JP2013186149A - カラーフィルタ用着色剤、着色組成物、およびカラーフィルタ - Google Patents
カラーフィルタ用着色剤、着色組成物、およびカラーフィルタ Download PDFInfo
- Publication number
- JP2013186149A JP2013186149A JP2012048717A JP2012048717A JP2013186149A JP 2013186149 A JP2013186149 A JP 2013186149A JP 2012048717 A JP2012048717 A JP 2012048717A JP 2012048717 A JP2012048717 A JP 2012048717A JP 2013186149 A JP2013186149 A JP 2013186149A
- Authority
- JP
- Japan
- Prior art keywords
- colorant
- color filter
- parts
- group
- coloring composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】高明度、高コントラスト比、高耐熱性であるという条件を全て同時に満足するカラーフィルタと、それに用いるカラーフィルタ用顔料組成物、カラーフィルタ用黄色着色組成物を提供すること。
【解決手段】特定のキノフタロン化合物を含有するカラーフィルタ用黄色着色剤であって、着色剤の一次粒子サイズについて、5nm未満の粒子の割合が10%未満、及び50nmを超える粒子の割合が5%未満であるカラーフィルタ用黄色着色剤。
【選択図】なし
【解決手段】特定のキノフタロン化合物を含有するカラーフィルタ用黄色着色剤であって、着色剤の一次粒子サイズについて、5nm未満の粒子の割合が10%未満、及び50nmを超える粒子の割合が5%未満であるカラーフィルタ用黄色着色剤。
【選択図】なし
Description
本発明は、カラー液晶表示装置、およびカラー撮像管素子等に用いられるカラーフィルタの製造に使用されるカラーフィルタ用着色剤、着色組成物、およびそれを用いて形成されるカラーフィルタに関するものである。
液晶表示装置は、2枚の偏光板に挟まれた液晶層が、1枚目の偏光板を通過した光の偏光度合いを制御して、2枚目の偏光板を通過する光量をコントロールすることにより表示を行う表示装置であり、ツイストネマチック(TN)型液晶を用いるタイプが主流となっている。液晶表示装置は、2枚の偏光板の間にカラーフィルタを設けることによりカラー表示が可能となり、近年、テレビやパソコンモニタ等に用いられるようになったことから、カラーフィルタに対して高コントラスト化、高明度化、高色再現性の要求が高まっている。
カラーフィルタは、ガラス等の透明な基板の表面に2種以上の異なる色相の微細な帯(ストライプ)状のフィルタセグメントを平行又は交差して配置したもの、あるいは微細なフィルタセグメントを縦横一定の配列で配置したものからなっている。一般的に赤、緑、及び青の3色フィルタセグメントで形成されることが多く、各セグメントは、数ミクロン〜数100ミクロンと微細であり、しかも色相毎に所定の配列で整然と配置されている。
一般的に、カラー液晶表示装置では、カラーフィルタの上に液晶を駆動させるための透明電極が蒸着あるいはスパッタリングにより形成され、さらにその上に液晶を一定方向に配向させるための配向膜が形成されている。これらの透明電極及び配向膜の性能を充分に得るには、その形成を一般に200℃以上、好ましくは230℃以上の高温で行う必要がある。このため、現在、カラーフィルタの製造方法としては、耐熱性、耐光性に優れる顔料を着色剤とする顔料分散法と呼ばれる方法が主流となっている。
緑色フィルタの製造には、調色用着色剤として黄色顔料が用いられており、特に、C.I.ピグメントイエロー138、C.I.ピグメントイエロー139、C.I.ピグメントイエロー150、C.I.ピグメントイエロー185などが主に用いられている。中でも高い透過率が得られるという点で、C.I.ピグメントイエロー138が用いられることが多い。しかし、C.I.ピグメントイエロー138は、比較的明度に優れるものの、より一層の明度向上が望まれている。また、近年、カラーフィルタに対する高コントラスト化の要望が強いが、C.I.ピグメントイエロー138は、コントラスト比が低いという問題を抱えている。
今まで以上に一次粒子径を小さくしたときに、高いコントラスト比が得られる一方で、カラーフィルタ製造工程に対する加工耐性が劣ることが多く、具体的には、緑色カラーフィルタに加工する際に、微細なキノフタロン化合物を含む着色組成物を使用すると、フィルタセグメント作製工程における通常100〜280℃の熱硬化処理において、あるいは200℃以上に曝されるITO成膜工程において、異物が発生することや、コントラスト比が大きく低下する場合がある。
このような状況下で、高明度、高コントラスト比が得られ、かつ耐熱性に優れたキノフタロン化合物の開発が強く求められている。
微細な顔料を製造する方法としては、顔料、水溶性無機塩、水溶性有機溶剤とをニーダー中で、混練する方法が挙げられる。
特許文献1には、粗製のキノフタロン顔料100部と食塩1000部、及びジエチレングリコール120部をニーダー中で内容温度を90〜100℃に保って15時間摩砕を行って得られたキノフタロン顔料をカラーフィルタ用着色剤として使用するとの記載がある。しかしながら、90〜100℃という高温下で摩砕しており、コントラスト比について所望とする特性を得るには至っていない。
特許文献1には、粗製のキノフタロン顔料100部と食塩1000部、及びジエチレングリコール120部をニーダー中で内容温度を90〜100℃に保って15時間摩砕を行って得られたキノフタロン顔料をカラーフィルタ用着色剤として使用するとの記載がある。しかしながら、90〜100℃という高温下で摩砕しており、コントラスト比について所望とする特性を得るには至っていない。
また、特許文献2には、平均一次粒子径10〜30nmの顔料、(B)水酸基、カルボン酸基、スルホン酸基、アミノ基及びそれらの塩から選択されるキノフタロン化合物を含有する顔料組成物は、分散性、コントラスト比双方が良好であり、明度も向上するという記載がある。しかしながら、耐熱性については言及がない。
一方、キノフタロン化合物としては、C.I.ピグメントイエロー138の分散を安定化するための顔料分散剤が知られている。例えば、特許文献3には、スルホン酸を含有したキノフタロン化合物が、特許文献4には、フタルイミドメチル基が付加したキノフタロン化合物が開示されている。これらはいずれも、C.I.ピグメントイエロー138の分散を容易にするための顔料分散剤であって、これら顔料分散剤を使用することで、C.I.ピグメントイエロー138の分散性は改善されるが、コントラストについては所望とする特性を得るには至っていない。
以上のような従来技術では、耐熱性については言及がなく、高明度、高コントラスト比を与え、耐熱性に優れたカラーフィルタに用いるキノフタロン化合物の開発が強く求められている。
本発明の課題は、高明度、高コントラスト比、高耐熱性であるという条件を全て同時に満足するカラーフィルタと、それに用いるためのカラーフィルタ用顔料組成物、カラーフィルタ用黄色着色組成物を提供することである。
本発明者らは、鋭意研究を重ねた結果、キノフタロン化合物を含有するカラーフィルタ用黄色着色剤であって、着色剤の一次粒子サイズが特定の粒子径の範囲にある着色剤を、カラーフィルタに使用したときに、高明度、高コントラスト比が得られ、同時に耐熱性が向上することを見出し、本発明に至った。
すなわち、本発明は、下記一般式(1)で表されるキノフタロン化合物を含有するカラーフィルタ用黄色着色剤であって、着色剤の一次粒子サイズについて、5nm未満の粒子の割合が10%未満、及び50nmを超える粒子の割合が5%未満であることを特徴とするカラーフィルタ用黄色着色剤に関する。
[一般式(1)中、R1〜R13は、それぞれ独立に、水素原子、ハロゲン原子、置換基を有しても良いアルキル基、置換基を有しても良いアルコキシル基、置換基を有しても良いアリール基、−SO3H;−COOH;およびこれら酸性基の1価〜3価の金属塩;アルキルアンモニウム塩、置換基を有しても良いフタルイミドメチル基、または置換基を有しても良いスルファモイル基を示す。
R1〜R4、R5〜R9、R10〜R13の隣接した基は、一体となって、環を形成しても良い。]
R1〜R4、R5〜R9、R10〜R13の隣接した基は、一体となって、環を形成しても良い。]
また、本発明は、キノフタロン化合物が、C.I.ピグメントイエロー138である前記カラーフィルタ用黄色着色組成物に関する。
また、本発明は、少なくとも着色剤、バインダー樹脂、および有機溶剤からなるカラーフィルタ用着色組成物であって、着色剤が、前記着色剤であるカラーフィルタ用着色組成物に関する。
また、本発明は、さらに緑色着色剤を含有する前記カラーフィルタ用着色組成物に関する。
また、本発明は、さらに光重合性単量体および/または光重合開始剤を含有する前記カラーフィルタ用着色組成物に関する。
また、本発明は、少なくとも1つの赤色フィルタセグメント、少なくとも1つの緑色フィルタセグメントおよび少なくとも1つの青色フィルタセグメントを備えるカラーフィルタにおいて、少なくとも1つの緑色フィルタセグメントが、前記カラーフィルタ用着色組成物により形成されてなるカラーフィルタに関する。
高明度かつ高コントラスト比であって、耐熱性に優れたカラーフィルタ用着色剤、着色組成物、およびそれを用いたカラーフィルタを提供することができる。
以下、本発明を詳細に説明する。なお、本明細書における「C.I.」とは、カラーインデックスを意味する。また、本明細書では、「カラーフィルタ用黄色着色剤」を、「黄色着色剤」あるいは「着色剤」ということがある。
一般式(1)で表されるキノフタロン化合物を含有するカラーフィルタ用黄色着色剤は、一次粒子のサイズについて、5nm未満の粒子の個数割合が10%未満であり、50nmを超える粒子の個数割合が5%未満であることを特徴とする。5nm未満の粒子の割合が10%以上多い場合は、耐熱性が低下し、その結果、その結果、明度の低下やコントラスト比が低下する恐れがある。また、50nmを超える粒子の割合が5%以上の場合では、粗大粒子が存在することで、明度やコントラスト比が低下する。
<キノフタロン化合物>
まず、一般式(1)で表されるキノフタロン化合物について説明する。
まず、一般式(1)で表されるキノフタロン化合物について説明する。
ここで、ハロゲン原子としては、フッ素、塩素、臭素、ヨウ素が挙げられる。
また、置換基を有してもよいアルキル基としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、tert−ブチル基、ネオペンチル基、へキシル基、オクチル基、ステアリル基、2−エチルへキシル基等の直鎖又は分岐アルキル基の他、トリクロロメチル基、トリフルオロメチル基、2,2,2−トリフルオロエチル基、2,2−ジブロモエチル基、2,2,3,3−テトラフルオロプロピル基、2−エトキシエチル基、2−ブトキシエチル基、2−ニトロプロピル基、ベンジル基、4−メチルベンジル基、4−tert−ブチルベンジル基、4−メトキシベンジル基、4−ニトロベンジル基、2,4−ジクロロベンジル基等の置換基を有するアルキル基が挙げられる。
また、置換基を有してもよいアルコキシル基としては、メトキシ基、エトキシ基、プロポキシ基、イソプロポキシ基、n−ブトキシ基、イソブチルオキシ基、tert−ブチルオキシ基、ネオペンチルオキシ基、2,3−ジメチル−3−ペンチルオキシ基、へキシルオキシ基、オクチルオキシ基、ステアリルオキシ基、2−エチルへキシルオキシ基等の直鎖又は分岐アルコキシル基の他、トリクロロメトキシ基、トリフルオロメトキシ基、2,2,2−トリフルオロエトキシ基、2,2,3,3−テトラフルオロプロピルオキシ基、2,2−ジトリフルオロメチルプロポキシ基、2−エトキシエトキシ基、2−ブトキシエトキシ基、2−ニトロプロポキシ基、ベンジルオキシ基等の置換基を有するアルコキシル基が挙げられる。
また、置換基を有してもよいアリール基としては、フェニル基、ナフチル基、アンスリル基等のアリール基の他、p−メチルフェニル基、p−ブロモフェニル基、p−ニトロフェニル基、p−メトキシフェニル基、2,4−ジクロロフェニル基、ペンタフルオロフェニル基、2−アミノフェニル基、2−メチル−4−クロロフェニル基、4−ヒドロキシ−1−ナフチル基、6−メチル−2−ナフチル基、4,5,8−トリクロロ−2−ナフチル基、アントラキノニル基、2−アミノアントラキノニル基等の置換基を有するアリール基が挙げられる。
また、酸性基としては、−SO3H、−COOHが挙げられ、これら酸性基の1価〜3価の金属塩としては、ナトリウム塩、カリウム塩、マグネシウム塩、カルシウム塩、鉄塩、アルミニウム塩等が挙げられる。また、酸性基のアルキルアンモニウム塩としては、オクチルアミン、ラウリルアミン、ステアリルアミン等の長鎖モノアルキルアミンのアンモニウム塩、パルミチルトリメチルアンモニウム、ジラウリルジメチルアンモニウム、ジステアリルジメチルアンモニウム塩等の4級アルキルアンモニウム塩が挙げられる。
置換基を有してもよいフタルイミドメチル基(C6H4(CO)2N−CH2−)、および、置換基を有してもよいスルファモイル基(H2NSO2−)における「置換基」としては、上記のハロゲン原子、置換基を有してもよいアルキル基、置換基を有しても良いアルコキシル基、置換基を有してもよいアリール基等が挙げられる。
一般式(1)のR1〜R4、R5〜R9、R10〜R13の隣接した基は、一体となって、環を形成しても良い。ここでいう環とは、炭化水素芳香環および複素芳香環等が挙げられ、炭化水素芳香環としては、ベンゼン環、ナフタレン環、アントラセン環、フェナントレン環等が、また、複素芳香環としては、ピリジン環、ピラジン環、ピロール環、キノリン環、キノキサリン環、フラン環、ベンゾフラン環、チオフェン環、ベンゾチオフェン環、オキサゾール環、チアゾール環、イミダゾール環、ピラゾール環、インドール環、カルバゾール環などが挙げられる。
本発明のカラーフィルタ用着色剤に用いられるキノフタロン化合物の具体例として、下記に示すキノフタロン化合物(a)〜(n)等が挙げられるが、本発明はこれらに限定されるものではない。
<キノフタロン化合物の製造法>
本発明で使用されるキノフタロン化合物は、従来公知の製造法が使用でき、特に制限されないが、例えば、特許公報2930774号記載の方法によって製造することができる。以下、一般式(1)で表されるキノフタロン化合物の一般的な製造法について述べる。下記一般式(2)で表される8−アミノキナルジン1当量に対して、下記一般式(3)で表される無水フタル酸2〜3当量を、安息香酸中、窒素雰囲気下、160〜200℃で加熱して縮合反応させる。8−アミノキナルジンと反応させる無水フタル酸は、2種類以上を混合して使用してもよい。キノフタロン化合物の製造方法はこれらの方法に限定されるものではない。
本発明で使用されるキノフタロン化合物は、従来公知の製造法が使用でき、特に制限されないが、例えば、特許公報2930774号記載の方法によって製造することができる。以下、一般式(1)で表されるキノフタロン化合物の一般的な製造法について述べる。下記一般式(2)で表される8−アミノキナルジン1当量に対して、下記一般式(3)で表される無水フタル酸2〜3当量を、安息香酸中、窒素雰囲気下、160〜200℃で加熱して縮合反応させる。8−アミノキナルジンと反応させる無水フタル酸は、2種類以上を混合して使用してもよい。キノフタロン化合物の製造方法はこれらの方法に限定されるものではない。
本発明の黄色着色剤は、2種類以上のキノフタロン化合物を含有していてもよい。
このとき別々に製造したキノフタロン化合物同士を混合しても良いし、同時に2種類以上のキノフタロン化合物を共合成法によって製造して、着色剤に使用しても良い。
