JP2017052247A - 昇華型インクジェット捺染転写紙及びその製造方法 - Google Patents
昇華型インクジェット捺染転写紙及びその製造方法 Download PDFInfo
- Publication number
- JP2017052247A JP2017052247A JP2015179885A JP2015179885A JP2017052247A JP 2017052247 A JP2017052247 A JP 2017052247A JP 2015179885 A JP2015179885 A JP 2015179885A JP 2015179885 A JP2015179885 A JP 2015179885A JP 2017052247 A JP2017052247 A JP 2017052247A
- Authority
- JP
- Japan
- Prior art keywords
- fine particles
- ink
- sublimation
- mass
- receiving layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
基材上に昇華型捺染インク受容層が形成されてなり、
前記基材は、JIS P 8140に準拠した10秒コッブ吸水度が5〜20g/m2であり、
前記昇華型捺染インク受容層は、少なくとも水溶性樹脂と、微細粒子Aと、微細粒子Bとを含有したインク受容層塗料からなり、
前記水溶性樹脂は、少なくともカルボキシメチルセルロースナトリウムであり、
前記微細粒子Aは、少なくとも平板結晶構造を有する無機微粒子で、該平板結晶構造を有する無機微粒子は、0.4〜2.3μmの範囲にメジアン径d50を有し、アスペクト比が5以上であり、
前記微細粒子Bは、少なくともシリカ粒子であり、
前記微細粒子Aと前記微細粒子Bとの割合(微細粒子A/微細粒子B)は、質量比で、15/85〜85/15であり、
前記カルボキシメチルセルロースナトリウムの量は、固形分で、微細粒子A100質量部に対して50質量部と微細粒子B100質量部に対して120質量部との合計以上、かつ、微細粒子Aと微細粒子Bとの合計100質量部に対して400質量部以下であり、
前記インク受容層塗料の塗工量(乾燥)は、2〜12g/m2である
ことを特徴とする、昇華型インクジェット捺染転写紙
に関する。
前記昇華型インクジェット捺染転写紙の製造方法であって、
微細粒子Aの高濃度分散体を調製した後、該高濃度分散体に所定の割合で溶媒を添加して希釈し、得られた希釈分散体に直ちに微細粒子Bを添加して分散させ、微細粒子A及び微細粒子Bの混合分散スラリーを調製する工程と、
前記混合分散スラリーに水溶性樹脂を添加して混合し、インク受容層塗料を調製する工程と、
基材上に前記インク受容層塗料を塗工し、該基材上に昇華型捺染インク受容層を形成させる工程とからなる
ことを特徴とする、昇華型インクジェット捺染転写紙の製造方法
に関する。
本発明の昇華型インクジェット捺染転写紙は、基材上に昇華型捺染インク受容層が形成されている。
・LBKP
広葉樹晒クラフトパルプ
JIS P 8121−2に準拠したフリーネス(CSF):530ml
・NBKP
針葉樹晒クラフトパルプ
JIS P 8121−2に準拠したフリーネス(CSF):580ml
・CMC
セロゲン5A(第一工業製薬(株)製)
・PVA
クラレポバールPVA105((株)クラレ製、ケン化度:98〜99mol%、
重合度:500)
・粒子−A
平板結晶構造を有する無機微粒子
二級クレー(メジアン径d50:0.7μm、アスペクト比:8)
・粒子−B1
合成非晶質シリカ粒子
カープレックス80(DSL.ジャパン(株)製、平均粒子径:15.0μm)
・粒子−B2
合成非晶質シリカ粒子
ファインシールX−37B(OSCジャパン(株)製、平均粒子径:3.7μm)
LBKP 85質量%とNBKP 15質量%とを配合し、助剤として、クラフトパルプ全量100質量部に対して、カチオン化デンプンを0.8質量部、アルキルケテンダイマー(内添サイズ剤)を1.1質量部、アニオン変性ポリアクリルアマイドを0.3質量部添加して紙料を調製した。この紙料を抄紙機で抄紙し、坪量が100g/m2、JIS P 8119に準拠したベック平滑度が100秒、JIS P 8140に準拠した10秒コッブ吸水度が10g/m2のクラフト紙を製造した(以下、基材−1という)。
