JP2013119610A - ポリアミド樹脂組成物及び成形品 - Google Patents
ポリアミド樹脂組成物及び成形品 Download PDFInfo
- Publication number
- JP2013119610A JP2013119610A JP2011268968A JP2011268968A JP2013119610A JP 2013119610 A JP2013119610 A JP 2013119610A JP 2011268968 A JP2011268968 A JP 2011268968A JP 2011268968 A JP2011268968 A JP 2011268968A JP 2013119610 A JP2013119610 A JP 2013119610A
- Authority
- JP
- Japan
- Prior art keywords
- polyamide
- acid
- resin composition
- polyamide resin
- isophthalic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明のポリアミド樹脂組成物は、(A):(a)アジピン酸とヘキサメチレンジアミンとからなる単位と、(b)イソフタル酸とヘキサメチレンジアミンとからなる単位と、を、含むポリアミドであって、当該ポリアミド中における全カルボン酸成分中のイソフタル酸成分比率(x)が、0.05≦(x)≦0.5であり、特定の式(1)で示される(Y)が、−0.3≦(Y)≦0.8である(A)ポリアミドと、(B):ハロゲン系難燃剤とを含有する。
【選択図】図1
Description
また、ポリアミド樹脂は自動車分野で広く採用されているが、このような用途では、使用環境が熱的、力学的に厳しく、特にドアミラー等に代表される自動車外装部品では衝撃特性と、表面外観性との両方を要求される場合が多く、更には難燃性にも優れるポリアミド樹脂材料が要求されているのが現状である。
よって、特に、上述したようなハイサイクル成形時の成形品表面外観の安定性、更には耐衝撃特性を向上させた、過酷な成形条件下においても物性変化が少ないポリアミド樹脂が要求されている。
また、耐衝撃性を改良することができる材料として、テレフタル酸成分と、イソフタル酸成分とを導入したポリアミド6T/6Iからなるポリアミド開示されている(例えば、特許文献5参照。)。
また、ポリアミドの特徴である、機械特性のバランスを保持しつつ、成形品表面外観の安定性を維持することが困難であり、このようなポリアミドが要望されている。
すなわち、本発明は、以下の通りである。
(A):(a)アジピン酸とヘキサメチレンジアミンとからなる単位と、
(b)イソフタル酸とヘキサメチレンジアミンとからなる単位と、
を、含むポリアミドであって、
当該ポリアミド中における全カルボン酸成分中のイソフタル酸成分比率(x)が、0.05≦(x)≦0.5であり、
かつ、下記式(1)で示される(Y)が、−0.3≦(Y)≦0.8である(A)ポリアミドと、
(Y)=[(EG)−(x)]/[1−(x)] ・・・(1)
(前記式(1)中、(EG)は、(A)ポリアミド中に含有されている全カルボキシル末端基中のイソフタル酸末端基比率を示し、下記式(2)で示される。
(EG)=イソフタル酸末端基量/全カルボキシル末端基量 ・・・(2))
(B):ハロゲン系難燃剤と、を、含有するポリアミド樹脂組成物。
〔2〕
前記式(1)で示される(Y)の範囲が0.05≦(Y)≦0.8である、前記〔1〕に記載のポリアミド樹脂組成物。
〔3〕
前記(B)ハロゲン系難燃剤が臭素化ポリスチレンである、前記〔1〕又は〔2〕に記載のポリアミド樹脂組成物。
〔4〕
(C)難燃助剤と、
(D)α,β不飽和ジカルボン酸無水物を含む重合体と、
(E)無機充填材と、をさらに含有し、
前記(A)ポリアミド100質量部に対して、
前記(B)ハロゲン系難燃剤の含有量が30〜60質量部であり、
前記(C)難燃助剤の含有量が0.1〜30質量部であり、
前記(D)α,β不飽和ジカルボン酸無水物を含む重合体の含有量が0.1〜20質量部であり、
前記(E)無機充填材の含有量が1〜200質量部である、前記〔1〕乃至〔3〕のいずれか一に記載のポリアミド樹脂組成物。
〔5〕
前記(C)難燃助剤が、酸化アンチモン類及び/又は水酸化マグネシウムである、前記〔4〕に記載のポリアミド樹脂組成物。
〔6〕
前記〔1〕乃至〔5〕のいずれか一項に記載のポリアミド樹脂組成物を含む成形品。
なお、本発明は、以下の実施形態に制限されるものではなく、その要旨の範囲内で種々変形して実施することができる。
本実施形態のポリアミド樹脂組成物は、
(A):(a)アジピン酸とヘキサメチレンジアミンとからなる単位と、
(b)イソフタル酸とヘキサメチレンジアミンとからなる単位と、
を、含むポリアミドであって、
当該ポリアミド中における全カルボン酸成分中のイソフタル酸成分比率(x)が、0.05≦(x)≦0.5であり、
かつ、下記式(1)で示される(Y)が、−0.3≦(Y)≦0.8である(A)ポリアミドと、
(Y)=[(EG)−(x)]/[1−(x)] ・・・(1)
(前記式(1)中、(EG)は、(A)ポリアミド中に含有されている全カルボキシル末端基中のイソフタル酸末端基比率を示し、下記式(2)で示される。
(EG)=イソフタル酸末端基量/全カルボキシル末端基量 ・・・(2))
(B):ハロゲン系難燃剤と、を、含有するポリアミド樹脂組成物である。
以下、本実施形態のポリアミド樹脂組成物の構成成分について説明する。
