JP2014148655A - 硬化性樹脂組成物及び電子部品装置 - Google Patents
硬化性樹脂組成物及び電子部品装置 Download PDFInfo
- Publication number
- JP2014148655A JP2014148655A JP2013019773A JP2013019773A JP2014148655A JP 2014148655 A JP2014148655 A JP 2014148655A JP 2013019773 A JP2013019773 A JP 2013019773A JP 2013019773 A JP2013019773 A JP 2013019773A JP 2014148655 A JP2014148655 A JP 2014148655A
- Authority
- JP
- Japan
- Prior art keywords
- group
- epoxy resin
- resin composition
- compound
- curable resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)エポキシ樹脂、(B)フェノール樹脂、(C)硬化促進剤、及び(D)マレイミド化合物を含有し、前記(C)硬化促進剤が下記一般式(I−1)で示される化合物を含有し、前記(D)マレイミド化合物が、1分子中にマレイミド基を2つ有する化合物と1分子中にマレイミド基を3つ以上有する化合物とを含む硬化性樹脂組成物。式(I−1)中、R1〜R3は、それぞれ独立して、炭素数1〜18の炭化水素基であり、R1〜R3のうち2以上が互いに結合して環状構造を形成してもよく、R4〜R7は、それぞれ独立して、水素原子、水酸基、又は炭素数1〜18の有機基であり、R4〜R7のうち2以上が互いに結合して環状構造を形成してもよい。
【選択図】なし
Description
<1> (A)エポキシ樹脂、(B)フェノール樹脂、(C)硬化促進剤、及び(D)マレイミド化合物を含有し、前記(C)硬化促進剤が下記一般式(I−1)で示される化合物を含有し、前記(D)マレイミド化合物が、1分子中にマレイミド基を2つ有する化合物と1分子中にマレイミド基を3つ以上有する化合物とを含む硬化性樹脂組成物。
本発明による硬化性樹脂組成物は、(A)エポキシ樹脂、(B)フェノール樹脂、(C)硬化促進剤、及び(D)マレイミド化合物を含有し、前記(C)硬化促進剤が下記一般式(I−1)で示される化合物を含有し、前記(D)マレイミド化合物が、1分子中にマレイミド基を2つ有する化合物と1分子中にマレイミド基を3つ以上有する化合物とを含む。
本発明による硬化性樹脂組成物は、上記成分(A)〜(D)に加えて無機充填剤を更に含有してもよい。また、必要に応じて、カップリング剤、イオン交換体、離型剤、応力緩和剤、難燃剤、着色剤等の添加剤を含有してもよい。以下、本発明の硬化性樹脂組成物を構成する主な成分について説明する。
本発明の硬化性樹脂組成物は、(A)エポキシ樹脂を含む。エポキシ樹脂としては、1分子中に2個以上のエポキシ基を有するエポキシ樹脂を用いることができる。具体的には、フェノールノボラック型エポキシ樹脂、オルソクレゾールノボラック型エポキシ樹脂をはじめとする、フェノール、クレゾール、キシレノール、レゾルシン、カテコール、ビスフェノールA、ビスフェノールF等のフェノール化合物及びα−ナフトール、β−ナフトール、ジヒドロキシナフタレン等のナフトール化合物からなる群より選ばれる少なくとも1種のフェノール性化合物と、ホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド等の脂肪族アルデヒド化合物とを酸性触媒下で縮合又は共縮合させて得られるノボラック樹脂をエポキシ化したノボラック型エポキシ樹脂;上記フェノール性化合物と、ベンズアルデヒド、