JP2012158657A - 帯電防止性組成物及び成形体 - Google Patents
帯電防止性組成物及び成形体 Download PDFInfo
- Publication number
- JP2012158657A JP2012158657A JP2011018207A JP2011018207A JP2012158657A JP 2012158657 A JP2012158657 A JP 2012158657A JP 2011018207 A JP2011018207 A JP 2011018207A JP 2011018207 A JP2011018207 A JP 2011018207A JP 2012158657 A JP2012158657 A JP 2012158657A
- Authority
- JP
- Japan
- Prior art keywords
- antistatic
- surfactant
- composition
- group
- antistatic composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)界面活性剤、(B)イオン液体、並びに(C)ケイ素、カルシウム、アルミニウム及びジルコニウムからなる群より選択される一種以上の原子とその他の原子とを有する無機化合物が配合されてなることを特徴とする帯電防止性組成物;かかる帯電防止性組成物及び(F)熱可塑性樹脂が配合されてなる成形用組成物を用いて得られたことを特徴とする成形体。
【選択図】なし
Description
このような練り込み型の帯電防止剤としては、これまでに界面活性剤(特許文献1参照)、イオン液体(特許文献2参照)が開示されている。
一方、帯電防止剤としてイオン液体を使用した場合には、樹脂組成物の取り扱い性が悪化して、樹脂組成物が成形機内で十分に撹拌されないことにより、成形品表面に凹凸が生じて品質が低下してしまうという問題点があった。
本発明は、(A)界面活性剤、(B)イオン液体、並びに(C)ケイ素、カルシウム、アルミニウム及びジルコニウムからなる群より選択される一種以上の原子とその他の原子とを有する無機化合物が配合されてなることを特徴とする帯電防止性組成物を提供する。
本発明の帯電防止性組成物は、さらに、(D)熱可塑性樹脂が配合されてなるものでもよい。
本発明の帯電防止性組成物においては、前記(A)界面活性剤が、窒素原子を有するノニオン性界面活性剤であり、前記(B)イオン液体がイミダゾリウム系カチオンを有するものであることが好ましい。
本発明の帯電防止性組成物においては、前記(C)無機化合物が、ケイ酸カルシウム、シリカ、炭酸カルシウム、アルミナ又はジルコニアであることが好ましい。
本発明の帯電防止性組成物においては、前記(D)熱可塑性樹脂が、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリスチレン、ポリ酢酸ビニル、ポリメタクリル酸メチル、AS樹脂又はABS樹脂であることが好ましい。
また、本発明は、上記本発明の帯電防止性組成物及び(F)熱可塑性樹脂が配合されてなる成形用組成物を用いて得られたことを特徴とする成形体を提供する。
本発明の帯電防止性組成物は、(A)界面活性剤、(B)イオン液体、並びに(C)ケイ素、カルシウム、アルミニウム及びジルコニウムからなる群より選択される一種以上の原子とその他の原子とを有する無機化合物(以下、「(C)無機化合物」と略記する)が配合されてなることを特徴とする。
本発明の帯電防止性組成物は、(A)界面活性剤及び(B)イオン液体を併用することで、これらのいずれかを単独で使用した帯電防止剤(組成物)の場合よりも、顕著に高い帯電防止能を成形体に付与できる。
前記(A)界面活性剤は、帯電防止効果を有するものであれば特に限定されず、アニオン性界面活性剤、カチオン性界面活性剤、ノニオン性界面活性剤及び両性界面活性剤のいずれでもよい。
前記ノニオン性界面活性剤としては、窒素原子を有する界面活性剤、又はエステル系界面活性剤が好ましい。
