JP2012238722A - 六方晶フェライト凝集粒子およびそれを用いた磁気記録媒体 - Google Patents
六方晶フェライト凝集粒子およびそれを用いた磁気記録媒体 Download PDFInfo
- Publication number
- JP2012238722A JP2012238722A JP2011106742A JP2011106742A JP2012238722A JP 2012238722 A JP2012238722 A JP 2012238722A JP 2011106742 A JP2011106742 A JP 2011106742A JP 2011106742 A JP2011106742 A JP 2011106742A JP 2012238722 A JP2012238722 A JP 2012238722A
- Authority
- JP
- Japan
- Prior art keywords
- particles
- aggregated particles
- hexagonal ferrite
- precursor
- aggregated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】六方晶フェライト粒子の一次粒子がその形態を保ちつつ、複数個集合して形成されている凝集粒子であって、その形状はSEMの1000倍程度の倍率で観察した際に球形近似形状をしており、その平均粒径が20μm以上、100μm以下である六方晶フェライト粒子からなる凝集粒子とする。
【選択図】図1
Description
本発明の凝集粒子は、例えば下記のような手法を用いて製造することができる。
本発明に従う粒子は、主組成となる鉄とアルカリ土類金属(A)の他、保磁力を調整するための2価、4価の添加元素(M1,M2)を含んでもよく、形状を制御するための添加元素であるビスマス、および熱安定性を改善するためのニオブの添加を含む。
本発明の粒子は、次に示す物理特性を有する。すなわち、平均粒子径(板状であるときは板径、球形である場合には直径に該当する)が10〜50nm、好ましくは10〜25nmである。50nmよりも大きいと、記録媒体化した時のノイズが高くなるため高密度記録に適さない。また、10nmよりも小さい粒子になると、熱安定性が悪くなるので好ましくない。
得られた磁性粉を、以下に示す方法により物性を評価した。
本発明に従う粒子は、走査型電子顕微鏡(例えば、日立ハイテクノロジー株式会社の日立走査電子顕微鏡S−4700)等を用いて確認される大きさが100μm以下の凝集粒子を形成する。このとき、おおよそ凝集粒子の形態は、球状や楕円体あるいは瓢箪状といった球形近似の形態をしている。本発明では、球状や回転楕円状あるいは瓢箪状といった球形近似の形態を「球形近似形状」と呼ぶ。
最終的に得られた六方晶フェライト磁性粉を下記に示す方法により評価した。まず、鉄は、粉体を溶解し平沼産業株式会社製の平沼自動滴定装置(CONTIME−980型)を使用して定量した。その他の成分の定量は、粉体を溶解させ、日本ジャーレルアッシュ株式会社製の高周波誘導プラズマ発光分析装置ICP(IRIS/AP)を使用し定量した。
粒子の比表面積は、BET一点法を用いて測定した。測定装置はユアサイオニクス株式会社製の4ソーブUSを使用して測定した。
磁性粉末をφ6mmのプラスチック製容器に詰め、東英工業株式会社製のVSM装置(VSM−P7−15)を使用して、外部磁場795.8kA/m(10kOe)で、保磁力Hc(Oe、kA/m)、飽和磁化σs(Am2/kg)、粉体のBSFD(バルク状態におけるSFD値)を測定した。なお、SFD値は、VSM装置によって得られたヒステリシス曲線の微分曲線の半値幅を保磁力で規格化した値(無単位)である。
得られた磁性粉末(最終製品としての磁性粉末)0.35gを秤量して(内径45mm、深さ13mm)のポットに入れ、蓋を開けた状態で10分間放置した後、マイクロピペットでビヒクル(日本ゼオン株式会社製の塩化ビニル系樹脂MR−555(20質量%)と、東洋紡株式会社製のバイロン(登録商標)UR−8200(30質量%)、シクロヘキサノン(50質量%)と、アセチルアセトン(0.3質量%)と、ステアリン酸−n−ブチル(0.3質量%)の混合溶液)1.1mLを添加し、その直後にスチールボール(2φ)30g、ナイロンボール(8φ)10個をポットに加えて、蓋を閉じた状態で10分間静置した。
原料として、酸化鉄(テツゲン製HRT)31.04g、炭酸バリウム(堺化学工業/工業用)48.14g、ホウ酸(Borax製/工業用)26.16g、酸化ビスマス(関東化学株式会社製/試薬)3.65g、酸化ニオブ(高純度化学研究所製/試薬)1.03gをそれぞれ秤量し、均一になるように粉砕しながら混合した。このときのBi/Fe比は3.5at%、Nb/Fe比は1.0at%である。得られた混合物は、大きさが均一になるように、自動乳鉢で10分間擂り潰し処理を行った。こうして得られた混合物を白金製るつぼに挿入し、1400℃で溶解させた上、60分間維持することで、完全に混合物を溶解させ、溶湯の状態とした。
実施例1において、水アトマイズにおける噴射水の圧力を種々変化させて、前駆体の大きさを変更した以外は同様の操作を繰り返した。得られた結果を表1および2にあわせて示す。
実施例1において、洗浄に用いる酢酸の濃度を3質量%に希釈したものを用いた以外は同様の操作を繰り返した。すなわち、薄い酢酸で洗浄をおこなった。得られた結果を表1および2に示す。
溶湯を急冷する方法を水アトマイズ法から、双ロール法中に溶湯を流し込んで急冷するいわゆる双ロール法とし、熱処理後にボールミルを用いて粉砕処理を施した以外は実施例1を繰り返した。
Claims (9)
- 六方晶フェライト粒子の一次粒子が複数個集合して形成されている凝集粒子であって、前記凝集粒子の平均粒径が20μm以上、100μm以下であり、ホウ素の含有量が0.5質量%以下である、六方晶フェライト凝集粒子。
- 前記凝集粒子を構成する一次粒子は、ホウ素ガラス成分により結合されている、請求項1に記載の六方晶フェライト凝集粒子。
- 走査型電子顕微鏡により観察される球形近似形状の凝集粒子の個数割合が10%以上である、請求項1または2に記載の六方晶フェライト凝集粒子。
- 前記凝集粒子を構成する一次粒子の平均一次粒子径は10〜30nmである、請求項1ないし3のいずれかに記載の六方晶フェライト凝集粒子。
- 前記凝集粒子を構成する一次粒子は、Nbを5.0質量%以下含む、請求項1ないし4のいずれかに記載の六方晶フェライト凝集粒子。
- 前記凝集粒子を構成する一次粒子は、Ndを5.0質量%以下含む、請求項1ないし4のいずれかに記載の六方晶フェライト凝集粒子。
- 前記凝集粒子を構成する一次粒子は、Biを10.0質量%以下含む、請求項1ないし6のいずれかに記載の六方晶フェライト凝集粒子。
- ガラス結晶化法により六方晶フェライトを形成するにあたり、ガラス成分とフェライト成分を溶融して溶湯とし、急冷することにより形成した前駆体であって、その飽和磁化値が0.05〜0.20Am2/kgである六方晶フェライトの前駆体。
- 請求項1ないし5のいずれかに記載の凝集粒子を用いて形成された、塗布型磁気記録媒体。