JP2018158960A - 粘着付与樹脂エマルジョン及び水系粘・接着剤組成物 - Google Patents
粘着付与樹脂エマルジョン及び水系粘・接着剤組成物 Download PDFInfo
- Publication number
- JP2018158960A JP2018158960A JP2017055315A JP2017055315A JP2018158960A JP 2018158960 A JP2018158960 A JP 2018158960A JP 2017055315 A JP2017055315 A JP 2017055315A JP 2017055315 A JP2017055315 A JP 2017055315A JP 2018158960 A JP2018158960 A JP 2018158960A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- component
- resin emulsion
- softening point
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
JIS K 2531の環球法により測定した。
(C)成分の重量平均分子量(Mw)はゲルパーミエーションクロマトグラフィー(GPC)法により、標準ポリスチレンの検量線から求めた、ポリスチレン換算値として算出した。なお、GPC法は以下の条件で測定した。
分析装置:HLC−8120(東ソー(株)製)
カラム:TSKgelSuperHM−L×3本
溶離液:テトラヒドロフラン
注入試料濃度:5mg/mL
流量:0.6mL/min
注入量:100μL
カラム温度:40℃
検出器:RI
撹拌機、冷却管、温度計および窒素導入管を備えた反応装置に、重合ロジン(樹脂酸ダイマー65%、酸価145mgKOH/g、軟化点140℃)100部、ペンタエリスリトール13部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で14時間反応させ、エステル化を完了させた。その後、0.1MPaの水蒸気を4時間吹き込み、重合ロジンエステル1を得た。得られた重合ロジンエステル1の軟化点を表1に示す(以下同様)。
製造例1−1と同様の反応装置に、重合ロジン(製造例1−1と同一のもの)100部、ペンタエリスリトール14部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、0.1MPaの水蒸気を3時間吹き込み、重合ロジンエステル2を得た。
製造例1−1と同様の反応装置に、重合ロジン(製造例1−1と同一のもの)75部、ガムロジン25部(酸価160mgKOH/g、軟化点70℃)、ペンタエリスリトール12部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、0.1MPaの水蒸気を3時間吹き込み、重合ロジンエステル3を得た。
製造例1−1と同様の反応装置に、重合ロジン(製造例1−1と同一のもの)50部、ガムロジン50部(製造例1−3と同一のもの)、ペンタエリスリトール12部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、0.1MPaの水蒸気を3時間吹き込み、重合ロジンエステル4を得た。
製造例1−1と同様の反応装置に、重合ロジン(製造例1−1と同一のもの)100部、ペンタエリスリトール14部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、0.1MPaの水蒸気を6時間吹き込み、比較用重合ロジンエステル1を得た。
製造例1−1と同様の反応装置に、重合ロジン(製造例1−1と同一のもの)25部、ガムロジン75部(製造例1−3と同一のもの)、ペンタエリスリトール12部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、0.1MPaの水蒸気を3時間吹き込み、比較用重合ロジンエステル2を得た。
製造例1−1と同様の反応装置に、不均化ロジン(酸価160mgKOH/g、軟化点75℃)100部、グリセリン12部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、減圧下に水分等を除去し、不均化ロジンエステル1を得た。
製造例1−1と同様の反応装置に、不均化ロジン(比較製造例1と同一のもの)100部、ペンタエリスリトール12部を仕込んだ後、窒素ガス気流下に250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、減圧下に水分等を除去し、不均化ロジンエステル2を得た。
