JP2012160435A - リチウムイオン二次電池 - Google Patents
リチウムイオン二次電池 Download PDFInfo
- Publication number
- JP2012160435A JP2012160435A JP2011289016A JP2011289016A JP2012160435A JP 2012160435 A JP2012160435 A JP 2012160435A JP 2011289016 A JP2011289016 A JP 2011289016A JP 2011289016 A JP2011289016 A JP 2011289016A JP 2012160435 A JP2012160435 A JP 2012160435A
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- electrolyte
- active material
- electrode active
- lithium ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明により提供されるリチウムイオン二次電池500は、正極活物質534Aを有する正極530と、負極活物質544Aを有する負極540と、非水溶媒と支持塩とSEI形成材料とを含む液状電解質(電解液P)537と、正極活物質534Aと電解液Pとの間に介在された非流動性(典型的にはゲル状または固体状)の電解質536とを備える。
【選択図】図5
Description
このような負極における還元反応を抑制するために、該還元反応を抑制する被膜(SEI)を負極表面に形成し得る材料(SEI形成材料)が添加された電解液を用いることも考えられる。しかし、正極の電位が高いと上記SEI形成材料が正極において酸化分解されてしまい、負極表面がSEIによって適切に被覆され難くなる。このため、SEI形成材料の添加効果が十分に発揮されず、充放電サイクル特性の向上(例えば容量劣化の改善)が困難となる場合があり得る。
本発明の一実施態様に係るリチウムイオン二次電池500は、図4に示されるように、容器510内に、正極集電体532上に正極活物質層534を有する正極530と、負極集電体542上に負極活物質層544を有する負極540と、電解質ゲル536(電解質組成物Q)と、液状電解質(電解液P)537とを備える。正極活物質層534は正極活物質534Aを主成分とする層であり、負極活物質層544は負極活物質544Aを主成分とする層である。正極活物質層534は、電解質ゲル536で被覆されている。液状電解質537は、負極活物質層544には接するが、正極活物質層534には直に接しないように該電池内に含まれている。換言すれば、互いに相の異なる電解質組成物(電解質ゲルQ,電解液P)が、正極側(「正極に接するように」の意味)および負極側(「負極に接するように」の意味)にそれぞれ配置された構成を有する。すなわち、正極側に配置された電解質組成物Qはゲル相であり、負極側に配置された電解液Pは溶液相である。
LiFePO4を用いて作用極を作製する。詳しくは、LiFePO4と、アセチレンブラック(導電材)と、PVDF(結着剤)とを、これらの質量比が85:5:10となるように混合し、N−メチル−2−ピロリドン(NMP)に分散させてスラリー状の組成物を調製する。これをアルミニウム箔状に塗付し、乾燥後にロールプレスして作用極(正極)シートを作製する。上記作用極と、対極としての金属リチウムと、作用極としての金属リチウムと、測定対象たる電解液とを用いて三極セルを構築する。この三極セルに対し、該作用極から完全にLiを脱離させる処理を行う。具体的には、温度25℃において、該作用極の理論容量から予測した電池容量(Ah)の1/5の電流値で4.2Vまで定電流充電を行い、4.2Vにおいて電流値が初期電流値(すなわち、電池容量の1/5の電流値)の1/50となるまで定電圧充電を行う。次いで、測定対象電解液の酸化電位が含まれると予測される電圧範囲(典型的には4.2Vよりも高い電圧範囲)において、任意の電圧で定電圧充電を所定時間(例えば、10時間程度)行い、その際の電流値を測定する。より具体的には、上記電圧範囲のなかで電圧を段階的に(例えば、0.2Vステップで)高くし、各段階において定電圧充電を所定時間(例えば、10時間程度)行い、その際の電流値を測定する。定電圧充電時の電流値が0.1mAより大きくなったときの電位を、上記電解液の酸化電位とする。