本実施形態のポリアミド樹脂組成物を構成するポリアミド(以下、(A)ポリアミド、ポリアミド(A)、又は単にポリアミドと記載する場合もある。)は、
(a)アジピン酸とヘキサメチレンジアミンとからなる単位と、
(b)イソフタル酸とヘキサメチレンジアミンとからなる単位と、
を、含む。
当該(A)ポリアミド中における全カルボン酸成分中のイソフタル酸成分比率(x)は、0.05≦(x)≦0.5であり、好ましくは0.05≦(x)≦0.4であり、さらに好ましくは0.05≦(x)≦0.3である。
ここで、(A)ポリアミド中における全カルボン酸成分中のイソフタル酸成分比率(x)とは、ポリアミド中に含まれる(b)イソフタル酸とヘキサメチレンジアミンとからなる単位の比率を示している。
前記イソフタル酸成分比率(x)が0.05以上であると、ポリアミドの融点、固化温度が抑制され、本実施形態のポリアミド樹脂組成物の成形体表面外観性が安定的なものとなる。また、イソフタル酸成分比率(x)が0.5以下であるとポリアミドの結晶性の低下を抑制でき、本実施形態のポリアミド樹脂組成物の成形体において十分な機械的強度が得られる。
(Y)=[(EG)−(x)]/[1−(x)] ・・・(1)
式(1)中、(x)は、上述したように、(A)ポリアミド中における全カルボン酸成分中のイソフタル酸成分比率であり、ポリアミド中における(b)イソフタル酸とヘキサメチレンジアミンとからなる単位の比率を示す。
(EG)は、全カルボキシル末端基中のイソフタル酸末端基比率を示し、下記式(2)で示される。
(EG)=イソフタル酸末端基量/全カルボキシル末端基量 ・・・(2)
後述の実施例及び比較例に基づくポリアミドの、前記ブロック化比率(Y)とポリアミド中における全カルボン酸成分中のイソフタル酸成分比率(x)との関係を表した図を図1に示す。
図1の説明を下記に示す。
横軸:全カルボン酸中のイソフタル酸成分比率(x)
縦軸:全カルボキシル末端基中のイソフタル酸末端基比率(EG)
実線の四角形で囲まれた領域:二つの四角全体により囲まれた領域が0.05≦(x)≦0.5であり、かつ−0.3≦(Y)≦0.8である領域。図1中上側の四角形のみに囲まれた領域が0.05≦(x)≦0.5であり、かつ0.05≦(Y)≦0.8である領域。
一点鎖線:(EG)=(x)
破線量矢印:[(EG)−(x)]と[1−(x)]の関係を示す。
◇:後述する実施例に用いたポリアミド
■:後述する比較例に用いたポリアミド
イソフタル酸成分比率(x)を上記範囲内とし、かつ前記(Y)の範囲を−0.3≦(Y)≦0.8とすることにより、本実施形態のポリアミド樹脂組成物は、過酷な成形条件下における成形体表面外観の安定性、耐衝撃特性が優れ、成形条件変更による離型性低下が少ないものとなる。
ポリアミド中のイソフタル酸成分比率(x)、イソフタル酸末端基量、及び全カルボキシル末端基量の定量方法は、特に制限されないが、核磁気共鳴法(NMR)により求めることができる。具体的には1H−NMRにより求めることができる。
本実施形態のポリアミド樹脂組成物を構成する(A)ポリアミドには、本実施形態の目的を損なわない範囲で、アジピン酸、イソフタル酸以外の、脂肪族ジカルボン酸、脂環族ジカルボン酸、芳香族ジカルボン酸、及びヘキサメチレンジアミン以外の主鎖から分岐した置換基を持つジアミン、脂肪族ジアミン、芳香族ジアミン、重縮合可能なアミノ酸、ラクタム等を共重合成分として用いることができる。
脂環族ジカルボン酸は、無置換でも置換基を有していてもよい。
種々の置換基としては、例えば、炭素数1〜6のアルキル基、炭素数6〜12のアリール基、炭素数7〜20のアリールアルキル基、クロロ基及びブロモ基等のハロゲン基、炭素数3〜10のアルキルシリル基、並びにスルホン酸基及びナトリウム塩等のその塩である基等が挙げられる。
本実施形態のポリアミド樹脂組成物を構成するポリアミド及びその他の共重合成分を重合させたポリアミド共重合体の原料として、分子量調節や耐熱水性向上のために、末端封止剤を更に添加することができる。
例えば、本実施形態に用いるポリアミド、又は上述したポリアミド共重合体を重合する際に、公知の末端封止剤を更に添加することにより、重合量を制御することができる。
それらの中でもモノカルボン酸及びモノアミンが好ましい。
これらの末端封止剤は、1種類を単独で用いてもよいし、2種類以上を組み合わせて用いてもよい。
これらのモノカルボン酸は、1種類を単独で用いてもよいし、2種類以上を組み合わせて用いてもよい。
これらのモノアミンは、1種類を単独で用いてもよいし、2種類以上を組み合わせて用いてもよい。
本実施形態のポリアミド樹脂組成物を構成する(A)ポリアミドの製造方法としては、上述したようにその他の共重合成分を有するポリアミド共重合体である場合を含めて、前記全カルボン酸成分中のイソフタル酸成分比率(x)が0.05≦(x)≦0.5であり、上記式(1)におけるブロック化比率の指標である(Y)の範囲が−0.3≦(Y)≦0.8、好ましくは0.05≦(Y)≦0.8となるようなポリアミド(又はポリアミド共重合体)が得られればよい。
ポリアミドの製造方法としては、例えば、アジピン酸、イソフタル酸、ヘキサメチレンジアミン、及び必要に応じてその他の成分の混合物の水溶液、又は水の懸濁液を加熱し、溶融状態を維持したまま重合させる方法(熱溶融重合法);熱溶融重合法で得られたポリアミドを融点以下の温度で固体状態を維持したまま重合度を上昇させる方法(熱溶融重合・固相重合法);アジピン酸、イソフタル酸、ヘキサメチレンジアミン、及び必要に応じてその他の成分の混合物の水溶液、又は水の懸濁液を加熱し、析出したプレポリマーをさらにニーダー等の押出機で再び溶融させて重合度を上昇させる方法(プレポリマー・押出重合法);アジピン酸、イソフタル酸、ヘキサメチレンジアミン、及び必要に応じてその他の成分の混合物、固体塩又は重縮合物を、固体状態を維持したまま重合(固相重合法)させる方法等が挙げられる。
