JP2012111793A - 粘着剤組成物および表面保護粘着フィルム - Google Patents
粘着剤組成物および表面保護粘着フィルム Download PDFInfo
- Publication number
- JP2012111793A JP2012111793A JP2010259250A JP2010259250A JP2012111793A JP 2012111793 A JP2012111793 A JP 2012111793A JP 2010259250 A JP2010259250 A JP 2010259250A JP 2010259250 A JP2010259250 A JP 2010259250A JP 2012111793 A JP2012111793 A JP 2012111793A
- Authority
- JP
- Japan
- Prior art keywords
- polymer
- weight
- polymer block
- block
- aromatic alkenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】重合体(ii):重合体ブロックAおよび重合体ブロックBを含み、一般式A−B−Aもしくは一般式(A−B)x−Y(式中、xは1以上の整数を表し、Yはカップリング剤残基を表す。)で表される構造を有するブロック共重合体(II)またはその水素添加物を含有し、前記重合体(ii)の全体の芳香族アルケニル化合物単位含有率(St(A+B))は、30〜50重量%であり、前記重合体(ii)にそれぞれ含まれるAの総量とBの総量との重量比(A:B)が5:95〜25:75の範囲内であり、さらに、前記重合体(ii)の合計重量の100重量部に対し、20重量部以上の粘着付与剤と、2~10重量部の軟化剤と、を含有することを特徴とする粘着剤組成物。
【選択図】なし
Description
特許文献1には、適当な初期粘着力を確保しつつ、展開性に優れ、被着体に対する剥離後の糊残りが防止された表面保護粘着フィルムが得られることが記載されている。
その一方で、高い粘着力を有する表面保護粘着フィルムでは、展開力が重く、また糊残りが発生するという不具合が生じることがある。
前記重合体(i)および前記重合体(ii)にそれぞれ含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比(A:B)が5:95〜25:75の範囲内である。粘着剤組成物はさらに、前記重合体(i)および前記重合体(ii)の合計重量の100重量部に対し、20重量部以上の粘着付与剤と、2~10重量部の軟化剤と、を含有する。
重合体ブロックA:
芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロック
重合体ブロックB:
共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロック
本明細書において数値範囲を表すために用いられる記号「〜」は、特に記載の無い限り、当該数値範囲がその両端の数値を含むことを意図して用いられる。
本明細書において、用語「芳香族アルケニル化合物単位含有率」等において用いられる重合体の繰り返し単位の「含有率」とは、繰り返し単位が由来するモノマーに換算した重量比、すなわち、前記重合体を形成するための全モノマーの重量に対する、前記繰り返し単位が由来するモノマーの重量の比(重量%)、すなわち重合体の芳香族アルケニル化合物含量[alkenyl aromatic compound content]を意味する。ここで、「前記重合体を形成するための全モノマーの重量」は、前記重合体の重量に近似する。また、同様に、本明細書において、重合体ブロックの繰り返し単位の「含有率」とは、繰り返し単位が由来するモノマーに換算した重量比、すなわち、前記重合体ブロックを形成するための全モノマーの重量に対する、前記繰り返し単位が由来するモノマーの重量の比(重量%)を意味する。ここで、「前記重合体ブロックを形成するための全モノマーの重量」は、前記重合体ブロックの重量に近似する。
本明細書において、「ビニル結合の含有率」は、赤外吸収スペクトル法を用い、モレロ法により算出した1,2−ビニル結合および3,4−ビニル結合の総含有率を意味する。
本発明の粘着剤組成物は、下記重合体(ii)を含有する。粘着剤組成物は、下記重合体(i)をさらに含有してもよい。本明細書中、「重合体(i)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式[A−B]n(式中、Aは重合体ブロックAを、Bは重合体ブロックBを、nは1〜3の整数を表す。)で表される構造を有する共重合体(I)またはその水素添加物である。