サリチルアルデヒド等の芳香族アルデヒド化合物とを酸性触媒下で縮合又は共縮合させて得られるトリフェニルメタン型フェノール樹脂をエポキシ化したトリフェニルメタン型エポキシ樹脂;上記フェノール化合物及びナフトール化合物と、アルデヒド化合物とを酸性触媒下で共縮合させて得られるノボラック樹脂をエポキシ化した共重合型エポキシ樹脂;ビスフェノールA、ビスフェノールF等のジグリシジルエーテルであるジフェニルメタン型エポキシ樹脂;アルキル置換又は非置換のビフェノールのジグリシジルエーテルであるビフェニル型エポキシ樹脂;スチルベン系フェノール化合物のジグリシジルエーテルであるスチルベン型エポキシ樹脂;ビスフェノールS等のジグリシジルエーテルである硫黄原子含有エポキシ樹脂;ブタンジオール、ポリエチレングリコール、ポリプロピレングリコール等のアルコール類のグリシジルエーテルであるエポキシ樹脂;フタル酸、イソフタル酸、テトラヒドロフタル酸等の多価カルボン酸化合物のグリシジルエステル型エポキシ樹脂;アニリン、ジアミノジフェニルメタン、イソシアヌル酸等の窒素原子に結合した活性水素をグリシジル基で置換したグリシジルアミン型エポキシ樹脂;ジシクロペンタジエンとフェノール化合物の共縮合樹脂をエポキシ化したジシクロペンタジエン型エポキシ樹脂;分子内のオレフィン結合をエポキシ化して得られるビニルシクロヘキセンジエポキシド、3,4−エポキシシクロヘキシルメチル−3,4−エポキシシクロヘキサンカルボキシレート、2−(3,4−エポキシ)シクロヘキシル−5,5−スピロ(3,4−エポキシ)シクロヘキサン−m−ジオキサン等の脂環型エポキシ樹脂;パラキシリレン変性フェノール樹脂のグリシジルエーテルであるパラキシリレン変性エポキシ樹脂;メタキシリレン変性フェノール樹脂のグリシジルエーテルであるメタキシリレン変性エポキシ樹脂;テルペン変性フェノール樹脂のグリシジルエーテルであるテルペン変性エポキシ樹脂;ジシクロペンタジエン変性フェノール樹脂のグリシジルエーテルであるジシクロペンタジエン型エポキシ樹脂;シクロペンタジエン変性フェノール樹脂のグリシジルエーテルであるシクロペンタジエン変性エポキシ樹脂;多環芳香環変性フェノール樹脂のグリシジルエーテルである多環芳香環変性エポキシ樹脂;ナフタレン環含有フェノール樹脂のグリシジルエーテルであるナフタレン型エポキシ樹脂;ハロゲン化フェノールノボラック型エポキシ樹脂;ハイドロキノン型エポキシ樹脂;トリメチロールプロパン型エポキシ樹脂;オレフィン結合を過酢酸等の過酸で酸化して得られる線状脂肪族エポキシ樹脂;ジフェニルメタン型エポキシ樹脂;フェノールアラルキル樹脂、ナフトールアラルキル樹脂等のアラルキル型フェノール樹脂のエポキシ化物であるアラルキル型エポキシ樹脂;などが挙げられる。これらは1種単独で用いても2種以上を組み合わせて用いてもよい。
以下、好ましいエポキシ樹脂の具体例を示す。
また、一般式(III)〜(XI)における炭素数1〜18の有機基はアルキル基又はアリール基であることが好ましい。
本発明の硬化性樹脂組成物は、(B)フェノール樹脂を含む。フェノール樹脂の種類としては特に制限はない。例えば、硬化剤として一般に使用される1分子中に2個以上のフェノール性水酸基を有するフェノール樹脂又は多価フェノールが挙げられる。具体的には、レゾルシン、カテコール、ビスフェノールA、ビスフェノールF、置換又は非置換のビフェノール等の1分子中に2個のフェノール性水酸基を有する化合物;フェノール、クレゾール、キシレノール、レゾルシン、カテコール、ビスフェノールA、ビスフェノールF、フェニルフェノール、アミノフェノール等のフェノール化合物及びα−ナフトール、β−ナフトール、ジヒドロキシナフタレン等のナフトール化合物からなる群より選ばれる少なくとも一種のフェノール性化合物と、ホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド、ベンズアルデヒド、サリチルアルデヒド等のアルデヒド化合物とを酸性触媒下で縮合又は共縮合させて得られるノボラック型フェノール樹脂;上記フェノール性化合物と、ジメトキシパラキシレン、ビス(メトキシメチル)ビフェニル等とから合成されるフェノールアラルキル樹脂、ナフトールアラルキル樹脂等のアラルキル型フェノール樹脂;パラキシリレン及び/又はメタキシリレン変性フェノール樹脂;メラミン変性フェノール樹脂;テルペン変性フェノール樹脂;上記フェノール性化合物と、ジシクロペンタジエンとから共重合により合成されるジシクロペンタジエン型フェノール樹脂及びジシクロペンタジエン型ナフトール樹脂;シクロペンタジエン変性フェノール樹脂;多環芳香環変性フェノール樹脂;ビフェニル型フェノール樹脂;上記フェノール性化合物と、ベンズアルデヒド、サリチルアルデヒド等の芳香族アルデヒド化合物とを酸性触媒下で縮合又は共縮合させて得られるトリフェニルメタン型フェノール樹脂;これら2種以上を共重合して得た共重合型フェノール樹脂などが挙げられる。これらのフェノール樹脂は、1種単独で用いても2種以上を組み合わせて用いてもよい。
本発明の硬化性樹脂組成物は(C)硬化促進剤を含有し、前記硬化促進剤は、下記一般式(I−1)で示される化合物から選ばれる少なくとも1種類の化合物を含む。
炭素数が6〜18である芳香族炭化水素基としては、流動性の観点からは置換基を含めた炭素数が6〜12のアリール基が好ましく、炭素数6〜10のアリール基がより好ましく、フェニル基、p-トリル基又はp-メトキシフェニル基が更に好ましい。
ホスフィンと、1,4−ベンゾキノン、2,5−トルキノン等の対応するキノン誘導体とがともに溶解する溶媒中で両者を溶解させ、付加反応させる方法、及びトリフェニルホスフィン、トリ−p−トリルホスフィン等の対応する3級ホスフィンと、4−ブロモフェノール、4−クロロフェノール、3−クロロフェノール、2−クロロフェノール等のハロゲン化フェノール化合物を反応させた後に、脱ハロゲン化水素の工程を経る方法を挙げることができる。上記溶媒としては、芳香族炭化水素系溶媒、脂肪族炭化水素系溶媒、ケトン系溶媒、アルコール系溶媒、エーテル系溶媒、アミド系溶媒、エステル系溶媒、水等が挙げられる。これら溶媒は1種単独で使用しても、2種類以上を併用してもよい。
上記付加反応における反応温度は、反応が進行し、生成する一般式(I−1)で示される化合物(生成物)が安定に保持される温度であれば、限定されるものではなく、反応速度及び生成物の安定性の観点から−20℃〜200℃であることが好ましい。
本発明の硬化性樹脂組成物は、(D)マレイミド化合物を含み、前記(D)マレイミド化合物が、1分子中にマレイミド基を2つ有する化合物(以下「第一のマレイミド化合物」と称する場合がある)、及び1分子中にマレイミド基を3つ以上有する化合物(以下「第二のマレイミド化合物」と称する場合がある)の双方を含む。第一のマレイミド化合物及び第二のマレイミド化合物を含むことにより、硬化性樹脂組成物の均一性が向上するため、硬化後の耐熱性が向上する。この理由は明らかではないが以下のように考えることができる。第一のマレイミド化合物及び第二のマレイミド化合物の両者を含むことで融点が低下するため混練性が高まり、より均一な硬化性樹脂組成物を得ることができる。これにより硬化後の耐熱性が向上するものと考えられる。
マレイミド化合物は、第一のマレイミド化合物及び第二のマレイミド化合物以外に更に他のマレイミド化合物を含有してもよい。
硬化性樹脂組成物が他のマレイミド化合物を含有する場合、(D)マレイミド化合物の総量に対する、他のマレイミド化合物の含有率は、50質量%以下であることが好ましく、30質量%以下であることがより好ましく、20質量%以下であることが更に好ましい。
本発明の硬化性樹脂組成物は、(E)無機充填剤を必要に応じて更に含有してもよい。特に、硬化性樹脂組成物を封止用成形材料として用いる場合には、無機充填剤を含有することが好ましい。