前記窒素原子を有する界面活性剤としては、アルキルアミン誘導体、ポリオキシエチレン脂肪酸アミドが例示できる。
前記エステル系界面活性剤としては、多価アルコール脂肪酸エステルが例示できる。
前記ポリオキシエチレンアルキルアミンにおけるアルキル基は、直鎖状、分岐鎖状及び環状のいずれでもよい。
前記アルキルジエタノールアミンにおけるアルキル基は、炭素数が8〜25であることが好ましく、直鎖状又は分岐鎖状であることが好ましい。
前記(B)イオン液体は、帯電防止効果を有するものであれば特に限定されず、公知のものから適宜選択できる。
(B)イオン液体を構成するカチオン部としては、イミダゾリウム系カチオン、ピリジニウム系カチオン、アンモニウム系カチオン、ホスホニウム系カチオンが例示でき、一つ以上のアルキル基を有するものが好ましく、二つ以上のアルキル基を有するものがより好ましい。
前記直鎖状又は分岐鎖状のアルキル基は、炭素数が1〜10であることが好ましく、前記アルキル基としては、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、イソブチル基、sec−ブチル基、tert−ブチル基、n−ペンチル基、イソペンチル基、ネオペンチル基、tert−ペンチル基、1−メチルブチル基、n−ヘキシル基、2−メチルペンチル基、3−メチルペンチル基、2,2−ジメチルブチル基、2,3−ジメチルブチル基、n−ヘプチル基、2−メチルヘキシル基、3−メチルヘキシル基、2,2−ジメチルペンチル基、2,3−ジメチルペンチル基、2,4−ジメチルペンチル基、3,3−ジメチルペンチル基、3−エチルペンチル基、2,2,3−トリメチルブチル基、n−オクチル基、イソオクチル基、ノニル基、デシル基が例示できる。なかでも、炭素数が1〜5であるものがより好ましい。
前記環状のアルキル基は、単環状及び多環状のいずれでもよく、炭素数が3〜10であることが好ましく、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、シクロノニル基、シクロデシル基、ノルボルニル基、イソボルニル基、1−アダマンチル基、2−アダマンチル基、トリシクロデシル基が例示できる。
塩化物イオン(Cl−)、臭化物イオン(Br−)等のハロゲンイオン;
AlCl4 −、Al2Cl7 −等のアルミニウム原子を有する無機イオン;
硝酸イオン(NO3 −)、ホウ酸イオン(B(OH)4 −)、リン酸二水素イオン(H2PO4 −)、過塩素酸イオン(ClO4 −)等の無機オキソ酸イオン;
トリフルオロメチルスルホネートイオン(CF3−S−(=O)3)等のトリフルオロアルキルスルホネートイオン;
酢酸イオン(CH3COO−)等の脂肪族モノカルボン酸イオン;
マレイン酸イオン、コハク酸イオン、アジピン酸イオン等の脂肪族ジカルボン酸イオン;
安息香酸イオン(C6H5COO−)、サリチル酸イオン(C6H4(OH)COO−)等の芳香族モノカルボン酸イオン;
フタル酸イオン等の芳香族ジカルボン酸イオン;
トリフルオロ酢酸イオン(CF3COO−)等のフッ素化脂肪族カルボン酸イオン;
メタンスルホン酸イオン(CH3SO3 −)等の脂肪族スルホン酸イオン;
ベンゼンスルホン酸イオン(C6H5SO3 −)、トルエンスルホン酸イオン(CH3C6H4SO3 −)、ドデシルベンゼンスルホン酸イオン(C12H25C6H4SO3 −)等の芳香族スルホン酸イオン;
トリフルオロメタンスルホン酸イオン(CF3SO3 −)、ヘプタフルオロプロパンスルホン酸イオン(C3F7COO−)、ノナフルオロブタンスルホン酸(C4F9SO3 −)等のフッ素化脂肪族スルホン酸イオン;
ビス(トリフルオロメタンスルホニル)イミドイオン((CF3SO2)2N−、TFSI)、ビス(ペンタフルオロエタンスルホニル)イミドイオン((C2F5SO2)2N−)等のビス(フッ素化アルカンスルホン酸)イミドイオン;
(CF3SO2)(CF3CO)N−等のモノ(フッ素化アルカンスルホン酸)イミドイオン;
トリス(トリフルオロメタンスルホニル)メチドイオン((CF3SO2)3C−)等のトリス(フッ素化アルカンスルホン酸)メチドイオン;
パーフルオロアルキルフルオロボレートイオン;
パーフルオロアルキルフルオロホスフェートイオン;
ボロジカテコレート、ボロジグリコレート、ボロジサリチレート、ボロテトラキス(トリフルオロアセテート)、ビス(オキサラト)ボレート等の四配位ホウ酸イオン;
メチル硫酸、エチル硫酸等の硫酸エステルイオン;
テトラフルオロホウ酸イオン(BF4 −)、ヘキサフルオロリン酸イオン(PF6 −)、ヘキサフルオロヒ酸イオン(AsF6 −)、ヘキサフルオロアンチモン酸イオン(SbF6 −)、ヘキサフルオロニオブ酸イオン(NbF6 −)、ヘキサフルオロタンタル酸イオン(TaF6 −)等の含フッ素無機イオン;
等が例示できる。
前記(C)無機化合物は、(A)界面活性剤及び(B)イオン液体を付着させ、帯電防止性組成物や、後述する成形用組成物において、(A)界面活性剤及び(B)イオン液体を均一に分散させると推測される。
(C)無機化合物は、ケイ素(Si)、カルシウム(Ca)、アルミニウム(Al)及びジルコニウム(Zr)からなる群より選択される一種以上の原子とその他の原子とを含む無機化合物であればよい。そして、高分子化合物及び低分子化合物のいずれでもよく、多孔質及び非多孔質のいずれでもよい。
本発明の帯電防止性組成物としては、さらに、(D)熱可塑性樹脂が配合されてなるもの(以下、「マスターバッチ」と略記する)も、好ましい実施形態として例示できる。後述する成形用組成物を用いて成形体を製造する際に、マスターバッチを利用することで、より均一な組成の成形用組成物が得られ、その結果、より良好な品質の成形体が得られる。
本発明の帯電防止性組成物は、前記(A)界面活性剤、(B)イオン液体、(C)無機化合物、及び必要に応じて(D)熱可塑性樹脂以外に、さらに、これらに該当しない(E)その他の成分が配合されてもよい。
前記(E)その他の成分としては、アルコール類、エーテル類、カルボン酸類、カルボン酸塩類、ポリアルキレンオキサイドが例示できる。
前記アルコール類は、高級アルコール、多価アルコールが好ましい。
前記高級アルコールとしては、ラウリルアルコール、ミリスチルアルコール、セチルアルコール、ステアリルアルコール、セトステアリルアルコール、イソステアリルアルコール等の、炭素数が10以上の直鎖状又は分岐鎖状の一価の(水酸基を一つ有する)アルコール例示できる。
前記多価アルコールとしては、エチレングリコール、ジエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、ポリブチレングリコール、グリセリン、ソルビトール、マルチトール等の、二価以上の(水酸基を二つ以上有する)アルコールが例示できる。
前記エーテル類としては、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンセチルエーテル、ポリオキシエチレンステアリルエーテル等のポリオキシエチレンアルキルエーテル;ポリオキシエチレンオレイルエーテル等のポリオキシエチレンアルケニルエーテル;ジメチルエーテル、エチルメチルエーテル、ジエチルエーテル、ジイソプロピルエーテル等のジアルキルエーテル;フェノールメチルエーテル等のヒドロキシアリールアルキルエーテル;フラン、ジベンゾフラン、テトラヒドロフラン等の環状エーテル;メチルグリシジルエーテル、エチルグリシジルエーテル、ブチルグリシジルエーテル、2−エチルヘキシルグリシジルエーテル、デシルグリシジルエーテル、ネオンペンチルグリコールグリシジルエーテル、p−(sec−ブチル)フェニルグリシジルエーテル、p−(tert−ブチル)フェニルグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、トリメチロールプロパンポリグリシジルエーテル等のグリシジルエーテル類等が例示できる。
前記カルボン酸類は、高級カルボン酸が好ましく、脂肪酸がより好ましく、飽和脂肪酸が特に好ましい。