本明細書中、「重合体(ii)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは2以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)
で表される構造を有する共重合体(II)またはその水素添加物である。
なお、本明細書中、前記重合体(i)と前記重合体(ii)とからなる組成物を、単に「共重合体組成物」と称する場合がある。
前記重合体(i)と前記重合体(ii)に含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比が5:95〜25:75の範囲内である。
上述のように、「重合体ブロックA」は、芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロックである。
上述のように、「重合体ブロックB」は、共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロックである。
なお、「重合体ブロックB」は、本発明の効果を妨げない範囲において、共役ジエン化合物単位、および芳香族アルケニル化合物単位以外の繰り返し単位も含んでいてもよい。
「共重合体(I)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式[A−B]n(式中、Aは重合体ブロックAを、Bは重合体ブロックBを、nは1〜3の整数を表す。)で表される構造を有する共重合体である。
な生産性が良好となる。なお、粘着力および材料強度を向上させるという観点から、nが1〜2であることがより好ましく、1であることが特に好ましい。すなわち、「一般式[A−B]nで示される構造を有する共重合体」としては、一般式A−Bで示される構造を有するブロック共重合体が特に好ましい。
、共役ジエンモノマーに由来する二重結合が80%以上、好ましくは90%以上、より好ましくは95%以上、水素添加により不飽和結合が飽和結合に水素添加された水素添加物であることが好ましい。
。なお、本明細書中、水素添加の比率(水素添加率)は、四塩化炭素を溶媒として用い、270MHz、lH−NMRスペクトルから算出した水素添加率を意味する。
重合体(i)は、単独(1種)であってもよく、2種以上の組み合わせであってもよい。
「共重合体(II)」は、下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは2以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)
で表される構造を有する共重合体である。
末端の重合体ブロックAは共重合体(II)全体の2重量%以上を占めていることが好ましい。重合体ブロックAの効果を確実に発揮させるためである。なお、一部の共重合体(II)の末端が−Bの構造を有していても、末端の重合体ブロックBの含有率が共重合体(II)全体の2重量%未満である場合には、末端が重合体ブロックAであるのと同様の効果を発揮させることができる。すなわち、前記構造は実質的に末端が重合体ブロックAであるとみなすことができる。
重合体(ii)は、単独(1種)であってもよく、2種以上の組み合わせであってもよい。
上述のように、本発明の粘着剤組成物は、重合体(ii)を構成成分として含有するか、または重合体(i)と重合体(ii)とからなる共重合体組成物を構成成分として含有する。この共重合体組成物において、重合体(i)と重合体(ii)との重量比は、90:10〜0:100の範囲内であることが好ましい。重合体(i)を含ませることにより、被着体の表面から粘着剤層が浮き上がり、フィルムが剥離してしまう不具合(浮き)を有効に防止することができるという好ましい効果を発揮させることができる。一方、重合体(i)と重合体(ii)との総量100重量部中、重合体(ii)を10重量部以上含ませることにより、被着体の表面からフィルムを剥離させる際に、被着体の表面に粘着剤が残存して被着体の表面を汚染してしまう不具合(糊残り)を有効に防止することができるという好ましい効果を発揮させることができる。
粘着剤層の浮きや糊残りをより確実に防止するという観点から、重合体(i)と重合体(ii)との重量比は50:50〜15:85の範囲内であることが好ましい。
本発明の表面保護粘着フィルムは、基材層と、前記で説明した本発明の粘着剤組成物からなる粘着剤層と、を有する。
好ましくは、当該粘着剤層は、当該基材層の一方の表面上に積層されている。
当該基材層として好ましくは、ポリオレフィン基材層である。
当該「ポリオレフィン」としては、例えば、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、直鎖低密度ポリエチレン、エチレン−α−オレフィン共重合体、エチレン−エチルアクリレート共重合体、エチレン−酢酸ビニル共重合体、エチレン−メチルアクリレート共重合体、エチレン−n−ブチルアクリレート共重合体、およびポリプロピレン(ホモポリマー、ランダムコポリマー、ブロックコポリマー)等が挙げられる。