これら別々に製造したキノフタロン化合物を使用する場合は、2種の顔料を分散する前に単純に混合してもよいし、ソルトミリング処理により粉砕混合してもよい。
このとき別々に製造したキノフタロン化合物同士を混合しても良いし、同時に2種類以上のキノフタロン化合物を共合成法によって製造して、着色剤に使用しても良い。
これら別々に製造したキノフタロン化合物を使用する場合は、2種の顔料を分散する前に単純に混合してもよいし、ソルトミリング処理により粉砕混合してもよい。
本発明のカラーフィルタ用黄色着色剤は、上記キノフタロン化合物と、水溶性無機塩、水溶性有機溶剤、および必要に応じて他の顔料とを、混練機内においてソルトミリング処理することで得ることができる。
ソルトミリング処理とは、キノフタロン化合物と水溶性無機塩と水溶性有機溶剤との混合物を、ニーダー、2本ロールミル、3本ロールミル、ボールミル、アトライター、サンドミル等の混練機を用いて、加熱しながら機械的に混練した後、水洗により水溶性無機塩と水溶性有機溶剤を除去する処理である。水溶性無機塩は、破砕助剤として働くものであり、ソルトミリング時に無機塩の硬度の高さを利用してキノフタロン化合物が破砕される。キノフタロン化合物をソルトミリング処理する際の条件を最適化することにより、一次粒子径が非常に微細であり、また、分布の幅がせまく、シャープな粒度分布をもつ黄色着色剤を得ることができる。
ソルトミリング処理時の混練機内の温度としては、60〜70℃で実施する。60〜70℃の範囲で温度制御をすることで、本発明の粒子径の範囲にあるカラーフィルタ用黄色着色剤を得ることができる。60℃より低い温度であると5nm未満の小さい一次粒子の割合が10%以上存在し、耐熱性が低下し、しいては明度やコントラスト比低下の恐れがある。一方、70℃より高い温度であると、十分に一次粒子が微細にならない恐れがある。混練する時間は、無機塩や水溶性有機溶剤の使用割合や混練温度により異なるが、6〜40時間が好ましい。中でも、キノフタロン化合物の品質と生産効率のバランスから、10〜24時間がより好ましい。
水溶性無機塩としては、塩化ナトリウム、塩化バリウム、塩化カリウム、硫酸ナトリウム等を用いることができるが、価格の点から塩化ナトリウム(食塩)を用いるのが好ましい。水溶性無機塩は、処理効率と生産効率の両面から、キノフタロン化合物100重量部に対して、50〜2000重量部用いることが好ましく、400〜1500重量部用いることがより好ましい。また、水溶性無機塩の粒子径は、特に限定されるものではないが、体積基準のメディアン粒子径(D50)で1〜50μmであることが好ましい。D50が50μm以下だと、粗製キノフタロン化合物を微細にするための処理時間が短く、D50が1μm以上だと、水溶性無機塩を得るためのエネルギーが少なくて済む。又、水溶性無機塩の粒子径は、乾式仕様のレーザー回折式粒度分布測定機を用いて求めることが可能である。
水溶性有機溶剤は、キノフタロン化合物及び水溶性無機塩を湿潤する働きをするものであり、水に溶解(混和)し、かつ用いる無機塩を実質的に溶解しないものであれば特に限定されない。ただし、ソルトミリング時に温度が上昇し、溶剤が蒸発し易い状態になるため、安全性の点から、沸点120℃以上の高沸点溶剤が好ましい。例えば、2−メトキシエタノール、2−ブトキシエタノール、2−(イソペンチルオキシ)エタノール、2−(ヘキシルオキシ)エタノール、ジエチレングリコール、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコール、トリエチレングリコールモノメチルエーテル、液状のポリエチレングリコール、1−メトキシ−2−プロパノール、1−エトキシ−2−プロパノール、ジプロピレングリコール、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル、液状のポリプロピレングリコール等が用いられる。水溶性有機溶剤は、キノフタロン化合物100重量部に対して、5〜1000重量部用いることが好ましく、50〜500重量部用いることがより好ましい。
本発明において、キノフタロン化合物をソルトミリング処理する際には、微細化を促進する目的や、結晶安定化剤、カラーフィルタの分散性向上の目的で、色素誘導体を添加してもよい。添加する色素誘導体としては、特に制限はないが、有機顔料、アントラキノン、アクリドンまたはトリアジンに、塩基性置換基、酸性置換基、または置換基を有していても良いフタルイミドメチル基を導入した化合物などが挙げられる。
キノフタロン化合物をソルトミリング処理する際には、必要に応じて樹脂を添加してもよい。用いられる樹脂の種類は特に限定されず、天然樹脂、変性天然樹脂、合成樹脂、天然樹脂で変性された合成樹脂等を用いることができる。用いられる樹脂は、室温で固体であり、水不溶性であることが好ましく、かつ上記有機溶剤に一部可溶であることがさらに好ましい。樹脂の使用量は、キノフタロン化合物100重量部に対して、2〜200重量部の範囲であることが好ましい。
本発明の着色組成物は、色相の調整の目的で、本発明の効果を損なわない範囲で、キノフタロン化合物以外の黄色着色剤を含有してもよい。
本発明の着色組成物に使用可能な黄色着色剤としては、C.I.ピグメントイエロー 1、2、3、4、5、6、10、12、13、14、15、16、17、18、24、31、32、34、35、35:1、36、36:1、37、37:1、40、42、43、53、55、60、61、62、63、65、73、74、77、81、83、93、94、95、97、98、100、101、104、106、108、109、110、113、114、115、116、117、118、119、120、123、126、127、128、129、139、147、150、151、152、153、154、155、156、161、162、164、166、167、168、169、170、171、172、173、174、175、176、177、179、180、181、182、185、187、188、192、193、194、196、198、199、213、214等の黄色顔料を用いることができる。
本発明の着色組成物に使用可能な黄色着色剤としては、C.I.ピグメントイエロー 1、2、3、4、5、6、10、12、13、14、15、16、17、18、24、31、32、34、35、35:1、36、36:1、37、37:1、40、42、43、53、55、60、61、62、63、65、73、74、77、81、83、93、94、95、97、98、100、101、104、106、108、109、110、113、114、115、116、117、118、119、120、123、126、127、128、129、139、147、150、151、152、153、154、155、156、161、162、164、166、167、168、169、170、171、172、173、174、175、176、177、179、180、181、182、185、187、188、192、193、194、196、198、199、213、214等の黄色顔料を用いることができる。
特にフィルタセグメントの耐熱性、耐光性、および明度の観点からC.I.ピグメントイエロー139、150、185が好ましい。
さらに、本発明の着色組成物は、所望とする色特性に応じて、緑色着色剤を含有してもよい。本発明の着色組成物に使用可能な緑色着色剤としては、例えば、C.I.ピグメントグリーン7、10、36、37、58等の緑色顔料が挙げられる。
<カラーフィルタ用着色組成物>
本発明のカラーフィルタ用着色組成物は、前記で説明した着色剤の他に、バインダー樹脂、有機溶剤から構成される。
<バインダー樹脂>
本発明の着色組成物に含まれるバインダー樹脂としては、従来公知の熱可塑性樹脂、および熱硬化性樹脂が挙げられる。
熱可塑性樹脂としては、例えば、アクリル樹脂、ブチラール樹脂、スチレンーマレイン酸共重合体、塩素化ポリエチレン、塩素化ポリプロピレン、ポリ塩化ビニル、塩化ビニル−酢酸ビニル共重合体、ポリ酢酸ビニル、ポリウレタン系樹脂、ポリエステル樹脂、ビニル系樹脂、アルキッド樹脂、ポリスチレン樹脂、ポリアミド樹脂、ゴム系樹脂、環化ゴム系樹脂、セルロース類、ポリエチレン(HDPE、LDPE)、ポリブタジエン、及びポリイミド樹脂等が挙げられる。
本発明のカラーフィルタ用着色組成物は、前記で説明した着色剤の他に、バインダー樹脂、有機溶剤から構成される。
<バインダー樹脂>
本発明の着色組成物に含まれるバインダー樹脂としては、従来公知の熱可塑性樹脂、および熱硬化性樹脂が挙げられる。
熱可塑性樹脂としては、例えば、アクリル樹脂、ブチラール樹脂、スチレンーマレイン酸共重合体、塩素化ポリエチレン、塩素化ポリプロピレン、ポリ塩化ビニル、塩化ビニル−酢酸ビニル共重合体、ポリ酢酸ビニル、ポリウレタン系樹脂、ポリエステル樹脂、ビニル系樹脂、アルキッド樹脂、ポリスチレン樹脂、ポリアミド樹脂、ゴム系樹脂、環化ゴム系樹脂、セルロース類、ポリエチレン(HDPE、LDPE)、ポリブタジエン、及びポリイミド樹脂等が挙げられる。
カラーフィルタ用着色組成物として用いる場合には、可視光領域の400〜700nmの全波長領域において分光透過率が好ましくは80%以上、より好ましくは95%以上の樹脂であることが好ましい。また、アルカリ現像型着色レジストの形態で用いる場合には、酸性基含有エチレン性不飽和単量体を共重合したアルカリ可溶性ビニル系樹脂を用いることが好ましい。また、さらに光感度を向上させるために、エチレン性不飽和活性二重結合を有するエネルギー線硬化性樹脂を用いることもできる。
酸性基含有エチレン性不飽和モノマーを共重合したアルカリ可溶性樹脂としては、例えば、カルボキシル基、スルホン基等の酸性基を有する樹脂が挙げられる。アルカリ可溶性樹脂として具体的には、酸性基を有するアクリル樹脂、α−オレフィン/(無水)マレイン酸共重合体、スチレン/スチレンスルホン酸共重合体、エチレン/(メタ)アクリル酸共重合体、又はイソブチレン/(無水)マレイン酸共重合体等が挙げられる。中でも、酸性基を有するアクリル樹脂、及びスチレン/スチレンスルホン酸共重合体から選ばれる少なくとも1種の樹脂、特に酸性基を有するアクリル樹脂は、耐熱性、透明性が高いため、好適に用いられる。
エチレン性不飽和活性二重結合を有するエネルギー線硬化性樹脂としては、水酸基、カルボキシル基、アミノ基等の反応性の置換基を有する高分子にイソシアネート基、アルデヒド基、エポキシ基等の反応性置換基を有する(メタ)アクリル化合物やケイヒ酸を反応させて、(メタ)アクリロイル基、スチリル基等の光架橋性基を該高分子に導入した樹脂が用いられる。又、スチレン−無水マレイン酸共重合物やα−オレフィン−無水マレイン酸共重合物等の酸無水物を含む高分子をヒドロキシアルキル(メタ)アクリレート等の水酸基を有する(メタ)アクリル化合物によりハーフエステル化したものも用いられる。
熱可塑性樹脂として、アルカリ可溶性能とエネルギー線硬化性能とを併せもつものも、カラーフィルタ用着色組成物として好ましい。
上記熱可塑性樹脂を構成するモノマーとして以下のものが挙げられる。例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、n−プロピル(メタ)アクリレート、イソプロピル(メタ)アクリレート、n−ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、t−ブチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、ステアリル(メタ)アクリレート、ラウリル(メタ)アクリレート、テトラヒドロフルフリル(メタ)アクリレート、イソボルニル(メタ)アクリレート、フェニル(メタ)アクリレート、ベンジル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート、フェノキシジエチレングリコール(メタ)アクリレート、メトキシポリプロピレングリコール(メタ)アクリレート、又はエトキシポリエチレングリコール(メタ)アクリレート等の(メタ)アクリレート類、
あるいは、(メタ)アクリルアミド、N,N−ジメチル(メタ)アクリルアミド、N,N−ジエチル(メタ)アクリルアミド、N−イソプロピル(メタ)アクリルアミド、ダイアセトン(メタ)アクリルアミド、又はアクリロイルモルホリン等の(メタ)アクリルアミド類、スチレン、又はα−メチルスチレン等のスチレン類、エチルビニルエーテル、n−プロピルビニルエーテル、イソプロピルビニルエーテル、n−ブチルビニルエーテル、又はイソブチルビニルエーテル等のビニルエーテル類、酢酸ビニル、又はプロピオン酸ビニル等の脂肪酸ビニル類が挙げられる。
あるいは、シクロヘキシルマレイミド、フェニルマレイミド、メチルマレイミド、エチルマレイミド、1,2−ビスマレイミドエタン1,6−ビスマレイミドヘキサン、3−マレイミドプロピオン酸、6,7−メチレンジオキシ−4−メチル−3−マレイミドクマリン、4,4’−ビスマレイミドジフェニルメタン、ビス(3−エチル−5−メチル−4−マレイミドフェニル)メタン、N,N’−1,3−フェニレンジマレイミド、N,N’−1,4−フェニレンジマレイミド、N−(1−ピレニル)マレイミド、N−(2,4,6−トリクロロフェニル)マレイミド、N−(4−アミノフェニル)マレイミド、N−(4−ニトロフェニル)マレイミド、N−ベンジルマレイミド、N−ブロモメチル−2,3−ジクロロマレイミド、N−スクシンイミジル−3−マレイミドベンゾエート、N−スクシンイミジル−3−マレイミドプロピオナート、N−スクシンイミジル−4−マレイミドブチラート、N−スクシンイミジル−6−マレイミドヘキサノアート、N−[4−(2−ベンゾイミダゾリル)フェニル]マレイミド、9−マレイミドアクリジン等のN-置換マレイミド類が挙げられる。
あるいは、(メタ)アクリルアミド、N,N−ジメチル(メタ)アクリルアミド、N,N−ジエチル(メタ)アクリルアミド、N−イソプロピル(メタ)アクリルアミド、ダイアセトン(メタ)アクリルアミド、又はアクリロイルモルホリン等の(メタ)アクリルアミド類、スチレン、又はα−メチルスチレン等のスチレン類、エチルビニルエーテル、n−プロピルビニルエーテル、イソプロピルビニルエーテル、n−ブチルビニルエーテル、又はイソブチルビニルエーテル等のビニルエーテル類、酢酸ビニル、又はプロピオン酸ビニル等の脂肪酸ビニル類が挙げられる。
あるいは、シクロヘキシルマレイミド、フェニルマレイミド、メチルマレイミド、エチルマレイミド、1,2−ビスマレイミドエタン1,6−ビスマレイミドヘキサン、3−マレイミドプロピオン酸、6,7−メチレンジオキシ−4−メチル−3−マレイミドクマリン、4,4’−ビスマレイミドジフェニルメタン、ビス(3−エチル−5−メチル−4−マレイミドフェニル)メタン、N,N’−1,3−フェニレンジマレイミド、N,N’−1,4−フェニレンジマレイミド、N−(1−ピレニル)マレイミド、N−(2,4,6−トリクロロフェニル)マレイミド、N−(4−アミノフェニル)マレイミド、N−(4−ニトロフェニル)マレイミド、N−ベンジルマレイミド、N−ブロモメチル−2,3−ジクロロマレイミド、N−スクシンイミジル−3−マレイミドベンゾエート、N−スクシンイミジル−3−マレイミドプロピオナート、N−スクシンイミジル−4−マレイミドブチラート、N−スクシンイミジル−6−マレイミドヘキサノアート、N−[4−(2−ベンゾイミダゾリル)フェニル]マレイミド、9−マレイミドアクリジン等のN-置換マレイミド類が挙げられる。
特に、N-置換マレイミド由来の構成単位を有することが好ましく、なかでも耐熱性の点からシクロヘキシルマレイミド、メチルマレイミド、エチルマレイミド、1,2−ビスマレイミドエタンが好ましく、特にシクロヘキシルマレイミドが好ましい。
熱硬化性樹脂としては、例えば、エポキシ樹脂、ベンゾグアナミン樹脂、ロジン変性マレイン酸樹脂、ロジン変性フマル酸樹脂、メラミン樹脂、尿素樹脂、及びフェノール樹脂等が挙げられる。