前記飽和脂肪酸は、炭素数が10以上であることが好ましく、ステアリン酸、カプリン酸、ラウリン酸、ミリスチン酸、パルミチン酸、ベヘン酸等が例示できる。
前記カルボン酸塩類は、高級カルボン酸塩が好ましく、炭化水素鎖中の一つ以上の水素原子が水酸基で置換されていてもよい脂肪酸塩がより好ましく、前記脂肪酸塩は飽和脂肪酸塩であることが好ましい。そして、前記カルボン酸塩類は、金属塩が好ましい。
前記飽和脂肪酸金属塩は、これを構成する脂肪酸残基の炭素数が10以上であるものが好ましく、ステアリン酸バリウム、ステアリン酸カルシウム、ステアリン酸亜鉛、ステアリン酸アルミニウム、ステアリン酸マグネシウム、ステアリン酸リチウム等のステアリン酸金属塩;12−ヒドロキシステアリン酸リチウム、12−ヒドロキシステアリン酸亜鉛、12−ヒドロキシステアリン酸カルシウム、12−ヒドロキシステアリン酸マグネシウム等の12−ヒドロキシステアリン酸金属塩が例示できる。
前記ポリアルキレンオキサイドとしては、ポリエチレンオキサイド、ポリプロピレンオキサイド、ポリテトラメチレンオキサイド等が例示でき、数平均分子量が1万〜70万のものが好ましい。
例えば、混合温度は、(A)界面活性剤の融点以上の温度であることが好ましく、(D)熱可塑性樹脂を使用しない場合であれば、40〜90℃の温度範囲が例示できる。そして、前記成分の溶液又は分散物を使用した場合には、溶媒の沸点以上の温度で混合することで、配合成分の混合と溶媒の除去とを同時に行ってもよい。混合方法は特に限定されず、撹拌子又は撹拌翼等を回転させて混合する方法、ミキサーを使用して混合する方法、超音波を印加して混合する方法等、公知の方法から適宜選択すれば良い。
本発明の成形体は、上記本発明の帯電防止性組成物及び(F)熱可塑性樹脂が配合されてなる成形用組成物を用いて得られたことを特徴とする。
本発明の成形体は、前記帯電防止性組成物を使用したことにより、表面状態が良好でかつ帯電防止効果が高いものとなる。
これに対して、本発明の帯電防止性組成物は、(A)界面活性剤及び(B)イオン液体を併用することで、(B)イオン液体の配合量を大きく低減すると共に、成形体に十分な帯電防止能も付与している。そして、本発明においては、成形用組成物における(B)イオン液体の配合量が0.3質量%以下となるように、帯電防止性組成物の配合量を調節することが好ましい。このような範囲とすることで、得られる成形体の着色や臭気を抑制するより高い効果が得られる。
使用した原料を以下に示す。
[(A)界面活性剤]
(A)−1:ポリオキシエチレンアルキルアミン(ES100、日油社製)
(A)−2:グリセリン脂肪酸エステル(EN1100、日油社製)
[(B)イオン液体]
(B)−1:1−エチル−3−メチルイミダゾリウム トリフルオロメチルスルホネート(メルク社製)
[(C)無機化合物]
(C)−1:短冊状ケイ酸カルシウム(ドバモライトパウダーTK、日本インシュレーション社製、吸油量624ml/100g)
[(F)熱可塑性樹脂]
(F)−1:ポリプロピレン(プライムポリプロJ2023GR、プライムポリマー社製)
[実施例1]
(帯電防止性組成物の製造)
界面活性剤(A)−1(0.5質量部)、及びイオン液体(B)−1(0.05質量部)を、これらの合計濃度が30%となるようにアセトンに溶解させ、アセトン溶液を調製した。
次いで、得られたアセトン溶液に、無機化合物(C)−1(0.1375質量部)を添加し、70℃で撹拌しながらアセトンを揮発させて除去することで、帯電防止性組成物を得た。
得られた帯電防止性組成物の全量と、熱可塑性樹脂(F)−1(99.45質量部)とを混合し、二軸押出機(オメガ30、スティール社製)を使用して、得られた混合物を190℃の温度で溶融混錬した後、210℃、28tの条件で射出成形して、成形体を得た。
得られた成形体を、ポリエチレン製の袋に入れて室温で1日間静置し、次いで、ポリエチレン製の袋から取り出して、23℃、相対湿度50%の環境下で3日間静置して、経時させた。経時後の成形体について、下記方法で表面抵抗率(Ω/□)を測定して帯電防止効果を評価し、さらに表面を目視で観察して、表面状態を評価した。それぞれの評価基準は以下の通りである。評価結果を表1に示す。
