JP2011231589A - 吹き付け深堀壁及びその製造方法 - Google Patents
吹き付け深堀壁及びその製造方法 Download PDFInfo
- Publication number
- JP2011231589A JP2011231589A JP2010105518A JP2010105518A JP2011231589A JP 2011231589 A JP2011231589 A JP 2011231589A JP 2010105518 A JP2010105518 A JP 2010105518A JP 2010105518 A JP2010105518 A JP 2010105518A JP 2011231589 A JP2011231589 A JP 2011231589A
- Authority
- JP
- Japan
- Prior art keywords
- wall
- layer
- coating
- deep
- sprayed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明は、建造物の壁面に、厚塗りと凹凸模様を形成した吹き付け深堀壁であって、樹脂発泡粒子と、モルタルに合成ゴムディスバージョンを加えたポリマーセメントモルタルを混合した下塗り層1と、骨材を含むか又は含まない樹脂又は合成ゴムディスバージョンを含む中塗り層2と、シロキサン架橋型アクリル−珪素重合体を含む上塗り層3が、この順番に吹き付け塗装により形成されており、前記下塗り層1は厚塗りと深堀の凹凸模様を有し、前記中塗り層2は下塗り層の表面を円滑化し、前記上塗り層3は親水性防汚膜である。
【選択図】図1
Description
(1)樹脂発泡粒子と、モルタルに合成ゴムを含むポリマーセメントモルタルを混合した下塗り層と、
(2)骨材を含むか又は含まない樹脂又は合成ゴムを含む中塗り層と、
(3)シロキサン架橋型アクリル−珪素重合体を含む上塗り層
が、この順番に形成されており、
前記下塗り層は厚塗りと深堀の凹凸模様を有し、
前記中塗り層は下塗り層の表面を円滑化し、
前記上塗り層は親水性防汚膜であることを特徴とする。
(1)樹脂発泡粒子と、モルタルに合成ゴムディスバージョンを加えたポリマーセメントモルタルを混合した下塗り塗装材を、吹き付け塗装により、厚塗りかつ深堀の凹凸模様に形成し、乾燥後、
(2)骨材を含むか又は含まない樹脂又は合成ゴムディスバージョンを含む中塗り塗装材を塗装し、乾燥後、
(3)シロキサン架橋型アクリル−珪素重合体を含む上塗り材を塗装し、乾燥することを特徴とする。
下塗り材は、樹脂発泡粒子と、モルタルに合成ゴムディスバージョンを加えたポリマーセメントモルタルと、必要な場合調整水を加えて混合し作成する。例えば合成ゴムディスバージョン液18kgに対して、モルタルパウダー75kgを加え(ポリマーセメントモルタル合計93kg)、さらに保水剤(例えばメチルセルロース)164gと、樹脂発泡粒子を45リットル加えて混合する。下塗り材は、乾燥後の比重が0.9〜1.2g/cm3程度が好ましい。これにより、吹付塗装により厚塗りしても塗装材が液ダレすることがない状態になる。また、比重が軽いことから、塗膜全体の重量を軽くでき、高層建築物にも好適な深堀壁を形成できる。
中塗り層は下塗り層の大きな凹凸を埋めて表面を円滑な面に修正するため、及び必要な場合は骨材発色させるために形成する。中塗り層は骨材を含んでいてもよいし、含まなくてもよい。斫り出し壁の場合には骨材を使用し、ダイキャスト壁の場合には使用しなくても良い。前記において骨材とは、自然石、自然石に顔料を加えて焼き付けた焼付け骨材、セラミック、レンガ、陶磁器、鋼滓等を粉砕し、平均粒子径0.1〜5mm程度に篩分けして整えた粒子をいう。骨材は、例えばダイキャスト壁の場合は、骨材として細かい砂を使用するのが好ましい。御影石の斫り出し壁の場合は、骨材が複数色(例えば3色)の塗材であり、前記複数色の塗材が非混合多色状に同時吹きされているのが好ましい。