本発明の着色組成物は、熱硬化性樹脂を含むとさらに耐熱性の面で好ましく、例えば、なかでも、エポキシ樹脂、メラミン樹脂がより好適に使用出来、特にメラミン樹脂がより好ましく、なかでも、メチロールイミノ基を有するメラミン化合物またはその縮合物がさらに好ましい。
本発明の着色組成物は、熱硬化性樹脂を含むとさらに耐熱性の面で好ましく、例えば、なかでも、エポキシ樹脂、メラミン樹脂がより好適に使用出来、特にメラミン樹脂がより好ましく、なかでも、メチロールイミノ基を有するメラミン化合物またはその縮合物がさらに好ましい。
熱硬化性樹脂は、着色剤100重量部に対し、5〜60重量部の範囲で添加することが好ましい。10重量部未満であると耐熱性・耐光性向上への効果が小さくなり、60重量部を超えるとアルカリ現像の際の現像性悪化のため好ましくない。
バインダー樹脂の重量平均分子量(Mw)は、着色剤を好ましく分散させるためには、5,000〜100,000の範囲が好ましく、より好ましくは8,000〜50,000の範囲である。また数平均分子量(Mn)は2,500〜50,000の範囲が好ましく、Mw/Mnの値は10以下であることが好ましい。
ここで重量平均分子量(Mw)、数平均分子量(Mn)は、東ソー株式会社製ゲルパーミエイションクロマトグラフィー「HLC−8120GPC」において、分離カラムを4本直列に繋ぎ、充填剤には順に東ソー株式会社製「TSK−GEL SUPER H5000」、「H4000」、「H3000」、及び「H2000」を用い、移動相にテトラヒドロフランを用いて測定したポリスチレン換算分子量である。
ここで重量平均分子量(Mw)、数平均分子量(Mn)は、東ソー株式会社製ゲルパーミエイションクロマトグラフィー「HLC−8120GPC」において、分離カラムを4本直列に繋ぎ、充填剤には順に東ソー株式会社製「TSK−GEL SUPER H5000」、「H4000」、「H3000」、及び「H2000」を用い、移動相にテトラヒドロフランを用いて測定したポリスチレン換算分子量である。
バインダー樹脂をカラーフィルタ用色組成物として使用する場合には、顔料分散性、現像性、及び耐熱性の観点から、顔料吸着基及び現像時のアルカリ可溶基として働くカルボキシル基、顔料担体及び溶剤に対する親和性基として働く脂肪族基及び芳香族基のバランスが、顔料分散性、現像性、さらには耐久性にとって重要であり、酸価20〜300mgKOH/gの樹脂を用いることが好ましい。酸価が、20mgKOH/g未満では、現像液に対する溶解性が悪く、微細パターン形成するのが困難である。300mgKOH/gを超えると、微細パターンが残らなくなる。
バインダー樹脂は、着色剤100重量部に対して、20〜500重量部用いることが好ましい。
<有機溶剤>
本発明の着色組成物には、着色剤を充分に着色剤担体中に分散、浸透させ、ガラス基板等の基板上に乾燥膜厚が0.2〜5μmとなるように塗布してフィルタセグメントを形成することを容易にするために有機溶剤を含有させることができる。
本発明の着色組成物には、着色剤を充分に着色剤担体中に分散、浸透させ、ガラス基板等の基板上に乾燥膜厚が0.2〜5μmとなるように塗布してフィルタセグメントを形成することを容易にするために有機溶剤を含有させることができる。
有機溶剤としては、例えば乳酸エチル、ベンジルアルコール、1,2,3−トリクロロプロパン、1,3−ブタンジオール、1,3−ブチレングリコール、1,3−ブチレングリコールジアセテート、1,4−ジオキサン、2−ヘプタノン、2−メチル−1,3−プロパンジオール、3,5,5−トリメチル−2−シクロヘキセン−1−オン、3,3,5−トリメチルシクロヘキサノン、3−エトキシプロピオン酸エチル、3−メチル−1,3−ブタンジオール、3−メトキシ−3−メチル−1−ブタノール、3−メトキシ−3−メチルブチルアセテート、3−メトキシブタノール、3−メトキシブチルアセテート、4−ヘプタノン、m−キシレン、m−ジエチルベンゼン、m−ジクロロベンゼン、N,N−ジメチルアセトアミド、N,N−ジメチルホルムアミド、n−ブチルアルコール、n−ブチルベンゼン、n−プロピルアセテート、o−キシレン、o−クロロトルエン、o−ジエチルベンゼン、o−ジクロロベンゼン、p−クロロトルエン、p−ジエチルベンゼン、sec−ブチルベンゼン、tert−ブチルベンゼン、γ−ブチロラクトン、イソブチルアルコール、イソホロン、エチレングリコールジエチルエーテル、エチレングリコールジブチルエーテル、エチレングリコールモノイソプロピルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノエチルエーテルアセテート、エチレングリコールモノターシャリーブチルエーテル、エチレングリコールモノブチルエーテル、エチレングリコールモノブチルエーテルアセテート、エチレングリコールモノプロピルエーテル、エチレングリコールモノヘキシルエーテル、エチレングリコールモノメチルエーテル、エチレングリコールモノメチルエーテルアセテート、ジイソブチルケトン、ジエチレングリコールジエチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールモノイソプロピルエーテル、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノメチルエーテル、シクロヘキサノール、シクロヘキサノールアセテート、シクロヘキサノン、ジプロピレングリコールジメチルエーテル、ジプロピレングリコールメチルエーテルアセテート、ジプロピレングリコールモノエチルエーテル、ジプロピレングリコールモノブチルエーテル、ジプロピレングリコールモノプロピルエーテル、ジプロピレングリコールモノメチルエーテル、ダイアセトンアルコール、トリアセチン、トリプロピレングリコールモノブチルエーテル、トリプロピレングリコールモノメチルエーテル、プロピレングリコールジアセテート、プロピレングリコールフェニルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノブチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルプロピオネート、ベンジルアルコール、メチルイソブチルケトン、メチルシクロヘキサノール、酢酸n−アミル、酢酸n−ブチル、酢酸イソアミル、酢酸イソブチル、酢酸プロピル、二塩基酸エステル等が挙げられる。
中でも、本発明の着色剤の分散が良好なことから、乳酸エチル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート等のグリコールアセテート類、ベンジルアルコール等の芳香族アルコール類やシクロヘキサノン等のケトン類を用いることが好ましい。
有機溶剤は、1種を単独で、若しくは2種以上を混合して用いることができる。また溶剤は、着色組成物を適正な粘度に調節し、目的とする均一な膜厚のフィルタセグメントを形成できることから、着色剤100重量部にして、500〜4000重量部用いることが好ましい。
<分散助剤>
着色剤を着色剤担体中に分散する際には、適宜、色素誘導体、樹脂型分散剤、界面活性剤等の分散助剤を用いることができる。分散助剤は、着色剤の分散に優れ、分散後の着色剤の再凝集を防止する効果が大きいので、分散助剤を用いて着色剤を着色剤担体中に分散してなる着色組成物を用いた場合には、分光透過率の高いカラーフィルタが得られる。
着色剤を着色剤担体中に分散する際には、適宜、色素誘導体、樹脂型分散剤、界面活性剤等の分散助剤を用いることができる。分散助剤は、着色剤の分散に優れ、分散後の着色剤の再凝集を防止する効果が大きいので、分散助剤を用いて着色剤を着色剤担体中に分散してなる着色組成物を用いた場合には、分光透過率の高いカラーフィルタが得られる。
<色素誘導体>
色素誘導体としては、有機顔料、アントラキノン、アクリドンまたはトリアジンに、塩基性置換基、酸性置換基、または置換基を有していても良いフタルイミドメチル基を導入した化合物があげられ、例えば、特開昭63−305173号公報、特公昭57−15620号公報、特公昭59−40172号公報、特公昭63−17102号公報、特公平5−9469号公報、特許第4585781号公報等に記載されているものを使用でき、これらは単独または2種類以上を混合して用いることができる。
色素誘導体としては、有機顔料、アントラキノン、アクリドンまたはトリアジンに、塩基性置換基、酸性置換基、または置換基を有していても良いフタルイミドメチル基を導入した化合物があげられ、例えば、特開昭63−305173号公報、特公昭57−15620号公報、特公昭59−40172号公報、特公昭63−17102号公報、特公平5−9469号公報、特許第4585781号公報等に記載されているものを使用でき、これらは単独または2種類以上を混合して用いることができる。
色素誘導体の配合量は、着色剤の分散性向上の観点から、着色剤100重量部に対して、好ましくは0.5重量部以上、さらに好ましくは1重量部以上、最も好ましくは3重量部以上である。また、耐熱性、耐光性の観点から、着色剤100重量部に対して、好ましくは40重量部以下、さらに好ましくは35重量部以下である。
<樹脂型分散剤>
樹脂型分散剤は、添加着色剤に吸着する性質を有する着色剤親和性部位と、着色剤担体と相溶性のある部位とを有し、添加着色剤に吸着して着色剤担体への分散を安定化する働きをするものである。樹脂型分散剤として具体的には、ポリウレタン、ポリアクリレート等のポリカルボン酸エステル、不飽和ポリアミド、ポリカルボン酸、ポリカルボン酸(部分)アミン塩、ポリカルボン酸アンモニウム塩、ポリカルボン酸アルキルアミン塩、ポリシロキサン、長鎖ポリアミノアマイドリン酸塩、水酸基含有ポリカルボン酸エステルや、これらの変性物、ポリ(低級アルキレンイミン)と遊離のカルボキシル基を有するポリエステルとの反応により形成されたアミドやその塩等の油性分散剤、(メタ)アクリル酸−スチレン共重合体、(メタ)アクリル酸−(メタ)アクリル酸エステル共重合体、スチレン−マレイン酸共重合体、ポリビニルアルコール、ポリビニルピロリドン等の水溶性樹脂や水溶性高分子化合物、ポリエステル系、変性ポリアクリレート系、エチレンオキサイド/プロピレンオキサイド付加化合物、リン酸エステル系等が用いられ、これらは単独または2種以上を混合して用いることができるが、必ずしもこれらに限定されるものではない。
樹脂型分散剤は、添加着色剤に吸着する性質を有する着色剤親和性部位と、着色剤担体と相溶性のある部位とを有し、添加着色剤に吸着して着色剤担体への分散を安定化する働きをするものである。樹脂型分散剤として具体的には、ポリウレタン、ポリアクリレート等のポリカルボン酸エステル、不飽和ポリアミド、ポリカルボン酸、ポリカルボン酸(部分)アミン塩、ポリカルボン酸アンモニウム塩、ポリカルボン酸アルキルアミン塩、ポリシロキサン、長鎖ポリアミノアマイドリン酸塩、水酸基含有ポリカルボン酸エステルや、これらの変性物、ポリ(低級アルキレンイミン)と遊離のカルボキシル基を有するポリエステルとの反応により形成されたアミドやその塩等の油性分散剤、(メタ)アクリル酸−スチレン共重合体、(メタ)アクリル酸−(メタ)アクリル酸エステル共重合体、スチレン−マレイン酸共重合体、ポリビニルアルコール、ポリビニルピロリドン等の水溶性樹脂や水溶性高分子化合物、ポリエステル系、変性ポリアクリレート系、エチレンオキサイド/プロピレンオキサイド付加化合物、リン酸エステル系等が用いられ、これらは単独または2種以上を混合して用いることができるが、必ずしもこれらに限定されるものではない。
上記分散剤のうち少量の添加量で分散体の粘度が低くなり高いコントラストを示すという理由から、塩基性官能基を有する高分子分散剤が好ましく、窒素原子含有グラフト共重合体や、側鎖に3級アミノ基、4級アンモニウム塩基、含窒素複素環などを含む官能基を有する、窒素原子含有アクリル系ブロック共重合体およびウレタン系高分子分散剤などが好ましい。
樹脂型分散剤は、着色剤100重量部に対して、5〜200重量部使用することが好ましく、成膜性の観点から10〜100重量部使用することがより好ましい。
樹脂型分散剤は、着色剤100重量部に対して、5〜200重量部使用することが好ましく、成膜性の観点から10〜100重量部使用することがより好ましい。
市販の樹脂型分散剤としては、ビックケミー・ジャパン社製のDsperbyk−101、103、107、108、110、111、116、130、140、154、161、162、163、164、165、166、170、171、174、180、181、182、183、184、185、190、2000、2001、2020、2025、2050、2070、2095、2150、2155またはAnti−Terra−U、203、204、またはBYK−P104、P104S、220S、6919、またはLactimon、Lactimon−WSまたはBykumen等、日本ルーブリゾール社製のSOLSPERSE−3000、9000、13000、13240、13650、13940、16000、17000、18000、20000、21000、24000、26000、27000、28000、31845、32000、32500、32550、33500、32600、34750、35100、36600、38500、41000、41090、53095、55000、76500等、チバ・ジャパン社製のEFKA−46、47、48、452、4008、4009、4010、4015、4020、4047、4050、4055、4060、4080、4400、4401、4402、4403、4406、4408、4300、4310、4320、4330、4340、450、451、453、4540、4550、4560、4800、5010、5065、5066、5070、7500、7554、1101、120、150、1501、1502、1503、等、味の素ファインテクノ社製のアジスパーPA111、PB711、PB821、PB822、PB824等が挙げられる。
<界面活性剤>
界面活性剤としては、ラウリル硫酸ナトリウム、ポリオキシエチレンアルキルエーテル硫酸塩、ドデシルベンゼンスルホン酸ナトリウム、スチレン−アクリル酸共重合体のアルカリ塩、ステアリン酸ナトリウム、アルキルナフタリンスルホン酸ナトリウム、アルキルジフェニルエーテルジスルホン酸ナトリウム、ラウリル硫酸モノエタノールアミン、ラウリル硫酸トリエタノールアミン、ラウリル硫酸アンモニウム、ステアリン酸モノエタノールアミン、スチレン−アクリル酸共重合体のモノエタノールアミン、ポリオキシエチレンアルキルエーテルリン酸エステル等のアニオン性界面活性剤;ポリオキシエチレンオレイルエーテル、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンアルキルエーテルリン酸エステル、ポリオキシエチレンソルビタンモノステアレート、ポリエチレングリコールモノラウレート等のノニオン性界面活性剤;アルキル4級アンモニウム塩やそれらのエチレンオキサイド付加物等のカオチン性界面活性剤;アルキルジメチルアミノ酢酸ベタイン等のアルキルベタイン、アルキルイミダゾリン等の両性界面活性剤が挙げられ、これらは単独でまたは2種以上を混合して用いることができるが、必ずしもこれらに限定されるものではない。
界面活性剤としては、ラウリル硫酸ナトリウム、ポリオキシエチレンアルキルエーテル硫酸塩、ドデシルベンゼンスルホン酸ナトリウム、スチレン−アクリル酸共重合体のアルカリ塩、ステアリン酸ナトリウム、アルキルナフタリンスルホン酸ナトリウム、アルキルジフェニルエーテルジスルホン酸ナトリウム、ラウリル硫酸モノエタノールアミン、ラウリル硫酸トリエタノールアミン、ラウリル硫酸アンモニウム、ステアリン酸モノエタノールアミン、スチレン−アクリル酸共重合体のモノエタノールアミン、ポリオキシエチレンアルキルエーテルリン酸エステル等のアニオン性界面活性剤;ポリオキシエチレンオレイルエーテル、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンアルキルエーテルリン酸エステル、ポリオキシエチレンソルビタンモノステアレート、ポリエチレングリコールモノラウレート等のノニオン性界面活性剤;アルキル4級アンモニウム塩やそれらのエチレンオキサイド付加物等のカオチン性界面活性剤;アルキルジメチルアミノ酢酸ベタイン等のアルキルベタイン、アルキルイミダゾリン等の両性界面活性剤が挙げられ、これらは単独でまたは2種以上を混合して用いることができるが、必ずしもこれらに限定されるものではない。