これらは単独または2種以上を組み合わせて用いることができる。また、「ポリオレフィン」は、置換基を有するポリオレフィンであってもよく、ポリオレフィン以外の樹脂が添加されていてもよい。さらに、表面保護粘着フィルムの製造過程で生じた、ポリオレフィン基材層の端材や表面保護粘着フィルムの端材が添加されていてもよい。
基材層は、単層でもよいし、組成の異なる2種以上の多層構造を有している層であってもよい。
基材層は、表面保護粘着フィルムの用途等によって、その厚さを適宜調整することができる。通常、10〜100μm程度の厚さに設定することが適している。
前記粘着剤層は、本発明の粘着剤組成物からなる。当該粘着剤組成物は、前記重合体(ii)又は前記重合体(ii)および前記重合体(i)に加えて、必要に応じて、粘着付与剤、スチレン系ブロック相補強剤、軟化剤、酸化防止剤、光安定剤、紫外線吸収剤、充填剤、顔料、粘着昂進防止剤、オレフィン系樹脂、シリコーン系ポリマー、液状アクリル系共重合体、リン酸エステル系化合物等の公知の添加剤を適宜含有してもよい。
なお、「相溶」とは、共重合体組成物に粘着付与剤を配合することにより得られる配合物のtanδピーク温度が、共重合体組成物のtanδピーク温度とは異なる値になる状態のことをいう。なお、本明細書中、「tanδピーク温度」とは、tanδの最大となる温度を意味する。
本発明で用いられるスチレン系ブロック相補強剤としては、例えば、モノマー単位として、スチレンおよびα−メチルスチレン、p−メチルスチレン、p−クロロスチレン、クロロメチルスチレン、tert−ブチルスチレン、p−エチルスチレン、ジビニルベンゼン等のスチレン系化合物が挙げられる。これらは、単独または2種以上を組み合わせて用いることができる。つまり、スチレン系ブロック相補強剤は、これらモノマーを重合することによって得ることができる。2種以上のモノマーからなる共重合体の場合は、ブロック共重合体であってもよいし、ランダム共重合体であってもよい。なかでも、スチレン系ブロック相補強剤は、100℃程度以上の軟化点を有するものが好ましく、150℃以上がより好ましい。具体的には、イーストマンケミカル社製、商品名「ENDEX155」(軟化点155℃)、「ENDEX160」(軟化点160℃)等が好適に使用される。
具体的な市販品としては、荒川化学社製、商品名「スーパーエステルL」、「スーパーエステルA18」、出光興産社製、商品名「ダイアナプロセスオイル」等が好適に使用される。
光安定化剤としては、ヒンダードアミン系化合物が挙げられる。
紫外線吸収剤としては、特に限定されず、例えば、サリチル酸系、ベンゾフェノン系、ベンゾトリアゾール系、シアノアクリレート系等が挙げられる。
粘着昂進防止剤としては、脂肪酸アミド、ポリエチレンイミンの長鎖アルキルグラフト物、大豆油変性アルキド樹脂(例えば、荒川化学工業社製、商品名「アラキード251」等)、トール油変性アルキド樹脂(例えば、荒川化学工業社製、商品名「アラキード6300」等)などが挙げられる。
これらの添加剤は、単独で使用してもよいし、2種以上を併用してもよい。
粘着付与剤は、表面保護粘着フィルムを被着体から剥離する際の糊残りを防止できる量で使用することが適している。例えば、プリズムシート用の表面保護粘着フィルムとして使用する場合には、粘着剤組成物における粘着付与剤の含有量は、ゴム系樹脂成分[前記重合体(ii)、または前記重合体(i)および前記重合体(ii)(以下、これらをまとめて、芳香族アルケニルブロック共重合体と称する場合がある。)]100重量部に対し、好ましくは20重量部以上であり、より好ましくは20〜50重量部であり、さらに好ましくは25〜40重量部である。
粘着剤付与剤の含有量が20重量部以上であることで、帯電防止処理が施されている光学フィルムに対して、十分な初期粘着力を得ることができる。また、粘着剤付与剤の含有量が50重量部以下であることで、糊残りの発生が抑制される。
軟化剤の含有量が2重量部以上であることで、帯電防止処理が施されている光学フィルムに対しても、十分な初期粘着力が得られる。10重量部以下であることで、展開力が重くならず、糊残りの発生が抑制される。
表面保護粘着フィルムは、粘着剤層中に、前記重合体(ii)、または前記重合体(i)および前記重合体(ii)に加えて、特定の割合で粘着付与剤と軟化剤とを含有することにより、特に帯電防止処理が施されている光学フィルムに対して、初期粘着力を確保しつつ、展開性に優れ、被着体に対する糊残りを抑制することができる。
上述の表面保護粘着フィルムは、シート積層体に適用可能である。