本発明の他の一実施態様に係るリチウムイオン二次電池500は、図6に示されるように、容器510内に、正極集電体532上に正極活物質層634を有する正極630と、負極集電体542上に負極活物質層544を有する負極540と、液状電解質(電解液P)537とを備える。さらに、正極630と負極540との間に介在された絶縁層550を備えることが好ましい。正極活物質層634は正極活物質634Aを主成分とする層であり、負極活物質層544は負極活物質544Aを主成分とする層である。図7に模式的に示されるように、正極活物質634Aの粒子表面の少なくとも一部(図7に示す例では表面全体)は、固体電解質634Bで被覆されている。すなわち、正極活物質634Aと固体電解質634Bとは粒子レベルで複合化されている。したがって、液状電解質537は、負極活物質層544には接するが、正極活物質634Aには直に接しないように該電池内に含まれている。
正極活物質層に含まれる導電材の量は、正極活物質の種類や量に応じて適宜選択すればよく、例えば、1〜30質量%程度とすることができる。
正極合材として、LiNi0.5Mn1.5O4(正極活物質)とアセチレンブラック(導電材)とPVDF(結着剤)とを、これらの質量比が87:10:3となるように混合し、NMPに分散させてスラリー状組成物を調製した。この正極合材スラリーを、厚さ15μmのアルミニウム箔(正極集電体)の片面に塗付した後乾燥させて正極活物質層を形成し、ロールプレスして正極シートを作製した。この正極シートを、一角に幅10mmの帯状部が突き出た5cm×5cmの正方形に切り出した。その帯状部から上記活物質層を除去し、アルミニウム箔を露出させて端子部を形成し、端子部付きの正極シートを得た。
ECとDMCとを体積比1:1の割合で含む混合溶媒に、LiPF6を1mol/Lの濃度となるように溶解して非水電解液Bを調製した。非水電解液Aの代わりに該非水電解液Bを用いた他は例1と同様にして、1C容量が30mAhのラミネートセル型電池を構築した。なお、上記と同様にして測定された電解液Bの酸化電位は、4.6〜4.8Vであった。
上記非水電解液Bに、SEI形成材料としてのビニレンカーボネート(VC)を添加して、非水電解液B・VCを調製した。VCの添加量は、体積基準で、100部の非水電解液Bに対してVC3部とした。この電解液B・VC90部とPEO系ポリマー前駆体(第一工業製薬株式会社製、品番「TA140」)10部とを混合したものに、AIBN(熱重合開始剤)0.1部を加えて攪拌し、ポリマー前駆体溶液を得た。例1の負極シートの負極活物質層上にこのポリマー前駆体溶液を押し出し圧0.05MPaにて付与した後、該負極シートを温度60℃の乾燥炉に120分間保持して重合反応を進行させ、電解質ゲルpB・VCが付与された負極シートを作製した。これを例1と同様の面積および形状に切り出した後、例1と同様にして端子部を設けた。
上記非水電解液Bに、SEI形成材料としてのフルオロエチレンカーボネート(FEC)を添加して、非水電解液B・FECを調製した。FECの添加量は、体積基準で、100部の非水電解液Bに対してFEC3部とした。非水電解液B・VCに代えて当該非水電解液B・FECを用いた他は例3と同様にして、電解質ゲルpB・FECが付与された負極シートを得た。pB・VCゲル付き負極シートに代えて当該pB・FECゲル付き負極シートを用いた他は例3と同様にして、1C容量が30mAhのラミネートセル型電池を構築した。
非水電解液A90部とPEO系ポリマー前駆体(第一工業製薬株式会社製、品番「TA140」)10部とを混合したものに、AIBN(熱重合開始剤)0.1部を加えて攪拌し、ポリマー前駆体溶液を得た。例1の正極シートの正極活物質層上にこのポリマー前駆体溶液を押し出し圧0.05MPaにて付与した後、該正極シートを温度60℃の乾燥炉に120分間保持して重合反応を進行させ、電解質ゲルpAが付与された正極シートを作製した。これを、例1と同様の面積および形状に加工して、端子部を設けた。
上記電解液B・VCに代えて上記電解液B・FECを用いた他は例5と同様にして、1C容量が30mAhのラミネートセル型電池を構築した。
例1〜6に係る各電池セルを、二枚の板で挟み、350kgf(350kg/25cm2)の負荷がかかる状態に拘束した。拘束した各電池セルに対して、1/3Cのレートで4.9Vまで定電流(CC)充電する操作と、1/3Cのレートで3.5Vまで放電させる操作とを3回繰り返した。以下の測定等は、特に断りがない限り拘束したままの電池セルに対して行った。