全カルボン酸成分中のイソフタル酸成分比率(x)を上記数値範囲内に制御するための方法としては、原料の仕込み量の調整、重合条件の調整が有効である。
上記式(1)におけるブロック化比率の指標となる(Y)を上記数値範囲内に制御するためには、イソフタル酸成分のブロック化を制御することが必要である。具体的には、重合系内で、溶融状態を維持しながら、圧力を適宜調整し、重合温度を好ましくは100℃以上、より好ましくは120℃以上、さらに好ましくは170℃以上としながら、均一混合下において重縮合反応を進め、最終重合内部温度が好ましくは250℃以上、より好ましくは260℃以上になるような条件下で重合させる熱溶融重合法を用いることにより制御することができる。
また、重合装置も特に限定されず、公知の装置、例えば、オートクレーブ型の反応器、タンブラー型反応器、ニーダー等の押出機型反応器等を用いることができる。
バッチ式の熱溶融重合法の一例について以下に説明する。
重合温度条件については特に限定されないが、好ましくは100℃以上、より好ましくは120℃以上、さらに好ましくは170℃以上である。
例えば、アジピン酸、イソフタル酸、及びヘキサメチレンジアミンとの混合物、固体塩又は水溶液を110〜200℃の温度下で攪拌し、約60〜90%まで水蒸気を徐々に抜いて加熱濃縮する。
その後、内部圧力を約1.5〜5.0MPa(ゲージ圧)になるまで加熱を続ける。
その後、水及び/又はガス成分を除きながら、圧力を約1.5〜5.0MPa(ゲージ圧)に保ち、内部温度が好ましくは240℃以上、より好ましくは245℃以上に達した時点で、水及び/又はガス成分を除きながら圧力を徐々に抜き、最終内部温度が好ましくは250℃以上、より好ましくは260℃以上になるように、常圧で又は減圧して重縮合を行う熱溶融重合法を用いることができる。
さらには、アジピン酸、イソフタル酸、及びヘキサメチレンジアミンとの混合物、固体塩又は重縮合物を融点以下の温度で熱重縮合させる固相重合法等も用いることができる。これらの方法は必要に応じて組み合わせてもよい。
押出温度は、JIS−K7121に準じた示差走査熱量(DSC)測定で求まる融点よりも1〜100℃程度高い温度が好ましい。
剪断速度は、100(sec-1)以上程度であることが好ましく、平均滞留時間は0.1〜15分程度が好ましい。
上記押出条件とすることにより、着色や高分子量化できない等の問題の発生を効果的に抑制できる。
触媒としては、ポリアミドに用いられる公知のものであれば特に限定されず、例えば、リン酸、亜リン酸、次亜リン酸、オルト亜リン酸、ピロ亜リン酸、フェニルホスフィン酸、フェニルホスホン酸、2−メトキシフェニルホスホン酸、2−(2’−ピリジル)エチルホスホン酸、及びそれらの金属塩等が挙げられる。
金属塩の金属としては、カリウム、ナトリウム、マグネシウム、バナジウム、カルシウム、亜鉛、コバルト、マンガン、錫、タングステン、ゲルマニウム、チタン、アンチモンなどの金属塩やアンモニウム塩等が挙げられる。
また、エチルエステル、イソプロピルエステル、ブチルエステル、ヘキシルエステル、デシルエステル、イソデシルエステル、オクタデシルエステル、ステアリルエステル、フェニルエステル等のリン酸エステル類も用いることができる。
本実施形態のポリアミド樹脂組成物を構成する(A)ポリアミドは、蟻酸溶液粘度(JIS K 6816)が、好ましくは10〜30である。
蟻酸溶液粘度が10以上であると、実用上十分な機械的特性を有する成形体が得られ、蟻酸溶液粘度が30以下であると、成形時の流動性が良好なものとなり、表面外観性に優れた成形体が得られる。
本実施形態において用いられる(B)ハロゲン系難燃剤としては、ハロゲン元素を含む難燃剤であれば、特に限定されるものではなく、例えば、塩素系難燃剤や臭素系難燃剤などが挙げられる。
これら(B)ハロゲン系難燃剤を1種類で用いてもよいし、2種類以上を組み合わせて用いてもよい。
臭素化ポリスチレン中の臭素含有量は55〜75質量%が好ましい。臭素含有量を55質量%以上とすることにより、少ない臭素化ポリスチレンの配合量で難燃化に必要な臭素量を満足させることができ、ポリアミド共重合体の有する性質を損なうことなく、耐熱性、流動性、靭性、低吸水性、及び剛性に優れ、かつ難燃性に優れるポリアミド樹脂組成物を得ることができる。また、臭素含有量を75質量%以下とすることにより、押出や成形などの溶融加工時において熱分解を起こし難く、ガス発生などを抑制することができたり、耐熱変色性に優れるポリアミド樹脂組成物を得ることができる。
本実施形態のポリアミド樹脂組成物は、(C)難燃助剤をさらに含有することにより、難燃性にさらに優れるポリアミド樹脂組成物とすることができる。
