JP2017202574A - マット感を有する印刷物、及びその作製方法 - Google Patents
マット感を有する印刷物、及びその作製方法 Download PDFInfo
- Publication number
- JP2017202574A JP2017202574A JP2016093846A JP2016093846A JP2017202574A JP 2017202574 A JP2017202574 A JP 2017202574A JP 2016093846 A JP2016093846 A JP 2016093846A JP 2016093846 A JP2016093846 A JP 2016093846A JP 2017202574 A JP2017202574 A JP 2017202574A
- Authority
- JP
- Japan
- Prior art keywords
- varnish
- meth
- layer
- acrylate
- printed matter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
「塗り加工」は印刷された基材にニスを塗工したものを指し、ニスの種類としては、グロスタイプ、セミマットタイプ、マットタイプなどがある。
そこで品質良く製品化したい場合、「一般のUVオフセット印刷機」使用の場合、印刷後、オフラインの別工程にてロールコーターを用いマット加工を行うケースが多く、この場合、移動費、外注費、などコスト高となる現状がある。
一方で、UV擬似エンボス加工が挙げれるが、インラインコーター付きの印刷機が必要となり、通常の印刷機のオフセット胴ではこの加工はできない。
コーティング装置を必要とせずとも「一般のUV印刷機のオフセット胴」を用いて、手軽にマット加工を行う事ができる印刷物及びその作製方法の確立が望まれる。
従来のマット剤によるOPマットニスで見らえるバインダーからマット剤が突き出る状況(図1)から、本発明によるマット効果は円形に近い形で存在するはじきの粒(図2)となるため、爪や製造工程のコスレによって、突起が折れるという事が無くなり、傷が付き難くなる。
その他重合基を有する樹脂オリゴマーも挙げられ、分子中に重合性基を有さない非反応性樹脂類(イナート樹脂)と比較して反応性が高く、重合基を有する樹脂オリゴマーとしては、例えば、エポキシアクリレート、脂肪族アクリレート、ポリエステルアクリレート、ウレタンアクリレート等が挙げられ、これらを組合せて使用してよい。公知公用の各種バインダー樹脂を利用することができる。ここで述べるバインダー樹脂とは、適切な体質顔料との親和性と分散性を有し、ニスに要求されるレオロジー特性を有する樹脂全般を示しており、例えば非反応性樹脂としては、ジアリルフタレート樹脂、エポキシ樹脂、ポリウレタン樹脂、ポリエステル樹脂、石油樹脂、ロジンエステル樹脂、ポリ(メタ)アクリル酸エステル、セルロース誘導体、塩化ビニル−酢酸ビニル共重合体、ポリアマイド樹脂、ポリビニルアセタール樹脂、ブタジエン−アクリルニトリル共重合体等を挙げることができ、または樹脂分子中に少なくとも1つ以上の重合性基を有するエポキシアクリレート化合物、ウレタンアクリレート化合物、ポリエステルアクリレート化合物等を使用することもでき、これらバインダー樹脂化合物は、単独で使用しても、いずれか1種以上を組合せて使用してもよい。
また、前記数平均分子量が100,000〜500,000のポリジメチルシロキサンの25℃における動粘度の範囲は90,000〜550,000mm2/Sである事が好ましい。
尚、本発明におけるGPC(ゲルパーミエーションクロマトグラフィー)による数平均分子量(ポリスチレン換算)の測定は東ソー(株)社製HLC8220システムを用い以下の条件で行った。
分離カラム:東ソー(株)製TSKgelGMHHR−Nを4本使用。カラム温度:40℃。移動層:和光純薬工業(株)製テトラヒドロフラン。流速:1.0ml/分。試料濃度:1.0重量%。試料注入量:100マイクロリットル。検出器:示差屈折計。
表1、2の組成に従って、製造例1〜9、表3、4の組成に従って、製造比較例1〜8のワニスを3本ロールミルにて練肉することによって、各種紫外線硬化型下刷りワニスを得た。尚、表1〜4の数値は質量%である。