例1〜6に係る各電池セルに対し、温度25℃にて、1/5Cのレートで両端子間の電圧が4.9VとなるまでCC充電を行った後、電流値が1/50Cとなるまで定電圧(CV)充電を行って、満充電状態とした。次いで、1/5Cのレートで電圧が3.5VとなるまでCC放電させ、このときの放電容量を測定して初期容量とした。なお、充電終了後充電機をはずしたとき(過電圧が解除された状態)の両端子間電圧は、いずれも4.7〜4.8V程度であった。
初期容量測定後の各電池セルに対し、温度25℃にて、1/5CのレートにてSOCが60%となるまでCC充電を行った。SOC60%に調製した各電池セルに対し、1/3C,1C,3Cのレートで充電および放電を行い、そのときの過電圧を測定した。測定された過電圧値を対応する電流値(例えば、1/3Cでは10mA)で除することで抵抗を算出して初期直流抵抗とした。
別途作製し、コンディショニング処理を施した例1〜6に係る各電池セルを、初期容量の測定時と同様にして満充電状態とした。次いで、温度40℃で10日間保持した後、温度25℃で5時間保持し、1/5Cのレートで電圧が3.5VとなるまでCC放電させ、このときの放電容量を測定して保存後容量とした。この保存後容量の初期容量に対する百分率を保存後容量維持率として算出した。
保存後の各電池セルに対し、上記初期直流抵抗と同様にして直流抵抗を測定し、保存後の直流抵抗とした。該保存後直流抵抗の初期直流抵抗に対する百分率から、抵抗増加率(%)を算出した。
初期容量を測定した後、温度25℃にて1/5CのレートでSOC60%に調整した各電池に対し、温度40℃にて、2Cのレートで4.9VまでCC充電し、10分間休止した後、同じレートで3.5VまでCC放電し、10分間休止する充放電サイクルを、300サイクル繰り返した。その後、上記初期容量と同様にして放電容量を測定した。サイクル後の放電容量の初期容量に対する百分率を300cyc容量維持率(%)として求めた。
また、両極側に同じ耐還元性電解液Bを用いてなる例2の電池セルは、例1の電池セルに比べて保存後の容量低下は少なかった。これは、負極での副反応(還元分解)を抑制するSEIが負極表面に効果的に形成され、不可逆容量の発生が抑制されたことによると考えられる。しかし、保存後の抵抗増加率は151%と高かった。これは、満充電状態の電池内において、電解液中の有機溶媒が正極表面で酸化され被膜を形成することにより、正極抵抗が大きく増加したことによるものと考えられる。
ホソカワミクロン株式会社製の粒子設計装置「ナノクリエータFCM」を用い、FCM(Flash Creation Method)法に従って、Li1.5Al0.5Ge1.5(PO4)3(LAGP)の前駆体(アモルファス粉末)を正極活物質用コート材として調製した。詳しくは、Li源としてのナフテン酸リチウム溶液(溶媒:ホワイトスピリット;Li濃度1.2%),Al源としてのエチル−アセトアセテート−アルミニウム−ジ−n−ブチレート(Ethyl acetoacetato aluminum di−n−butyrate)溶液(溶媒:ミネラルスピリット;Al濃度:5.8%),Ge源としてのゲルマニウム溶液(溶媒:ミネラルスピリット;Ge濃度:9.8%),P源としてのジエチルホスホノ酢酸(P濃度:13.4%)を、Li:Al:Ge:P=1.5:0.5:1.5:3となるように混合してLAGP前駆体溶液を調製した。このLAGP前駆体溶液を、FCM法により、酸素流量30L/分、チャンバー内圧104Paの条件下において仮焼成してLAGP前駆体(アモルファス粉末状の正極活物質用コート材)を得た。
非水電解液Cに、VCを1.0%の濃度となるように添加して非水電解液C・VC1.0を得た。この非水電解液C・VC1.0を用いた他は例7と同様にして、1C容量が60mAhのラミネートセル型電池を構築した。
非水電解液Cに、VCを1.5%の濃度となるように添加して非水電解液C・VC1.5を得た。この非水電解液C・VC1.5を用いた他は例7と同様にして、1C容量が60mAhのラミネートセル型電池を構築した。
非水電解液Cに、VCを2.0%の濃度となるように添加して非水電解液C・VC2.0を得た。この非水電解液C・VC2.0を用いた他は例7と同様にして、1C容量が60mAhのラミネートセル型電池を構築した。
非水電解液Cを用いた他は例7と同様にして、1C容量が60mAhのラミネートセル型電池を構築した。
例1の端子部付正極シートおよび非水電解液C・VC1.0を用いた他は例7と同様にして、1C容量が60mAhのラミネートセル型電池を構築した。
例7〜12の各電池セルを、二枚の板で挟み、350kgf(350kg/25cm2)の負荷がかかる状態に拘束した。拘束した各電池セルに対して、1/5Cのレートで両端子間の電圧が4.9VまでCC充電してから同電圧値で電流値が1/50Cになるまで定電圧(CV)充電して満充電状態にする操作と、1/5Cのレートで3.5VまでCC放電させる操作とを3回繰り返した。VC残留量の測定を除き、以下の測定等は、特に断りがない限り拘束したままの電池セルに対して行った。