御影石の斫り出し壁に使用する骨材は、自然石粒子、セラミックス粒子、自然石粒子やセラミックス粒子の表面に着色顔料を付着させて焼き付けた着色骨材などが好ましく、骨材は比較的大粒であっても良い。無機粉体を含んでも良く、例えばシリカ、タルク、クレイなどの自然界に存在する鉱物粉体であり、前記骨材よりは細かい平均粒子に篩分けして調製する。塗布材には、その他増粘剤、pH調整剤、消泡剤、造膜助剤、水及び/又は溶剤を加えてもよい。中塗り層は、樹脂又は合成ゴムディスバージョンを含む塗材を吹付塗装又はローラー塗り又はコテ塗りして形成する。
上塗り層はシロキサン架橋型アクリル−珪素重合体を含む親水性防汚膜である。前記した下塗り層と中塗り層(以下併せて「基材層」ともいう。)の表面に、上塗り層としてシロキサン架橋型アクリル−珪素重合体を含む親水性防汚膜をスプレー塗装により形成する。上塗り層は1層でも良いし、何層か積層しても良い。光沢があってもよい場合は、艶消し剤を加えない上塗り層を1層とする。光沢を抑える場合は、何層か積層する。何層か積層する場合は、まず、艶消し剤を加えないシロキサン架橋型アクリル−珪素重合体を含む第1上塗りコーティング剤を塗装するのが好ましい。この塗料を塗布すると、塗料の一部は基材層に浸入するが、浸入しても塗料組成及び塗膜組成の均一性は保たれ、耐久性の高いコーティング膜となる。加えて、第1上塗りコーティング層は基材層とシロキサン結合により化学結合するため、強固な密着となり、長期間美装状態を保ち、かつメンテナンスが不要で耐久性の高いコーティング層となる。上塗り層の各1層あたりの乾燥膜厚は20〜400μmが好ましく、さらに好ましくは50〜300μmである。上塗り剤溶液の単位面積当たりの吹付塗装量でいうと、各1層あたり20〜200g/m2が好ましく、さらに好ましくは50〜200g/m2である。塗料に艶消し剤を含むと、塗料の一部が基材層に浸入する際に、艶消し剤はコーティング層に残されてしまい、艶消し剤の濃度が高い部分が生じ、長期間経過したときに剥離しやすくなる。
(1)CH2=CHCOO(CH2)3Si(OCH3)3
(2)CH2=C(CH3)COO(CH2)3Si(OCH3)3
(3)CH2=C(CH3)COO(CH2)3Si(CH3)(OCH3)2
(4)CH2=CHCOO(CH2)3Si(OC2H5)3
(5)CH2=CHCOO(CH2)3Si(CH3)(OC2H5)2
(6)CH2=C(CH3)COO(CH2)3Si(OC2H5)3
(7)CH2=C(CH3)COO(CH2)3Si(CH3)(OC2H5)2
(1)シルバー〜ホワイト色
Biflair, Iriodin100, Iriodin103, Iriodin111, Iriodin119, Iriodin120, Iriodin123, Iriodin153, Iriodin163, Iriodin 183, Iriodin6103, Miraval5311, Miraval5411, Miraval5511
(2)ゴールド色
Iriodin201, Iriodin249, Iriodin300, Iriodin302, Iriodin303, Iriodin305, Iriodin306, Iriodin323, Iriodin325, Iriodin326, Iriodin351, Iriodin355, Iriodin383, Iriodin5320, Iriodin5420, Iriodin7205
(3)レッド〜銅色
Iriodin500, Iriodin502, Iriodin504, Iriodin520, Iriodin522, Iriodin524, Iriodin530 Iriodin532, Iriodin534, Iriodin4505, Iriodin7217, Colorstream F10-00, Miraval5321, Miraval5421
(4)バイオレット色
