JP2018087186A - 化粧料用被膜の製造方法 - Google Patents
化粧料用被膜の製造方法 Download PDFInfo
- Publication number
- JP2018087186A JP2018087186A JP2017224826A JP2017224826A JP2018087186A JP 2018087186 A JP2018087186 A JP 2018087186A JP 2017224826 A JP2017224826 A JP 2017224826A JP 2017224826 A JP2017224826 A JP 2017224826A JP 2018087186 A JP2018087186 A JP 2018087186A
- Authority
- JP
- Japan
- Prior art keywords
- skin
- film
- cosmetic
- mass
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】20℃で固体状の油を少なくとも10質量%以上含有する化粧料を皮膚に施す化粧料適用工程と、皮膚に組成物を直接に静電スプレーして被膜を形成する静電プレー工程とを具備する。前記組成物が、以下の成分(a)及び成分(b)を含む。(a)水、アルコール及びケトンからなる群より選択される1種以上の揮発性物質。(b)被膜形成能を有するポリマー。
【選択図】図2
Description
20℃で固体状の油を少なくとも10質量%以上含有する化粧料を皮膚に施す化粧料適用工程と、皮膚に組成物を直接に静電スプレーして被膜を形成する静電スプレー工程とを具備し、
前記組成物が、以下の成分(a)及び成分(b)を含む、化粧料用被膜の製造方法に関するものである。
(a)水、アルコール及びケトンからなる群より選択される1種又は2種以上の揮発性物質。
(b)被膜形成能を有するポリマー。
[静電スプレー法により塗布する組成物]
本発明においては、所定の成分を含む組成物を皮膚に直接施して化粧料用被膜(以下、被膜ともいう。)を形成する。被膜の形成方法として、本発明では静電スプレー法を採用している。静電スプレー法は、組成物に正又は負の高電圧を印加して該組成物を帯電させ、帯電した該組成物を対象物に向けて噴霧する方法である。噴霧された組成物はクーロン反発力によって微細化を繰り返しながら空間に広がり、その過程で、又は対象物に付着した後に、揮発性物質である溶媒が乾燥することで、対象物の表面に被膜を形成する。
(a)水、アルコール及びケトンから選ばれる1種又は2種以上の揮発性物質。
(b)被膜形成能を有するポリマー。
以下、各組成物について説明する。
すなわち、前述の化粧料適用工程は、静電スプレー以外の方法で行われる。静電スプレー工程の前に、静電スプレー以外の方法で化粧料を施すことで、上述の効果を発現できる。
すなわち、静電スプレー工程において繊維の堆積物からなる多孔性被膜を形成する工程の前に、20℃で固体状の油を少なくとも10質量%以上含有する化粧料の化粧料適用工程を静電スプレー以外の方法で行うことにより、前記課題が達成できる。
本発明において、化粧料適用工程において用いられる化粧料は、20℃で固体状の油を少なくとも10質量%以上含有するものである。本発明において、20℃で固体状の油とは、示査走査熱容量測定装置(Differential scanning calorimetry:DSC)により、20℃以上に融解ピークが観察される油である。固体の試料が融解する場合、融解熱として基準物質より多くの熱エネルギーが吸収されるため、固体から液体への状態変化を示す融解ピークが認められる。本発明においては、当該ピークが20℃以上に認められる油を、20℃で固体状の油として定義する。具体的な測定方法は実施例に記載される方法による。