表2の製造例10の組成に従って、上刷りワニス2を3本ロールミルにて練肉することによって得た。また、参考例としてマット剤であるZEST PQHT(塩化ビニル樹脂)をワニス全量の5質量%添加したマットOPニスを表4の参考製造例1に従って同様に練肉した。
UV墨インキを簡易展色機(RIテスター、豊栄精工社製)を用い、インキ0.10mlを使用して、RIテスターのゴムロール及び金属ロール上に均一に引き伸ばし、コートボール紙(王子マテリア社製UFコート、米坪350g/m2)の表面に、200cm2の面積にわたって均一に塗布されるように展色し、展色物を作製した。なおRIテスターとは、紙やフィルムにインキを展色する試験機であり、インキの転移量や印圧を調整することが可能である。
インキ塗布後の展色物に活性エネルギー線である紫外線(UV)照射を行い、インキ皮膜を硬化させた。空冷メタルハライドランプ(出力120W/cm1灯)およびベルトコンベアを搭載したUV照射装置(アイグラフィックス社製、コールドミラー付属)を使用し、展色物をコンベア上に載せ、ランプ直下(照射距離11cm)を分速40メートルの速度で通過させることにより、インキ皮膜を硬化させた。
上記墨印刷物の表面に段落〔0043〕で得られた下刷りワニスを簡易展色機を用い、インキ0.10mlを使用して、RIテスターのゴムロール及び金属ロール上に均一に引き伸ばし、200cm2の面積にわたって均一に塗布されるように展色し、展色物を作製した。インキ塗布後の展色物に活性エネルギー線である紫外線(UV)照射を行い、インキ皮膜を硬化させた。空冷メタルハライドランプ(出力120W/cm1灯)およびベルトコンベアを搭載したUV照射装置を使用し、展色物をコンベア上に載せ、ランプ直下(照射距離11cm)を分速40メートルの速度で通過させることにより、インキ皮膜を硬化させた。
更に段落〔0044〕で得られた上刷りワニスを簡易展色機を用い、インキ0.10mlを使用して、RIテスターのゴムロール及び金属ロール上に均一に引き伸ばし、200cm2の面積にわたって均一に塗布されるように展色し、展色物を作製した。インキ塗布後の展色物に活性エネルギー線である紫外線(UV)照射を行い、インキ皮膜を硬化させた。空冷メタルハライドランプ(出力120W/cm1灯)およびベルトコンベアを搭載したUV照射装置を使用し、展色物をコンベア上に載せ、ランプ直下(照射距離11cm)を分速40メートルの速度で通過させることにより、インキ皮膜を硬化させた。
得られた印刷物をグロスメーター(Multi−Gloss268 コニカミノルタ製)を用い60°反射角の光沢値を測定した。適性値として5〜22を合格品とする。
得られた印刷物を目視にてマット感を評価した。
◎ :マット感が非常に強い。
○ :マット感が強い。
△ :マット感が弱い。
× :マット感が見られない。
得られた印刷物を目視にて黒色感を評価した。
○ :通常マットOPニス印刷物と黒色感が同等。
△ :通常マットOPニス印刷物より黒色感が若干劣る。
× :通常マットOPニス印刷物より黒色感が明らかに劣る。
学振型耐摩擦試験機にて、上質紙を貼付した荷重500gで得られた印刷物を500回擦り、塗膜の取られ具合を評価した。
○ :塗膜に一部に傷が付く。傷の数は5本以内。
△○:塗膜の一部に傷が付く。傷の数は5本以上
△ :塗膜面積の30%以上に傷が見られる。
△×:塗膜面積の50%以上に傷が見られる。
× :塗膜面積の全面に傷が見られる。
小森コーポレーション製UVオフセット印刷機にて1000枚印刷した後のブランケット・版の画線部に目視で確認し、インキの残り具合を評価した。
○ :ブランケット・版上に残るインキ量が通常UVOPニスと同等。
△ :ブランケット・版上に残るインキ量が通常UVOPニスよりやや多い。
× :ブランケット・版上に残るインキ量が通常UVOPニスより多い。
段落〔0043〕にて得られた下刷りワニス1(インキ)を25℃の環境下で平行版粘度計を用い、115gの荷重を落下させてから1分後のインキ膜の直径を比較する。
○ :インキ膜の直径が30mm以上
△ :インキ膜の直径が25〜30mm
× :インキ幕の直径が25mm未満
・ZEST PQHT:トクヤマ社製塩化ビニル樹脂