本発明の硬化性樹脂組成物は、上述の成分に加えて、以下に例示するカップリング剤、イオン交換体、離型剤、応力緩和剤、難燃剤、着色剤等の各種添加剤を更に含有してもよい。なお、本発明の硬化性樹脂組成物は、以下に例示する添加剤以外にも、必要に応じて当技術分野で周知の各種添加剤を含有してもよい。
本発明の封止用硬化性樹脂組成物は、樹脂成分と無機充填剤との接着性を高めるために、必要に応じてカップリング剤を含有してもよい。カップリング剤としては、エポキシシラン、メルカプトシラン、アミノシラン、アルキルシラン、ウレイドシラン、ビニルシラン等の各種シラン系化合物;チタン系化合物;アルミニウムキレート化合物;アルミニウム/ジルコニウム系化合物;などの公知のカップリング剤が挙げられる。
本発明の硬化性樹脂組成物は、必要に応じてイオン交換体を含有してもよい。特に、硬化性樹脂組成物を封止用成形材料として用いる場合には、封止される素子を備える電子部品装置の耐湿性及び高温放置特性を向上させる観点から、イオン交換体を含有することが好ましい。イオン交換体としては特に制限はなく、従来公知のものを用いることができる。具体的には、ハイドロタルサイト化合物、並びにマグネシウム、アルミニウム、チタン、ジルコニウム及びビスマスからなる群より選ばれる少なくとも1種の元素の含水酸化物等が挙げられる。これらのイオン交換体は、1種を単独で、又は2種以上を組み合わせて用いることができる。中でも、下記一般式(A)で示されるハイドロタルサイトが好ましい。
(0<X≦0.5、mは正の数)
本発明の硬化性樹脂組成物は、成形時における金型との良好な離型性を得る観点から、離型剤を含有してもよい。離型剤としては特に制限はなく、従来公知のものを用いることができる。具体的には、例えば、カルナバワックス、モンタン酸、ステアリン酸等の高級脂肪酸、高級脂肪酸金属塩、モンタン酸エステル等のエステル系ワックス、酸化ポリエチレン、非酸化ポリエチレン等のポリオレフィン系ワックスなどが挙げられる。これらの離型剤は1種を単独で用いても2種以上を組み合わせて用いてもよい。中でも、酸化型又は非酸化型のポリオレフィン系ワックスが好ましい。ポリオレフィン系ワックスとしては、市販品ではヘキスト社製のH4、PE、PEDシリーズ等の数平均分子量が500〜10000程度の低分子量ポリエチレンなどが挙げられる。
また、ポリオレフィン系ワックスに他の離型剤を併用する場合、他の離型剤の含有率は(A)エポキシ樹脂の総量に対して0.1質量%〜10質量%が好ましく、0.5質量%〜3質量%がより好ましい。
本発明の硬化性樹脂組成物は、シリコーンオイル、シリコーンゴム粉末等の応力緩和剤などを必要に応じて含有してもよい。応力緩和剤を含有することにより、パッケージの反り変形及びパッケージクラックの発生をより低減させることができる。応力緩和剤としては、一般に使用されている公知の可とう剤(応力緩和剤)であれば特に限定されるものではない。具体的には、例えば、シリコーン系、スチレン系、オレフィン系、ウレタン系、ポリエステル系、ポリエーテル系、ポリアミド系、ポリブタジエン系等の熱可塑性エラストマー、NR(天然ゴム)、NBR(アクリロニトリル−ブタジエンゴム)、アクリルゴム、ウレタンゴム、シリコーンパウダー等のゴム粒子、メタクリル酸メチル−スチレン−ブタジエン共重合体(MBS)、メタクリル酸メチル−シリコーン共重合体、メタクリル酸メチル−アクリル酸ブチル共重合体等のコア−シェル構造を有するゴム粒子などが挙げられる。これらの可とう剤は、1種を単独で用いても2種以上組み合わせて用いてもよい。中でも、シリコーン系可とう剤が好ましく、シリコーン系可とう剤としては、エポキシ基を有するもの、アミノ基を有するもの、これらをポリエーテル変性したもの等が挙げられる。