本実施形態において用いられる(C)難燃助剤としては、特に限定されるものではなく、例えば、三酸化二アンチモン、四酸化二アンチモン、五酸化二アンチモン、アンチモン酸ナトリウムなどの酸化アンチモン類;一酸化スズ、二酸化スズなどの酸化スズ類;酸化第二鉄、γ酸化鉄などの酸化鉄類;その他酸化亜鉛、ホウ酸亜鉛、酸化カルシウム、酸化アルミニウム(アルミナ)、酸化アルミニウム(ベーマイト)、酸化ケイ素(シリカ)、酸化チタン、酸化ジルコニウム、酸化マンガン、酸化モリブデン、酸化コバルト、酸化ビスマス、酸化クロム、酸化ニッケル、酸化銅、及び酸化タングステンなどの金属酸化物;水酸化マグネシウム、及び水酸化アルミニウムなどの金属水酸化物;アルミニウム、鉄、チタン、マンガン、亜鉛、モリブデン、コバルト、ビスマス、クロム、スズ、アンチモン、ニッケル、銅、及びタングステンなどの金属粉末;炭酸亜鉛、炭酸カルシウム、炭酸マグネシウム、及び炭酸バリウムなどの金属炭酸塩;ホウ酸マグネシウム、ホウ酸カルシウム、及びホウ酸アルミニウムなどの金属ホウ酸塩;並びにシリコーン;などが挙げられる。
これら(C)難燃助剤を1種類で用いてもよいし、2種類以上を組み合わせて用いてもよい。
平均粒径は、レーザー回折散乱法粒度分布測定装置や精密粒度分布測定装置を用いて測定することができる。
本実施形態のポリアミド樹脂組成物は、(D)α,β不飽和ジカルボン酸無水物を含む重合体をさらに含有することにより、難燃性並びに、靭性及び剛性などの機械物性にさらに優れるポリアミド樹脂組成物とすることができる。
本実施形態において用いられる(D)α,β不飽和ジカルボン酸無水物を含む重合体としては、例えば、α,β不飽和ジカルボン酸無水物を共重合成分として含む重合体やα,β不飽和ジカルボン酸無水物で変性された重合体などが挙げられる。
一般式(1):
α,β不飽和ジカルボン酸無水物で変性された重合体としては、例えば、α,β不飽和ジカルボン酸無水物で変性されたポリフェニレンエーテル樹脂やポリプロピレン樹脂などが挙げられる。
一般式(2):
本実施形態において、(D)α,β不飽和ジカルボン酸無水物を含む重合体が、芳香族ビニル化合物成分を含む場合には、芳香族ビニル化合物成分が(B)ハロゲン系難燃剤(臭素化ポリスチレンなど)と親和し、また、α,β不飽和ジカルボン酸無水物部分が(A)ポリアミドと親和ないし反応することにより、ポリアミドマトリックス中に(B)ハロゲン系難燃剤が分散するのを助け、ハロゲン系難燃剤を微分散させることができると考えられる。
α,β不飽和ジカルボン酸無水物成分の割合を1質量%以上とすることにより、靭性及び剛性などの機械物性及び難燃性に優れるポリアミド樹脂組成物を得ることができる。また、α,β不飽和ジカルボン酸無水物成分の割合を50質量%以下とすることにより、α,β不飽和ジカルボン酸無水物によるポリアミド樹脂組成物の劣化を防止することができる。
本実施形態のポリアミド樹脂組成物は、(E)無機充填材をさらに含有することにより、靭性及び剛性などの機械物性にさらに優れるポリアミド樹脂組成物とすることができる。
(E)無機充填材としては、1種類で用いてもよいし、2種類以上を組み合わせて用いてもよい。
また、(E)無機充填材としては、ウォラストナイトがより好ましく、ウォラストナイトの中でも、数平均繊維径が3〜30μmであり、重量平均繊維長が10〜500μmであり、前記アスペクト比(L/D)が3〜100であるものがさらに好ましく用いられる。さらに、(E)無機充填材としては、タルク、マイカ、カオリン、及び窒化珪素などがより好ましく、タルク、マイカ、カオリン、及び窒化珪素などの中でも、数平均繊維径が0.1〜3μmであるものがさらに好ましく用いられる。
(B)ハロゲン系難燃剤の含有量、また、任意成分である、(C)難燃助剤、(D)α,β不飽和ジカルボン酸無水物を含む重合体、及び(E)無機充填材の含有量は、特に限定されるものではない。
(B)ハロゲン系難燃剤の含有量を30質量部以上とすることにより、難燃性に優れるポリアミド樹脂組成物を得ることができる。また、(B)ハロゲン系難燃剤の含有量を60質量部以下とすることにより、溶融混練時に分解ガスの発生、成形加工時の流動性の低下や、成形金型に汚染性物質の付着を抑制することができる。さらに、靭性及び剛性などの機械物性や成形品外観の低下も抑制することができる。
(E)無機充填材を前記範囲で含有することにより、ポリアミド樹脂組成物の靭性及び剛性などの機械物性が良好に向上し、また、無機充填材の含有量を200質量部以下とすることにより、成形性に優れるポリアミド樹脂組成物を得ることができる。
本実施形態のポリアミド樹脂組成物には、必要に応じて、本実施形態の目的を損なわない範囲で、成形性改良剤を添加してもよい。
成形性改良剤としては、特に限定されないが、高級脂肪酸、高級脂肪酸金属塩、高級脂肪酸エステル、及び高級脂肪酸アミド等が挙げられる。
これらの中でも、ステアリン酸及びモンタン酸が好ましい。
金属塩の金属元素としては、元素周期律表の第1,2,3族元素、亜鉛、及びアルミニウム等が好ましく、カルシウム、ナトリウム、カリウム、及びマグネシウム等の、第1,2族元素、並びにアルミニウム等がより好ましい。
高級脂肪酸金属塩としては、例えば、ステアリン酸カルシウム、ステアリン酸アルミニウム、ステアリン酸亜鉛、ステアリン酸マグネシウム、モンタン酸カルシウム、及びモンタン酸ナトリウム、パルミチン酸カルシウム等が挙げられる。
これらの中でも、モンタン酸の金属塩及びステアリン酸の金属塩が好ましい。
炭素数8〜40の脂肪族カルボン酸と炭素数8〜40の脂肪族アルコールとのエステルが好ましい。
脂肪族アルコールとしては、例えば、ステアリルアルコール、ベヘニルアルコール、及びラウリルアルコール等が挙げられる。
高級脂肪酸エステルとしては、例えば、ステアリン酸ステアリル、ベヘン酸ベヘニル等が挙げられる。
高級脂肪酸アミドとしては、例えば、ステアリン酸アミド、オレイン酸アミド、エルカ酸アミド、エチレンビスステアリルアミド、エチレンビスオレイルアミド、N−ステアリルステアリルアミド、N−ステアリルエルカ酸アミド等が挙げられる。