製造例1−1と同様の反応装置に、ガムロジン(酸価160mgKOH/g、軟化点70℃)100部、フマル酸を1部仕込んだ後、窒素ガス気流下に系内温度が220℃となるまで加熱し、1時間反応させた。その後、ペンタエリスリトール13部を仕込んだ後、250℃で2時間反応させた後、さらに280℃まで昇温し同温度で12時間反応させ、エステル化を完了させた。その後、減圧下に水分等を除去し、ガムロジンエステルを得た。
窒素ガス導入管、温度計、還流冷却器および攪拌装置を備えた四つ口フラスコに、アクリル酸30部、メタクリル酸メチル12部、ポリオキシエチレンフェニルエーテル系の反応性乳化剤(商品名「アクアロンRN−20」、第一工業製薬(株)製)30部(固形分換算)、スチレンスルホン酸ソーダ15部、およびスチレン13部を仕込み、更にイオン交換水10部を加えて単量体水溶液とした。次いで該単量体水溶液に、2,4−ジフェニル−4−メチル−1−ペンテンを10部、過硫酸アンモニウム2.4部、イオン交換水72部を添加した。次いで、反応系を85℃まで昇温してから2時間保持し、ラジカル重合反応を行った。次いで、反応系に過硫酸アンモニウムを1部を添加し、更に1時間保温した。その後、反応系に48%水酸化ナトリウム水溶液を18部添加してからよく攪拌し、常温まで冷却した。こうして、固形分21.0%、重量平均分子量15,000の共重合体(C−1)の水溶液を得た。
製造例2−1と同様の反応装置に、アクリル酸30部、メタクリル酸メチル12部、ポリオキシエチレンフェニルエーテル系の反応性乳化剤(商品名「アクアロンRN−20」、第一工業製薬(株)製)30部(固形分換算)、スチレンスルホン酸ソーダ15部、およびスチレン13部を仕込み、更にイオン交換水10部を加えて単量体水溶液とした。次いで該単量体水溶液に、2,4−ジフェニル−4−メチル−1−ペンテンを15部、過硫酸アンモニウム2.4部、イオン交換水72部を添加した。次いで、反応系を85℃まで昇温してから2時間保持し、ラジカル重合反応を行った。次いで、反応系に過硫酸アンモニウムを1部を添加し、更に1時間保温した。その後、反応系に48%水酸化ナトリウム水溶液を18部添加してからよく攪拌し、常温まで冷却した。こうして、固形分21.0%、重量平均分子量10,000の共重合体(C−2)の水溶液を得た。
撹拌機、冷却管、温度計および滴下ロートを備えた容器に重合ロジンエステル1を100部、トルエンを70部仕込み、80℃にて3時間かけて溶解させた後、乳化剤C−1を5部(固形分換算)および水140部を添加し、1時間攪拌した。次いで、高圧乳化機(マントンガウリン社製)により400kg/cm2の圧力で高圧乳化して乳化物を得た。次いで、70℃、2.93×10−2MPaの条件下に6時間減圧蒸留を行い、固形分50%の粘着付与樹脂エマルジョン(A−1)を得た。
撹拌機、冷却管、温度計および滴下ロートを備えた容器に、C9系石油樹脂(商品名「日石ネオポリマー140」、JX日鉱日石エネルギー(株)製、軟化点140℃)100部を仕込み、トルエン70部に80℃にて3時間かけて溶解させた後、乳化剤C−1を5部(固形分換算)および水140部を添加し、1時間攪拌した。次いで、高圧乳化機(マントンガウリン社製)により400kg/cm2の圧力で高圧乳化して乳化物を得た。次いで、70℃、2.93×10−2MPaの条件下に6時間減圧蒸留を行い、固形分50%の粘着付与樹脂エマルジョン(B−1)を得た。
撹拌機、冷却管、温度計および滴下ロートを備えた容器に、重合ロジンエステル1を60部及びC9系石油樹脂(商品名「日石ネオポリマー140」、JX日鉱日石エネルギー(株)製、軟化点140℃)を40部仕込み、トルエン70部に80℃にて3時間かけて溶解させた後、乳化剤C−1を5部(固形分換算)および水140部を添加し、1時間攪拌した。次いで、高圧乳化機(マントンガウリン社製)により400kg/cm2の圧力で高圧乳化して乳化物を得た。次いで、70℃、2.93×10−2MPaの条件下に6時間減圧蒸留を行い、固形分50%の粘着付与樹脂エマルジョン(AB−1)を得た。
<(A)成分>
重合ロジンエステル1:製造例1−1を参照(軟化点180℃)
重合ロジンエステル2:製造例1−2を参照(軟化点160℃)
重合ロジンエステル3:製造例1−3を参照(軟化点135℃)
重合ロジンエステル4:製造例1−4を参照(軟化点125℃)
<(D)成分>
比較用重合ロジンエステル1:比較製造例1−1を参照(軟化点190℃)