抵抗測定器(ハイレスターUP、三菱化学アナリテック社製)を使用して、印加電圧500V、印加時間60秒の条件で成形体の表面抵抗率を測定した。
(帯電防止効果の評価)
表面抵抗率の測定値が1×1010未満であるものを◎、1×1010以上1×1011未満であるものを○、1×1011以上であるものを×とした。
(表面状態の評価)
成形体表面に明らかな凹凸が見られないものを○、明らかな凹凸が見られるものを×とした。
(A)界面活性剤、(B)イオン液体、(C)無機化合物及び(F)熱可塑性樹脂の種類並びに使用量を表1に示すようにしたこと以外は、実施例1と同様に、帯電防止性組成物及び成形体を製造し、成形体を評価した。評価結果を表1に示す。なお、表1中「−」は、その成分が未使用であることを示す。
これに対して、比較例1では、(A)界面活性剤を単独で使用した結果、帯電防止効果が不十分であった。また、比較例2及び3では、(B)イオン液体を単独で使用した結果、表面状態が不良であった。特に比較例3は、比較例2よりも帯電防止効果が向上したものの、表面状態がさらに悪化していた。
比較例3では、(B)イオン液体の使用量を10倍にすることで、比較例2よりも一桁小さい表面抵抗率を達成し、その値は実施例1と同程度の優れたものである。また、比較例1及び3の結果から明らかなように、(A)界面活性剤は(B)イオン液体よりも帯電防止能が大きく劣り、比較例1では比較例3よりも表面抵抗率が三桁も大きい。すると、比較例2の帯電防止性組成物の帯電防止能を向上させることを考えた場合、比較例2の帯電防止性組成物に、(B)イオン液体をさらに0.45質量部追加して使用量を10倍の0.5質量部とした比較例3の組成物に対して、(B)イオン液体ではなく(A)界面活性剤を0.45質量部追加して、(A)界面活性剤及び(B)イオン液体の総使用量を0.5質量部とした組成物を想定すると、このような組成物は、比較例3の組成物よりも、帯電防止効果が大きく劣る成形体を与えると予測される。ところが、実施例1での表面抵抗率は、比較例3と同程度である。実施例1での(A)界面活性剤の使用量は、0.45質量部ではなく0.5質量部であり、上記で想定した組成物よりも0.05質量部多いが、上記のように(A)界面活性剤が、(B)イオン液体よりも単独使用では帯電防止能で大きく劣ることを考慮すると、実施例1が比較例3と同程度の優れた表面抵抗率を示したことは、全く意外であり、実施例1は比較例1〜3の結果から想定される範囲を超える帯電防止効果を示している。すなわち、本発明においては、(A)界面活性剤及び(B)イオン液体を併用することで、これらを単独で使用した場合よりも、帯電防止能の点で極めて優れた相乗効果を発現していると推測される。
Claims (6)
- (A)界面活性剤、(B)イオン液体、並びに(C)ケイ素、カルシウム、アルミニウム及びジルコニウムからなる群より選択される一種以上の原子とその他の原子とを有する無機化合物が配合されてなることを特徴とする帯電防止性組成物。
- さらに、(D)熱可塑性樹脂が配合されてなることを特徴とする請求項1に記載の帯電防止性組成物。
- 前記(A)界面活性剤が、窒素原子を有するノニオン性界面活性剤であり、前記(B)イオン液体がイミダゾリウム系カチオンを有するものであることを特徴とする請求項1又は2に記載の帯電防止性組成物。
- 前記(C)無機化合物が、ケイ酸カルシウム、シリカ、炭酸カルシウム、アルミナ又はジルコニアであることを特徴とする請求項1〜3のいずれか一項に記載の帯電防止性組成物。
- 前記(D)熱可塑性樹脂が、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリスチレン、ポリ酢酸ビニル、ポリメタクリル酸メチル、AS樹脂又はABS樹脂であることを特徴とする請求項1〜3のいずれか一項に記載の帯電防止性組成物。
- 請求項1〜5のいずれか一項に記載の帯電防止性組成物及び(F)熱可塑性樹脂が配合されてなる成形用組成物を用いて得られたことを特徴とする成形体。