高級脂肪酸アミドとしては、好ましくは、ステアリン酸アミド、エルカ酸アミド、エチレンビスステアリルアミド、及びN−ステアリルエルカ酸アミドであり、より好ましくはエチレンビスステアリルアミド及びN−ステアリルエルカ酸アミドである。
本実施形態のポリアミド樹脂組成物には、必要に応じて、本実施形態の目的を損なわない範囲で、熱劣化、熱時の変色防止、耐熱エージング性、及び耐候性の向上を目的に劣化抑制剤を添加してもよい。
劣化抑制剤としては、特に限定されないが、例えば、酢酸銅及びヨウ化銅等の銅化合物;ヒンダードフェノール化合物等のフェノール系安定剤;ホスファイト系安定剤;ヒンダードアミン系安定剤;トリアジン系安定剤;及びイオウ系安定剤等が挙げられる。
これらの劣化抑制剤は、1種類を単独で用いてもよいし、2種類以上を組み合せて用いてもよい。
(着色剤)
本実施形態のポリアミド樹脂組成物には、必要に応じて、本実施形態の目的を損なわない範囲で、着色剤を添加してもよい。
着色剤としては、特に限定されないが、例えば、ニグロシン等の染料、酸化チタン及びカーボンブラック等の顔料;アルミニウム、着色アルミニウム、ニッケル、スズ、銅、金、銀、白金、酸化鉄、ステンレス、及びチタン等の金属粒子;マイカ製パール顔料、カラーグラファイト、カラーガラス繊維、及びカラーガラスフレーク等のメタリック顔料等が挙げられる。
本実施形態のポリアミド樹脂組成物には、必要に応じて、本実施形態の目的を損なわない範囲で、他の樹脂を添加してもよい。
このような樹脂としては、特に限定されるものではないが、後述する熱可塑性樹脂やゴム成分等が挙げられる。
ポリカーボネート、ポリフェニレンエーテル、ポリスルホン、ポリエーテルスルホン等のポリエーテル系樹脂;ポリフェニレンスルフィド、ポリオキシメチレン等の縮合系樹脂;ポリアクリル酸、ポリアクリル酸エステル、ポリメチルメタクリレート等のアクリル系樹脂;ポリエチレン、ポリプロピレン、ポリブテン、エチレン−プロピレン共重合体等のポリオレフィン系樹脂;ポリ塩化ビニル、ポリ塩化ビニリデン等の含ハロゲンビニル化合物系樹脂;フェノール樹脂;エポキシ樹脂等が挙げられる。
これらの熱可塑性樹脂は、1種類を単独で用いてもよいし、2種類以上を組み合せて用いてもよい。
これらのゴム成分は、1種類を単独で用いてもよいし、2種類以上を組み合せて用いてもよい。
本実施形態のポリアミド樹脂組成物の製造方法としては、(A)ポリアミドと(B)ハロゲン系難燃剤とを混合する方法であれば、特に限定されるものではない。また、ポリアミド樹脂組成物の製造方法としては、(C)難燃助剤、(D)α,β不飽和ジカルボン酸無水物を含む重合体、及び(E)無機充填材からなる群より選択される少なくとも1種をさらに混合する方法が挙げられる。さらに、上述したその他の添加剤をさらに混合してもよい。
(A)ポリアミドと(B)ハロゲン系難燃剤等との混合方法としては、例えば、(A)ポリアミドと(B)ハロゲン系難燃剤と、任意に、(C)難燃助剤、(D)α,β不飽和ジカルボン酸無水物を含む重合体、及び(E)無機充填材からなる群より選択される少なくとも1種とをヘンシェルミキサーなどを用いて混合し溶融混練機に供給し混練する方法や、単軸又は2軸押出機で(A)ポリアミドと(B)ハロゲン系難燃剤と、任意に、(C)難燃助剤及び/又は(D)α,β不飽和ジカルボン酸無水物を含む重合体とを予めヘンシェルミキサーなどを用いて混合したものを溶融混練機に供給し混練した後に、任意に、サイドフィダーから(E)無機充填材を配合する方法などが挙げられる。
混練機での剪断速度は100sec-1以上程度であることが好ましく、混練時の平均滞留時間は0.5〜5分程度であることが好ましい。
溶融混練を行う装置としては、公知の装置、例えば、単軸又は2軸押出機、バンバリーミキサー、及びミキシングロールなどの溶融混練機が好ましく用いられる。
本実施形態のポリアミド樹脂組成物を成形することにより、所定の成形品が得られる。
成形品を得る方法としては、特に限定されず、公知の成形方法を用いることができる。
例えば、押出成形、射出成形、真空成形、ブロー成形、射出圧縮成形、加飾成形、他材質成形、ガスアシスト射出成形、発砲射出成形、低圧成形、超薄肉射出成形(超高速射出成形)、及び金型内複合成形(インサート成形、アウトサート成形)等の成形方法が挙げられる。
本実施形態の成形品は、上述したポリアミド樹脂組成物を含み、過酷な成形条件下における成形体の表面外観の安定性、耐衝撃特性、難燃性に優れ、様々な用途に用いることができる。
例えば、自動車分野、電気・電子分野、機械・工業分野、事務機器分野、航空・宇宙分野において、好適に用いることができる。
〔測定方法〕
<ポリアミドのイソフタル酸成分比率、イソフタル酸末端基、及び全カルボキシル末端基の定量>
ポリアミドを用いて、1H−NMRにより求めた。
溶媒として重硫酸を用いた。
装置は日本電子製、「ECA400型」を用いた。
繰返時間は12秒、積算回数は64回で測定した。
各成分の特性シグナルの積分値より、イソフタル酸成分量、イソフタル酸末端基量、その他のカルボキシ末端基(例えばアジピン酸末端基)量を算出し、これらの値から、全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、及び上記式(1)のパラメータ(Y)をさらに算出した。
ポリアミドを蟻酸に溶解し、JIS K6810に準じて測定した。
装置は日精樹脂(株)製、「FN3000」を用いた。