本発明の硬化性樹脂組成物は、難燃性を付与する観点から、必要に応じて難燃剤を含有してもよい。難燃剤としては特に制限はなく、一般に使用されている公知の難燃剤から適宜選択できる。具体的には、ハロゲン原子、アンチモン原子、窒素原子又はリン原子を含む公知の有機若しくは無機の化合物、金属水酸化物などが挙げられる。これらの難燃剤は、1種を単独で用いても2種以上を組み合わせて用いてもよい。硬化性樹脂組成物が難燃剤を含有する場合、その含有率は、難燃効果が達成されれば特に制限はない。例えば、(A)エポキシ樹脂の総量に対して1質量%〜30質量%が好ましく、2質量%〜15質量%がより好ましい。
本発明の硬化性樹脂組成物は、必要に応じて着色剤を更に含有してもよい。着色剤としては、カーボンブラック、有機染料、有機顔料、酸化チタン、ピッチ、鉛丹、ベンガラ等の公知の着色剤を挙げることができる。着色剤の含有量は目的等に応じて適宜選択できる。
硬化性樹脂組成物の調製方法は特に制限されず、各種成分を均一に分散混合できるのであれば、いかなる手法を用いても調製できる。一般的な手法としては、所定の配合量の成分をミキサー等によって充分混合した後、ミキシングロール、押出機等によって溶融混練し、冷却し、粉砕する方法を挙げることができる。より具体的には、例えば、上述した成分の所定量を均一に撹拌して混合し、予め70℃〜140℃に加熱してあるニーダー、ロール、エクストルーダー等で混練し、冷却し、粉砕することで得ることができる。硬化性樹脂組成物は、パッケージの成形条件に合うような寸法及び質量でタブレット化すると取り扱いが容易である。
本発明の電子部品装置は、素子と、前記素子を封止する上述の硬化性樹脂組成物の硬化物と、を備える。本発明の硬化性樹脂組成物を用いて作製した電子部品装置は信頼性に優れる。
電子部品装置としては、例えば、リードフレーム、配線済みのテープキャリア、配線板、ガラス、シリコンウエハ等の支持部材に、半導体チップ、トランジスタ、ダイオード、サイリスタ等の能動素子、コンデンサ、抵抗体、コイル等の受動素子などの素子を搭載して得られた素子部を本発明の硬化性樹脂組成物で封止したものが挙げられる。より具体的には、例えば、リードフレーム上に半導体素子を固定し、ボンディングパッド等の素子の端子部とリード部をワイヤボンディング、バンプ等で接続した後、本発明の硬化性樹脂組成物を用いてトランスファ成形などによって封止した構造を有する、DIP(Dual Inline Package)、PLCC(Plastic Leaded Chip Carrier)、QFP(Quad Flat Package)、SOP(Small Outline Package)、SOJ(Small Outline J−lead package)、TSOP(Thin Small Outline Package)、TQFP(Thin Quad Flat Package)等の一般的な樹脂封止型IC;テープキャリアにバンプで接続した半導体チップを、本発明の硬化性樹脂組成物で封止した構造を有する、TCP(Tape Carrier Package);配線板やガラス板上に形成した配線に、ワイヤボンディング、フリップチップボンディング、はんだ等で接続した半導体チップ、トランジスタ、ダイオード、サイリスタ等の能動素子及びコンデンサ、抵抗体、コイル等の受動素子からなる群より選ばれる少なくとも1種の素子を、本発明の硬化性樹脂組成物で封止した構造を有するCOB(Chip On Board);モジュール、ハイブリッドIC、マルチチップモジュール、裏面に配線板接続用の端子を形成した有機基板の表面に素子を搭載し、バンプ又はワイヤボンディングにより素子と有機基板に形成された配線を接続した後、本発明の硬化性樹脂組成物で素子を封止した構造を有するBGA(Ball Grid Array)、CSP(Chip Size Package);などが挙げられる。また、配線板においても本発明の硬化性樹脂組成物を有効に使用することができる。