比較用重合ロジンエステル2:比較製造例1−2を参照(軟化点115℃)
不均化ロジンエステル1:比較製造例1−3を参照(軟化点115℃)
不均化ロジンエステル2:比較製造例1−4を参照(軟化点125℃)
ガムロジンエステル:比較製造例1−5を参照(軟化点100℃)
<(B)成分>
C9系石油樹脂1:商品名「日石ネオポリマー140」、JX日鉱日石エネルギー(株)製(軟化点140℃)
C9系石油樹脂2:商品名「日石ネオポリマー120」、JX日鉱日石エネルギー(株)製(軟化点120℃)
<(E)成分>
C5/C9系石油樹脂:商品名「クイントンU−185」、日本ゼオン(株)製(軟化点85℃)
C5系石油樹脂:商品名「クイントンR−100」、日本ゼオン(株)製(軟化点100℃)
水素化C9石油樹脂:商品名「アルコンM−100」、荒川化学工業(株)製(軟化点100℃)
テルペン系石油樹脂:商品名「YSレジンPX−1000」、ヤスハラケミカル(株)製(軟化点100℃)
C−1:製造例3−1を参照(重量平均分子量15,000)
C−2:製造例3−2を参照(重量平均分子量10,000)
C−3:商品名「ネオハイテノールF−13」、第一工業製薬(株)製、重量平均分子量5,000)
実施例1
(A−1)成分60部と(B−1)成分40部とを配合し、粘着付与樹脂エマルジョンを得た。
表2に示す組成で配合し、粘着付与樹脂エマルジョンをそれぞれ得た。
撹拌装置、温度計、還流冷却管、滴下ロート及び窒素導入管を備えた反応容器に、窒素ガス気流下、水43.4部及びポリオキシエチレンアルキルエーテル硫酸エステルアンモニウム塩(アニオン性乳化剤:商品名「ハイテノールLA−16」,第一工業製薬(株)製)0.92部からなる水溶液を仕込み、70℃に昇温した。次いで、アクリル酸ブチル90部、アクリル酸2−エチルヘキシル7部及びアクリル酸3部からなる混合物と、過硫酸カリウム(重合開始剤)0.24部、重曹(pH調整剤)0.11部及び水8.83部からなる開始剤水溶液の1/10量を反応容器に添加し、窒素ガス気流下にて70℃、30分間予備重合反応を行った。次いで、上記混合物と上記開始剤水溶液の残りの9/10量を2時間にわたり反応容器に添加して乳化重合を行い、その後70℃で1時間保持して重合反応を完結させた。こうして得られたアクリル系重合体エマルジョンを室温まで冷却した後100メッシュ金網を用いてろ過し、固形分47.8%のアクリル系重合体エマルジョンを得た。
前記アクリル系重合体エマルジョン100部(固形分換算)と、実施例1の粘着付与樹脂エマルジョン10部(固形分換算)とを混合し、水系粘・接着剤組成物を得た。また実施例2〜13及び比較例1〜9の粘着付与樹脂エマルジョンでも同様に行い、水系粘・接着剤組成物を得た。
評価例1の水系粘・接着剤組成物をポリエステルフィルム(商品名「S−100」、三菱化学ポリエステルフィルム(株)製)厚み:38μm)に、サイコロ型アプリケーター(大佑機材(株)製)にて乾燥膜厚が35μm程度となるように塗布し、次いで105℃の循風乾燥機で5分間乾燥させて試料テープを作成した。評価例2〜13、比較評価例1〜9の水系粘・接着剤組成物についても、同様に塗布し、試料テープをそれぞれ作製した。
分光光度計((株)日立製作所製、商品名「U−3210形自記分光光度計」)を用い、試料テープに500nmの光を照射し、透過率(%)を測定した。結果を表2に示す(以下同様)
試料テープ(巾20mm×長さ28mm)を直径が12mmのポリプロピレン製円柱に屈曲して貼り付け、40℃で3日間後のテープの浮き(mm)を測定した。
試料テープ(巾25mm×長さ150mm)をポリプロピレン板に2kgのローラーで2往復させて貼り合せ、テープ末端に200gの荷重をかけ、90°剥離となるように固定し、23℃で1時間あたりの剥離距離(mm)を測定した。
Claims (6)
- 軟化点120〜180℃の重合ロジン誘導体(A)、芳香族系石油樹脂(B)及び乳化剤(C)
を含有する粘着付与樹脂エマルジョン。 - (A)成分が、重合ロジンエステルを含む請求項1の粘着付与樹脂エマルジョン。
- (B)成分の軟化点が、80〜160℃である請求項1又は2の粘着付与樹脂エマルジョン。
- (A)成分と(B)成分との含有割合が、固形分換算で(A)/(B)=60/40〜99/1である、請求項1〜3のいずれかの粘着付与樹脂エマルジョン。
- (C)成分が高分子量乳化剤を含む請求項1〜4のいずれかの粘着付与樹脂エマルジョン。
- 請求項1〜5のいずれかの粘着付与樹脂エマルジョンと、アクリル系重合体エマルジョンとを含有する水系粘・接着剤組成物。