JP2017014210A - 固形棒状化粧料 - Google Patents
固形棒状化粧料 Download PDFInfo
- Publication number
- JP2017014210A JP2017014210A JP2016130215A JP2016130215A JP2017014210A JP 2017014210 A JP2017014210 A JP 2017014210A JP 2016130215 A JP2016130215 A JP 2016130215A JP 2016130215 A JP2016130215 A JP 2016130215A JP 2017014210 A JP2017014210 A JP 2017014210A
- Authority
- JP
- Japan
- Prior art keywords
- solid bar
- powder
- eyebrows
- component
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
この固形棒状化粧料において、近年、塗布性と共に、着色剤及び体質材等の粉体成分を増量し、かつ、使用中の折損強度等も向上させる目的の固形棒状化粧料が知られている。
上記のように粉体成分を多量に含ませたい場合には、粉体成分を含む組成物を皿状の容器に詰めプレスして固形状の化粧料を得るのが一般的である。
(1) 少なくとも粉体成分を60〜90質量%と、固着樹脂成分と、シリコーン溶剤と、ワックス成分とを含有する固形棒状化粧料であって、該粉体成分が顔料及び体質材であることを特徴とする固形棒状化粧料。
(2) 前記顔料は親油性処理平板状顔料を含むことを特徴とする上記(1)に記載の固形棒状化粧料。
(3) 前記親油性処理平板状顔料の平均粒子径が5〜100μmであることを特徴とする上記(2)に記載の固形棒状化粧料。
本発明の固形棒状化粧料は、少なくとも粉体成分を60〜90質量%と、固着樹脂成分と、シリコーン溶剤と、ワックス成分とを含有する固形棒状化粧料であって、該粉体成分が顔料及び体質材であることを特徴とするものである。
平板状顔料としては、例えば、マイカ、マイカチタン、カルミン被膜マイカチタン、酸化クロム被膜マイカチタン、酸化鉄被膜マイカチタン、酸化鉄・カルミン被膜マイカチタン、酸化鉄・紺青被膜マイカチタン、青被覆マイカチタン、紺青被膜マイカチタン、ベンガラ被膜マイカ、ベンガラ被膜マイカチタン、ベンガラ・カルミン被膜マイカチタン、ベンガラ・酸化鉄被膜マイカチタン、ベンガラ・紺青被膜マイカチタン、ベンガラ・酸化鉄・紺青被膜マイカチタンなど、また、ガラスフレーク又は塊状フレークを母材とした上に、金属もしくは金属酸化物をコートした光輝性顔料、などの少なくとも1種(各単独又は2種以上の混合物、以下同様)が挙げられる。
好ましくは、塗膜の均一性及び塗布性の点から、酸化鉄被膜マイカチタン、マイカチタン、青被覆マイカチタンが挙げられ、特に、酸化鉄被膜マイカチタン、マイカチタンの使用が望ましい。更に好ましくは、これらの平板状顔料を親油化剤などにより親油性処理したものを挙げることができる。この親油性処理としては、ジメチコン(ジメチルポリシロキサン)、ハイドロゲンジメチコン、ラウロイルリシン、ステアリン酸、ステアリン酸変性、アミノ酸、アミノ酸変性等の親油化剤により親油性処理することが好ましく、特に好ましくは、ジメチコンやハイドロゲンジメチコン等のシリコーン系オイルにより処理することが好ましい。
この平板状顔料の含有量が10%未満では、実使用可能な強度を確保しながら、眉毛の上からのボカシ描画の塗布性の良好な物が得られず、一方、皮膚上への(ラインの)塗布性能、使用特性の点から50%以下とすることが望ましい。
用いることができる顔料としては、例えば、酸化チタン、鉄黒、カーボンブラック、紺青、群青、青色1号、ベンガラ、黄酸化鉄、酸化クロム、水酸化クロム、酸化亜鉛、酸化ジルコニウム、酸化コバルト、魚鱗箔、オキシ塩化ビスマス、青色2号、青色404号、赤色201号、赤色202号、赤色220号、赤色102号、赤色104号、黄色4号、黄色4号Alレーキなどの顔料などの少なくとも1種が挙げられる。また、これらの顔料も上記親油性処理ができるものであれば、親油性処理した顔料であってもよい。