クラフト紙の10秒コッブ吸水度が表1に示す値となるように、アルキルケテンダイマー(内添サイズ剤)の量を調整したほかは、製造例1と同様にしてクラフト紙を製造した(以下、各々基材−2〜基材−4という)。表1に、各クラフト紙の坪量及びベック平滑度を併せて示す。
水溶性樹脂としてCMCを、微細粒子Aとして粒子−Aを、微細粒子Bとして粒子−B1を、溶媒として水を用いた。水溶性樹脂(固形分)と微細粒子Aと微細粒子Bとの割合(水溶性樹脂:微細粒子A:微細粒子B)は、質量比で、200:75:25である。
組成及び各成分の添加割合を表2に示すように変更したほかは、調製例1と同様にして、表3に示す固形分濃度を有するインク受容層塗料を調製した(以下、各々塗料−2〜塗料−6という)。
水溶性樹脂としてCMCを、微細粒子Aとして粒子−Aを、溶媒として水を用いた。水溶性樹脂(固形分)と微細粒子Aとの割合(水溶性樹脂:微細粒子A)は、質量比で、200:100である。
組成を表4に示すように変更したほかは、比較調製例1と同様にして、表5に示す固形分濃度を有する比較塗料を調製した(以下、各々比較塗料−2〜比較塗料−3という)。
水溶性樹脂としてCMCを、微細粒子Bとして粒子−B1を、溶媒として水を用いた。水溶性樹脂(固形分)と微細粒子Bとの割合(水溶性樹脂:微細粒子B)は、質量比で、200:100である。
組成を表4に示すように変更したほかは、比較調製例4と同様にして、表5に示す固形分濃度を有する比較塗料を調製した(以下、各々比較塗料−5〜比較塗料−8という)。
組成及び各成分の添加割合を表4に示すように変更したほかは、調製例1と同様にして、表5に示す固形分濃度を有する比較塗料を調製した(以下、各々比較塗料−9〜比較塗料−12という)。
エアーナイフコーターを用い、基材−1の片面に、塗工量(乾燥)が8g/m2になるように塗料−1を塗工し、約130℃で乾燥して昇華型捺染インク受容層を形成させ、昇華型インクジェット捺染転写紙を製造した。
基材及び塗料の種類を表6に示すように変更したほかは、実施例1と同様にして、昇華型インクジェット捺染転写紙を製造した。
得られた昇華型インクジェット捺染転写紙について、以下の方法に従って特性を調べた。その結果を表7に示す。
各昇華型インクジェット捺染転写紙にインクジェットプリンタで黒ベタ印字をした直後、印字面をテッシュペーパーで擦り、拭取った際に、紙面上のインクの伸びの有無を目視で確認し、以下の評価基準に基づいて評価した。なお、評価3以上が実用レベルである。
(評価基準)
5:乾燥が非常に早く、拭取り後の紙面上でインクの伸びが全くない。
4:乾燥が早く、拭取り後の紙面上でインクの伸びが殆どない。
3:乾燥が若干遅く、拭取り後の紙面上でインクの伸びが僅かに認められるが、実用上問題はない。
2:乾燥が遅く、拭取り後の紙面上でインクの伸びが認められる。
1:乾燥が非常に遅く、装置汚れや印字部の汚れが認められ、拭取り後の紙面上でインクの伸びが長く、使用不可である。
各昇華型インクジェット捺染転写紙にインクジェットプリンタで赤100%+黄100%のベタ印字を行い、190℃で90秒間保持してポリエステル布素材への熱転写を行った。その後、昇華型インクジェット捺染転写紙に残ったインクの濃度及び布素材への転写濃度を調べ、以下の評価基準に基づいて評価した。なお、評価3以上が実用レベルである。
(評価基準)
5:紙面にはインクがわずかに残っている程度であり、布素材への転写濃度も高い。
4:紙面にはインクが残っているが、布素材への転写濃度にはほとんど影響が見られない。
3:紙面に残っているインクは少し濃度が高いが、布素材への転写濃度は「評価4」と比較して少し低下が感じられる程度で、実用上問題はない。
2:紙面に残っているインクは濃度が高く、布素材への転写濃度も「評価3」と比較して大きく低下している。
1:紙面に残っているインクはかなり濃度が高く、布素材への転写濃度は単独で見ても明らかに低下している。