すなわち、静電スプレー法として前述の構成を採用し、静電スプレー法以外の方法で予め皮膚に塗布する化粧料として、20℃で固体状の油を少なくとも10質量%以上含有させることで、被膜の密着性を高めることができるだけでなく、被膜に覆われた化粧料の耐水性を高め、べたつき感のない化粧料用被膜が形成できるという驚くべき効果を奏することが本発明者によって見出された。
トリグリセライド類としては、例えばトリ(カプリル・カプリン・ミリスチン・ステアリン酸)グリセリド等が挙げられる。これらのトリグリセライド類は、硬化油等の部分的に水素添加されたものであっても構わない。
セラミド類としては、例えば天然セラミド及び擬似セラミドが挙げられる。天然セラミドとしては、例えばスフィンゴシン、ジヒドロスフィンゴシン、フィトスフィンゴシン、及びスフィンガジエニンがアミド化されたセラミドType1〜7が挙げられる。擬似セラミドとしては、例えば特開2013−53146号公報記載のセラミド類が挙げられる。
高級脂肪酸としては炭素数12〜22の直鎖脂肪酸が挙げられる。例えば、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、及びベヘニン酸等が挙げられる。
すなわち、20℃で固体状の油を少なくとも10質量%以上含有する化粧料を、静電スプレー以外の方法で皮膚に施すには種々の方法を用いることができる。例えば、滴下や振りかけ等の方法によって化粧料を皮膚に施し、該化粧料を塗り広げて塗膜を形成する工程を備えることにより、皮膚になじませることで、該化粧料の薄層を形成することができる。化粧料を単に滴下したり振りかけたりしただけでもよいが、塗り広げて塗膜を形成する工程を備えることにより、皮膚になじませることが可能となり、被膜の密着性を十分に向上させることができる。滴下や振りかけを行わずに、化粧料を直接皮膚に塗布して塗膜を形成してもよい。滴下や振りかけを行うか行わないかを問わず、化粧料を皮膚に塗布して塗膜を形成する工程は、例えば使用者本人の指や、アプリケータ等の道具を用いた擦過等の方法を採用することができる。
また、化粧料を皮膚に施す量は、皮膚と被膜の密着性を向上させる観点、及び透明性を向上させる観点から、好ましくは5g/m2以上であり、より好ましくは10g/m2以上であり、更に好ましくは15g/m2以上であり、好ましくは50g/m2以下であり、より好ましくは45g/m2以下となるような量である。
更に、前記化粧料を皮膚に塗布する前、又はその後に、前記化粧料以外の化粧料を皮膚に施してもよい。
皮膚の表面に被膜を形成する化粧料用被膜の製造方法であって、
20℃で固体状の油を少なくとも10質量%以上含有する固体状化粧料を皮膚に施す化粧料適用工程と、皮膚に組成物を直接に静電スプレーして被膜を形成する静電スプレー工程とを具備し、
前記組成物が、以下の成分(a)及び成分(b)を含む、化粧料用被膜の製造方法。
(a)水、アルコール及びケトンからなる群より選択される1種又は2種以上の揮発性物質。
(b)被膜形成能を有するポリマー。
<2>
皮膚の表面に被膜を形成する化粧料用被膜の製造方法であって、
20℃で固体状の油を少なくとも10質量%以上含有する固体状化粧料を、静電スプレー以外の方法で皮膚に施す化粧料適用工程と、皮膚に組成物を直接に静電スプレーして被膜を形成する静電スプレー工程とを具備し、
前記組成物が、以下の成分(a)及び成分(b)を含む、化粧料用被膜の製造方法。
(a)水、アルコール及びケトンからなる群より選択される1種又は2種以上の揮発性物質。
(b)被膜形成能を有するポリマー。
<3>
前記静電スプレー工程において、皮膚に前記組成物を静電スプレーして多孔性被膜を形成する前記<1>又は<2>に記載の化粧料用被膜の製造方法。
<4>