樹脂型分散剤、界面活性剤を添加する場合の配合量は、着色剤100重量部に対して、好ましくは0.1〜55重量部、さらに好ましくは0.1〜45重量部である。樹脂型分散剤、界面活性剤の配合量が、0.1重量部未満の場合には、添加した効果が得られ難く、配合量が55重量部より多いと、過剰な分散剤により分散に悪影響を及ぼすことがある。
<着色組成物の製造方法>
本発明の着色組成物は、キノフタロン化合物を含有する着色剤、バインダー樹脂、および有機溶剤を混合したものを、三本ロールミル、二本ロールミル、サンドミル、ニーダー、またはアトライター等の各種分散手段を用いて微細に分散して製造することができる。また、本発明の着色組成物は、着色剤等を別々にバインダー樹脂および有機溶剤中に微細に分散したものを混合して製造することもできる。
本発明の着色組成物は、キノフタロン化合物を含有する着色剤、バインダー樹脂、および有機溶剤を混合したものを、三本ロールミル、二本ロールミル、サンドミル、ニーダー、またはアトライター等の各種分散手段を用いて微細に分散して製造することができる。また、本発明の着色組成物は、着色剤等を別々にバインダー樹脂および有機溶剤中に微細に分散したものを混合して製造することもできる。
微細化された着色剤をサンドミル等の分散機を用いて透明樹脂に分散すると、一次粒子が複数個集まった二次粒子からなる分散粒子の状態で分散され、分散状態の進行によりこの分散粒子は徐々に小さくなり、最終的には一次粒子の状態で分散されているようになるものであるが、分散状態を分散粒子の大きさで制御し、分散粒子の平均径が50nmから150nmの範囲内となるように分散させたものである。
分散が進むにつれ分散粒径は小さくなり、透明性が増し、コントラスト比は上昇するため、分散粒径は小さくなるほどよく、300nmくらいから良好なコントラスト比が得られるようになる。一方、分散が進行し、分散粒径が小さくなると分散体の粘度が上昇し、かつチキソトロピック性が大きくなる傾向がみられる。カラーフィルタ用着色組成物として用いる場合には、薄膜塗布されかつ塗膜表面が平滑であることが要求されるため、低粘度でかつニュートニアンフローであることが要求される。このため、通常の使用に好ましい粘度やチキソトロピック性を考慮すると、分散粒径を100nm程度に抑えることが好ましい。このように、平均一次粒子径が100nm以下の着色剤を用い、分散粒子の平均粒径を50nmから150nmの範囲内となるように分散度合いを制御することにより、粘度上昇およびチキソトロピック性が最小限に抑えられ、コントラスト比が非常に高い顔料分散体を得ることができる。
<粗大粒子の除去>
本発明の着色組成物は、遠心分離、焼結フィルタ、メンブレンフィルタ等の手段にて、5μm以上の粗大粒子、好ましくは1μm以上の粗大粒子、さらに好ましくは0.5μm以上の粗大粒子および混入した塵の除去を行うことが好ましい。このように着色組成物は、実質的に0.5μm以上の粒子を含まないことが好ましい。より好ましくは0.3μm以下であることが好ましい。
本発明の着色組成物は、遠心分離、焼結フィルタ、メンブレンフィルタ等の手段にて、5μm以上の粗大粒子、好ましくは1μm以上の粗大粒子、さらに好ましくは0.5μm以上の粗大粒子および混入した塵の除去を行うことが好ましい。このように着色組成物は、実質的に0.5μm以上の粒子を含まないことが好ましい。より好ましくは0.3μm以下であることが好ましい。
本発明の着色組成物は、さらに光重合性単量体および/または光重合開始剤を添加し、カラーフィルタ用着色組成物として使用することができる。
<光重合性単量体>
光重合性単量体には、紫外線や熱などにより硬化して透明樹脂を生成するモノマーもしくはオリゴマーが含まれ、これらを単独で、または2種以上混合して用いることができる。モノマーの配合量は、着色剤100重量部に対して、5〜400重量部であることが好ましく、光硬化性および現像性の観点から10〜300重量部であることがより好ましい。
光重合性単量体には、紫外線や熱などにより硬化して透明樹脂を生成するモノマーもしくはオリゴマーが含まれ、これらを単独で、または2種以上混合して用いることができる。モノマーの配合量は、着色剤100重量部に対して、5〜400重量部であることが好ましく、光硬化性および現像性の観点から10〜300重量部であることがより好ましい。
紫外線や熱などにより硬化して透明樹脂を生成するモノマー、オリゴマーとしては、例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、β−カルボキシエチル(メタ)アクリレート、ポリエチレングリコールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、トリエチレングリコールジ(メタ)アクリレート、トリプロピレングリコールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、1,6−ヘキサンジオールジグリシジルエーテルジ(メタ)アクリレート、ビスフェノールAジグリシジルエーテルジ(メタ)アクリレート、ネオペンチルグリコールジグリシジルエーテルジ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、トリシクロデカニル(メタ)アクリレート、エステルアクリレート、メチロール化メラミンの(メタ)アクリル酸エステル、エポキシ(メタ)アクリレート、ウレタンアクリレート等の各種アクリル酸エステルおよびメタクリル酸エステル、(メタ)アクリル酸、スチレン、酢酸ビニル、ヒドロキシエチルビニルエーテル、エチレングリコールジビニルエーテル、ペンタエリスリトールトリビニルエーテル、(メタ)アクリルアミド、N−ヒドロキシメチル(メタ)アクリルアミド、N−ビニルホルムアミド、アクリロニトリル等が挙げられるが、必ずしもこれらに限定されるものではない。
<光重合開始剤>
本発明のカラーフィルタ用着色組成物は、該組成物を紫外線照射により硬化させ、フォトリソグラフ法によりフィルタセグメントを形成する場合、光重合開始剤等を加えて溶剤現像型あるいはアルカリ現像型着色レジスト材の形態で調製することができる。光重合開始剤を使用する際の配合量は、着色剤100重量部に対して、2〜200重量部であることが好ましく、光硬化性および現像性の観点から5〜150重量部であることがより好ましい。
本発明のカラーフィルタ用着色組成物は、該組成物を紫外線照射により硬化させ、フォトリソグラフ法によりフィルタセグメントを形成する場合、光重合開始剤等を加えて溶剤現像型あるいはアルカリ現像型着色レジスト材の形態で調製することができる。光重合開始剤を使用する際の配合量は、着色剤100重量部に対して、2〜200重量部であることが好ましく、光硬化性および現像性の観点から5〜150重量部であることがより好ましい。
光重合開始剤としては、4−フェノキシジクロロアセトフェノン、4−t−ブチル−ジクロロアセトフェノン、ジエトキシアセトフェノン、1−(4−イソプロピルフェニル)−2−ヒドロキシ−2−メチルプロパン−1−オン、1−ヒドロキシシクロヘキシルフェニルケトン、2−メチル−1−[4−(メチルチオ)フェニル]−2−モルフォリノプロパン−1−オン、2−(ジメチルアミノ)−2−[(4−メチルフェニル)メチル]−1−[4−(4−モルフォリニル)フェニル]−1−ブタノン、または2−ベンジル−2−ジメチルアミノ−1−(4−モルフォリノフェニル)−ブタン−1−オン等のアセトフェノン系化合物;ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、またはベンジルジメチルケタール等のベンゾイン系化合物;ベンゾフェノン、ベンゾイル安息香酸、ベンゾイル安息香酸メチル、4−フェニルベンゾフェノン、ヒドロキシベンゾフェノン、アクリル化ベンゾフェノン、4−ベンゾイル−4’−メチルジフェニルサルファイド、または3,3’,4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン等のベンゾフェノン系化合物;チオキサントン、2−クロルチオキサントン、2−メチルチオキサントン、イソプロピルチオキサントン、2,4−ジイソプロピルチオキサントン、または2,4−ジエチルチオキサントン等のチオキサントン系化合物;2,4,6−トリクロロ−s−トリアジン、2−フェニル−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−メトキシフェニル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(p−トリル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−ピペロニル−4,6−ビス(トリクロロメチル)−s−トリアジン、2,4−ビス(トリクロロメチル)−6−スチリル−s−トリアジン、2−(ナフト−1−イル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2−(4−メトキシ−ナフト−1−イル)−4,6−ビス(トリクロロメチル)−s−トリアジン、2,4−トリクロロメチル−(ピペロニル)−6−トリアジン、または2,4−トリクロロメチル−(4’−メトキシスチリル)−6−トリアジン等のトリアジン系化合物;1,2−オクタンジオン,1−〔4−(フェニルチオ)−,2−(O−ベンゾイルオキシム)〕、またはO−(アセチル)−N−(1−フェニル−2−オキソ−2−(4’−メトキシ−ナフチル)エチリデン)ヒドロキシルアミン等のオキシムエステル系化合物;ビス(2,4,6−トリメチルベンゾイル)フェニルホスフィンオキサイド、または2,4,6−トリメチルベンゾイルジフェニルホスフィンオキサイド等のホスフィン系化合物;9,10−フェナンスレンキノン、カンファーキノン、エチルアントラキノン等のキノン系化合物; ボレート系化合物; カルバゾール系化合物;イミダゾール系化合物;あるいは、チタノセン系化合物等が用いられる。
これらの光重合開始剤は1種または必要に応じて任意の比率で2種以上混合して用いることができる。これらの光重合開始剤は、カラーフィルタ用着色組成物中の着色剤100重量部に対して、2〜200重量部であることが好ましく、光硬化性および現像性の観点から5〜150重量部であることがより好ましい。
<増感剤>
さらに、本発明のカラーフィルタ用着色組成物には、増感剤を含有させることができる。増感剤としては、カルコン誘導体、ジベンザルアセトン等に代表される不飽和ケトン類、ベンジルやカンファーキノン等に代表される1,2−ジケトン誘導体、ベンゾイン誘導体、フルオレン誘導体、ナフトキノン誘導体、アントラキノン誘導体、キサンテン誘導体、チオキサンテン誘導体、キサントン誘導体、チオキサントン誘導体、クマリン誘導体、ケトクマリン誘導体、シアニン誘導体、メロシアニン誘導体、オキソノ−ル誘導体等のポリメチン色素、アクリジン誘導体、アジン誘導体、チアジン誘導体、オキサジン誘導体、インドリン誘導体、アズレン誘導体、アズレニウム誘導体、スクアリリウム誘導体、ポルフィリン誘導体、テトラフェニルポルフィリン誘導体、トリアリールメタン誘導体、テトラベンゾポルフィリン誘導体、テトラピラジノポルフィラジン誘導体、フタロシアニン誘導体、テトラアザポルフィラジン誘導体、テトラキノキサリロポルフィラジン誘導体、ナフタロシアニン誘導体、サブフタロシアニン誘導体、ピリリウム誘導体、チオピリリウム誘導体、テトラフィリン誘導体、アヌレン誘導体、スピロピラン誘導体、スピロオキサジン誘導体、チオスピロピラン誘導体、金属アレーン錯体、有機ルテニウム錯体、またはミヒラーケトン誘導体、α−アシロキシエステル、アシルフォスフィンオキサイド、メチルフェニルグリオキシレート、ベンジル、9,10−フェナンスレンキノン、カンファーキノン、エチルアンスラキノン、4,4’−ジエチルイソフタロフェノン、3,3’または4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン、4,4’−ジエチルアミノベンゾフェノン等が挙げられる。
さらに、本発明のカラーフィルタ用着色組成物には、増感剤を含有させることができる。増感剤としては、カルコン誘導体、ジベンザルアセトン等に代表される不飽和ケトン類、ベンジルやカンファーキノン等に代表される1,2−ジケトン誘導体、ベンゾイン誘導体、フルオレン誘導体、ナフトキノン誘導体、アントラキノン誘導体、キサンテン誘導体、チオキサンテン誘導体、キサントン誘導体、チオキサントン誘導体、クマリン誘導体、ケトクマリン誘導体、シアニン誘導体、メロシアニン誘導体、オキソノ−ル誘導体等のポリメチン色素、アクリジン誘導体、アジン誘導体、チアジン誘導体、オキサジン誘導体、インドリン誘導体、アズレン誘導体、アズレニウム誘導体、スクアリリウム誘導体、ポルフィリン誘導体、テトラフェニルポルフィリン誘導体、トリアリールメタン誘導体、テトラベンゾポルフィリン誘導体、テトラピラジノポルフィラジン誘導体、フタロシアニン誘導体、テトラアザポルフィラジン誘導体、テトラキノキサリロポルフィラジン誘導体、ナフタロシアニン誘導体、サブフタロシアニン誘導体、ピリリウム誘導体、チオピリリウム誘導体、テトラフィリン誘導体、アヌレン誘導体、スピロピラン誘導体、スピロオキサジン誘導体、チオスピロピラン誘導体、金属アレーン錯体、有機ルテニウム錯体、またはミヒラーケトン誘導体、α−アシロキシエステル、アシルフォスフィンオキサイド、メチルフェニルグリオキシレート、ベンジル、9,10−フェナンスレンキノン、カンファーキノン、エチルアンスラキノン、4,4’−ジエチルイソフタロフェノン、3,3’または4,4’−テトラ(t−ブチルパーオキシカルボニル)ベンゾフェノン、4,4’−ジエチルアミノベンゾフェノン等が挙げられる。
さらに具体的には、大河原信ら編、「色素ハンドブック」(1986年、講談社)、大河原信ら編、「機能性色素の化学」(1981年、シーエムシー)、池森忠三朗ら編、及び「特殊機能材料」(1986年、シーエムシー)に記載の増感剤が挙げられるがこれらに限定されるものではない。また、その他、紫外から近赤外域にかけての光に対して吸収を示す増感剤を含有させることもできる。
増感剤は、必要に応じて任意の比率で2種以上用いても構わない。増感剤を使用する際の配合量は、着色組成物中に含まれる光重合開始剤100重量部に対して、3〜60重量部であることが好ましく、光硬化性、現像性の観点から5〜50重量部であることがより好ましい。
<アミン系化合物>
また、本発明の着色組成物には、溶存している酸素を還元する働きのあるアミン系化合物を含有させることができる。このようなアミン系化合物としては、トリエタノールアミン、メチルジエタノールアミン、トリイソプロパノールアミン、4−ジメチルアミノ安息香酸メチル、4−ジメチルアミノ安息香酸エチル、4−ジメチルアミノ安息香酸イソアミル、安息香酸2−ジメチルアミノエチル、4−ジメチルアミノ安息香酸2−エチルヘキシル、及びN,N−ジメチルパラトルイジン等が挙げられる。
また、本発明の着色組成物には、溶存している酸素を還元する働きのあるアミン系化合物を含有させることができる。このようなアミン系化合物としては、トリエタノールアミン、メチルジエタノールアミン、トリイソプロパノールアミン、4−ジメチルアミノ安息香酸メチル、4−ジメチルアミノ安息香酸エチル、4−ジメチルアミノ安息香酸イソアミル、安息香酸2−ジメチルアミノエチル、4−ジメチルアミノ安息香酸2−エチルヘキシル、及びN,N−ジメチルパラトルイジン等が挙げられる。
