JP2011153395A - 無機繊維用バインダー及び該バインダーで処理した無機繊維マット - Google Patents
無機繊維用バインダー及び該バインダーで処理した無機繊維マット Download PDFInfo
- Publication number
- JP2011153395A JP2011153395A JP2010016948A JP2010016948A JP2011153395A JP 2011153395 A JP2011153395 A JP 2011153395A JP 2010016948 A JP2010016948 A JP 2010016948A JP 2010016948 A JP2010016948 A JP 2010016948A JP 2011153395 A JP2011153395 A JP 2011153395A
- Authority
- JP
- Japan
- Prior art keywords
- binder
- inorganic fiber
- inorganic
- fiber mat
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(B)ホウ素系化合物:5質量部以上
を含有することを特徴とする無機繊維用バインダー。
【効果】本発明の無機繊維用バインダーを用いれば、フェノール樹脂を主成分とするバインダーで処理した場合と同等の復元率や表面強度等を持つ無機繊維マットを作製することができ、またその無機繊維マットからの揮発性有機化合物の放出量は極めて少ない。
【選択図】なし
Description
請求項1:
(A)ヒドロキシル基を持つ水溶性高分子:100質量部、及び
(B)ホウ素系化合物:5質量部以上
を含有することを特徴とする無機繊維用バインダー。
請求項2:
(A)ヒドロキシル基を持つ水溶性高分子がポリビニルアルコールである請求項1記載の無機繊維用バインダー。
請求項3:
(A)ヒドロキシル基を持つ水溶性高分子の重合度が500〜3,500である請求項1又は2記載の無機繊維用バインダー。
請求項4:
無機繊維が、グラスウール又はロックウールである請求項1乃至3のいずれか1項記載の無機繊維用バインダー。
請求項5:
請求項1乃至4のいずれか1項記載の無機繊維用バインダーで処理した無機繊維からなる無機繊維マット。
本発明の無機繊維用バインダーは、
(A)ヒドロキシル基を持つ水溶性高分子、及び
(B)ホウ素系化合物
を含有するものである。
表1に記載したポリビニルアルコール100部とホウ砂10部をイオン交換水に溶解し1.5%の濃度である無機繊維用バインダー水溶液を調製した。無機繊維としてグラスウールを用い、調製した無機繊維用バインダー水溶液を用いてスプレー塗布してグラスウールを処理し、実施例における処理条件、220℃、60秒で加熱乾燥して無機繊維マットを作製した。無機繊維マットへの無機繊維用バインダーの処理量は、処理後の無機繊維マットを質量基準として、無機繊維への付着量が無機繊維用バインダーの固形分比率で4%となるようにした。
実施例1において、ホウ砂の量をそれぞれ5部、20部、25部、35部とした以外は、実施例1と同様の製造方法により無機繊維用バインダー水溶液を調製し、無機繊維マットを作製した。
ポリビニルアルコールに代えて、フェノール樹脂ショーノールBRL−1015(水溶性フェノール:昭和高分子(株)製)を使用した以外は、実施例1と同様の方法により無機繊維用バインダー水溶液を調製し、無機繊維マットを作製した。
実施例1において、ホウ砂の量をそれぞれ0部、3部とした以外は、実施例1と同様の方法により無機繊維用バインダー水溶液を調製し、無機繊維マットを作製した。
ホウ砂に代えて、それぞれカルボジライトV−02(カルボジイミド系架橋剤:日清紡(株)製)、メイカネートTP−120(イソシアネート系架橋剤:名成化学工業(株)製)を使用した以外は、実施例1と同様の方法により無機繊維用バインダー水溶液を調製し、無機繊維マットを作製した。
実施例1〜8、比較例1〜5の無機繊維マットの復元率及びホルムアルデヒド放散速度を測定した。なお、ホルムアルデヒド放散速度はJIS−A1901に基づいて測定した。
無機繊維マットの梱包体製造時に、10cm×10cmのサンプルを取り出し、20kgの加重を1時間かけ、加重後の無機繊維マットの厚み(dx)を測定し、下記式(1)により復元率を求めた(n=5)。結果を表1に併記した。
R=(dx/d)×100 (1)
R :復元率(%)
dx:復元後の無機繊維マットの厚み(mm)
d :試験前の無機繊維マットの呼び厚み(mm)
また、無機繊維マットの梱包体を適宜切断し、表面積を440cm2に調整したものを、ホルムアルデヒドの放散速度の測定用試験体とした。ホルムアルデヒド放散速度の測定条件について、測定日数は7日間として、チャンバー内の温度を28℃、相対湿度を50%として、チャンバー体積を20L、換気回数を1時間当り0.5回とした。サンプリングには、DNPH(2,4−ジニトロフェニルヒドラジン)シリカショートボディ(Waters社製)を用いて、捕集体積は10Lとし、捕集流量は167mL/minとした。結果を表1に併記した。
2 バインダー付与装置
3 無機繊維
41,42,43,44,5 コンベア
6 成形炉
7 無機繊維マット
8 切断機
Claims (5)
- (A)ヒドロキシル基を持つ水溶性高分子:100質量部、及び
(B)ホウ素系化合物:5質量部以上
を含有することを特徴とする無機繊維用バインダー。 - (A)ヒドロキシル基を持つ水溶性高分子がポリビニルアルコールである請求項1記載の無機繊維用バインダー。
- (A)ヒドロキシル基を持つ水溶性高分子の重合度が500〜3,500である請求項1又は2記載の無機繊維用バインダー。
- 無機繊維が、グラスウール又はロックウールである請求項1乃至3のいずれか1項記載の無機繊維用バインダー。
- 請求項1乃至4のいずれか1項記載の無機繊維用バインダーで処理した無機繊維からなる無機繊維マット。