前記静電スプレー工程において、静電スプレー装置を用いて皮膚に前記組成物を静電スプレーして、繊維の堆積物からなる多孔性被膜を形成し、前記静電スプレー装置が、
前記組成物を収容する容器と、
前記組成物を吐出するノズルと、
前記容器中に収容されている前記組成物を前記ノズルに供給する供給装置と、
前記ノズルに電圧を印加する電源と、
を備える前記<1>ないし<3>のいずれか1に記載の化粧料用被膜の製造方法。
<5>
(a)の揮発性物質はその蒸気圧が20℃において0.01kPa以上、106.66kPa以下であることが好ましく、0.13kPa以上、66.66kPa以下であることがより好ましく、0.67kPa以上、40.00kPa以下であることが更に好ましく、1.33kPa以上、40.00kPa以下であることがより一層好ましい前記<1>ないし<4>のいずれか1に記載の化粧料用被膜の製造方法。
<6>
(a)の揮発性物質がアルコールであり、該アルコールとして一価の鎖式脂肪族アルコール、一価の環式脂肪族アルコール、及び一価の芳香族アルコールが好適に用いられ、これらのアルコールは1種を単独で、又は2種以上を組み合わせて用いることができ、
前記アルコールとして、エタノール、イソプロピルアルコール、ブチルアルコール、フェニルエチルアルコール、プロパノール、及びペンタノールが特に好適に用いられる前記<1>ないし<5>のいずれか1に記載の化粧料用被膜の製造方法。
<7>
(a)の揮発性物質が、エタノール、イソプロピルアルコール、ブチルアルコール、及び水から選ばれる1種又は2種以上であり、より好ましくはエタノール、及びブチルアルコールから選ばれる1種又は2種であり、最も好ましくはエタノールである前記<1>ないし<6>のいずれか1に記載の化粧料用被膜の製造方法。
(b)の被膜形成能を有するポリマーは、(a)の揮発性物質に溶解することが可能な物質であり、水溶性ポリマーと水不溶性ポリマーとを含み、ここで、溶解するとは20℃において分散状態にあり、その分散状態が目視で均一な状態、好ましくは目視で透明又は半透明な状態であることをいう前記<1>ないし<7>のいずれか1に記載の化粧料用被膜の製造方法。
<9>
水溶性である被膜形成能を有するポリマーとしては、プルラン、ヒアルロン酸、コンドロイチン硫酸、ポリ−γ−グルタミン酸、変性コーンスターチ、β−グルカン、グルコオリゴ糖、ヘパリン、ケラト硫酸等のムコ多糖、セルロース、ペクチン、キシラン、リグニン、グルコマンナン、ガラクツロン酸、サイリウムシードガム、タマリンド種子ガム、アラビアガム、トラガントガム、大豆水溶性多糖、アルギン酸、カラギーナン、ラミナラン、寒天(アガロース)、フコイダン、メチルセルロース、ヒドロキシプロピルセルロース、ヒドロキシプロピルメチルセルロース等の天然高分子、部分鹸化ポリビニルアルコール(架橋剤と併用しない場合)、低鹸化ポリビニルアルコール、ポリビニルピロリドン(PVP)、ポリエチレンオキサイド、ポリアクリル酸ナトリウムから選ばれる1種又は2種以上の水溶性の高分子であり、より好ましくはプルラン、並びに部分鹸化ポリビニルアルコール、低鹸化ポリビニルアルコール、ポリビニルピロリドン及びポリエチレンオキサイドから選ばれる1種又は2種以上の水溶性の高分子である前記<1>ないし<8>のいずれか1に記載の化粧料用被膜の製造方法。
<10>
水不溶性である被膜形成能を有するポリマーとしては、被膜形成後に不溶化処理できる完全鹸化ポリビニルアルコール、架橋剤と併用することで被膜形成後に架橋処理できる部分鹸化ポリビニルアルコール、ポリ(N−プロパノイルエチレンイミン)グラフト−ジメチルシロキサン/γ−アミノプロピルメチルシロキサン共重合体等のオキサゾリン変性シリコーン、ポリビニルアセタールジエチルアミノアセテート、ツエイン(とうもろこし蛋白質の主要成分)、ポリエステル、ポリ乳酸(PLA)、ポリアクリロニトリル樹脂、ポリメタクリル酸樹脂等のアクリル樹脂、ポリスチレン樹脂