JP2008303525A - X線造影性モノフィラメント - Google Patents
X線造影性モノフィラメント Download PDFInfo
- Publication number
- JP2008303525A JP2008303525A JP2008110212A JP2008110212A JP2008303525A JP 2008303525 A JP2008303525 A JP 2008303525A JP 2008110212 A JP2008110212 A JP 2008110212A JP 2008110212 A JP2008110212 A JP 2008110212A JP 2008303525 A JP2008303525 A JP 2008303525A
- Authority
- JP
- Japan
- Prior art keywords
- monofilament
- ray
- thermoplastic resin
- contrast
- radiopaque agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】放射線不透過剤を含有する熱可塑性樹脂からなるモノフィラメントであって、モノフィラメント中の放射線不透過剤の含有量が30〜80質量%、ヤング率が3.0cN/dtex以下、繊度が1000〜20000dtexであることを特徴とするX線造影性モノフィラメント。
【選択図】なし
Description
すなわち、本発明は、放射線不透過剤を含有する熱可塑性樹脂からなるモノフィラメントであって、モノフィラメント中の放射線不透過剤の含有量が30〜80質量%、ヤング率が3.0cN/dtex以下、繊度が1000〜20000dtexであることを特徴とするX線造影性モノフィラメントを要旨とするものである。
本発明のモノフィラメントは、放射線不透過剤を含有する熱可塑性樹脂からなるものであるが、熱可塑性樹脂に放射線不透過剤のような無機化合物を含有させることにより、柔軟性に乏しいものとなりやすい。このため、本発明においては、熱可塑性樹脂としては、X線不透過剤を高濃度に含有させても溶融紡糸が可能であり、かつ柔軟性を有するものを用いることが好ましく、中でも熱可塑性エラストマーを用いることが好ましい。
まず、従来公知の方法で放射線不透過剤と熱可塑性樹脂のコンパウンド樹脂チップをエクストルーダーで溶融し、紡糸口金より押し出して溶融紡糸を行う。
なお、紡糸温度は用いる熱可塑性樹脂の融点Tmに対して、(Tm+10)℃〜(Tm+80)℃の範囲とすることが好ましい。紡糸温度が高すぎると熱可塑性樹脂が熱分解を起こし、円滑な紡糸が困難になるとともに得られるモノフィラメントの物性が劣ったものとなりやすい。また、紡糸温度が低すぎると、未溶解物が残るため好ましくない。そして、紡出されたモノフィラメントを15〜40℃の水浴により冷却固化し、実質的に延伸することなく、20〜150m/分で巻き取り、X線造影性モノフィラメントを得る。
A)相対粘度
PET:フェノールと四塩化エタンの等質量混合物を溶媒とし、ウベローデ粘度計を使用して、試料濃度0.5g/100cc、温度20℃の条件で測定した。
ナイロン6:96%硫酸を溶媒とし、濃度1g/デシリットル、温度25℃の条件で常法により測定した。
B)熱可塑性樹脂のデュロメータ硬さ
JIS K 6325法により、米国ショアー社製のスプリング式硬さ試験器(デュロメータ)のタイプA及びタイプDを使用し、厚さ6mmの試験片を用いて測定した。
なお、比較例5、6については、JIS K 7202法により、ヒューチャーテック社製のロックウェル硬さ試験器M434H−27Pを使用し、厚さ6mmの試験片を用いてロックウェル硬さを測定した。
C)X線造影性モノフィラメントのヤング率
前記の方法で測定、算出した。
D)X線造影性モノフィラメントの繊度
JIS L 1013の正量繊度のA法により測定した。
E)X線造影性モノフィラメントの造影性
X線照射距離を1mとし、管電圧80kV、管電流400mAのX線発生装置(陽極:タングステン)、照射時間0.063秒の撮影条件にて、得られたX線造影性モノフィラメントを用いた不織布のX線写真を撮影し、目視によりX線造影性モノフィラメントの見え具合を以下の4段階で評価した。
◎:非常に鮮明に見える。
○:鮮明に見える。
△:やや鮮明に見える。
×:ほとんど見えない。
F)不織布の手触り感
得られたX線造影性モノフィラメントを用いた不織布の手触り感を以下の4段階で評価した。