シリンダー温度を320℃、金型温度を70℃に設定し、射出17秒、冷却20秒の射出成形条件で、ポリアミド又はポリアミド樹脂組成物を用いて100ショットまで成形を行い、成形体(ISO試験片)を得た。
得られた成形体(ISO試験片)の外観安定性は、堀場(株)製、ハンディ光沢度計「IG320」を用いてグロス値を測定し、下記方法により求めた。
外観安定性=((1):20〜30ショットISO試験片のグロス平均値)−((2):90〜100ショットISO試験片のグロス平均値)
上記の数値差が小さいほど、外観安定性に優れるものと判断した。
なお表1、2中、「(1)−(2)」とは、上記外観安定性の式により算出されるグロス値を示す。
上記外観安定性試験で得られた20〜25ショットISO試験片を用いて、ISO 179に準じてシャルピー衝撃強さ測定した。
測定値はn=6の平均値とした。
UL94(米国Under Writers Laboratories Incで定められた規格)の方法を用いて測定を行った。なお試験片(長さ127mm、幅12.7mm、厚みは1/32インチ)は射出成形機(日精樹脂(株)製PS40E)にUL試験片の金型(金型温度=80℃)を取り付けて、シリンダー温度=290℃で、ポリアミド樹脂組成物を成形することにより作製した。射出圧力はUL試験片成形する際の完全充填圧力+2%の圧力で行った。難燃等級は、UL94規格(垂直燃焼試験)に準じた。
<製造例1:ポリアミド(A1)の製造>
アジピン酸とヘキサメチレンジアミンとの等モル塩1237g、イソフタル酸とヘキサメチレンジアミンとの等モル塩263g、及び全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を、内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま1時間、オートクレーブの内部温度が245℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次に、1時間かけてオートクレーブ内の圧力を1MPaまで下げ、その後、オートクレーブ内を真空装置で650torrの減圧下に10分維持した。
このとき、重合の最終内部温度は265℃であった。
その後、オートクレーブ内を窒素で加圧し下部紡口(ノズル)から得られたポリマーをストランド状で排出し、水冷、カッティングを行いペレット状にして、100℃、窒素雰囲気下で12時間乾燥し、ポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1132g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩368gを用いた。
その他の条件は、製造例1と同様の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1044g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩456gを用いた。
その他の条件は、製造例1と同様の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩816g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩684gを用いた。
その他の条件は、製造例1と同様の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1237g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩263gを用いた。全等モル塩成分に対して0.5モル%過剰のアジピン酸を添加しなかった。
その他の条件は、製造例1の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1044g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩456gを用いた。全等モル塩成分に対して0.5モル%過剰のアジピン酸を添加しなかった。
その他の条件は、製造例1の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1114g、イソフタル酸とヘキサメチレンジアミンとの等モル塩386g、及び全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま1時間、オートクレーブの内部温度が245℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次に、1時間かけてオートクレーブ内の圧力を1MPaまで下げ、その後、オートクレーブ内を真空装置で400torrの減圧下に10分維持した。
このとき、重合の最終内部温度は265℃であった。
その後、オートクレーブ内を窒素で加圧し下部紡口(ノズル)から得られたポリマーをストランド状で排出し、水冷、カッティングを行いペレット状にして、100℃、窒素雰囲気下で12時間乾燥し、ポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1114g、イソフタル酸とヘキサメチレンジアミンとの等モル塩368g、及び全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま1時間、オートクレーブの内部温度が245℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次に、1時間かけてオートクレーブ内の圧力を1MPaまで下げ、その後、オートクレーブ内を真空装置で650torrの減圧下に20分維持した。