シート積層体とは、表面保護粘着フィルムと、表面保護粘着フィルムが貼り付けられた他のシートと、を備える。他のシートとしては、プリズムシート等の光学フィルムが用いられる。シート積層体において、表面保護粘着フィルムが貼り付けられる他のシートは、少なくともシート表面に帯電防止処理が施されていることが好ましい。
本発明の粘着剤組成物は、例えば、共重合体(I)および共重合体(II)をそれぞれブロック重合により合成し、これらを所定の質量比でブレンドした後に、所望により水素添加を行って、共重合体(I)またはその水素添加物、および共重合体(I)またはその水素添加物の混合物を得、および所望により配合される添加剤を慣用の方法で混合することによって製造される。
第1工程:[A−B]の構造を有する共重合体をブロック重合により合成する工程と、
第2工程:前記[A−B]の構造を有する共重合体の一部を、カップリング剤Y−Zx(但し、「Y」はカップリング剤残基、「Z」は脱離基、「X」は2以上の整数を示す。)によりカップリングさせ、{[A−B]x−Y}の構造を有する共重合体を合成する工程と、
水素添加物を得る場合には、更に、
第3工程:前記[A−B]の構造を有する共重合体及び前記{[A−B]x−Y}の構造を有する共重合体に水素添加することにより、それぞれ水素化された共重合体(I)と共重合体(II)とからなる共重合体組成物を得る工程と
を備える。
本発明の表面保護粘着フィルムは、光学板、プリズムシート、および拡散フィルム等の凹凸のある被着体に好適に用いることができるが、これに限定されるものではなく、例えば、表面が平滑なシートの表面保護にも使用することができる。
被着体となるシートを構成する材料としては、特に限定されないが、透光性を有する樹脂、例えばアクリル系樹脂、ポリカーボネート等が挙げられる。
重合体ブロックA
窒素置換された反応容器に、脱気・脱水されたシクロヘキサン500質量部、スチレン20質量部及びテトラヒドロフラン5質量部を仕込み、重合開始温度の40℃にてn−ブチルリチウム0.13質量部を添加して、昇温重合を行った。
重合体ブロックB
重合体Aの重合転化率が略100%に達した後、反応液を15℃に冷却し、次いで、1,3−ブタジエン70質量部およびスチレン10質量部を加え、更に昇温重合を行った。
「St(A+B)」は、全重合体の芳香族アルケニル化合物単位含有率であり、次式で表される数値を意味する。なお、これは、下記「St(B)」と下記「St(A)」との和に等しい。
式:
St(A+B)=(全重合体中の芳香族アルケニル化合物単位重量)/(全重合体中の全単量体単位重量)×100(重量%)
「St(B)」は、次式で表される数値を意味する。
式:
St(B)=(全重合体ブロックB中の芳香族アルケニル化合物単位重量)/(全重合体中の全単量体単位重量)×100(重量%)
「St(A)」は、次式で表される数値を意味する。
式:
St(A)=(全重合体ブロックA中の芳香族アルケニル化合物単位重量)/(全重合体中の全単量体単位重量)×100(重量%)
「St(b)」は、重合体ブロックBの芳香族アルケニル化合物単位含有率であり、次式で表される数値を意味する。
式:
St(b)=(全重合体ブロックB中の芳香族アルケニル化合物単位重量)/(全重合体ブロックB中の全単量体単位重量)×100(重量%)
また、表1中、「A:B」は、重合体ブロックAの総量と重合体ブロックBの総量との重量比を表す。
また、表1中、「(i):(ii)」は、重合体(i)と重合体(ii)の重量比を表す。
また、表1中、「共役ジエン含有率」は、重合体ブロックBの共役ジエン単位含有率を表す。
また、表1中、「ビニル結合含有率」は、重合体ブロックBのビニル結合の含有率を表す。
上記の各合成方法により得られた各共重合体組成物(表2)100重量部に、粘着付与剤として、アルコンP100(荒川化学工業社製)を40重量部、軟化剤として、スーパーエステルL(荒川化学工業社製)5重量部を配合し、各粘着剤組成物を得た。その組成を下記の表2に示す。
上記のようにして得られた各表面保護粘着フィルムについて、以下の項目を評価した。それらの結果を表3に示す。
上記のようにして共押出しにより製膜した各表面保護粘着フィルムの外観を目視にて評価し、外観上問題が無ければ「○」とした。
バインダー樹脂100重量部に帯電防止剤としてFC-440(3M社製)を3重量部配合して、凹凸を有する帯電防止処理されたプリズムシートを作成した。その後、各表面保護粘着フィルムを、帯電防止処理されたプリズムシートのレンズ面を覆うように貼り付けた。プリズムシートとしては、厚みが130μmのアクリル樹脂からなり、プリズムのピッチ50μm、高さ25μmであるものを用意した。貼り付け条件は、室温23℃および相対湿度50%の環境下、それぞれ2kgの圧着ゴムローラーを用いて、300mm/分の速度で貼り付け、その状態で30分間放置した後、JIS Z0237に準拠し、25mm幅における180度剥離強度を300mm/分の速度で測定した。この際の剥離方向はプリズムの稜線方向とした。このようにして測定された剥離強度を初期粘着力とした。
