JP2015530436A - 粘着剤組成物 - Google Patents
粘着剤組成物 Download PDFInfo
- Publication number
- JP2015530436A JP2015530436A JP2015529669A JP2015529669A JP2015530436A JP 2015530436 A JP2015530436 A JP 2015530436A JP 2015529669 A JP2015529669 A JP 2015529669A JP 2015529669 A JP2015529669 A JP 2015529669A JP 2015530436 A JP2015530436 A JP 2015530436A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- weight
- adhesive composition
- ionic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
これを改善するために、粘着剤組成物にイオン性帯電防止剤を混合使用するが、前記イオン性帯電防止剤の表面移行により析出されるブリードアウト(Bleed out)現象で、浮き立ち、気泡および剥離などを発生させることがある。特にこのような問題は、高温または高温多湿な環境に露出した場合、さらに悪くなることがある。
金属の腐食性を改善するために、粘着剤組成物の耐久性向上のために必須に使用される水素イオン発生単量体(例えば、カルボキシ基を有する単量体)の使用を排除している傾向がある。
これと関連して、水素イオン発生単量体を排除しながら、アミン基またはポリエチレングリコール基を導入し、帯電防止剤との相溶性を増加させたアクリル系共重合体を使用する方法が提案されている(特許文献1、2参照)。しかし、前記方法は、ブリードアウト現象による耐久性低下を改善するには非常に不足な効果を示しているのが実情である。
本発明の粘着剤組成物は、別に腐食防止剤成分を含有せずに、金属層の腐食を効果的に抑制することができる利点がある。
したがって、前記粘着剤組成物は、静電気が発生しやすいプラスチック製品、特に電気/電子機器などの分野で静電気回避用途にその活用度が高いものと予想される。
以下、本発明を詳しく説明する。
本発明の粘着剤組成物は、アクリル系共重合体の重合反応によって固定化されたイオン性単量体によってイオン性帯電防止剤の相溶性が向上する。
前記相溶性の向上により帯電防止剤成分が表面に移動して析出されるブリードアウト(Bleed out)現象が抑制され、耐久性に優れる。このような現象は、高温または高温・多湿な環境の下でも抑制され、優れた耐久性の維持が可能である。
また、本発明の粘着剤組成物は、イオン性帯電防止剤とともにイオン性単量体が帯電防止性を有するので、従来、帯電防止剤のみを利用した粘着剤組成物に比べてその性能が格別に向上する。
アクリル系共重合体に含有されるイオン性単量体は、アクリレート系単量体と共重合が可能になるようにビニル基を含み、イオン性帯電防止剤とイオン結合を形成できるものを使用する。
具体的には、アルカリ金属塩、アンモニウム塩、スルホニウム塩およびホスホニウム塩よりなる群から選択された陽イオンと;フッ素含有無機塩、フッ素含有有機塩およびヨウ化イオンよりなる群から選択された陰イオンからなるイオン性塩類であることができる。
このような添加剤は、本発明の効果を阻害しない範囲内で適切に含量を調節することができる。
製造例1
窒素ガスが還流され、温度調節が容易になるように冷却装置を設置した1Lの反応器にn−ブチルアクリレート(BA)85重量部、メチルアクリレート(MA)8重量部、2−ヒドロキシエチルアクリレート2.0重量部、下記化学式で表されるイオン性単量体5重量部からなる単量体混合物を投入した後、溶剤としてアセトン100重量部を投入した。次に、酸素を除去するために窒素ガスを1時間パージングした後、62℃に維持した。前記混合物を均一にした後、反応開始剤としてアゾビスイソブチロニトリル(AIBN)0.07重量部を投入し、6時間反応させて、重量平均分子量が約100万であるアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、下記化学式([化4])で表される単量体の代わりに、下記化学式([化5])で表される単量体を使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、下記化学式で表される単量体を使用せず、n−ブチルアクリレート(BA)を90重量部使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、n−ブチルアクリレート(BA)89.95重量部、メチルアクリレート(MA)8重量部、2−ヒドロキシエチルアクリレート2.0重量部、下記化学式で表