このとき、重合の最終内部温度は270℃であった。
その後、オートクレーブ内を窒素で加圧し下部紡口(ノズル)から得られたポリマーをストランド状で排出し、水冷、カッティングを行いペレット状にして、100℃、窒素雰囲気下で12時間乾燥し、ポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1109g、イソフタル酸とヘキサメチレンジアミンとの等モル塩368g、εカプロラクタム5g、及び全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま1時間、オートクレーブの内部温度が245℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次に、1時間かけてオートクレーブ内の圧力を1MPaまで下げ、その後、オートクレーブ内を真空装置で650torrの減圧下に10分維持した。
このとき、重合の最終内部温度は265℃であった。
その後、オートクレーブ内を窒素で加圧し下部紡口(ノズル)から得られたポリマーをストランド状で排出し、水冷、カッティングを行いペレット状にして、100℃、窒素雰囲気下で12時間乾燥し、ポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表1に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1500g、全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま1時間、オートクレーブの内部温度が260℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次に、1時間かけてオートクレーブ内の圧力を1MPaまで下げ、その後、オートクレーブ内を真空装置で650torrの減圧下に10分維持した。
このとき、重合の最終内部温度は290℃であった。
その後、オートクレーブ内を窒素で加圧し下部紡口(ノズル)から得られたポリマーをストランド状で排出し、水冷、カッティングを行いペレット状にして、100℃、窒素雰囲気下で12時間乾燥し、ポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1455g、及びイソフタル酸とヘキサメチレンジアミンの等モル塩45gを用いた。
その他の条件は、製造例10と同様の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1237g、イソフタル酸とヘキサメチレンジアミンとの等モル塩263g、及び全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま1時間、オートクレーブの内部温度が260℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次にバルブを閉止し、ヒーターを切り、約8時間かけてオートクレーブの内部温度を常温まで冷却し、蟻酸溶液粘度7のポリアミドを得た。
得られたポリアミドを粉砕した後、内容積10Lのエバポレーターに入れ、窒素気流下、200℃で10時間固相重合した。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩816g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩684gを用いた。
その他の条件は、製造例12と同様の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1220g、イソフタル酸とヘキサメチレンジアミンとの等モル塩280g、及び全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を、内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま2時間、オートクレーブの内部温度が260℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次に、1時間かけてオートクレーブ内の圧力を1MPaまで下げ、次にバルブを閉止し、ヒーターを切り、約8時間かけてオートクレーブの内部温度を常温まで冷却し、ポリアミドを得た。得られたポリアミドを粉砕した後、100℃、窒素雰囲気下で12時間乾燥し、ポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩570g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩930gを用いた。
その他の条件は、製造例1と同様の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩570g、及びイソフタル酸とヘキサメチレンジアミンとの等モル塩930gを用いた。
全等モル塩成分に対して0.5モル%過剰のアジピン酸を添加しなかった。
その他の条件は、製造例1と同様の方法によりポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
アジピン酸とヘキサメチレンジアミンとの等モル塩1237g、イソフタル酸とヘキサメチレンジアミンとの等モル塩263g、及び全等モル塩成分に対して0.5モル%過剰のアジピン酸を蒸留水1500gに溶解させ、原料モノマーの等モル50質量%均一水溶液を作製した。