<レベリング剤>
本発明の着色組成物には、透明基板上での組成物のレベリング性を良くするため、レベリング剤を添加することが好ましい。レベリング剤としては、主鎖にポリエーテル構造またはポリエステル構造を有するジメチルシロキサンが好ましい。主鎖にポリエーテル構造を有するジメチルシロキサンの具体例としては、東レ・ダウコーニング社製FZ−2122、ビックケミー社製BYK−333などが挙げられる。主鎖にポリエステル構造を有するジメチルシロキサンの具体例としては、ビックケミー社製BYK−310、BYK−370などが挙げられる。主鎖にポリエーテル構造を有するジメチルシロキサンと、主鎖にポリエステル構造を有するジメチルシロキサンとは、併用することもできる。レベリング剤の含有量は通常、着色組成物100重量部に対して、0.003〜0.5重量部用いることが好ましい。
本発明の着色組成物には、透明基板上での組成物のレベリング性を良くするため、レベリング剤を添加することが好ましい。レベリング剤としては、主鎖にポリエーテル構造またはポリエステル構造を有するジメチルシロキサンが好ましい。主鎖にポリエーテル構造を有するジメチルシロキサンの具体例としては、東レ・ダウコーニング社製FZ−2122、ビックケミー社製BYK−333などが挙げられる。主鎖にポリエステル構造を有するジメチルシロキサンの具体例としては、ビックケミー社製BYK−310、BYK−370などが挙げられる。主鎖にポリエーテル構造を有するジメチルシロキサンと、主鎖にポリエステル構造を有するジメチルシロキサンとは、併用することもできる。レベリング剤の含有量は通常、着色組成物100重量部に対して、0.003〜0.5重量部用いることが好ましい。
レベリング剤として特に好ましいものとしては、分子内に疎水基と親水基を有する、いわゆる界面活性剤の一種で、親水基を有しながらも水に対する溶解性が小さく、着色組成物に添加した場合、その表面張力低下能が低いという特徴を有し、さらに表面張力低下能が低いにも拘らずガラス板への濡れ性が良好なものが有用であり、泡立ちによる塗膜の欠陥が出現しない添加量において十分に帯電性を抑止できるものが好ましく使用できる。このような好ましい特性を有するレベリング剤として、ポリアルキレンオキサイド単位を有するジメチルポリシロキサンが好ましく使用できる。ポリアルキレンオキサイド単位としては、ポリエチレンオキサイド単位、ポリプロピレンオキサイド単位があり、ジメチルポリシロキサンは、ポリエチレンオキサイド単位とポリプロピレンオキサイド単位とを共に有していてもよい。
また、ポリアルキレンオキサイド単位のジメチルポリシロキサンとの結合形態は、ポリアルキレンオキサイド単位がジメチルポリシロキサンの繰り返し単位中に結合したペンダント型、ジメチルポリシロキサンの末端に結合した末端変性型、ジメチルポリシロキサンと交互に繰り返し結合した直鎖状のブロックコポリマー型のいずれであってもよい。ポリアルキレンオキサイド単位を有するジメチルポリシロキサンは、東レ・ダウコーニング株式会社から市販されており、例えば、FZ−2110、FZ−2122、FZ−2130、FZ−2166、FZ−2191、FZ−2203、FZ−2207が挙げられるが、これらに限定されるものではない。
レベリング剤には、アニオン性、カチオン性、ノニオン性、または両性の界面活性剤を補助的に加えることも可能である。界面活性剤は、2種以上混合して使用しても構わない。レベリング剤に補助的に加えるアニオン性界面活性剤としては、ポリオキシエチレンアルキルエーテル硫酸塩、ドデシルベンゼンスルホン酸ナトリウム、スチレン−アクリル酸共重合体のアルカリ塩、アルキルナフタリンスルホン酸ナトリウム、アルキルジフェニルエーテルジスルホン酸ナトリウム、ラウリル硫酸モノエタノールアミン、ラウリル硫酸トリエタノールアミン、ラウリル硫酸アンモニウム、ステアリン酸モノエタノールアミン、ステアリン酸ナトリウム、ラウリル硫酸ナトリウム、スチレン−アクリル酸共重合体のモノエタノールアミン、ポリオキシエチレンアルキルエーテルリン酸エステルなどが挙げられる。
レベリング剤に補助的に加えるカオチン性界面活性剤としては、アルキル4級アンモニウム塩やそれらのエチレンオキサイド付加物が挙げられる。レベリング剤に補助的に加えるノニオン性界面活性剤としては、ポリオキシエチレンオレイルエーテル、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンアルキルエーテルリン酸エステル、ポリオキシエチレンソルビタンモノステアレート、ポリエチレングリコールモノラウレートなどの;アルキルジメチルアミノ酢酸ベタインなどのアルキルベタイン、アルキルイミダゾリンなどの両性界面活性剤、また、フッ素系やシリコーン系の界面活性剤が挙げられる。
<硬化剤、硬化促進剤>
また本発明の着色組成物には、熱硬化性樹脂の硬化を補助するため、必要に応じて、硬化剤、硬化促進剤などを含んでいてもよい。硬化剤としては、フェノール系樹脂、アミン系化合物、酸無水物、活性エステル、カルボン酸系化合物、スルホン酸系化合物などが有効であるが、特にこれらに限定されるものではなく、熱硬化性樹脂と反応し得るものであれば、いずれの硬化剤を使用してもよい。また、これらの中でも、1分子内に2個以上のフェノール性水酸基を有する化合物、アミン系硬化剤が好ましく挙げられる。前記硬化促進剤としては、例えば、アミン化合物(例えば、ジシアンジアミド、ベンジルジメチルアミン、4−(ジメチルアミノ)−N,N−ジメチルベンジルアミン、4−メトキシ−N,N−ジメチルベンジルアミン、4−メチル−N,N−ジメチルベンジルアミン等)、4級アンモニウム塩化合物(例えば、トリエチルベンジルアンモニウムクロリド等)、ブロックイソシアネート化合物(例えば、ジメチルアミン等)、イミダゾール誘導体二環式アミジン化合物及びその塩(例えば、イミダゾール、2−メチルイミダゾール、2−エチルイミダゾール、2−エチル−4−メチルイミダゾール、2−フェニルイミダゾール、4−フェニルイミダゾール、1−シアノエチル−2−フェニルイミダゾール、1−(2−シアノエチル)−2−エチル−4−メチルイミダゾール等)、リン化合物(例えば、トリフェニルホスフィン等)、グアナミン化合物(例えば、メラミン、グアナミン、アセトグアナミン、ベンゾグアナミン等)、S−トリアジン誘導体(例えば、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン、2−ビニル−2,4−ジアミノ−S−トリアジン、2−ビニル−4,6−ジアミノ−S−トリアジン・イソシアヌル酸付加物、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン・イソシアヌル酸付加物等)などを用いることができる。これらは1種単独で使用してもよく、2種以上を併用してもよい。前記硬化促進剤の含有量としては、熱硬化性樹脂全量に対し、0.01〜15重量%が好ましい。
また本発明の着色組成物には、熱硬化性樹脂の硬化を補助するため、必要に応じて、硬化剤、硬化促進剤などを含んでいてもよい。硬化剤としては、フェノール系樹脂、アミン系化合物、酸無水物、活性エステル、カルボン酸系化合物、スルホン酸系化合物などが有効であるが、特にこれらに限定されるものではなく、熱硬化性樹脂と反応し得るものであれば、いずれの硬化剤を使用してもよい。また、これらの中でも、1分子内に2個以上のフェノール性水酸基を有する化合物、アミン系硬化剤が好ましく挙げられる。前記硬化促進剤としては、例えば、アミン化合物(例えば、ジシアンジアミド、ベンジルジメチルアミン、4−(ジメチルアミノ)−N,N−ジメチルベンジルアミン、4−メトキシ−N,N−ジメチルベンジルアミン、4−メチル−N,N−ジメチルベンジルアミン等)、4級アンモニウム塩化合物(例えば、トリエチルベンジルアンモニウムクロリド等)、ブロックイソシアネート化合物(例えば、ジメチルアミン等)、イミダゾール誘導体二環式アミジン化合物及びその塩(例えば、イミダゾール、2−メチルイミダゾール、2−エチルイミダゾール、2−エチル−4−メチルイミダゾール、2−フェニルイミダゾール、4−フェニルイミダゾール、1−シアノエチル−2−フェニルイミダゾール、1−(2−シアノエチル)−2−エチル−4−メチルイミダゾール等)、リン化合物(例えば、トリフェニルホスフィン等)、グアナミン化合物(例えば、メラミン、グアナミン、アセトグアナミン、ベンゾグアナミン等)、S−トリアジン誘導体(例えば、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン、2−ビニル−2,4−ジアミノ−S−トリアジン、2−ビニル−4,6−ジアミノ−S−トリアジン・イソシアヌル酸付加物、2,4−ジアミノ−6−メタクリロイルオキシエチル−S−トリアジン・イソシアヌル酸付加物等)などを用いることができる。これらは1種単独で使用してもよく、2種以上を併用してもよい。前記硬化促進剤の含有量としては、熱硬化性樹脂全量に対し、0.01〜15重量%が好ましい。
<その他の添加剤成分>
本発明の着色組成物には、組成物の経時粘度を安定化させるために貯蔵安定剤を含有させることができる。また、透明基板との密着性を高めるためにシランカップリング剤等の密着向上剤を含有させることもできる。
本発明の着色組成物には、組成物の経時粘度を安定化させるために貯蔵安定剤を含有させることができる。また、透明基板との密着性を高めるためにシランカップリング剤等の密着向上剤を含有させることもできる。
貯蔵安定剤としては、例えば、ベンジルトリメチルクロライド、ジエチルヒドロキシアミンなどの4級アンモニウムクロライド、乳酸、シュウ酸などの有機酸およびそのメチルエーテル、t−ブチルピロカテコール、テトラエチルホスフィン、テトラフェニルフォスフィンなどの有機ホスフィン、亜リン酸塩等が挙げられる。貯蔵安定剤は、着色剤100重量部に対して、0.1〜10重量部用いることが好ましい。
密着向上剤としては、ビニルトリス(β−メトキシエトキシ)シラン、ビニルエトキシシラン、ビニルトリメトキシシラン等のビニルシラン類、γ−メタクリロキシプロピルトリメトキシシラン等の(メタ)アクリルシラン類、β−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、β−(3,4−エポキシシクロヘキシル)メチルトリメトキシシラン、β−(3,4−エポキシシクロヘキシル)エチルトリエトキシシラン、β−(3,4−エポキシシクロヘキシル)メチルトリエトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルトリエトキシシラン等のエポキシシラン類、N−β(アミノエチル)γ−アミノプロピルトリメトキシシラン、N−β(アミノエチル)γ−アミノプロピルトリエトキシシラン、N−β(アミノエチル)γ−アミノプロピルメチルジエトキシシシラン、γ−アミノプロピルトリエトキシシラン、γ−アミノプロピルトリメトキシシラン、N−フェニル−γ−アミノプロピルトリメトキシシラン、N−フェニル−γ−アミノプロピルトリエトキシシラン等のアミノシラン類、γ−メルカプトプロピルトリメトキシシラン、γ−メルカプトプロピルトリエトキシシラン等のチオシラン類等のシランカップリング剤が挙げられる。密着向上剤は、着色組成物中の着色剤100重量部に対して、0.01〜10重量部、好ましくは0.05〜5重量部用いるのが良い。
<カラーフィルタ>
次に、本発明のカラーフィルタについて説明する。本発明のカラーフィルタは、本発明のカラーフィルタ用着色組成物を用いて形成されたフィルタセグメントを具備するものである。カラーフィルタとしては、赤色フィルタセグメント、緑色フィルタセグメント、および青色フィルタセグメントを具備するものが挙げられ、前記フィルタセグメントは、スピンコート方式あるいはダイコート方式によってカラーフィルタ用着色組成物を塗布したのち、紫外線等の活性エネルギー線を照射してフィルタセグメントとなる部分を硬化し、ついで現像することにより、基板上に形成される。
次に、本発明のカラーフィルタについて説明する。本発明のカラーフィルタは、本発明のカラーフィルタ用着色組成物を用いて形成されたフィルタセグメントを具備するものである。カラーフィルタとしては、赤色フィルタセグメント、緑色フィルタセグメント、および青色フィルタセグメントを具備するものが挙げられ、前記フィルタセグメントは、スピンコート方式あるいはダイコート方式によってカラーフィルタ用着色組成物を塗布したのち、紫外線等の活性エネルギー線を照射してフィルタセグメントとなる部分を硬化し、ついで現像することにより、基板上に形成される。
本発明のカラーフィルタ用着色組成物は、主に緑色フィルタセグメントの形成に用いられ、それ以外の各色のフィルタセグメントは、従来用いられる赤色着色組成物、青色着色組成物を用いて形成することができる。本発明のカラーフィルタ用着色組成物以外の各色の着色組成物は、各色顔料、前記バインダー樹脂、前記光重合性組成物等を含有する各着色組成物を用いて形成することができる。
赤色フィルタセグメントは、赤色顔料と顔料担体を含む赤色着色組成物を用いて形成することができる。赤色着色組成物には、例えば、C.I.ピグメント レッド 7、14、41、48:1、48:2、48:3、48:4、57:1、81、81:1、81:2、81:3、81:4、122、146、168、169、177、178、184、185、187、200、202、208、210、242、246、254、255、264、270、272、273、274,276、277、278、279、280、281、282、283、284、285、286、又は287等の赤色顔料が用いられる。また赤色を呈する塩基性染料、酸性染料の造塩化合物を使用することもできる。
また赤色着色組成物には、C.I.ピグメント オレンジ 43、71、又は73等の橙色顔料及び/またはC.I.ピグメント イエロー 1、2、3、4、5、6、10、12、13、14、15、16、17、18、24、31、32、34、35、35:1、36、36:1、37、37:1、40、42、43、53、55、60、61、62、63、65、73、74、77、81、83、93、94、95、97、98、100、101、104、106、108、109、110、113、114、115、116、117、118、119、120、123、126、127、128、129、138、139、147、150、151、152、153、154、155、156、161、162、164、166、167、168、169、170、171、172、173、174、175、176、177、179、180、181、182、185、187、188、193、194、198、199、213、又は214等の黄色顔料を併用することができる。
青色着色組成物には、例えば、C.I.ピグメント ブルー 15、15:1、15:2、15:3、15:4、15:6、16、22、60、64等の青色顔料が用いられ、また、C.I.ピグメント バイオレット 1、19、23、27、29、30、32、37、40、42、50等の紫色顔料を併用することができる。また青色や紫色を呈する塩基性染料、酸性染料の造塩化合物を使用することもできる。
透明基板としては、ソーダ石灰ガラス、低アルカリ硼珪酸ガラス、無アルカリアルミノ硼珪酸ガラスなどのガラス板や、ポリカーボネート、ポリメタクリル酸メチル、ポリエチレンテレフタレートなどの樹脂板が用いられる。また、ガラス板や樹脂板の表面には、パネル化後の液晶駆動のために、酸化インジウム、酸化錫などからなる透明電極が形成されていてもよい。
<カラーフィルタの製造方法>
本発明のカラーフィルタは、印刷法またはフォトリソグラフィー法により、製造することができる。
本発明のカラーフィルタは、印刷法またはフォトリソグラフィー法により、製造することができる。