エポキシ樹脂として、以下を用意した。
・エポキシ樹脂1:エポキシ当量168、軟化点62℃のトリフェニルメタン型エポキシ樹脂(ジャパンエポキシレジン株式会社、商品名1032H60)
・エポキシ樹脂2:エポキシ当量195、軟化点60℃のオルソクレゾールノボラック型エポキシ樹脂(DIC株式会社、商品名N−500P1)
・エポキシ樹脂3:エポキシ当量282、軟化点56℃のビフェニレンアラルキル型エポキシ樹脂(日本化薬株式会社、商品名NC−3000)
・フェノール樹脂1:水酸基当量103、軟化点84℃のトリフェニルメタン型フェノール樹脂(エアウォーター株式会社、商品名HE−910−10)
・フェノール樹脂2:水酸基当量110、軟化点95℃の1,6−ジヒドロキシナフタレンアラルキル樹脂(新日鐵化学株式会社、商品名HE−910−10)
・フェノール樹脂3:水酸基当量106、軟化点85℃のフェノールノボラック樹脂(日立化成株式会社、商品名HP−850N)
・フェノール樹脂4:水酸基当量190、軟化点80℃のビフェニレンアラルキル型フェノール樹脂(エアウォーター株式会社、商品名HE−200C−10)
・硬化促進剤1:トリフェニルホスフィンと1,4−ベンゾキノンの付加反応物
・硬化促進剤2:トリ−p−トリルホスフィンと1,4−ベンゾキノンの付加反応物
・硬化促進剤3:トリ−n−ブチルホスフィンと1,4−ベンゾキノンの付加反応物
・硬化促進剤4:4−トリフェニルホスホニオフェノラート
・硬化促進剤A:トリフェニルホスフィン
・硬化促進剤B:トリ−p−トリルホスフィン
・硬化促進剤C:1,8−ジアザビシクロ[5.4.0]ウンデカ−7−エン
・マレイミド1:ポリフェニルメタンマレイミド(大和化成工業株式会社、商品名BMI−2300)
・マレイミドA:4,4’−ジフェニルメタンジマレイミド(大和化成工業株式会社、商品名BMI−1000)
・マレイミドB:2,2’−ビス[4−(4−マレイミドフェノキシ)フェニル]プロパン(大和化成工業株式会社、商品名BMI−4000)
・マレイミドC:3,3’−ジメチル−5,5’−ジエチル−4,4’−ジフェニルメタンビスマレイミド(大和化成工業株式会社、商品名BMI−5100)
・平均粒径17.5μm、比表面積3.8m2/gの球状溶融シリカ
・カップリング剤:エポキシシラン(γ−グリシドキシプロピルトリメトキシシラン)
・着色剤:カーボンブラック(三菱化学株式会社、商品名MA−100)
・離型剤:カルナバワックス(株式会社セラリカNODA)
上述の成分をそれぞれ表1に示す質量部でアルミカップ中に添加し、ホットプレート上で80℃、5分の条件で加熱することにより溶解性を確認した。均一に溶解したものを○、均一ではなかったものを×とした。表1に示すように分子内に2つのマレイミド基を有する分子と分子内に3つのマレイミド基を有する分子が混ざっているマレイミド1が均一に溶解したため、次にこれらを用いて硬化性樹脂組成物の評価を行った。
上述の成分をそれぞれ表2及び表3に示す質量部で配合し、混練温度80℃、混練時間15分の条件でロール混練を行うことによって、それぞれ実施例1〜12、比較例1〜6の硬化性樹脂組成物を得た。
次に、実施例1〜12、及び比較例1〜6によって得られた硬化性樹脂組成物を、以下に示す各種試験によって評価した。評価結果を表4及び表5に示す。なお、硬化性樹脂組成物の成形は、トランスファ成形機を用い、金型温度180℃、成形圧力6.9MPa、硬化時間90秒の条件下で行った。また、後硬化は250℃で6時間行った。
EMMI−1−66に準じたスパイラルフロー測定用金型を用いて、上記条件で硬化性樹脂組成物を成形した。次いで、硬化性樹脂組成物の成形物の流動距離(cm)を測定した。
硬化性樹脂組成物を上記条件で直径50mm×厚さ3mmの円板に成形した。成形後直ちにショアD型硬度計を用いて硬化性樹脂組成物の成形物の硬度を測定した。