、ポリビニルブチラール樹脂、ポリエチレンテレフタレート樹脂、ポリブチレンテレフタレート樹脂、ポリウレタン樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリアミドイミド樹脂から選ばれる1種又は2種以上の水不溶性ポリマーであり、より好ましくは被膜形成後に不溶化処理できる完全鹸化ポリビニルアルコール、架橋剤と併用することで被膜形成後に架橋処理できる部分鹸化ポリビニルアルコール、ポリビニルブチラール樹脂、ポリ(N−プロパノイルエチレンイミン)グラフト−ジメチルシロキサン/γ−アミノプロピルメチルシロキサン共重合体等のオキサゾリン変性シリコーン、水溶性ポリエステル、及びツエインから選ばれる1種又は2種以上の水不溶性ポリマーである前記<1>ないし<9>のいずれか1に記載の化粧料用被膜の製造方法。
<11>
前記組成物における成分(a)の含有量は、50質量%以上であることが好ましく、55質量%以上であることが更に好ましく、60質量%以上であることが一層好ましく、また98質量%以下であることが好ましく、96質量%以下であることが更に好ましく、94質量%以下であることが一層好ましく、前記組成物における成分(a)の含有量は、50質量%以上98質量%以下であることが好ましく、55質量%以上96質量%以下であることが更に好ましく、60質量%以上94質量%以下であることが一層好ましい前記<1>ないし<10>のいずれか1に記載の化粧料用被膜の製造方法。
前記組成物における成分(b)の含有量は、2質量%以上であることが好ましく、4質量%以上であることが更に好ましく、6質量%以上であることが一層好ましく、また50質量%以下であることが好ましく、45質量%以下であることが更に好ましく、40質量%以下であることが一層好ましく、前記組成物における成分(b)の含有量は、2質量%以上50質量%以下であることが好ましく、4質量%以上45質量%以下であることが更に好ましく、6質量%以上40質量%以下であることが一層好ましい前記<1>ないし<11>のいずれか1に記載の化粧料用被膜の製造方法。
<13>
前記組成物中に、成分(a)及び成分(b)のみが含まれているか、あるいは成分(a)及び成分(b)に加えて他の成分が含まれており、
前記他の成分として、(b)の被膜形成能を有するポリマーの可塑剤、着色顔料、体質顔料、染料、界面活性剤、UV防御剤、香料、忌避剤、酸化防止剤、安定剤、防腐剤、各種ビタミンが用いられる前記<1>ないし<12>のいずれか1に記載の化粧料用被膜の製造方法。
<14>
前記組成物中に他の成分が含まれる場合、当該他の成分の配合割合は、0.1質量%以上30質量%以下であることが好ましく、0.5質量%以上20質量%以下であることが更に好ましい前記<13>に記載の化粧料用被膜の製造方法。
<15>
前記組成物は、その粘度が、25℃において、好ましくは1mPa・s以上、更に好ましくは10mPa・s以上、一層好ましくは50mPa・s以上であり、好ましくは5000mPa・s以下、更に好ましくは2000mPa・s以下、一層好ましくは1500mPa・s以下であり、前記組成物の粘度は、25℃において、好ましくは1mPa・s以上5000mPa・s以下であり、更に好ましくは10mPa・s以上2000mPa・s以下であり、一層好ましくは50mPa・s以上1500mPa・s以下である前記<1>ないし<14>のいずれか1に記載の化粧料用被膜の製造方法。
<16>
静電スプレー法を静電スプレー装置を用いて行い、
前記静電スプレー装置はノズルを備えており、
前記ノズルは、金属を初めとする各種の導電体、又はプラスチック、ゴム、セラミック等の非導電体からなり、その先端から前記組成物の吐出が可能な形状をしている前記<1>ないし<15>のいずれか1に記載の化粧料用被膜の製造方法。
静電スプレー法を静電スプレー装置を用いて行い、