印刷法によるフィルタセグメントの形成は、印刷インキとして調製した着色組成物の印刷と乾燥を繰り返すだけでパターン化ができるため、カラーフィルタの製造法としては、低コストであり、かつ量産性に優れている。さらに、印刷技術の発展により高い寸法精度および平滑度を有する微細パターンの印刷を行うことができる。印刷を行うためには、印刷の版上にて、あるいはブランケット上にてインキが乾燥、固化しないような組成とすることが好ましい。また、印刷機上でのインキの流動性制御も重要であり、分散剤や体質顔料によってインキ粘度の調整も行うことができる。
フォトリソグラフィー法によりフィルタセグメントを形成する場合は、上記溶剤現像型あるいはアルカリ現像型着色レジスト材として調製した着色組成物を、透明基板上に、スプレーコートやスピンコート、スリットコート、ロールコート等の塗布方法により、乾燥膜厚が0.2〜5μmとなるように塗布する。必要により乾燥された膜には、この膜と接触あるいは非接触状態で設けられた所定のパターンを有するマスクを通して紫外線露光を行う。その後、溶剤またはアルカリ現像液に浸漬するかもしくはスプレーなどにより現像液を噴霧して未硬化部を除去して所望のパターンを形成したのち、同様の操作を他色について繰り返してカラーフィルタを製造することができる。さらに、着色レジスト材の重合を促進するため、必要に応じて加熱を施すこともできる。フォトリソグラフィー法によれば、上記印刷法より精度の高いカラーフィルタが製造できる。
現像に際しては、アルカリ現像液として炭酸ナトリウム、水酸化ナトリウム等の水溶液が使用され、ジメチルベンジルアミン、トリエタノールアミン等の有機アルカリを用いることもできる。また、現像液には、消泡剤や界面活性剤を添加することもできる。
なお、紫外線露光感度を上げるために、上記着色レジスト材を塗布乾燥後、水溶性あるいはアルカリ水溶性樹脂、例えばポリビニルアルコールや水溶性アクリル樹脂等を塗布乾燥し酸素による重合阻害を防止する膜を形成した後、紫外線露光を行うこともできる。
なお、紫外線露光感度を上げるために、上記着色レジスト材を塗布乾燥後、水溶性あるいはアルカリ水溶性樹脂、例えばポリビニルアルコールや水溶性アクリル樹脂等を塗布乾燥し酸素による重合阻害を防止する膜を形成した後、紫外線露光を行うこともできる。
本発明のカラーフィルタは、上記方法の他に電着法、転写法などにより製造することができるが、本発明の着色組成物はいずれの方法にも用いることができる。なお、電着法は、基板上に形成した透明導電膜を利用して、コロイド粒子の電気泳動により各色フィルタセグメントを透明導電膜の上に電着形成することでカラーフィルタを製造する方法である。また、転写法は剥離性の転写ベースシートの表面に、あらかじめフィルタセグメントを形成しておき、このフィルタセグメントを所望の基板に転写させる方法である。
透明基板あるいは反射基板上に各色フィルタセグメントを形成する前に、あらかじめブラックマトリクスを形成することができる。ブラックマトリクスとしては、クロムやクロム/酸化クロムの多層膜、窒化チタニウムなどの無機膜や、遮光剤を分散した樹脂膜が用いられるが、これらに限定されない。また、前記の透明基板あるいは反射基板上に薄膜トランジスター(TFT)をあらかじめ形成しておき、その後に各色フィルタセグメントを形成することもできる。また本発明のカラーフィルタ上には、必要に応じてオーバーコート膜や透明導電膜などが形成される。
以下に、本発明を実施例に基づいて説明するが、本発明はこれによって限定されるものではない。実施例および比較例中、特に断りの無い限り「部」とは「質量部」を意味する。まず、実施例に先だって、キノフタロン化合物の平均一次粒子径の測定方法、着色組成物に使用する色素誘導体(1)およびキノフタロン化合物(a)、(b)、(c)の製造方法について説明する。
(着色剤の平均一次粒子径の測定方法)
以下に示す方法により、着色剤の平均一次粒子径を測定(算出)した。着色剤の粉末にプロピレングリコールモノメチルエーテルアセテートを加え、樹脂型分散剤としてDisperbyk−161を少量添加し、超音波洗浄機の水浴中で1分間分散処理して測定用試料を調整した。この試料を透過型電子顕微鏡(TEM)により、200個以上の着色剤の一次粒子が観察出来る写真を5〜10万倍で6葉(6視野分)撮影し、任意に1000個の一次粒子の大きさを測定した。具体的には、個々の着色剤の一次粒子の短軸径と長軸径を1nm単位で計測し、その平均値を個々の粒子の着色剤の一次粒子径とし、合計1000個の着色剤の一次粒子径を5nm刻みで粒度分布を作成した。
以下に示す方法により、着色剤の平均一次粒子径を測定(算出)した。着色剤の粉末にプロピレングリコールモノメチルエーテルアセテートを加え、樹脂型分散剤としてDisperbyk−161を少量添加し、超音波洗浄機の水浴中で1分間分散処理して測定用試料を調整した。この試料を透過型電子顕微鏡(TEM)により、200個以上の着色剤の一次粒子が観察出来る写真を5〜10万倍で6葉(6視野分)撮影し、任意に1000個の一次粒子の大きさを測定した。具体的には、個々の着色剤の一次粒子の短軸径と長軸径を1nm単位で計測し、その平均値を個々の粒子の着色剤の一次粒子径とし、合計1000個の着色剤の一次粒子径を5nm刻みで粒度分布を作成した。
(色素誘導体(1)の製造)
特許第4585781号公報に記載の合成方法に従い、色素誘導体(1)を得た。
特許第4585781号公報に記載の合成方法に従い、色素誘導体(1)を得た。
化合物(1)100部、2,3−ナフタレンジカルボン酸無水物70部、および安息香酸143部を加え、180℃に加熱し、4時間反応させた。TOF−MSにより、キノフタロン化合物(a)の生成、および原料の化合物(1)の消失を確認した。さらに、室温まで冷却後、反応混合物をジメチルホルムアミド2500部に投入し、室温下にて1時間攪拌した。生成物を濾別し、メタノールにて洗浄、乾燥を行い、120部のキノフタロン化合物(a)を得た。TOF−MSによる質量分析の結果、計算値605.95に対し、606.92であり、キノフタロン化合物(a)であることを同定した。また、元素分析を行ったところ、計算値(C)59.44%、(H)2.00%、(N)4.62%に対して、実測値(C)59.49%、(H)2.02%、(N)4.58%であり、キノフタロン化合物(a)であることを確認した。
(キノフタロン化合物(b)の製造)
特開2008−81566号公報に記載の合成方法に従い、化合物(2)を得た。
特開2008−81566号公報に記載の合成方法に従い、化合物(2)を得た。
化合物(2)100部、2,3−ナフタレンジカルボン酸無水物70部、および安息香酸143部を加え、170℃に加熱し、4時間反応させた。TOF−MSにより、キノフタロン化合物(b)の生成、および原料の化合物(2)の消失を確認した。さらに、室温まで冷却後、反応混合物をジメチルホルムアミド2500部に投入し、室温下にて1時間攪拌した。生成物を濾別し、メタノールにて洗浄、乾燥を行い、120部のキノフタロン化合物(b)を得た。TOF−MSによる質量分析の結果、計算値605.95に対し、実測値606.95であり、キノフタロン化合物(b)であることを同定した。また、元素分析を行ったところ、計算値(C)59.44%、(H)2.00%、(N)4.62%に対して、実測値(C)59.60%、(H)1.99%、(N)4.64%であり、キノフタロン化合物(b)であることを確認した。
(キノフタロン化合物(c)の製造)
2,3−ナフタレンジカルボン酸無水物70部をテトラブロモ無水フタル酸部に変えた以外は、化合物(b)の製造と同様に行い、キノフタロン化合物(c)を得た。TOF−MSによる質量分析の結果、計算値871.76に対し、実測値871.68であり、キノフタロン化合物(c)であることを同定した。また、元素分析を行ったところ、計算値(C)35.82%、(H)0.69%、(N)3.21%に対して、実測値(C)35.89%、(H)0.70%、(N)3.18%であり、キノフタロン化合物(c)であることを確認した。
2,3−ナフタレンジカルボン酸無水物70部をテトラブロモ無水フタル酸部に変えた以外は、化合物(b)の製造と同様に行い、キノフタロン化合物(c)を得た。TOF−MSによる質量分析の結果、計算値871.76に対し、実測値871.68であり、キノフタロン化合物(c)であることを同定した。また、元素分析を行ったところ、計算値(C)35.82%、(H)0.69%、(N)3.21%に対して、実測値(C)35.89%、(H)0.70%、(N)3.18%であり、キノフタロン化合物(c)であることを確認した。
[実施例1]
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)100部、塩化ナトリウム1200部、およびジエチレングリコール120部をステンレス製1ガロンニーダー(井上製作所社製)に仕込み、65℃で15時間混練し、ソルトミリング処理した。得られた混練物を3リットルの温水に投入し、70℃に加熱しながら1時間撹拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、80℃で一昼夜乾燥し、98部の黄色着色剤(Y−1)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が5.5%、5〜20nmが14.2%、20〜35nmが67.1%、35〜50nmが11.2%、50nmを超える粒子が2.0%であった。
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)100部、塩化ナトリウム1200部、およびジエチレングリコール120部をステンレス製1ガロンニーダー(井上製作所社製)に仕込み、65℃で15時間混練し、ソルトミリング処理した。得られた混練物を3リットルの温水に投入し、70℃に加熱しながら1時間撹拌してスラリー状とし、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、80℃で一昼夜乾燥し、98部の黄色着色剤(Y−1)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が5.5%、5〜20nmが14.2%、20〜35nmが67.1%、35〜50nmが11.2%、50nmを超える粒子が2.0%であった。
[実施例2]
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)をキノフタロン化合物(a)に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、96部の黄色着色剤2(Y−2)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が7.6%、5〜20nmが15.5%、20〜35nmが68.8%、35〜50nmが7.1%、50nmを超える粒子が1.0%であった。
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)をキノフタロン化合物(a)に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、96部の黄色着色剤2(Y−2)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が7.6%、5〜20nmが15.5%、20〜35nmが68.8%、35〜50nmが7.1%、50nmを超える粒子が1.0%であった。
[実施例3]
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)をキノフタロン化合物(b)に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、98部の黄色着色剤3(Y−3)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が6.3%、5〜20nmが12.5%、20〜35nmが60.9%、35〜50nmが18.1%、50nmを超える粒子が2.2%であった。
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)をキノフタロン化合物(b)に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、98部の黄色着色剤3(Y−3)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が6.3%、5〜20nmが12.5%、20〜35nmが60.9%、35〜50nmが18.1%、50nmを超える粒子が2.2%であった。
[実施例4]
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)をキノフタロン化合物(c)に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、97部の黄色着色剤4(Y−4)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が3.5%、5〜20nmが10.3%、20〜35nmが63.1%、35〜50nmが19.1%、50nmを超える粒子が4.0%であった。
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)をキノフタロン化合物(c)に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、97部の黄色着色剤4(Y−4)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が3.5%、5〜20nmが10.3%、20〜35nmが63.1%、35〜50nmが19.1%、50nmを超える粒子が4.0%であった。
[実施例5]
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)100部を、C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)70部とキノフタロン化合物(a)30部の混合物に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、95部の黄色着色剤5(Y−5)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が7.1%、5〜20nmが26.4%、20〜35nmが63.0%、35〜50nmが3.0%、50nmを超える粒子が0.5%であった。
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)100部を、C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)70部とキノフタロン化合物(a)30部の混合物に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、95部の黄色着色剤5(Y−5)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が7.1%、5〜20nmが26.4%、20〜35nmが63.0%、35〜50nmが3.0%、50nmを超える粒子が0.5%であった。
[実施例6]
65℃で15時間混練するところを、60度20時間に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、98部の黄色着色剤6(Y−6)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が6.0%、5〜20nmが26.8%、20〜35nmが58.6%、35〜50nmが6.8%、50nmを超える粒子が1.8%であった。