コンディショニング処理後の例7〜12の各電池セルから採取した非水電解液サンプルについて、ガスクロマトグラフィー(GC)(島津製作所製の型式「GC−17A」)を用いて非水電解液中のVC残留量(%)を測定した。
上記と同様にしてコンディショニング処理を施した例7〜12の各電池セルに対し、上記と同様の手順にて初期容量を測定した。なお、充電終了後充電機をはずしたとき(過電圧が解除された状態)の両端子間電圧は、いずれも4.7〜4.8V程度であった。
例7〜12の各電池セルに対し、上記と同様の手順にて初期直流抵抗を測定した。
例7〜12に係る各電池セルにつき、上記のとおり初期容量を測定した後、温度60℃にて2Cのレートで4.9VまでCC充電し、10分間休止した後、同じレートで3.5VまでCC放電し、10分間休止する充放電サイクルを、100サイクル繰り返した。その後、上記初期容量と同様にして放電容量を測定し、100サイクル後の放電容量とし、初期容量に対する百分率を100cyc容量維持率(%)として求めた。100サイクル後の各電池セルにつき、最初の100サイクルと同じ充放電サイクルを、さらに100サイクル繰り返した。併せて200サイクル後の各電池につき、100cyc容量維持率と同様にして、200サイクル後の放電容量を測定し、初期容量に対する百分率を200cyc容量維持率(%)として求めた。なお、例12の電池セルについては、100cyc容量維持率が低かったため、100サイクル完了時点でサイクル試験を終了した。
SEI形成材料の添加量が最も多い例10の電池セルは、例7〜9および例12と比べて初期抵抗が若干高かった。これは、該添加量が多くなったことで、例10の正極活物質表面の固体電解質層の厚みが増したことによるものと考えられる。
20 捲回電極体
30 正極シート
32 正極集電体
34 正極活物質層
36 電解質組成物Q
37 電解液P
38 正極端子
40 負極シート
42 負極集電体
44 負極活物質層
48 負極端子
50 セパレータ
100,500 リチウムイオン二次電池
530,630 正極
534,634 正極活物質層
534A,634A 正極活物質
634B 固体電解質
536 電解質ゲル(電解質組成物Q)
537 液状電解質(電解液P)
540 負極
544 負極活物質層
544A 負極活物質
550 絶縁層(セパレータ)
800 電源装置
804 電子制御ユニット(制御装置)
Claims (9)
- 正極活物質を有する正極と、
負極活物質を有する負極と、
非水溶媒と支持塩とSEI形成材料とを含む電解液Pと、
前記正極活物質と前記電解液Pとの間に介在された非流動性の電解質Qと、
を備える、リチウムイオン二次電池。 - 前記非流動性の電解質Qは、非水溶媒と支持塩とを含む電解質組成物Qであり、前記正極活物質は該電解質組成物Qによって被覆されており、ここで、前記電解質組成物Qは、ゲル状をなし、該組成物Qに含まれる非水溶媒の酸化電位(対Li/Li+)は、前記電解液Pに含まれる非水溶媒の酸化電位(対Li/Li+)よりも高い、請求項1に記載のリチウムイオン二次電池。
- 前記正極活物質は、スピネル型リチウムニッケルマンガン酸化物を含む、請求項1または2に記載のリチウムイオン二次電池。
- 前記電解質組成物Qに含まれる非水溶媒は、酸化電位(対Li/Li+)が4.3Vよりも高い、請求項1から3のいずれか一項に記載のリチウムイオン二次電池。
- 前記電解質組成物Qに含まれる非水溶媒は、酸化電位(対Li/Li+)が、前記電池の満充電状態における前記正極活物質の電位(対Li/Li+)よりも高い、請求項1から4のいずれか一項に記載のリチウムイオン二次電池。
- 前記電解質組成物Qに含まれる非水溶媒のうち95体積%以上は、フッ素化されたカーボネートの少なくとも一種からなる、請求項1から5のいずれか一項に記載のリチウムイオン二次電池。
- 前記電解質組成物Qと前記負極との間に配置された多孔質プラスチック層をさらに備える、請求項1から6のいずれか一項に記載のリチウムイオン二次電池。
- 上限電圧が4.3V以上である、請求項1から7のいずれか一項に記載のリチウムイオン二次電池。
- 請求項1から8のいずれか一項に記載のリチウムイオン二次電池と、
前記電池に電気的に接続され、該電池の少なくとも上限電圧値を規定する制御回路と、
を備え、
前記上限電圧値が4.3V以上に設定されている、電源装置。