Iriodin211, Iriodin223, Iriodin259, Iriodin7215, Iriodin7219, Colorstream T10-01, Colorstream T10-06, Miraval5422, Miraval5423
(5)ブルー〜グリーン色
Iriodin221, Iriodin231, Iriodin299, Iriodin7225, Iriodin7235, Colorstream T10-02, Colorstream T10-03, Colorstream T10-04, Colorstream T10-05, Miraval5325, Miraval5424, Miraval5425, Miraval5426
建造物の下地としては、メタルラス、ワイヤラス、ラスシートなどのラス下地と、コンクリート、レンガ、ALCパネル、PCパネルなどの躯体下地に大別される。本発明はどのように下地にも適用できる。本発明の下塗り材は、下地との接着強力が高く、とくに付着性向上処理を必要とせず、下地に直接下塗り材を塗装できる。近年はタイル貼り壁面の劣化によるタイルの剥離が問題になっているが、タイル貼り壁面が下地の場合は、ネットを貼り付け、アンカーボルトで固定し、前記ネットの上に本発明の下塗り材で使用する合成ゴムディスバージョンを塗装し、この上に下塗り塗装材を塗装するのが好ましい。
(1)サンシャインウェザーメーターによる促進試験
試験機:スガ試験機社製、型番“WE−SUN−HC−DC”
光源:1灯式・セリウム入り有芯カーボンを上下各4本組み合わせ
光線波長:280〜400nm
放射照度:フィルター付き255±45W/m2、フィルターなし285±50W/m2
光フィルター:耐熱性光学ガラス板使用・8枚1組、255nm以下の短波長成分をカット、355nmまでの成分を10〜50%透過
放出電力:50V、60A(3000W)
雰囲気温度:63±3℃
シャワー:120分中18分間降雨先降り運転
スプレー水量:2100±100ml/min(pH6.0〜8.0、水温16±5℃)
試料枚数:70×150mm、76枚
運転サイクル:60Hr
(2)ひび割れ有無
サンシャインウェザーメーターによる促進試験後の試料表面を目視により観察し、次のように評価した。
(3)変色
サンシャインウェザーメーターによる促進試験後の試料表面を目視により観察し、次のように評価した。
(4)意匠性
目視観察により判断した。
実施例1は御影石の斫り出し壁の例を示す。
コンクリートの躯体下地に下塗り層を直接吹付塗装した。下塗り材として、下記の材料を使用した。
(1)オバナヤ・セメンテックス社製商品名"セメンテックスCMS−1"(カチオンSBR系ポリマーセメントモルタル)のA材(マトリックス樹脂液)18kg、B材(無機パウダー、モルタルエースMS−1)75kg、A材+B材合計93kg
(2)粒子径0.4〜0.9mm(平均粒子径6.5mm、篩い分けにより測定)、嵩比重0.1g/cm3、発泡倍率10倍のポリスチレン発泡粒子を43.5リットル
(3)保水剤(メチルセルロース、松本油脂製薬株式会社製商品名“マーポローズ”)675g
(4)調整水を11.25kg
以上を容器に入れて混合して調整した。比重は約1であった。この下塗り材を図3に示す口径が18mmのリシンガンに入れて壁表面に吹付塗装により大玉状に塗装した。吹付塗装後、外気で乾燥した。表面研磨はしなかった。得られた下塗り層は、図1Aの断面図に示すような形状で、最大厚さが15mm、かつ凹凸の差も15mmの厚さであった。単位面積当たりの塗布量は、乾燥重量で2〜3kg/m2であった。得られた下塗り層を鉄製ハンマーで強く叩いても破壊することは無く、弾性もあり、強い地震にも耐えられることがわかった。
吹き付け材としては、次の成分に調合したものを用いた。
(1)骨材 61.60重量部
(2)アクリルエマルジョン(固形分50%) 25.20重量部
(3)増粘剤(ヒドロキシメチルセルロース) 11.35重量部
