JP2012251586A - 伝動ベルト - Google Patents
伝動ベルト Download PDFInfo
- Publication number
- JP2012251586A JP2012251586A JP2011123698A JP2011123698A JP2012251586A JP 2012251586 A JP2012251586 A JP 2012251586A JP 2011123698 A JP2011123698 A JP 2011123698A JP 2011123698 A JP2011123698 A JP 2011123698A JP 2012251586 A JP2012251586 A JP 2012251586A
- Authority
- JP
- Japan
- Prior art keywords
- belt
- oils
- fats
- transmission belt
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ベルトの長手方向に延びて心線3が埋設された伝動ベルト1において、少なくともプーリとの接触部を、ポリウレタン及びトリグリセリドを主成分とする融点50〜80℃の油脂類を含む樹脂組成物で形成する。前記油脂類は硬化油であってもよい。前記油脂類のヨウ素価は30以下であってもよい。さらに、前記油脂類は、トリグリセリドであってもよい。前記ポリウレタンはウレタンプレポリマーと硬化剤との硬化物であり、前記油脂類の割合は前記ウレタンプレポリマー100質量部に対して10質量部未満であってもよい。本発明の伝動ベルト1は、自転車用歯付ベルトであってもよい。
【選択図】図1
Description
ポリウレタン(又はウレタンエラストマー)は、特に限定されず、慣用のポリウレタンが利用できるが、成形性などの点から、ウレタンプレポリマーと硬化剤との硬化物(二液硬化型ポリウレタン)であってもよい。
本発明では、油脂類として、融点50〜80℃の油脂類を用いる。このような融点を有する油脂類を用いることにより、使用時にベルト本体の温度が約50℃程度まで上昇した際、融点50℃以上の油脂類は部分的に流動することにより、ベルトの表面にブリードアウトし(ベルト表面に滲み出し)、ブリードアウトした油脂類は、ベルトの表面で潤滑層を形成する。形成された潤滑油は、その一部がベルトから剥離しても、大部分がプーリ表面に移行して残存するため、ベルトとプーリ間の摺動性が維持され、ベルトの長寿命化が可能となる。さらに、本発明では、高温時の摺動性だけでなく、室温程度でも摺動性を向上できる。
前記樹脂組成物は、慣用の添加剤、例えば、安定剤(耐候安定剤、酸化防止剤、熱安定剤、光安定剤など)、充填剤、可塑剤、滑剤、着色剤、溶媒などを含んでいてもよい。これらの添加剤は単独で又は二種以上組み合わせて使用できる。これらの添加剤のうち、本発明の歯付ベルトは、前記油脂類の配合により高い摺動性を有するため、滑剤や可塑剤を配合しない組成物であっても、ベルトの耐久性を向上できる。そのため、前記樹脂組成物は、滑剤や可塑剤(特に可塑剤)を実質的に含有しなくてもよい。滑剤や可塑剤などの添加剤を含有する場合、添加剤の割合は、ポリウレタン100質量部に対して30質量部以下、好ましくは1〜20質量部、さらに好ましくは3〜15質量部程度である。
本発明の伝動ベルトのベルト本体には、走行の安定性及びベルト強度などの点から、ベルトの長手方向に沿って延びて心線(通常、複数の心線)が埋設されている。
基準油脂分析試験法(日本油化学会制定)に準拠して測定した。
得られた歯付ベルトを25℃の環境で7日間放置し、その歯部表面における油脂の滲み出しの程度(ブリードアウト性)を、以下の基準で目視により観察した。なお、ラードを用いた比較例1のブリードアウト性を基準として評価とした。
4:滲み出し量が比較例1よりも多い
3:比較例1と同等の滲み出し量がある
2:滲み出し量が比較例1よりも少ない
1:滲み出しがない。
得られた歯付ベルトについて、25℃及び50℃における歯部表面の摺動性を、以下の基準で触覚により評価した。なお、ラードを用いた比較例1の25℃における摺動性を基準として評価とした。
4:摺動性が比較例1よりも高い
3:25℃における比較例1の摺動性と同等である
2:摺動性が比較例1よりも低い
1:粘着性がある。
牛脂硬化油:日油(株)製、融点54℃
牛脂極度硬化油:日油(株)製、融点60℃
大豆極度硬化油:横関油脂工業(株)製、融点68℃
菜種極度硬化油:横関油脂工業(株)製、融点69℃
ラード(豚脂):日油(株)製、融点40℃
やし油:花王(株)製、融点−20℃
ソルビタントリステアレート:花王(株)製、融点56℃
ひまし硬化油:豊国製油(株)製、融点87℃。
ウレタンプレポリマーとして、TDI末端ポリテトラメチレングリコールエーテル(日本ポリウレタン工業(株)製「コロネート4095」)100質量部に、硬化剤としてMOCA(イハラケミカル工業(株)製「キュアミンMT」)10質量部及び表1に示す油脂類5質量部を配合し、樹脂組成物を調製した。
2…歯部
3…心線
Claims (7)
- ベルトの長手方向に延びて心線が埋設された伝動ベルトであって、少なくともプーリとの接触部が、ポリウレタン及びトリグリセリドを主成分とする融点50〜80℃の油脂類を含む樹脂組成物で形成されている伝動ベルト。
- 油脂類が硬化油である請求項1記載の伝動ベルト。
- 油脂類のヨウ素価が30以下である請求項1又は2記載の伝動ベルト。
- 油脂類がトリグリセリドである請求項1〜3のいずれかに記載の伝動ベルト。
- ポリウレタンがウレタンプレポリマーと硬化剤との硬化物であり、油脂類の割合が前記ウレタンプレポリマー100質量部に対して10質量部未満である請求項1〜4のいずれかに記載の伝動ベルト。
- ベルト本体の少なくとも一方の面に、前記長手方向に所定の間隔をおいて形成され、かつプーリと噛み合わせるための複数の歯部を有する歯付ベルトである請求項1〜5のいずれかに記載の伝動ベルト。
- 自転車用歯付ベルトである請求項1〜6のいずれかに記載の伝動ベルト。