・炭酸カルシウム PC:白石カルシウム(株)社製 一次粒子径1500NM(長径)
・ハイフィラー :含水ケイ酸マグネシウムのハイフィラー(タルク)#5000PJ、松村産業(株)社製
・チタン CR58−2:塩素法ルチル型酸化チタン、平均粒子径28(μm)、吸油量18、石原産業(株)社製
・ダイソーダップ A:ジアクリルフタレート樹脂、ダイソー製
・アロニックス M−7300K:ポリエステルアクリレート、東亜合成(株)社製
・DPHA:MIRAMER M−600、ジペンタエリスリトールヘキサアクリレート
、MIWON社製
・SR355NS:ジトリメチロールプロパンテトラアクリレート(DITMPTA)、サートマー社製
・MIRAMER M−240:ビスフェノールA(EO変性)ジアクリレート、東洋ケミカルズ(株)社製
・MIRAMER M−3130:トリメチロールプロパン(EO変性)トリアクリレート、東洋ケミカルズ(株)社製
・IRGACURE 907:α−アミノアルキルフェノン系光重合開始剤、2−メチル−1−[4−(メチルチオ)フェニル]−2−モノフォリノプロパン−1−オン等は数平均分子量(279.4)、BASF社製
・IRGACURE 184:1−ヒドロキシシロヘキシルフェニルケトン、BASF社製
・S−381−N1:ポリエチレンワックス、シャムロック社製
・TEGO RAD 2700、シリコーンアクリレート(数平均分子量:7000)、エボニック社製
・シリコン KF−96 100CS:ジメチルシロキサン構造を持つシリコーンオイル、信越化学工業(株)社製
・シリコン TSF−451−6M、ジメチルシロキサン構造を持つシリコーンオイル(数平均分子量:60,000)、動粘度60,000mm2/S、(株)タナック社製
・シリコン TSF−451−10M、ジメチルシロキサン構造を持つシリコーンオイル(数平均分子量:100,000)、動粘度100,000mm2/S、(株)タナック社製
・シリコン TSF−451−50M、ジメチルシロキサン構造を持つシリコーンオイル(数平均分子量:500,000)、動粘度500,000mm2/S、(株)タナック社製
・シリコン TSF−451−60M、ジメチルシロキサン構造を持つシリコーンオイル(数平均分子量:600,000)、動粘度600,000mm2/S、(株)タナック社製
・Q−1301:ニトロソアミン系重合開始剤、和光純薬工業(株)社製
また、参考例で示す通り、マット剤を含有したマットOPニスを使用し、ニスコーターを用いた極一般的なマット加工を施した印刷物では、マット調の視覚効果は得られても、耐摩耗性が得られず、ブラン残り・版残り等の印刷適性も劣る。
2.一般的なOPマットニス層
3.マット剤
4.本発明の紫外線硬化型下刷りワニス層
5.ハジキによる紫外線硬化型上塗りワニス層
Claims (4)
- 基材上に、紫外線硬化型インキを用いた印刷層が設けられ、前記基材及び印刷層の表面上に、部分的又は全面に紫外線硬化型下刷りワニス1による下刷り層が設けられ、前記基材、印刷層及び下刷り層の上に、紫外線硬化型上刷りワニス2による上刷り層が全面又は部分的に設けられ、前記下刷り層と前記上刷り層とが重なる部分は、上刷り層がはじきにより微粒子状となりマット調の視覚効果を発現させ、重ならない部分は連続した皮膜で光沢調となること特徴とする印刷物であって、
前記紫外線硬化型下刷りワニス1が、(メタ)アクリレートモノマー及び/又は(メタ)アクリレートオリゴマー、樹脂、光重合開始剤、体質顔料、及び助剤を含有し、前記助剤として数平均分子量が100,000〜500,000のポリジメチルシロキサンをワニス全量の0.5〜15質量%を含有することを特徴とする印刷物。
- 前記紫外線硬化型上刷りワニス2が、(メタ)アクリレートモノマー及び/又は(メタ)アクリレートオリゴマー、樹脂、光重合開始剤、及び体質顔料を含有するワニス2を用いた請求項1記載の印刷物。
- 更に前記紫外線硬化型下刷りワニス1及び/又は紫外線硬化型上刷りワニス2が、酸化チタンを各ワニス全量の0.1〜5質量%含有する請求項1又は2記載の印刷物。
- 前記の紫外線硬化型下刷りワニス1による下塗り層、及び紫外線硬化型上刷りワニス2による上塗り層が、オフセット印刷によって形成する請求項1に記載の印刷物の作製方法。