(4)pH調整剤(アンモニア水) 0.17重量部
(5)消泡剤(アルコール系) 0.03重量部
(6)造膜助剤(アルコール系) 0.39重量部
(7)水 1.26重量部
作業性や貯蔵の便のために増粘剤、pH調整剤、消泡剤、造膜助剤等が混入されている。ここで、造膜助剤とは、エマルジョンの透明造膜の温度を下げるためのものである。骨材としては、白色骨材は寒水石等の自然石を粉砕したもの、黒色は黒曜石等の自然石を粉砕したもの、灰色は寒水石を粉砕したものと黒曜石を粉砕したものを別々に混合して使用した。すなわち、黒色、灰色、白色の3色の塗装材を準備した。骨材の粒度分布は、建築物用壁装材の模様の表現によって自由に選択することができるが、その強度や美観から、次の表1に示す粒度分布のものを採用した。表1において、メッシュとは1インチ(25.4mm)あたりの篩目の数をいう。なお、骨材の色は目的により様々のものを使用でき、骨材も焼付け骨材、セラミックスなどさまざまなものを使用できる。
(1)第1上塗り材
第1上塗り材として、下記のコーティング剤(クリヤー液)と硬化剤を混合しスプレー塗布した。
A.クリヤー液(基剤)
エトキシシリル基含有ビニル重合体(数平均分子量15000) 43重量部
添加剤(消泡剤+光安定剤+顔料分散剤) 1重量部
溶剤(酢酸エチル) 2重量部
溶剤(酢酸ブチル) 2重量部
溶剤(キシレン) 45重量部
基剤 計93重量部
B.硬化剤
有機錫(ジブチル錫ジラウレ−ト)の混合物 1重量部(有機錫は0.1重量部)
溶剤(キシレン) 6重量部
硬化剤 計7重量部
AとBの合計100重量部
塗布量100g/m2(乾燥重量(固形分)で50g/m2)1回塗り
(2)中間塗りコーティング剤(半艶)
A.半艶消しクリヤー液(基剤)
アルコキシシリル基含有ビニル重合体(数平均分子量15000) 41重量部
添加剤(消泡剤+光安定剤+顔料分散剤) 1重量部
溶剤(酢酸エチル) 2重量部
溶剤(酢酸ブチル) 2重量部
溶剤(キシレン) 42重量部
艶消し剤(平均粒子径8μmのシリカ)5重量部
基剤 計93重量部
B.硬化剤
有機錫(ジブチル錫ジラウレ−ト)の混合物 2重量部(有機錫は0.2重量部)
溶剤(キシレン) 5重量部
硬化剤 計7重量部
AとBの合計100重量部
塗布量100g/m2(乾燥重量(固形分)で50g/m2)2回塗り
(3)上塗りコーティング剤(艶消し)
A.艶消しクリヤー(基剤)
アルコキシシリル基含有ビニル重合体(数平均分子量15000) 40重量部
添加剤(消泡剤+光安定剤+顔料分散剤) 1重量部
溶剤(酢酸エチル) 2重量部
溶剤(酢酸ブチル) 2重量部
溶剤(キシレン) 41重量部
艶消し剤(平均粒子径8μmのシリカ)7重量部
基剤 計93重量部
B.硬化剤
有機錫(ジブチル錫ジラウレ−ト)の混合物 2重量部(有機錫は0.2重量部)
溶剤(キシレン) 5重量部
硬化剤 計7重量部
AとBの合計100重量部
塗布量100g/m2(乾燥重量(固形分)で50g/m2)1回塗り
実施例2はダイキャスト壁の例を示す。
実施例1の下塗り層と同一とした。ただし、単位面積当たりの塗布量は、乾燥重量で2.8〜3.8kg/m2とし、最大厚さが14mm、かつ凹凸の差も14mmの厚さであった。単位面積当た。得られた下塗り層を鉄製ハンマーで強く叩いても破壊することは無く、弾性もあり、強い地震にも耐えられることがわかった。
中塗り材として、下記のものを使用した。
(1)ハマキャスト社製商品名“ハマフレックス・S”(アクリルゴム系外壁用塗膜防水材:骨材は含まない。)100kgと水4〜6kgを混合して、ウールローラーを用いて乾燥重量で0.8〜1.2kg/m2で塗装し、乾燥した。この工程により、下塗り層の大きな凹凸は埋められて滑らかな表面となっていた。
(2−1)次いで、良好な表面の仕上げを行うための更なる表面の平滑と均一な発色を確保するための下地材サーフェーサーとして、鈴鹿塗料社製商品名“スズカプラサフ”(主材100kgと水5〜15kgを混合して調整したもの)をカップガンを用いて乾燥重量で0.6〜1.2kg/m2で吹き付け塗装し、乾燥した。