前記静電スプレー装置はノズル及び筐体を備えており、
前記筐体の長手方向の一端に、前記ノズルが配置されており、
前記ノズルは、前記組成物の吹き出し方向を、前記筐体の縦方向と一致させて、肌側に向かい凸状になるように該筐体に配置されている前記<1>ないし<16>のいずれか1に記載の化粧料用被膜の製造方法。
<18>
噴霧された前記組成物を、溶媒である揮発性物質を液滴から揮発させ、溶質である被膜形成能を有するポリマーを固化させつつ、電位差によって伸長変形させながら繊維を形成する前記<1>ないし<17>のいずれか1に記載の化粧料用被膜の製造方法。
<19>
静電スプレー法を静電スプレー装置を用いて行い、
前記静電スプレー装置はノズルを備えており、
前記ノズルと皮膚との間の距離を、50mm以上、150mm以下にする前記<1>ないし<18>のいずれか1に記載の化粧料用被膜の製造方法。
<20>
静電スプレー法によって形成された被膜の坪量は、0.1g/m2以上であることが好ましく、1g/m2以上であることが更に好ましく、30g/m2以下であることが好ましく、20g/m2以下であることが更に好ましく、被膜の坪量は、0.1g/m2以上30g/m2以下であることが好ましく、1g/m2以上20g/m2以下であることが更に好ましい前記<1>ないし<19>のいずれか1に記載の化粧料用被膜の製造方法。
<21>
20℃で固体状の前記油が、ワックス、コレステロール類誘導体、フィトステロール類誘導体、ジペンタエリトリット脂肪酸エステル類、トリグリセライド類、ラノリン、ラノステロール類誘導体、ワセリン、セラミド類、高級アルコール、又は高級脂肪酸である前記<1>ないし<20>のいずれか1に記載の化粧料用被膜の製造方法。
<22>
前記化粧料中での20℃で固体状の前記油の含有量が、好ましくは10質量%超100質量%以下である前記<1>ないし<21>のいずれか1に記載の化粧料用被膜の製造方法。
前記化粧料は、20℃で固体状の前記油以外に、水、20℃において液体状の油、ポリオール、界面活性剤、感触調整剤、着色顔料等の粉体、紫外線吸収剤、水溶性高分子等の増粘剤、皮膜剤、糖、金属イオン封鎖剤、低級アルコール、pH調整剤、皮膚コンディショニング剤、ビタミン、酸化防止剤、制汗剤、香料、植物抽出物、又は防腐剤を含有する前記<1>ないし<22>のいずれか1に記載の化粧料用被膜の製造方法。
<24>
前記化粧料が水を含有し、前記化粧料中での水の含有量は、0.1質量%以上90質量%以下が好ましく、0.5質量%以上85質量%以下がより好ましく、1質量%以上80質量%以下が更に好ましい前記<1>ないし<23>のいずれか1に記載の化粧料用被膜の製造方法。
<25>
前記化粧料が20℃において液体の油を含有し、
20℃において液体の前記油が、流動パラフィン、軽質イソパラフィン、流動イソパラフィン、スクワラン、スクワレン等の直鎖又は分岐の炭化水素油;ホホバ油、オリーブ油等の植物油、液状ラノリン等の動物油、モノアルコール脂肪酸エステル、多価アルコール脂肪酸エステル等のエステル油;ジメチルポリシロキサン、ジメチルシクロポリシロキサン、メチルフェニルポリシロキサン、メチルハイドロジェンポリシロキサン、高級アルコール変性オルガノポリシロキサン等のシリコーン油等である前記<1>ないし<24>のいずれか1に記載の化粧料用被膜の製造方法。
<26>
前記化粧料中での20℃において液体の前記油の含有量は、5質量%以下であり、より好ましくは1質量%以下であり、更に好ましくは0.5質量%以下である前記<1>ないし<25>のいずれか1に記載の化粧料用被膜の製造方法。
<27>
前記化粧料がポリオールを含有し、