この顔料(上記平板状顔料を除く)の含有量の範囲は、後述するように、該顔料と上記平板状顔料及び体質材との合計含有量の範囲内で好適な量が調整される。
この体質材、上記平板状顔料及び上記顔料のからなる粉体成分の合計含有量が60%未満では、眉毛上へのボカシラインの塗布性の良好な物が得られず、一方、90%超過では、強度が弱すぎたり、脆すぎたりして実使用に耐えられなくなり、好ましくない。
好ましい体質材の含有量は、固形棒状化粧料全量に対して、5〜15%が望ましい。
具体的に用いることができる固着樹脂成分としては、例えば、(アクリレーツ/アクリル酸ベヘニル/メタクリル酸ジメチコン)コポリマー、(アクリレーツ/アクリル酸ステアリル/メタクリル酸ジメチコン)コポリマー、アクリレーツ/アクリル酸エチルヘキシル/メタクリル酸ジメチコン)コポリマー、トリメチルシロキシケイ酸などを少なくとも1種を挙げることができる。
この固着樹脂成分の合計含有量が1%未満であると、均一で固着力のある塗膜が得られず、一方、15%超過では、脆い塗膜の描線となる。
このシリコーン溶剤の含有量が1%未満であると、眉毛上へのボカシラインの塗布性の良好な物が得られず、一方、20%超過では、強度が弱すぎたり、脆すぎたりして実使用に耐えられなくなる。
好ましくは、塗布性、光沢付与の点から、上記炭化水素系ワックスなどが挙げられる。
これらのワックス成分の含有量が0.5%未満では、固形棒状化粧料の芯としての保形性が困難となり、一方、10%超過では、眉上への良好な塗布感が得られず、好ましくない。
このゲル化剤の含有量は、固形棒状化粧料全量に対して、好ましくは、0.1〜5%、更に好ましくは、0.5〜2.0%とすることが望ましい。
この油性成分の合計含有量は、固形棒状化粧料全量に対して、好ましくは、使用性-滑らかな塗布感付与の点から、0〜15%、更に好ましくは、2〜10%とすることが望ましい。
特に、本発明の固形棒状化粧料では、直径6mm以下の芯繰り出し容器に使用した場合にでも、実使用特性を損なわない強度を備えたアイブロウ等に好適な固形棒状化粧料が得られることとなる。
すなわち、本発明の固形棒状化粧料は、少なくとも顔料及び体質材を含む粉体成分を60〜90質量%と、固着樹脂成分と、シリコーン溶剤と、ワックス成分とを含有するものであり、固着樹脂成分が各成分を均一に分散する事により、折損強度などの機械的強度は実用的な範囲とすることができ、更に、均一に分散された多量の粉体成分が、ワックス成分により、点接着されており、塗布と言う軽い摩擦力により崩れる事により、眉毛上へのボカシ描画に優れると共に、眉毛への付着力に優れ、しかも、その形状により皮膚上へラインを引けることができ、経時安定性に優れ、特に高温での安定性に優れ、かつ、粉体成分が多く、芯表面へのワックス成分の分布が少ない事により、経時後の表面の発粉現象が起きないものとなる。
下記表1に示す配合処方の固形棒状化粧料(配合単位:質量%、全量100質量%)をロール分散、溶解、調製して、押し出し成形により円柱状の各固形棒状化粧料(φ2×60mm)を得た。
なお、表1中の粉体成分として用いる顔料の欄における「ベンガラ、黒酸化鉄、酸化チタン、グンジョウ(群青)、コンジョウ(紺青)」の配合比率(質量比)は、順番に60:20:10:5:5であり、また、顔料の欄の2種、体質材Aの欄の2種の各平均粒子径は5〜20μmの範囲内のものを用いた。
これらの結果を下記表1及び表2に示す。
得られた各固形棒状化粧料を70℃の恒温槽に12時間静置し、取り出し直後に正常に使用可能か否かを下記評価基準で評価した。
評価基準:
○:問題なく、良好に使用できる。
△:棒状化粧料として容器より繰り出せるが、変形している
×:溶解変形状態となり、容器より棒状化粧料は繰り出せず使用できない。
−:棒状化粧料として初期より正常に塗布できない為、評価基準に対応なし