各表面保護粘着フィルムを、室温23℃および相対湿度50%の環境下、(2)の初期粘着力評価に用いたプリズムシートの表面に、それぞれ2kgの圧着ゴムローラーを用いて、300mm/分の速度で貼り付けた。その後、ポリカーボネート板(厚み2mm)で表面保護粘着フィルムを貼り付けたプリズムシートを挟み、6.0×10−3MPaの圧力を加え、その状態で60℃および相対湿度90%の環境下、48時間放置した。これを室温に取り出し、30分間放置した後、JIS Z0237に準拠し、25mm幅における180度剥離強度を300mm/分の速度で測定した。
このようにして測定された剥離強度を経時粘着力とし、初期粘着力から経時粘着力の変化率(粘着昂進率)を次式で算出した。
変化率(粘着昂進率)=(経時粘着力/初期粘着力)×100
実施例および比較例の各表面保護粘着フィルムの50mm幅の巻回体を巻き戻し速度を変更したこと以外はJIS Z0237に準拠し、15m/分の巻戻し速度で巻戻し力を測定し、展開力とした。
粘着力(初期)
○(優 ):0.1N/25mm以上
×(不良):0.1N/25mm未満
粘着力(変化率)
◎(優 ):200%未満
○(良 ):200%以上500%以下
×(不良):500%超
展開力
◎(優 ):2.0N/50mm未満
○(良 ):2.0N/50mm以上3.5N/50mm以下
×(不良):3.5N/50mm超
本発明の表面保護粘着フィルムは、プリズムシート、拡散フィルム等の表面保護に好適に用いられる。
2 シート部
3 レンズ部(プリズム)
3a レンズ部の頂部(プリズム頂角)
4 第1の表面保護粘着フィルム
5 基材層
6 粘着剤層
7 第2の表面保護粘着フィルム
Claims (3)
- 重合体(ii):下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは1以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)で表される構造を有する共重合体(II)またはその水素添加物を含有し、
前記重合体(ii)の芳香族アルケニル化合物単位含有率(St(A+B))は、30〜50重量%であり、
前記重合体(ii)に含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比(A:B)が5:95〜25:75の範囲内であり、
さらに、前記重合体(ii)100重量部に対し、
20重量部以上の粘着付与剤と、
2~10重量部の軟化剤と、
を含有することを特徴とする粘着剤組成物。
重合体ブロックA:
芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロック
重合体ブロックB:
共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロック - 重合体(i):下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式[A−B]n(式中、Aは重合体ブロックAを、Bは重合体ブロックBを、nは1〜3の整数を表す。)で表される構造を有する共重合体(I)またはその水素添加物と、
重合体(ii):下記重合体ブロックAおよび下記重合体ブロックBを含み、一般式A−B−A(式中の記号は前記と同意義を表す。)もしくは一般式(A−B)x−Y(式中、xは1以上の整数を表し、Yはカップリング剤残基を、その他の記号は前記と同意義を表す。)で表される構造を有する共重合体(II)またはその水素添加物と、
を含有し、
前記重合体(i)および前記重合体(ii)の全体の芳香族アルケニル化合物単位含有率(St(A+B))は、30〜50重量%であり、
前記重合体(i)および前記重合体(ii)にそれぞれ含まれる重合体ブロックAの総量と重合体ブロックBの総量との重量比(A:B)が5:95〜25:75の範囲内であり、
さらに、
前記重合体(i)および前記重合体(ii)の合計重量100重量部に対し、20重量部以上の粘着付与剤と、
2~10重量部の軟化剤と、
を含有することを特徴とする粘着剤組成物。
重合体ブロックA:
芳香族アルケニル化合物単位が連続し、芳香族アルケニル化合物単位を主体とする重合体ブロック
重合体ブロックB:
共役ジエン単位と芳香族アルケニル化合物単位がランダムに含まれる芳香族アルケニル−共役ジエン共重合体ブロックであって、芳香族アルケニル化合物単位含有率(St(b))が10〜35重量%である重合体ブロック - 基材層と、請求項1又は2に記載の粘着剤組成物からなる粘着剤層と、を有する表面保護粘着フィルム。