前記ポリオールが、エチレングリコール、プロピレングリコール、1,3−プロパンジオール、1,3−ブタンジオール等のアルキレングリコール類;ジエチレングリコール、ジプロピレングリコール、ポリエチレングリコール、ポリプロピレングリコール等のポリアルキレングリコール類;グリセリン、ジグリセリン、トリグリセリン等のグリセリン類等である前記<1>ないし<26>のいずれか1に記載の化粧料用被膜の製造方法。
前記化粧料中での前記ポリオールの含有量は、0.1質量%以上20質量%以下が好ましく、0.5質量%以上15質量%以下がより好ましく、1質量%以上12質量%以下が一層好ましい前記<1>ないし<27>のいずれか1に記載の化粧料用被膜の製造方法。
<29>
前記化粧料が界面活性剤を含有し、
前記界面活性剤が、イオン性界面活性剤又は非イオン性界面活性剤であり、
前記イオン性界面活性剤が、アニオン界面活性剤、カチオン界面活性剤、又は両性界面活性剤である前記<1>ないし<28>のいずれか1に記載の化粧料用被膜の製造方法。
<30>
前記界面活性剤がイオン性界面活性剤であり、
前記イオン性界面活性剤がアニオン界面活性剤であり、
前記アニオン界面活性剤が、ポリオキシエチレン炭素数12〜22のアルキルエーテルリン酸又はその塩、炭素数12〜22のN−アルキロイルメチルタウリンナトリウム、及びN−炭素数12〜22のアシルグルタミン酸塩から選ばれる1種又は2種以上である前記<29>に記載の化粧料用被膜の製造方法。
前記界面活性剤は、1種又は2種以上を組み合わせて用いることができ、該界面活性剤の含有量は、対イオンを除いた化合物の含有量で表して、前記化粧料中に0.01質量%以上が好ましく、0.05質量%以上がより好ましく、0.1質量%以上が更に好ましく、5質量%以下が好ましく、4質量%以下がより好ましく、3質量%以下が更に好ましく、2.5質量%以下が更により好ましい前記<29>又は<30>に記載の化粧料用被膜の製造方法。
<32>
前記化粧料が感触調整剤を含有し、
前記感触調整剤がシリコーン油であり、
前記シリコーン油が、ジメチルポリシロキサン、ジメチルシクロポリシロキサン、メチルフェニルポリシロキサン、メチルハイドロジェンポリシロキサン、又は高級アルコール変性オルガノポリシロキサンである前記<1>ないし<31>のいずれか1に記載の化粧料用被膜の製造方法。
前記化粧料中での前記シリコーン油の含有量が10質量%以下であり、より好ましくは5質量%以下であり、更に好ましくは1質量%以下であり、更に一層好ましくは0.1質量%以下であり、
前記シリコーン油の動粘度は、25℃において3mm2/s以上が好ましく、4mm2/s以上がより好ましく、5mm2/s以上が更に好ましく、30mm2/s以下が好ましく、20mm2/s以下がより好ましく、10mm2/s以下が一層好ましい前記<32>に記載の化粧料用被膜の製造方法。
<34>
前記化粧料が着色顔料を含有し、
前記化粧料中での前記着色顔料の含有量は、0.1質量%未満が好ましく、0.05質量%以下がより好ましく、0.01質量%以下が更に好ましく、0.001質量%以下が一層好ましい前記<1>ないし<33>のいずれか1に記載の化粧料用被膜の製造方法。
<35>
前記化粧料を前記皮膚に施す量は、前記化粧料の坪量が好ましくは0.1g/m2以上、より好ましくは0.2g/m2以上となるような量であり、好ましくは40g/m2以下、より好ましくは35g/m2以下となるような量であり、
化粧料を皮膚に施す量は、化粧料の坪量が好ましくは0.1g/m2以上40g/m2以下、より好ましくは0.2g/m2以上35g/m2以下となるような量であり、
化粧料を皮膚に施す量は、好ましくは5g/m2以上であり、より好ましくは10g/m2以上であり、更に好ましくは15g/m2以上であり、好ましくは50g/m2以下であり、より好ましくは45g/m2以下であり、となるような量である前記<1>ないし<34>のいずれか1に記載の化粧料用被膜の製造方法。
<36>