されるイオン性単量体0.05重量部からなる単量体混合物を使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、n−ブチルアクリレート(BA)89重量部、メチルアクリレート(MA)8重量部、2−ヒドロキシエチルアクリレート2.0重量部、下記化学式で表されるイオン性単量体1重量部からなる単量体混合物を使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、n−ブチルアクリレート(BA)81重量部、メチルアクリレート(MA)8重量部、2−ヒドロキシエチルアクリレート2.0重量部、下記化学式で表されるイオン性単量体9重量部からなる単量体混合物を使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、n−ブチルアクリレート(BA)75重量部、メチルアクリレート(MA)8重量部、2−ヒドロキシエチルアクリレート2.0重量部、下記化学式で表されるイオン性単量体15重量部からなる単量体混合物を使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、下記化学式で表される単量体の代わりに、アクリルアミドを5重量部使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、下記化学式で表される単量体の代わりに、メトキシエチルアクリレートを5重量部使用してアクリル系共重合体を製造した。
前記製造例1と同一に実施するが、下記化学式で表される単量体の代わりに、アクリル酸を5重量部使用してアクリル系共重合体を製造した。
下記表1のようにアクリル系共重合体、イオン性帯電防止剤、架橋剤(日本ポリウレタン工業社製、CORONATE−L、0.5重量部)およびシランカップリング剤(信越化学工業社製、KBM−403、0.5重量部)を混合した後、エチルアセテートで希釈して、固形分の濃度15重量%の粘着剤組成物を製造した。この際、表1は、アクリル系共重合体およびイオン性帯電防止剤を記載し、その他の架橋剤およびシランカップリング剤は、同一の成分および含量を使用した。
厚さ185μmのヨード系偏光板に前記製造した粘着層を粘着加工で積層して、粘着剤付き偏光板を製造した。製造した偏光板を23℃、60%RHの条件下で20日間保管した。
前記実施例および比較例で製造された粘着剤組成物、粘着剤付き偏光板の物性を下記の方法で測定し、その結果を下記表2に示した。
製造された粘着剤付き偏光板を表面抵抗測定器(MCP−HT450、Mitsubishi chemical社製)を利用して粘着剤層の3地点をそれぞれ10回ずつ測定し、その平均値で示した。
その後、粘着剤付き偏光板を60℃で24時間放置した後、前記と同一の方法で測定した。
粘着剤付き偏光板の離型フィルムを剥離し、粘着剤層の表面とコーニングガラスを接合した後、80℃(耐熱性)/60℃、90RH%(耐湿熱性)で300時間放置した後、見掛けを確認した。
<評価基準>
気泡と剥離現象が視認される:×
気泡や剥離現象が若干視認されるが、偏光板性能は維持する:○
気泡と剥離現象が視認されない:◎
粘着剤付き偏光板の離型フィルムを剥離した後、粘着剤層の表面とアルミニウム板を接合した後、60℃、95%RHの雰囲気の下で250時間放置し、試験片を製造した。
前記積層体から粘着剤層を剥離し、前記粘着剤層と接触したアルミニウム板の表面を目視で観察し、腐食の有無を評価した。
<評価基準>
アルミニウム板表面が全く腐食されない:◎
アルミニウム板表面が若干腐食されるが、アルミニウム板の機能は維持する:○
アルミニウム板表面が腐食される:×
Claims (7)
- ビニル基を有するイオン性単量体が含有されたアクリル系共重合体、およびイオン性帯電防止剤を含有する粘着剤組成物。
- 前記ビニル基を有するイオン性単量体は、下記化学式で表される、請求項1に記載の粘着剤組成物。
- 前記アクリル系共重合体は、炭素数1〜12のアルキル基を有する(メタ)アクリレート単量体およびビニル基を有するイオン性単量体を含有する、請求項1に記載の粘着剤組成物。
- 前記ビニル基を有するイオン性単量体は、炭素数1〜12のアルキル基を有する(メタ)アクリレート単量体100重量部に対して0.1〜10重量部を含有する、請求項3に記載の粘着剤組成物。
- 前記イオン性帯電防止剤は、アルカリ金属塩、アンモニウム塩、スルホニウム塩およびホスホニウム塩よりなる群から選択された陽イオンと;
フッ素含有無機塩、フッ素含有有機塩およびヨウ化イオンよりなる群から選択された陰イオンからなるイオン性塩類である、請求項1に記載の粘着剤組成物。 - 前記イオン性帯電防止剤は、アクリル系共重合体100重量部に対して0.1〜5重量部を含有する、請求項5に記載の粘着剤組成物。
- 前記粘着剤組成物は、架橋剤をさらに含有する、請求項1に記載の粘着剤組成物。