65℃で15時間混練するところを、60度20時間に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、98部の黄色着色剤6(Y−6)を得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が6.0%、5〜20nmが26.8%、20〜35nmが58.6%、35〜50nmが6.8%、50nmを超える粒子が1.8%であった。
[比較例1]
塩化ナトリウム1200部を300部に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、97部の黄色着色剤7(Y−7)得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が0.3%、5〜20nmが2.5%、20〜35nmが9.6%、35〜50nmが36.4%、50nmを超える粒子が51.2%であった。
塩化ナトリウム1200部を300部に変えた以外は、黄色着色剤1(Y−1)の製造と同様に行い、97部の黄色着色剤7(Y−7)得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が0.3%、5〜20nmが2.5%、20〜35nmが9.6%、35〜50nmが36.4%、50nmを超える粒子が51.2%であった。
[比較例2]
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)100部、塩化ナトリウム1200部、およびジエチレングリコール120部をステンレス製1ガロンニーダー(井上製作所社製)に仕込み、80℃で15時間混練した。次に、この混練物を温水に投入し、約70℃に加熱しながら1時間撹拌してスラリー状として、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、80℃で一昼夜乾燥し、96部の黄色着色剤8(Y−8)得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が0.2%、5〜20nmが4.7%、20〜35nmが55.3%、35〜50nmが19.3%、50nmを超える粒子が20.5%であった。
C.I.ピグメントイエロー138(BASF社製「パリオトールイエローK0961−HD」)100部、塩化ナトリウム1200部、およびジエチレングリコール120部をステンレス製1ガロンニーダー(井上製作所社製)に仕込み、80℃で15時間混練した。次に、この混練物を温水に投入し、約70℃に加熱しながら1時間撹拌してスラリー状として、濾過、水洗を繰り返して塩化ナトリウムおよびジエチレングリコールを除いた後、80℃で一昼夜乾燥し、96部の黄色着色剤8(Y−8)得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が0.2%、5〜20nmが4.7%、20〜35nmが55.3%、35〜50nmが19.3%、50nmを超える粒子が20.5%であった。
[比較例3]
80℃で15時間混練する工程を50℃15時間に変えた以外は、黄色着色剤8(Y−8)の製造と同様に行い、98部の黄色着色剤9(Y−9)得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が15.3%、5〜20nmが28.5%、20〜35nmが49.3%、35〜50nmが6.7%、50nmを超える粒子が0.2%であった。
80℃で15時間混練する工程を50℃15時間に変えた以外は、黄色着色剤8(Y−8)の製造と同様に行い、98部の黄色着色剤9(Y−9)得た。TEM写真から粒度分布を調べたところ、5nm未満の粒子が15.3%、5〜20nmが28.5%、20〜35nmが49.3%、35〜50nmが6.7%、50nmを超える粒子が0.2%であった。
製造した黄色着色剤1〜9(Y−1〜9)の内容を表1に示す。
<バインダー樹脂溶液の製造方法>
(アクリル樹脂溶液1の調製)
セパラブル4口フラスコに温度計、冷却管、窒素ガス導入管、滴下管および撹拌装置を取り付けた反応容器にシクロヘキサノン196部を仕込み、80℃に昇温し、反応容器内を窒素置換した後、滴下管より、n−ブチルメタクリレート37.2部、2−ヒドロキシエチルメタクリレート12.9部、メタクリル酸12.0部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亞合成株式会社製「アロニックスM110」)20.7部、2,2’−アゾビスイソブチロニトリル1.1部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、アクリル樹脂の溶液を得た。室温まで冷却した後、樹脂溶液約2部をサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20質量%になるようにメトキシプロピルアセテートを添加してアクリル樹脂溶液1を調製した。重量平均分子量(Mw)は26000であった。
(アクリル樹脂溶液1の調製)
セパラブル4口フラスコに温度計、冷却管、窒素ガス導入管、滴下管および撹拌装置を取り付けた反応容器にシクロヘキサノン196部を仕込み、80℃に昇温し、反応容器内を窒素置換した後、滴下管より、n−ブチルメタクリレート37.2部、2−ヒドロキシエチルメタクリレート12.9部、メタクリル酸12.0部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亞合成株式会社製「アロニックスM110」)20.7部、2,2’−アゾビスイソブチロニトリル1.1部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、アクリル樹脂の溶液を得た。室温まで冷却した後、樹脂溶液約2部をサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20質量%になるようにメトキシプロピルアセテートを添加してアクリル樹脂溶液1を調製した。重量平均分子量(Mw)は26000であった。
(アクリル樹脂溶液2の調製)
セパラブル4口フラスコに温度計、冷却管、窒素ガス導入管、滴下管および撹拌装置を取り付けた反応容器にシクロヘキサノン207部を仕込み、80℃に昇温し、反応容器内を窒素置換した後、滴下管より、メタクリル酸20部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亜合成社製アロニックスM110)20部、メタクリル酸メチル45部、2−ヒドロキシエチルメタクリレート8.5部、及び2,2'−アゾビスイソブチロニトリル1.33部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、共重合体樹脂溶液を得た。次に得られた共重合体溶液全量に対して、窒素ガスを停止し乾燥空気を1時間注入しながら攪拌したのちに、室温まで冷却した後、2−メタクリロイルオキシエチルイソシアネート(昭和電工社製カレンズMOI)6.5部、ラウリン酸ジブチル錫0.08部、シクロヘキサノン26部の混合物を70℃で3時間かけて滴下した。滴下終了後、更に1時間反応を継続し、アクリル樹脂の溶液を得た。室温まで冷却した後、樹脂溶液約2部をサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20質量%になるようにシクロヘキサノンを添加してアクリル樹脂溶液2を調製した。重量平均分子量(Mw)は18000であった。
セパラブル4口フラスコに温度計、冷却管、窒素ガス導入管、滴下管および撹拌装置を取り付けた反応容器にシクロヘキサノン207部を仕込み、80℃に昇温し、反応容器内を窒素置換した後、滴下管より、メタクリル酸20部、パラクミルフェノールエチレンオキサイド変性アクリレート(東亜合成社製アロニックスM110)20部、メタクリル酸メチル45部、2−ヒドロキシエチルメタクリレート8.5部、及び2,2'−アゾビスイソブチロニトリル1.33部の混合物を2時間かけて滴下した。滴下終了後、更に3時間反応を継続し、共重合体樹脂溶液を得た。次に得られた共重合体溶液全量に対して、窒素ガスを停止し乾燥空気を1時間注入しながら攪拌したのちに、室温まで冷却した後、2−メタクリロイルオキシエチルイソシアネート(昭和電工社製カレンズMOI)6.5部、ラウリン酸ジブチル錫0.08部、シクロヘキサノン26部の混合物を70℃で3時間かけて滴下した。滴下終了後、更に1時間反応を継続し、アクリル樹脂の溶液を得た。室温まで冷却した後、樹脂溶液約2部をサンプリングして180℃、20分加熱乾燥して不揮発分を測定し、先に合成した樹脂溶液に不揮発分が20質量%になるようにシクロヘキサノンを添加してアクリル樹脂溶液2を調製した。重量平均分子量(Mw)は18000であった。
(バインダー樹脂の重量平均分子量)
アクリル樹脂の重量平均分子量は、GPC(ゲルパーミエーションクロマトグラフィ)により測定したポリスチレン換算の重量平均分子量である。
アクリル樹脂の重量平均分子量は、GPC(ゲルパーミエーションクロマトグラフィ)により測定したポリスチレン換算の重量平均分子量である。
<黄色着色組成物の作製>
[実施例7]
(黄色着色組成物1(YP−1)の作製)
下記の成分からなる混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5μmのフィルタで濾過し、黄色着色組成物1(YP−1)を作製した。
黄色着色剤1(Y−1) 9.5部
色素誘導体(1) 0.5部
樹脂型分散剤(味の素ファインテクノ社製「PB821」) 1.0部
アクリル樹脂溶液1 45.0部
プロピレングリコールモノメチルエーテルアセテート 44.0部
[実施例7]
(黄色着色組成物1(YP−1)の作製)
下記の成分からなる混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5μmのフィルタで濾過し、黄色着色組成物1(YP−1)を作製した。
黄色着色剤1(Y−1) 9.5部
色素誘導体(1) 0.5部
樹脂型分散剤(味の素ファインテクノ社製「PB821」) 1.0部
アクリル樹脂溶液1 45.0部
プロピレングリコールモノメチルエーテルアセテート 44.0部
[実施例8〜12、比較例4〜6]
(黄色着色組成物2〜9(YP−2〜9)の作製)
黄色着色剤1(Y−1)を表2に記載の黄色着色剤に変更した以外は、黄色着色組成物1(YP−1)と同様にして、黄色着色組成物2〜9(YP−2〜9)を作製した。
(黄色着色組成物2〜9(YP−2〜9)の作製)
黄色着色剤1(Y−1)を表2に記載の黄色着色剤に変更した以外は、黄色着色組成物1(YP−1)と同様にして、黄色着色組成物2〜9(YP−2〜9)を作製した。
<黄色着色組成物の評価>
黄色着色組成物(YP−1〜9)の評価は、黄色着色組成物を用いた塗膜を作製し、その明度、コントラスト比、および耐熱性を測定することで評価を行なった。以下に、評価方法を示す。
(明度評価)
黄色着色組成物を、100mm×100mm、1.1mm厚のガラス基板上に、スピンコーターを用いて、着色膜の膜厚が異なる4種類の基板を塗布し、230℃で20分加熱することで塗膜を得た。この際、塗膜の膜厚は、230℃での熱処理後で、C光源においてx=0.440になるように塗布条件(スピンコーターの回転数、時間)を適時変更して塗布した。得られた塗膜を顕微分光光度計(オリンパス光学社製「OSP−SP100」)を用いて明度(Y)を測定し、下記基準に従って判定した。
○:89.0以上
△:87.5以上〜89.0未満
×:87.5未満
黄色着色組成物(YP−1〜9)の評価は、黄色着色組成物を用いた塗膜を作製し、その明度、コントラスト比、および耐熱性を測定することで評価を行なった。以下に、評価方法を示す。
(明度評価)
黄色着色組成物を、100mm×100mm、1.1mm厚のガラス基板上に、スピンコーターを用いて、着色膜の膜厚が異なる4種類の基板を塗布し、230℃で20分加熱することで塗膜を得た。この際、塗膜の膜厚は、230℃での熱処理後で、C光源においてx=0.440になるように塗布条件(スピンコーターの回転数、時間)を適時変更して塗布した。得られた塗膜を顕微分光光度計(オリンパス光学社製「OSP−SP100」)を用いて明度(Y)を測定し、下記基準に従って判定した。
○:89.0以上
△:87.5以上〜89.0未満
×:87.5未満
(コントラスト比評価)
液晶ディスプレー用バックライトユニットから出た光は、偏光板を通過して偏光され、ガラス基板上に塗布された着色組成物の塗膜を通過し、もう一方の偏光板に到達する。この際、偏光板と偏光板の偏光面が平行であれば、光は偏光板を透過するが、偏光面が直行している場合には光は偏光板により遮断される。しかし、偏光板によって偏光された光が着色組成物の塗膜を通過する際に、着色剤粒子によって散乱等が起こり、偏光面の一部にずれが生じると、偏光板が平行のときは透過する光量が減り、偏光板が直行のときは一部光が透過する。この透過光を偏光板上の輝度として測定し、偏光板が平行の際の輝度と、直行の際の輝度との比を、コントラスト比として算出した。
(コントラスト比)=(平行のときの輝度)/(直行のときの輝度)
従って、塗膜中の着色剤により散乱が起こると、平行のときの輝度が低下し、かつ直行のときの輝度が増加するため、コントラスト比が低くなる。
液晶ディスプレー用バックライトユニットから出た光は、偏光板を通過して偏光され、ガラス基板上に塗布された着色組成物の塗膜を通過し、もう一方の偏光板に到達する。この際、偏光板と偏光板の偏光面が平行であれば、光は偏光板を透過するが、偏光面が直行している場合には光は偏光板により遮断される。しかし、偏光板によって偏光された光が着色組成物の塗膜を通過する際に、着色剤粒子によって散乱等が起こり、偏光面の一部にずれが生じると、偏光板が平行のときは透過する光量が減り、偏光板が直行のときは一部光が透過する。この透過光を偏光板上の輝度として測定し、偏光板が平行の際の輝度と、直行の際の輝度との比を、コントラスト比として算出した。
(コントラスト比)=(平行のときの輝度)/(直行のときの輝度)
従って、塗膜中の着色剤により散乱が起こると、平行のときの輝度が低下し、かつ直行のときの輝度が増加するため、コントラスト比が低くなる。
なお、輝度計としては色彩輝度計(トプコン社製「BM−5A」)、偏光板としては偏光板(日東電工社製「NPF−G1220DUN」)を用いた。測定に際しては、測定部分に1cm角の孔を開けた黒色マスクを介して測定した。明度評価をしたものと同じ塗膜を用いて、4種の膜厚の異なる塗布基盤の色相x値とコントラスト比の関係から、色相x=0.440のときのコントラスト比を算出し、下記基準に従って判定した。
○:3000以上
△:2000以上〜3000未満
×:2000未満
○:3000以上
△:2000以上〜3000未満
×:2000未満
(耐熱性試験)
明度、コントラスト比を評価した塗膜基板を、さらに250℃で1時間再加熱した。上記と同様の方法でコントラスト比を測定し、250℃で加熱する前のコントラスト比に対する比を下記基準に従って判定した。
○:0.9倍以上1倍以下
△:0.75倍以上0.9倍未満
×:0.75倍未満
明度、コントラスト比を評価した塗膜基板を、さらに250℃で1時間再加熱した。上記と同様の方法でコントラスト比を測定し、250℃で加熱する前のコントラスト比に対する比を下記基準に従って判定した。
○:0.9倍以上1倍以下
△:0.75倍以上0.9倍未満
×:0.75倍未満
実施例および比較例で作成した黄色着色組成物について、黄色着色組成物中で使用した黄色着色剤の種類と併せて、評価結果を表2に示す。
表2より、一般式(1)で表されるキノフタロン化合物を着色剤として使用した実施例7〜12の黄色着色組成物は、明度、コントラスト比が高く、耐熱性に優れていることが明らかになった。一方、比較例4、5の黄色着色組成物は、0.06μmを超える粒径の大きい粒子を多く含み、明度、コントラスト比が低い。また、比較例6の黄色着色組成物は、0.02μm以下の粒子を多く含み、コントラスト比は優れるものの、耐熱性に劣ることがわかる。