この水溶液を内容積5.4Lのオートクレーブに仕込み、窒素置換した。
110〜150℃の温度下で前記水溶液を撹拌しながら、溶液濃度70質量%まで水蒸気を徐々に抜いて濃縮した。
その後、オートクレーブの内部温度を220℃に昇温した。
このとき、オートクレーブは1.8MPaまで昇圧した。
そのまま1時間、オートクレーブの内部温度が260℃になるまで加熱し、水蒸気を徐々に抜いて圧力を1.8MPaに保ちながら1時間反応させた。
次にバルブを閉止し、ヒーターを切り、約8時間かけてオートクレーブの内部温度を常温まで冷却し、蟻酸溶液粘度7のポリアミドを得た。
得られたポリアミドの全カルボン酸中のイソフタル酸成分比率(x)、全カルボキシル末端基中のイソフタル酸末端基比率(EG)、上記式(1)で示されるパラメータ(Y)、蟻酸溶液粘度等のポリマー特性を上記記載の方法により測定及び算出した。これらを下記表2に示す。
(B1)臭素化ポリスチレン(ALBEMARLE CORPORATION製 商品名SAYTEX(登録商標)HP−7010G (元素分析より求めた臭素含有量:63質量%))
(C1)三酸化二アンチモン 第一エフ・アール製 商品名 三酸化アンチモン
(D1)スチレンと無水マレイン酸との共重合体(NOVA Chemicals製 商品名 DYLARK(登録商標)332(スチレン85質量%及び無水マレイン酸15質量%の共重合体))
(E1)ガラス繊維(GF)(日本電気硝子製 商品名 ECS03T275H 平均繊維径10μmφ、カット長3mm)
東芝機械社製、TEM35mm2軸押出機(設定温度:前290℃、スクリュー回転数300rpm)を用いて、押出機最上流部に設けられたトップフィード口より製造例1で作成したポリアミド(A1)と、(B)ハロゲン系難燃剤、(C)難燃助剤、及び(D)α,β不飽和ジカルボン酸無水物を含む重合体とを予めブレンドしたものを供給し、押出機下流側(トップフィード口より供給された樹脂が十分溶融している状態)のサイドフィード口より(E)無機充填材を供給し、ダイヘッドより押し出された溶融混練物をストランド状で冷却し、ペレタイズしてポリアミド樹脂組成物ペレットを得た。配合量は(A)ポリアミド100質量部に対して、(B)ハロゲン系難燃剤45.0質量部、(C)難燃助剤7.0質量部、(D)α,β不飽和ジカルボン酸無水物を含む重合体4.0質量部、及び(E)無機充填材70.0質量部とした。
また、得られたポリアミド樹脂組成物を用いて、上記記載の方法により成形品を製造し、ハイサイクル成形時の外観安定性、衝撃特性、難燃性の評価を行った。評価結果を下記表1に示す。
製造例1のポリアミド(A1)に代えて、上述した製造例2〜16のポリアミド(A2)〜(A16)を用いた以外は、実施例1に記載した方法でポリアミド樹脂組成物を得た。
また、得られたポリアミド樹脂組成物を用いて、上記記載の方法により成形品を製造し、ハイサイクル成形時の外観安定性、衝撃特性、難燃性の評価を行った。評価結果を下記表1及び表2に示す。
製造例1のポリアミド(A1)に代えて、製造例17のポリアミド(A17)を用いた以外は実施例1と同様に行った。しかしながら溶融粘度が低いため、押出加工性が悪く、ペレット状のポリアミド樹脂組成物を得ることができなかった。
一方、(Y)が、−0.3≦(Y)≦0.8の範囲外である比較例3、4、5のポリアミド樹脂組成物の成形品、及び(x)が、0.05≦(x)≦0.5の範囲外である比較例1、2、6、7のポリアミド樹脂組成物の成形品は、表面外観の安定性が大きく低下することが確認された。なお、比較例8では成形品を得ることができなかった。
Claims (6)
- (A):(a)アジピン酸とヘキサメチレンジアミンとからなる単位と、
(b)イソフタル酸とヘキサメチレンジアミンとからなる単位と、
を、含むポリアミドであって、
当該ポリアミド中における全カルボン酸成分中のイソフタル酸成分比率(x)が、0.05≦(x)≦0.5であり、
かつ、下記式(1)で示される(Y)が、−0.3≦(Y)≦0.8である(A)ポリアミドと、
(Y)=[(EG)−(x)]/[1−(x)] ・・・(1)
(前記式(1)中、(EG)は、(A)ポリアミド中に含有されている全カルボキシル末端基中のイソフタル酸末端基比率を示し、下記式(2)で示される。
(EG)=イソフタル酸末端基量/全カルボキシル末端基量 ・・・(2))
(B):ハロゲン系難燃剤と、を、含有するポリアミド樹脂組成物。 - 前記式(1)で示される(Y)の範囲が0.05≦(Y)≦0.8である、請求項1に記載のポリアミド樹脂組成物。
- 前記(B)ハロゲン系難燃剤が臭素化ポリスチレンである、請求項1又は2に記載のポリアミド樹脂組成物。
- (C)難燃助剤と、
(D)α,β不飽和ジカルボン酸無水物を含む重合体と、
(E)無機充填材と、をさらに含有し、
前記(A)ポリアミド100質量部に対して、
前記(B)ハロゲン系難燃剤の含有量が30〜60質量部であり、
前記(C)難燃助剤の含有量が0.1〜30質量部であり、
前記(D)α,β不飽和ジカルボン酸無水物を含む重合体の含有量が0.1〜20質量部であり、
前記(E)無機充填材の含有量が1〜200質量部である、請求項1乃至3のいずれか一項に記載のポリアミド樹脂組成物。 - 前記(C)難燃助剤が、酸化アンチモン類及び/又は水酸化マグネシウムである、請求項4に記載のポリアミド樹脂組成物。
- 請求項1乃至5のいずれか一項に記載のポリアミド樹脂組成物を含む成形品。