硬化性樹脂組成物を上記条件で3.0mm×3.0mm×19mmの試験片に成形し、後硬化した。次いで、セイコーインスツルメンツ社製熱分析システム(TMA/SS6000)を用いて昇温速度5℃/分の条件で線膨張曲線の測定を行い、その屈曲点をガラス転移温度(TMA)(℃)とした。
硬化性樹脂組成物を上記条件で長さ80mm×幅10mm×厚さ3mmの大きさに成形し、後硬化した。次いで、ダイヤモンドカッターで長さ55mmに切断し、粘弾性測定装置ARES(レオメトリックサイエンティフィックエフイー株式会社製)を用い、ダイナミックモードで昇温速度5℃、周波数6.28rad/sの条件でのtanδの測定からガラス転移温度(DMA)(℃)を求めた。得られた値が大きいほど高温で常温との差が小さいことを意味し、硬化後の耐熱性に優れると判断できる。
上記(4)における測定から60℃及び250℃における貯蔵弾性率を求め、60℃の弾性率に対する250℃の弾性率の比率を計算した。
Claims (8)
- (A)エポキシ樹脂、(B)フェノール樹脂、(C)硬化促進剤、及び(D)マレイミド化合物を含有し、前記(C)硬化促進剤が下記一般式(I−1)で示される化合物を含有し、前記(D)マレイミド化合物が、1分子中にマレイミド基を2つ有する化合物と1分子中にマレイミド基を3つ以上有する化合物とを含む硬化性樹脂組成物。
〔式(I−1)中、R1〜R3は、それぞれ独立して、炭素数1〜18の炭化水素基であり、R1〜R3のうち2以上が互いに結合して環状構造を形成してもよく、R4〜R7は、それぞれ独立して、水素原子、水酸基、又は炭素数1〜18の有機基であり、R4〜R7のうち2以上が互いに結合して環状構造を形成してもよい。〕 - (C)硬化促進剤が下記一般式(I−2)で示される化合物を含有する請求項1に記載の硬化性樹脂組成物。
〔式(I−2)中、R1〜R3は、それぞれ独立して、炭素数1〜18の炭化水素基であり、R1〜R3のうち2以上が互いに結合して環状構造を形成してもよく、R4〜R7は、それぞれ独立して、水素原子、又は炭素数1〜18の有機基であり、R4〜R7のうち2以上が互いに結合して環状構造を形成してもよい。〕 - (C)硬化促進剤が下記一般式(I−3)で示される化合物を含有する請求項1に記載の硬化性樹脂組成物。
〔式(I−3)中、R1〜R3は、それぞれ独立して、炭素数1〜18の脂肪族炭化水素基であり、R1〜R3のうち2以上が互いに結合して環状構造を形成してもよく、R4〜R6は、それぞれ独立して、水素原子、又は炭素数1〜18の有機基であり、R4〜R6のうち2以上が互いに結合して環状構造を形成してもよい。〕 - 更に(E)無機充填剤を含有する請求項1〜請求項3のいずれか1項に記載の硬化性樹脂組成物。
- (A)エポキシ樹脂が、ビフェニル型エポキシ樹脂、スチルベン型エポキシ樹脂、ジフェニルメタン型エポキシ樹脂、硫黄原子含有型エポキシ樹脂、ノボラック型エポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、トリフェニルメタン型エポキシ樹脂、共重合型エポキシ樹脂及びアラルキル型エポキシ樹脂からなる群より選ばれる1以上のエポキシ樹脂を含む請求項1〜請求項4のいずれか1項に記載の硬化性樹脂組成物。
- (B)フェノール樹脂が、アラルキル型フェノール樹脂、ジシクロペンタジエン型フェノール樹脂、トリフェニルメタン型フェノール樹脂、共重合型フェノール樹脂及びノボラック型フェノール樹脂からなる群より選ばれる1以上のフェノール樹脂を含む請求項1〜請求項5のいずれか1項に記載の硬化性樹脂組成物。
- (D)マレイミド化合物が、ポリフェニルメタンマレイミドを含む請求項1〜請求項6のいずれか1項に記載の硬化性樹脂組成物。
- 素子と、前記素子を封止する請求項1〜請求項7のいずれか1項に記載の硬化性樹脂組成物の硬化物と、を備える電子部品装置。