<緑色着色組成物の作製>
(緑色着色組成物1(GP−1)の作製)
下記の成分からなる混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5μmのフィルタで濾過し緑色着色組成物1(GP−1)を作製した。
緑色顔料(C.I.ピグメントグリーン58) 10.0部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 45.0部
プロピレングリコールモノメチルエーテルアセテート 44.0部
(緑色着色組成物1(GP−1)の作製)
下記の成分からなる混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5μmのフィルタで濾過し緑色着色組成物1(GP−1)を作製した。
緑色顔料(C.I.ピグメントグリーン58) 10.0部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 45.0部
プロピレングリコールモノメチルエーテルアセテート 44.0部
(緑色着色組成物(GP−2)の作製)
下記の混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5μmのフィルタで濾過し緑色着色組成物2(GP−2)を作製した。
緑色顔料(C.I.ピグメントグリーン36) 10.0部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 45.0部
プロピレングリコールモノメチルエーテルアセテート 44.0部
下記の混合物を均一になるように攪拌混合した後、直径0.5mmのジルコニアビーズを用いて、アイガーミル(アイガージャパン社製「ミニモデルM−250 MKII」)で5時間分散した後、5μmのフィルタで濾過し緑色着色組成物2(GP−2)を作製した。
緑色顔料(C.I.ピグメントグリーン36) 10.0部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 45.0部
プロピレングリコールモノメチルエーテルアセテート 44.0部
<感光性着色組成物の作製>
[実施例13]
(感光性着色組成物1(GR−1)の作製)
下記組成の混合物を均一になるように攪拌混合した後、1μmのフィルタで濾過し、感光性着色組成物1(GR−1)を作製した。
黄色着色組成物1(YP−1) 22.5部
緑色着色組成物1(GP−1) 22.5部
アクリル樹脂溶液2 4.5部
光重合性単量体(東亞合成社製「アロニックスM402」) 3.6部
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) 1.3部
増感剤(保土谷化学工業社製「EAB−F」) 0.2部
エチレングリコールモノメチルエーテルアセテート 45.4部
[実施例13]
(感光性着色組成物1(GR−1)の作製)
下記組成の混合物を均一になるように攪拌混合した後、1μmのフィルタで濾過し、感光性着色組成物1(GR−1)を作製した。
黄色着色組成物1(YP−1) 22.5部
緑色着色組成物1(GP−1) 22.5部
アクリル樹脂溶液2 4.5部
光重合性単量体(東亞合成社製「アロニックスM402」) 3.6部
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) 1.3部
増感剤(保土谷化学工業社製「EAB−F」) 0.2部
エチレングリコールモノメチルエーテルアセテート 45.4部
[実施例14〜20、比較例7〜9]
(感光性着色組成物2〜11(GR−2〜11)の作製)
表3に示した黄色着色組成物と緑色着色組成物を使用し、かつ、塗膜評価の際にC光源でx=0.290、y=0.600の色度に合うように黄色着色組成物と緑色着色組成物の比率を変更(着色組成物の全量が45部となるように比率を変更)する以外は、感光性着色組成物1(GR−1)と同様に、感光性着色組成物2〜11(GR−2〜11)を作製した。
(感光性着色組成物2〜11(GR−2〜11)の作製)
表3に示した黄色着色組成物と緑色着色組成物を使用し、かつ、塗膜評価の際にC光源でx=0.290、y=0.600の色度に合うように黄色着色組成物と緑色着色組成物の比率を変更(着色組成物の全量が45部となるように比率を変更)する以外は、感光性着色組成物1(GR−1)と同様に、感光性着色組成物2〜11(GR−2〜11)を作製した。
<感光性着色組成物の塗膜評価>
得られた感光性着色組成物1〜11(GR−1〜11)を用いて作製した塗膜の、明度およびコントラスト比、耐熱性の評価を下記方法で行った。
得られた感光性着色組成物1〜11(GR−1〜11)を用いて作製した塗膜の、明度およびコントラスト比、耐熱性の評価を下記方法で行った。
(明度評価)
感光性着色組成物を、100mm×100mm、1.1mm厚のガラス基板上に、スピンコーターを用いて、4種類の着色膜の膜厚が異なる塗布基板を得た。次に70℃で20分乾燥し、超高圧水銀ランプを用いて、300mJ/cm2で紫外線露光を行い、23℃のアルカリ現像液で現像を行った。アルカリ現像液としては、炭酸ナトリウム1.5重量%、炭酸水素ナトリウム0.5重量%、陰イオン系界面活性剤(花王社製「ペリレックスNBL」)8.0重量%、および水90重量%からなるものを用いた。さらに、230℃で30分加熱することで塗膜を得た。顕微分光光度計(オリンパス光学社製「OSP−SP100」)を用い、得られた塗膜の明度(Y)を測定し、下記基準に従って評価判定した。尚、作製した塗膜は、230℃での熱処理後で、表3に示した色度(C光源)となるようにした。
○:59.5以上
△:58.0以上〜59.5未満
×:58.0未満
感光性着色組成物を、100mm×100mm、1.1mm厚のガラス基板上に、スピンコーターを用いて、4種類の着色膜の膜厚が異なる塗布基板を得た。次に70℃で20分乾燥し、超高圧水銀ランプを用いて、300mJ/cm2で紫外線露光を行い、23℃のアルカリ現像液で現像を行った。アルカリ現像液としては、炭酸ナトリウム1.5重量%、炭酸水素ナトリウム0.5重量%、陰イオン系界面活性剤(花王社製「ペリレックスNBL」)8.0重量%、および水90重量%からなるものを用いた。さらに、230℃で30分加熱することで塗膜を得た。顕微分光光度計(オリンパス光学社製「OSP−SP100」)を用い、得られた塗膜の明度(Y)を測定し、下記基準に従って評価判定した。尚、作製した塗膜は、230℃での熱処理後で、表3に示した色度(C光源)となるようにした。
○:59.5以上
△:58.0以上〜59.5未満
×:58.0未満
(コントラスト比評価)
塗膜のコントラスト比の測定法については、実施例13〜20、および比較例7〜9の黄色着色組成物のコントラスト比測定と同様の方法で測定した。明度評価をしたものと同じ塗膜を用いて、4種の膜厚の異なる塗布基盤の色相x値とコントラスト比の関係から、色相x=0.59のときのコントラストを算出し、下記基準に従って判定した。
○:3500以上
△:3000以上〜3500未満
×:3000未満
塗膜のコントラスト比の測定法については、実施例13〜20、および比較例7〜9の黄色着色組成物のコントラスト比測定と同様の方法で測定した。明度評価をしたものと同じ塗膜を用いて、4種の膜厚の異なる塗布基盤の色相x値とコントラスト比の関係から、色相x=0.59のときのコントラストを算出し、下記基準に従って判定した。
○:3500以上
△:3000以上〜3500未満
×:3000未満
(耐熱性試験)
明度、コントラスト比を評価した塗膜基板を、さらに250℃で1時間再加熱した。上記と同様の方法でコントラスト比を測定し、250℃で加熱する前の値に対する比を求め、下記基準に従って判定した。
○:0.9倍以上1倍以下
△:0.75倍以上0.9倍未満
×:0.75倍未満
明度、コントラスト比を評価した塗膜基板を、さらに250℃で1時間再加熱した。上記と同様の方法でコントラスト比を測定し、250℃で加熱する前の値に対する比を求め、下記基準に従って判定した。
○:0.9倍以上1倍以下
△:0.75倍以上0.9倍未満
×:0.75倍未満
実施例および比較例で作成した感光性着色組成物の評価結果を表3に示す。
表3の結果より、カラーフィルタ形成において、本発明の着色剤および着色組成物を使用した実施例は、比較例よりも、高い明度とコントラストを有し、耐熱性が優れていることがわかった。
<カラーフィルタの作製>
カラーフィルタの作製に使用する赤色感光性着色組成物と青色感光性着色組成物の作製を行った。尚、緑色については本発明の感光性着色組成物1(GR−1)を使用した。
カラーフィルタの作製に使用する赤色感光性着色組成物と青色感光性着色組成物の作製を行った。尚、緑色については本発明の感光性着色組成物1(GR−1)を使用した。
(赤色着色組成物1(RP−1)の作製)
下記に示す配合組成の混合物を均一に撹拌混合し、直径0.1mmのジルコニアビーズを用いて、ピコミルで8時間分散した後、5μmのフィルタで濾過し、赤色着色組成物1(RP−1)を作製した。
赤色顔料1(C.I.ピグメントレッド254) 8.5部
赤色顔料2(C.I.ピグメントレッド177) 3.5部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 35.0部
プロピレングリコールモノメチルエーテルアセテート 52.0部
下記に示す配合組成の混合物を均一に撹拌混合し、直径0.1mmのジルコニアビーズを用いて、ピコミルで8時間分散した後、5μmのフィルタで濾過し、赤色着色組成物1(RP−1)を作製した。
赤色顔料1(C.I.ピグメントレッド254) 8.5部
赤色顔料2(C.I.ピグメントレッド177) 3.5部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 35.0部
プロピレングリコールモノメチルエーテルアセテート 52.0部
(赤色感光性着色組成物1(RR−1)の調製)
下記組成の混合物を均一になるように攪拌混合した後、1μmのフィルタで濾過し、赤色感光性着色組成物1(RR−1)を作製した。
赤色着色組成物1(RP−1) 42.0部
アクリル樹脂溶液2 13.2部
光重合性単量体(東亞合成社製「アロニックスM400」) 2.8部
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) 2.0部
増感剤(保土谷化学工業社製「EAB−F」) 0.4部
エチレングリコールモノメチルエーテルアセテート 39.6部
下記組成の混合物を均一になるように攪拌混合した後、1μmのフィルタで濾過し、赤色感光性着色組成物1(RR−1)を作製した。
赤色着色組成物1(RP−1) 42.0部
アクリル樹脂溶液2 13.2部
光重合性単量体(東亞合成社製「アロニックスM400」) 2.8部
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) 2.0部
増感剤(保土谷化学工業社製「EAB−F」) 0.4部
エチレングリコールモノメチルエーテルアセテート 39.6部
(青色着色組成物1(BP−1)の調製)
下記に示す配合組成の混合物を均一に撹拌混合し、直径0.1mmのジルコニアビーズを用いて、ピコミルで8時間分散した後、5μmのフィルタで濾過し、青色着色組成物1(BP−1)を作製した。
青色顔料(C.I.ピグメントブルー15:6) 7.2部
紫色顔料(C.I.ピグメントバイオレット23) 4.8部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 35.0部
プロピレングリコールモノメチルエーテルアセテート 52.0部
下記に示す配合組成の混合物を均一に撹拌混合し、直径0.1mmのジルコニアビーズを用いて、ピコミルで8時間分散した後、5μmのフィルタで濾過し、青色着色組成物1(BP−1)を作製した。
青色顔料(C.I.ピグメントブルー15:6) 7.2部
紫色顔料(C.I.ピグメントバイオレット23) 4.8部
樹脂型分散剤(チバ・ジャパン社製「EFKA4300」) 1.0部
アクリル樹脂溶液1 35.0部
プロピレングリコールモノメチルエーテルアセテート 52.0部
(青色感光性着色組成物1(BR−1)の調製)
下記組成の混合物を均一になるように攪拌混合した後、1μmのフィルタで濾過し、青色感光性着色組成物1(BR−1)を作製した。
青色着色組成物1(BP−1) 34.0部
アクリル樹脂溶液2 15.2部
光重合性単量体(東亞合成社製「アロニックスM400」) 3.3部
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) 2.0部
増感剤(保土谷化学工業社製「EAB−F」) 0.4部
エチレングリコールモノメチルエーテルアセテート 45.1部
下記組成の混合物を均一になるように攪拌混合した後、1μmのフィルタで濾過し、青色感光性着色組成物1(BR−1)を作製した。
青色着色組成物1(BP−1) 34.0部
アクリル樹脂溶液2 15.2部
光重合性単量体(東亞合成社製「アロニックスM400」) 3.3部
光重合開始剤(チバ・ジャパン社製「イルガキュアー907」) 2.0部
増感剤(保土谷化学工業社製「EAB−F」) 0.4部
エチレングリコールモノメチルエーテルアセテート 45.1部
ガラス基板上にブラックマトリクスをパターン加工し、該基板上にスピンコーターで赤色感光性着色組成物1(RR−1)をx=0.640、y=0.330になるような膜厚に塗布し着色被膜を形成した。該被膜にフォトマスクを介して、超高圧水銀ランプを用いて300mJ/cm2の紫外線を照射した。次いで0.2重量%の炭酸ナトリウム水溶液からなるアルカリ現像液によりスプレー現像して未露光部分を取り除いた後、イオン交換水で洗浄し、この基板を230℃で20分加熱して、赤色フィルタセグメントを形成した。同様の方法により、本発明の緑色の感光性着色組成物1(GR−1)をx=0.290、y=0.600になるような膜厚に、青色感光性着色組成物1(BR―1)を用いてx=0.150、y=0.060になるような膜厚にそれぞれ塗布し、緑色フィルタセグメント、青色フィルタセグメントを形成して、カラーフィルタを得た。
本発明の感光性着色組成物1(GR−1)を用いることにより、高明度、高コントラスト比であり、耐熱性に優れたカラーフィルタを作製することが可能であった。
Claims (6)
- 下記一般式(1)で表されるキノフタロン化合物を含有するカラーフィルタ用黄色着色剤であって、着色剤の一次粒子サイズについて、5nm未満の粒子の割合が10%未満、及び50nmを超える粒子の割合が5%未満であることを特徴とするカラーフィルタ用黄色着色剤。
R1〜R4、R5〜R9、R10〜R13の隣接した基は、一体となって、環を形成しても良い。] - キノフタロン化合物が、C.I.ピグメントイエロー138である請求項1記載のカラーフィルタ用黄色着色剤。
- 少なくとも着色剤、バインダー樹脂、および有機溶剤からなるカラーフィルタ用着色組成物であって、着色剤が、請求項1または2記載の着色剤であることを特徴とするカラーフィルタ用着色組成物。
- さらに緑色着色剤を含有することを特徴とする請求項3記載のカラーフィルタ用着色組成物。
- さらに光重合性単量体および/または光重合開始剤を含有することを特徴とする請求項3または4記載のカラーフィルタ用着色組成物。
- 少なくとも1つの赤色フィルタセグメント、少なくとも1つの緑色フィルタセグメントおよび少なくとも1つの青色フィルタセグメントを備えるカラーフィルタにおいて、少なくとも1つの緑色フィルタセグメントが、請求項3〜5記載のカラーフィルタ用着色組成物により形成されてなるカラーフィルタ。