前記化粧料を前記皮膚に塗布する前、又はその後に、前記化粧料以外の化粧料を前記皮膚に施す前記<1>ないし<35>のいずれか1に記載の化粧料用被膜の製造方法。
<37>
前記化粧料適用工程において前記化粧料を皮膚に塗布する、<1>ないし<36>のいずれか1に記載の化粧料用被膜の製造方法。
熱分析用アルミニウム製サンプルパンにサンプルを10mg充填し、示査走査熱容量測定装置(Differential scanning calorimetry:DSC;メトラートレド社製)を用い、測定試料と基準(空のサンプル管)との間の熱量の差を計測した。測定は、1℃/分で0℃から150℃まで昇温し、融解ピーク温度を測定した。
(1)噴霧用組成物の調製
噴霧用組成物の成分(a)として99.5%エタノール、及び1−ブタノールを用いた。成分(b)としてポリアクリル酸を用いた。両成分の配合割合は、成分(a)のエタノールを52%、1−ブタノールを26%とし、成分(b)を22%とした。
(2)化粧料適用工程で用いる化粧料の準備
化粧料として、化粧料6を55mg用いた。化粧料6の組成を以下の表1に示す。
(3)化粧料適用工程
前記の化粧料6を、ヒトの前腕部内側に滴下し、直径4cm以上6cm未満の面積に指で塗り広げてなじませて薄層を形成した。滴下量は55mgであり、広げた領域が濡れている、あるいはしっとりしている、若しくは質感が相違する等により、化粧料6の存在を目視、あるいは感触により理解することができる程度の量を適用した。その結果、化粧料6を皮膚に施す量は、該化粧料6の坪量が28.0g/m2であり、化粧料の総坪量は0.25g/m2となるような量となった。
(4)静電スプレー工程
図1に示す構成を有し、図2に示す外観を有する静電スプレー装置10を用い、(3)の化粧料適用工程で形成された薄層に向けて静電スプレー法を20秒間行った。静電スプレー法の条件は以下に示すとおりとした。
・印加電圧:10kV
・ノズルと皮膚との距離:100mm
・噴霧用組成物の吐出量:5ml/h
・環境:25℃、30%RH
この静電スプレーによって、皮膚の表面に繊維の堆積物からなる多孔性被膜が形成された。被膜は直径約4cmの円であり、質量は約5.5mgであった。上述した方法で測定された繊維の太さは506nmであった。
実施例1における噴霧用組成物及び化粧料を表2に示すものに変えた以外は、実施例1と同様にして、被膜を形成した。化粧料1ないし7の組成を以下の表1に示す。
〔実施例3及び4〕
実施例2における噴霧用組成物を表2に示すものに変えた以外は、実施例2と同様にして、被膜を形成した。
本比較例は、実施例1ないし4において化粧料適用工程を行わなかった例である。これ以外は実施例1と同様にして、繊維の堆積物からなる多孔性被膜を得た。
本比較例は、実施例5及び8において、化粧料のみ塗布した例である。本比較例では静電スプレー法による被膜の形成は行っていない。
(1)噴霧用組成物の調製
噴霧用組成物の成分(a)として99.5%エタノールを用いた。成分(b)としてポリビニルブチラールを用いた。その他の成分として、ラウロイルグルタミン酸ジ(フィトステリル/オクチルドデシル)を用いた。各成分の配合割合は、成分(a)のエタノールを80%、成分(b)のポリビニルブチラールを14%、その他の成分のラウロイルグルタミン酸ジ(フィトステリル/オクチルドデシル)を6%とした。
(2)静電スプレー工程によるシートの作製
図1に示す構成を有し、図2に示す外観を有する静電スプレー装置10を用い、ステンレス鋼板に向けて静電スプレー法を20秒間行った。静電スプレー法の条件は以下に示すとおりとした。
・印加電圧:10kV
・ノズルと皮膚との距離:100mm
・噴霧用組成物の吐出量:5ml/h
・環境:25℃、30%RH
この静電スプレーによって、ステンレス鋼板の表面に繊維の堆積物からなる多孔性被膜が形成された。被膜は直径約4cmの円であり、質量は約5.5mgであった。上述した方法で測定された繊維の太さは506nmであった。
