。
得られた被覆種子の外観、剥離性及び光沢感について下記の方法で測定した。
評価結果を表3に示す。また、得られた被覆種子の発芽率を下記の方法で測定した。測定結果を表3に合わせて示す。
(発芽試験)
長さ60cm、2.5cm幅で蛇腹状に折ったろ紙に2粒×10列になるように種子を挟み込み、そこに水15mLを滴下した後、温度25℃で約2000ルクスの光条件下で保存して7日目の発芽率(%)を測定した。
光沢被覆材10mLを15mLの試験管に入れ、14日間静置後に目視によって下記基準で評価した。
「○」:沈殿分離なし。
「△」:不明瞭ながら沈殿層あり。
「×」:沈殿層あり。
沈殿層の有無の評価試験において沈殿層が形成された光沢被覆材について、試験管を上下に5回撹拌し目視によって再分散性を下記基準で評価した。
「○」:容易に再分散できる。
「△」:撹拌によって概ね再分散できる。
「×」:撹拌しても再分散できない。
光沢被覆材を水で2倍に希釈し、アプリケーターを用いて厚さ50μmとなるように黒色のケント紙(厚み0.5mm、60°鏡面光沢度:4.6)に塗布し一晩乾燥させる。そしてさらに恒温恒湿室に1日静置する。その後、光源:ハロゲン電球、受光絞り:60°、測定角度:60°として、測定装置(デジタル光沢計GM-3D型(村上色彩技術研究所製))を用いて60°鏡面光沢度を測定する。
処理装置の内壁等への光沢被覆材の付着状態を目視により下記基準で評価した。
「○」:全く付着なし。
「△」:わずかに付着あり。
「×」:大量に付着あり。
被覆種子の外観(着色状態)を目視により下記基準で評価した。
「○」:着色良好。
「△」:着色にややくすみ有り。
「×」:着色が不十分。
被覆種子5gを50mLスチロール棒瓶に封入し、30分振盪した後、剥離状態を目視によって下記基準で評価した。
「○」:まったく剥離なし。
「△」:わずかに剥離あり。
「×」:大量の剥離あり。
被覆種子の光沢感を目視により下記基準で評価した。
「○」:光沢感が良好。
「△」:光沢感やや良好
「×」:光沢感が不十分。
Claims (6)
- 光輝材、タルク、ポリビニルアルコール、エチレン・酢酸ビニル共重合体及び水媒体を含む水懸濁性の種子用光沢被覆材であって、
種子用光沢被覆材における光輝材の含有量が10質量%以上30質量%以下であり、
光輝材:タルクの質量比率が3.5:1〜1:1であり、
ポリビニルアルコール:エチレン・酢酸ビニル共重合体の質量比率が3:1〜0.5:1であることを特徴とする水懸濁性の種子用光沢被覆材。 - 水で2倍に希釈し平板に塗布して測定されるJIS Z8741に準拠した60°鏡面光沢度が6以上である請求項1記載の記載の種子用光沢被覆材。
- 前記光輝材が、表面修飾された雲母、表面修飾されたガラス片、天然パールエッセンス、金属粉からなる群から選択される少なくとも一つである請求項1又は2記載の種子用光沢被覆材。
- 前記光輝材の質量平均粒子径が0.1μm以上100μm以下である請求項1〜3のいずれかに記載の種子用光沢被覆材。
- タルクの質量平均粒子径が0.1μm以上20μm以下である請求項1〜4のいずれかに種子用光沢被覆材。
- 請求項1〜5のいずれかに記載の種子用光沢被覆材で表面が被覆されていることを特徴とする種子。