(2−2)下色付けとして、神東塗料社製商品名“NYポリン”(アクリルウレタン塗料:シルバー色)を使用し、カップガンを用いて2回吹付し、乾燥重量で0.2〜0.3kg/m2で塗装した。この中塗り層2の外観は波模様であった。
第1上塗りコーティング剤(クリヤー、主材14kg+硬化剤1kg)の中に、メルク社製商品名“Iriodin103”を1kg混合してカップガンを用いて吹付塗装し、乾燥させた。この吹付を2回行い、塗装量は乾燥重量で計0.2kg/m2とした。その上に第2上塗り材(艶消し)を1回塗布した。塗装量は乾燥重量で0.1kg/m2とした。得られた塗装物は、サンシャインウェザーメーターによる促進試験で7000時間(35年に相当)までは、変色、ひび割れ、クラックはなく、耐久性のあることが確認できた。このキャスト壁は、シルバー〜ホワイト色の金属色の単色であり、外観は深堀のキャスト模様に近似した波模様を形成していた。吹付塗装壁全体の最大厚さは15mm、かつ凹凸の差は13mmであった。
実施例1において、下塗り材のオバナヤ・セメンテックス社製商品名"セメンテックスCMS−2"(カチオンSBR系ポリマーセメントモルタル)のA材(マトリックス樹脂液)に代えて、アクリルエマルジョンを同量使用した以外は実施例1と同様にスプレー塗装した。得られた塗装物は、液ダレを起こし、修復作業が必要であった。また、実施例1と同様にハンマーで叩いたところ、弾性はなく、塗装面は破壊して剥離した。
2 中塗り層
3 上塗り層
4 スプレーガン
5 上塗り塗材
10 下地壁
20 リシンガン
21 ホッパー部
22 吹付ガン部
23 吹付口
24 エアー管
25 エアーストッパー
30 3頭式スプレーガン
31,32,33 タンク
34,35,36 噴射ノズル
37,38,39 吹き付け材
40,41 取っ手
Claims (8)
- 建造物の壁面に、厚塗りと凹凸模様を形成した吹き付け深堀壁であって、
(1)樹脂発泡粒子と、モルタルに合成ゴムを含むポリマーセメントモルタルを混合した下塗り層と、
(2)骨材を含むか又は含まない樹脂又は合成ゴムを含む中塗り層と、
(3)シロキサン架橋型アクリル−珪素重合体を含む上塗り層
が、この順番に形成されており、
前記下塗り層は厚塗りと深堀の凹凸模様を有し、
前記中塗り層は下塗り層の表面を円滑化し、
前記上塗り層は親水性防汚膜であることを特徴とする吹き付け深堀壁。 - 前記合成ゴムが、カチオン性スチレン−ブタジエンゴム(SBR)ディスバージョンである請求項1に記載の吹き付け深堀壁。
- 前記下塗り層は、下塗り材のポリマーセメントモルタル100kgに対して、樹脂発泡粒子が5〜50リットルの範囲混合されている請求項1又は2に記載の吹き付け深堀壁。
- 前記下塗り層は、最大厚さが5〜20mm、かつ凹凸の差も5〜20mmの厚さに吹き付けられている請求項1〜3のいずれかに記載の吹き付け深堀壁。
- 前記深堀壁は、ダイキャスト壁又は御影石の斫り出し壁の模様を呈する請求項1〜4のいずれか1項に記載の吹き付け深堀壁。
- 前記ダイキャスト壁は、骨材を含まず、中塗り層及び/又は上塗り層に金属色を発色する顔料を含む請求項5に記載の吹き付け深堀壁。
- 前記御影石の斫り出し壁は、中塗り層の骨材が複数色の塗材であり、前記複数色の塗材が非混合多色状に同時吹きされている請求項5に記載の吹き付け深堀壁。
- 請求項1〜7のいずれか1項に記載の吹き付け深堀壁の製造方法であって、
(1)樹脂発泡粒子と、モルタルに合成ゴムディスバージョンを加えたポリマーセメントモルタルを混合した下塗り塗装材を、吹き付け塗装により、厚塗りでかつ深堀の凹凸模様に形成し、乾燥後、
(2)骨材を含むか又は含まない樹脂又は合成ゴムディスバージョンを含む中塗り塗装材を塗装し、乾燥後、
(3)シロキサン架橋型アクリル−珪素重合体を含む上塗り材を塗装し、乾燥することを特徴とする吹き付け深堀壁の製造方法。