(3)化粧料適用工程
前記の化粧料1又は4を、ヒトの前腕部内側に滴下し、直径4cm以上6cm未満の面積に指で塗り広げてなじませて薄層を形成した。滴下量は55mgであり、広げた領域が濡れている、あるいはしっとりしている、若しくは質感が相違する等により、化粧料1又は4の存在を目視、あるいは感触により理解することができる程度の量を適用した。その結果、化粧料1又は4を皮膚に施す量は、該化粧料1又は4の坪量が28.0g/m2であり、化粧料の総坪量は0.25g/m2となるような量となった。
(4)シートの貼布工程
(2)の静電スプレー工程で得られたシートを、工程(4)で得られた化粧料適用工程で形成された薄層の上に静かにのせ軽く押さえた。
実施例及び比較例で形成された被膜について、皮膚との密着性、耐水性及びべたつき感のなさを以下の方法で評価した。
評価は、皮膚と垂直な方向から被膜に指で触れて微細振動荷重を与え、また皮膚と平行な方向に指を往復させて被膜に剪断力を加え、その後の被膜の状態を目視観察することで行った。その結果を表2に示す。評価基準は以下のとおりとした。
1 指で垂直方向に微細振動荷重を与えると被膜がほぼすべて剥離する。
2 指で垂直方向に微細振動荷重を与えると被膜を形成する繊維が一部剥離する。
3 垂直方向は剥離しないが、平行方向に剪断力を与えると被膜がほぼすべて剥離する。
4 垂直方向は剥離しないが、指で平行方向に剪断力を与えると被膜又は繊維が一部剥離する。
5 垂直方向に剥離せず、且つ平行方向に剪断力を与えても、被膜又は繊維が剥離しない。
評価は、皮膚上に形成された被膜の上から、水道の蛇口より100ml/秒で水を1分間流し、その後、タオルで水分を拭き取り、被膜の状態を目視観察した。被膜が全く剥離せず耐水性に最も優れていたものを「5」、被膜がすべて剥離して耐水性が全くないものを「1」として5段階評価を行った。
被膜を形成した直後から3分の間で以下の評価を行った。
専門パネラーが、前腕部内側に被膜を形成し、形成した被膜上で手指を100g重/cm2でスライドさせながら、べたつき感を評価した。べたつき感の評価は、被膜に全くべたつきがなく使用感に最も優れていたものを「5」、被膜がべたつき、使用感が良好でないものを「1」として5段階評価を行った。評価結果は専門パネラー3名の評価結果の平均値として表2に示す。
11 低電圧電源
12 高電圧電源
13 補助的電気回路
14 マイクロギヤポンプ
15 容器
16 ノズル
17 管路
18 フレキシブル管路
19 電流制限抵抗
20 筐体
Claims (4)
- 皮膚の表面に被膜を形成する化粧料用被膜の製造方法であって、
20℃で固体状の油を少なくとも10質量%以上含有する化粧料を皮膚に施す化粧料適用工程と、皮膚に組成物を直接に静電スプレーして被膜を形成する静電スプレー工程とを具備し、
前記組成物が、以下の成分(a)及び成分(b)を含む、化粧料用被膜の製造方法。
(a)水、アルコール及びケトンからなる群より選択される1種又は2種以上の揮発性物質。
(b)被膜形成能を有するポリマー。 - 前記静電スプレー工程において、皮膚に前記組成物を静電スプレーして多孔性被膜を形成する請求項1に記載の化粧料用被膜の製造方法。
- 前記静電スプレー工程において、静電スプレー装置を用いて皮膚に前記組成物を静電スプレーして、繊維の堆積物からなる多孔性被膜を形成し、前記静電スプレー装置が、
前記組成物を収容する容器と、
前記組成物を吐出するノズルと、
前記容器中に収容されている前記組成物を前記ノズルに供給する供給装置と、
前記ノズルに電圧を印加する電源と、
を備える請求項1又は2に記載の化粧料用被膜の製造方法。 - 前記化粧料適用工程において前記化粧料を皮膚に塗布する、請求項1ないし3のいずれか一項に記載の化粧料用被膜の製造方法。