得られた各固形棒状化粧料を室温(25℃)下に6ヶ月間静置し、各固形棒状化粧料表面の観察を行い粉体の析出の仕方を下記評価基準で官能評価した。
評価基準:
○:発粉は全くなかった。
△:わずかな発粉を認める。
×:発粉を認める。
得られた各固形棒状化粧料をアイブロウペンシルとしてモニター25人の皮膚(眉毛)に使用してもらい下記評価基準で評価した。
評価基準:
○:15人以上が硬さほどよく良好に使用できたと回答。
△:15人以上が硬めであるが良好に使用できたと回答。
△△:15人以上が柔らかめであるが、良好に使用できたと回答。
×:10人以上が描線塗布には適さないと回答。
得られた各固形棒状化粧料をアイブロウペンシルとしてモニター25人の皮膚(眉毛等)に使用してもらい下記評価基準で評価した。
評価基準:
○: モニター全員の眉毛上にはっきり塗布色を確認できた。
△: 8割以下であるが、眉毛上に塗布色を確認できた
×: モニター全員の眉毛上に塗布色を確認できなかった。
得られた各固形棒状化粧料をアイブロウペンシルとしてモニター25人の皮膚(眉毛等)に使用してもらい下記評価基準で評価した。
評価基準:
○: モニターの20人以上が、眉毛上にふわっとボカシた塗布色を認めた。
△: モニターの10人以上が、眉毛上塗布色を認めるが、眉毛に軽さがなく、
べたつき感を感じた。
×: モニター全員の眉毛上にふわっとぼかした塗布ができない。
得られた各固形棒状化粧料の成形性について下記評価基準で評価した。
評価基準:
○:棒状化粧料として成形でき、正常に塗布できる。
△:棒状化粧料として成形できるが、塗布時に折れ、くずれ等を生じる。
×:棒状化粧料として成形できない。
得られた各固形棒状化粧料をキャップなしアイブロウペンシル容器、キャップ付きのアイブロウペンシル気密容器を用いて、下記評価基準で評価した。
評価基準:
○:キャップなし容器での保存、使用が可能
×:キャップ付きの気密容器で保存しないと成分が揮発し、化粧料として使用できなくなる。
比較例を個別的に見ると、比較例1、2及び3は、多量のワックス成分が含まれることから、温度変化等により粉体の析出が見られた。これは、時間の経過により温度や湿度差によりワックス成分が流動することによって粉状のワックスの析出が起こったものと考えられた。また、比較例1、2及び3は、ワックス成分の割合が粉体成分に対し多いため眉上への塗布が可能なパウダーアイブロウとしての使用には適さないことが確認された。比較例4及び5は、揮発成分が揮発した後、パウダーアイブロウとしての使用感が得られるものの、使用着後には多量のシリコーン溶剤の含有が災いして眉毛同士がべた付いて使用感の悪いものとなってしまったり、揮発を止めるため、キャップ付の高価な容器が必要となると考えられる。そして、比較例1〜5の何れもが、ワックス成分の割合が粉体成分に対し多いため、高温での経時試験後には形状を保てなくなっており、本発明の効果を発揮できないことが判った。次に、比較例6は粉体成分が90質量%超過のため、耐温度性、アイブロウペンシルとしての使用性に不適である。比較例7〜9は順次、固着樹脂成分を含有しない場合、シリコーン溶剤を含有しない場合であり、ゲル化剤及びワックス成分を含有しない場合であり、また、比較例10及び11は粉体成分として顔料、体質材を各単独で用いた場合であり、これらの場合は、本発明の効果を発揮できないことが判った。
これに対して、本発明の範囲内となる実施例1〜7は、多量の粉体成分同士の粘着によって、却って形状を保持可能等であり、本発明の効果を発揮できるものと確認された。
Claims (3)
- 少なくとも粉体成分を60〜90質量%と、固着樹脂成分と、シリコーン溶剤と、ワックス成分とを含有する固形棒状化粧料であって、該粉体成分が顔料及び体質材であることを特徴とする固形棒状化粧料。
- 前記顔料は親油性処理平板状顔料を含むことを特徴とする請求項1に記載の固形棒状化粧料。
- 前記親油性処理平板状顔料の平均粒子径が5〜100μmであることを特徴とする請求項2に記載の固形棒状化粧料。