デジタル画像の各昇華型インクジェット捺染転写紙紙面への画像濃度再現性を目視で観察し、以下の評価基準に基づいて評価した。なお、評価3以上が実用レベルである。
(評価基準)
5:原版との濃度の差異が認められず、画像濃度再現性に優れている。
4:原版との濃度の差異が殆ど認められず、画像濃度再現性が良好である。
3:原版との濃度の差異が僅かに認められ、画像濃度再現性にやや劣るが、実用上問題はない。
2:原版との濃度の差異が多く認められ、画像濃度再現性に劣り、使用不可である。
1:原版との濃度の差異が著しく、画像濃度再現性が殆どなく、使用不可である。
各昇華型インクジェット捺染転写紙にインクジェットプリンタで赤100%+黄100%のベタ印字を行い、昇華型インクジェット捺染転写紙とポリエステル布素材とフェルト基布とをこの順に重ね、フェルト基布には切れ込み傷を付けて熱伝達が不均一になり易い状態にしたうえで、190℃で15秒間保持して布素材への熱転写を行った。その後、フェルト基布の切れ込み傷に該当する位置での、布素材への転写画像の濃淡の有無を確認し、以下の評価基準に基づいて評価した。なお、評価3以上が実用レベルである。
(評価基準)
5:切れ込み傷の影響は全く見られない。
4:切れ込み傷の深い部分で僅かに薄い残像が見られるが、傷の浅い部分では残像は見られない。
3:切れ込み傷の深い部分で形状がほぼ分かり、傷の浅い部分でも形状が薄らと確認できるが、実用上問題はない。
2:切れ込み傷の深い部分だけでなく、傷の浅い部分でも形状が分かる。
1:切れ込み傷が明らかな濃淡として現れ、傷の浅い部分でもはっきりと形状が分かる。
各昇華型インクジェット捺染転写紙の昇華型捺染インク受容層の表面に、粉の付着を判別し易い透明で巾15mm程度の市販のセロハンテープ(ニチバン(株)製、No.405)を、長さ5cm程度に渡って2kgローラーで1往復して圧着させた後、転写紙本体が破れてしまわない速さで引き剥がした。剥がしたセロハンテープの糊面を目視にて観察して塗料の粉が付着しているか否かを調べ、粉落ちを以下の評価基準に基づいて評価した。なお、評価「優」が実用レベルである。
(評価基準)
優:粉落ちが認められない。
劣:僅かでも粉落ちが認められる。
以下の評価基準に基づいて総合評価した。
(評価基準)
○:前記(1)〜(5)において、全て実用レベルである。
×:前記(1)〜(5)において、実用レベルを満たさないものが1つでもある。
Claims (2)
- 基材上に昇華型捺染インク受容層が形成されてなり、
前記基材は、JIS P 8140に準拠した10秒コッブ吸水度が5〜20g/m2であり、
前記昇華型捺染インク受容層は、少なくとも水溶性樹脂と、微細粒子Aと、微細粒子Bとを含有したインク受容層塗料からなり、
前記水溶性樹脂は、少なくともカルボキシメチルセルロースナトリウムであり、
前記微細粒子Aは、少なくとも平板結晶構造を有する無機微粒子で、該平板結晶構造を有する無機微粒子は、0.4〜2.3μmの範囲にメジアン径d50を有し、アスペクト比が5以上であり、
前記微細粒子Bは、少なくともシリカ粒子であり、
前記微細粒子Aと前記微細粒子Bとの割合(微細粒子A/微細粒子B)は、質量比で、15/85〜85/15であり、
前記カルボキシメチルセルロースナトリウムの量は、固形分で、微細粒子A100質量部に対して50質量部と微細粒子B100質量部に対して120質量部との合計以上、かつ、微細粒子Aと微細粒子Bとの合計100質量部に対して400質量部以下であり、
前記インク受容層塗料の塗工量(乾燥)は、2〜12g/m2である
ことを特徴とする、昇華型インクジェット捺染転写紙。 - 請求項1に記載の昇華型インクジェット捺染転写紙の製造方法であって、
微細粒子Aの高濃度分散体を調製した後、該高濃度分散体に所定の割合で溶媒を添加して希釈し、得られた希釈分散体に直ちに微細粒子Bを添加して分散させ、微細粒子A及び微細粒子Bの混合分散スラリーを調製する工程と、
前記混合分散スラリーに水溶性樹脂を添加して混合し、インク受容層塗料を調製する工程と、
基材上に前記インク受容層塗料を塗工し、該基材上に昇華型捺染インク受容層を形成させる工程とからなる
ことを特徴とする、昇華型インクジェット捺染転写紙の製造方法。