◎:柔軟であり、手術用ガーゼとして好適である。
○:柔軟であり、手術用ガーゼとして好適であるが、やや異物感を感じる。
△:柔軟性にやや乏しく、異物感を感じるが、手術用ガーゼとして使用できる。
×:柔軟性に乏しく(硬く)、手術用ガーゼとして使用できない。
熱可塑性樹脂としてASTM D−1238法によるメルトフローレート値(以下MFR)が33g/10分(温度220℃、荷重10kg)のポリエステルエラストマー(東レ社製Hytrel SB704、デュロメータ硬さA70)を用い、放射線不透過剤として硫酸バリウムを用いた。モノフィラメント中の硫酸バリウム含有量が35質量%となるように調製したコンパウンド樹脂チップをエクストルーダー型溶融押出機に供給し、溶融紡糸を行った。紡糸温度225℃で溶融し、孔径3.0mmの紡糸孔を有する紡糸口金より吐出させて、20℃の水浴により冷却固化し、実質的に延伸することなく、巻取速度20m/分で巻き取り、3800dtex/1fのX線造影性モノフィラメントを得た。
溶融紡糸セルロース繊維(単糸繊度1.7dtex、繊維長38mm、レンチング社登録商標『レンチング・リヨセル』)をランダムカードにて開繊し、15g/m2の繊維ウエブを得た。この繊維ウエブの上に得られたX線造影モノフィラメントを流れ方向(縦方向)に100mm間隔で直線状に配列するように配置させ、その上に上記で得たのと同様の15g/m2の繊維ウエブを堆積して積層物を得た。得られた積層物を100メッシュのメッシュ状支持体上に載置し、ノズル孔径0.1mmの噴射孔が孔間隔0.6mmで横方向に一列に配置された噴射装置を用い、噴射圧力6.9Mpaで2回処理し、次に反転させて反対面より噴射圧力9.8Mpaで2回処理した後、余剰の水分を除去し130℃の乾燥機により乾燥処理を行い、不織布を得た。
モノフィラメント中の硫酸バリウムの含有量が表1に示す値となるように変更した以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
熱可塑性樹脂としてASTM D−1238法によるMFRが98g/10分(温度220℃、荷重10kg)のポリエステルエラストマー(東レ社製Hytrel SB754、デュロメータ硬さA75)を用い、モノフィラメント中の硫酸バリウム含有量が表1に示す値となるように調整したコンパウンド樹脂チップを用いた以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
熱可塑性樹脂としてASTM D−1238法によるMFRが10g/10分(温度190℃、荷重2.16kg)のポリエステルエラストマー(東レ社製Hytrel 3046、デュロメータ硬さD27)を用い、モノフィラメント中の硫酸バリウム含有量が表1に示す値となるように調整したコンパウンド樹脂チップを用いた以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
熱可塑性樹脂としてASTM D−1238法によるMFRが18g/10分(温度220℃、荷重2.16kg)のポリエステルエラストマー(東レ社製Hytrel 4767、デュロメータ硬さD47)を用い、モノフィラメント中の硫酸バリウム含有量が表1に示す値となるように調整したコンパウンド樹脂チップを用いて、紡糸温度240℃で溶融した以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
モノフィラメント中の硫酸バリウムの含有量、繊度が表1に示す値となるように変更した以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
モノフィラメント中の硫酸バリウムの含有量、繊度が表1に示す値となるように変更した以外は、実施例9と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
X線不透過剤を次硝酸ビスマス(実施例19)、酸化タングステン(実施例20)に変更し、モノフィラメント中のこれらの含有量が表1に示す値となるように変更した以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
熱可塑性樹脂としてASTM D−1238法によるMFRが10g/10分(温度230℃、荷重2.16kg)のポリエアミドエラストマー(アルケマ社製Pebax 3533SN01、デュロメータ硬さD33)を用い、モノフィラメント中の硫酸バリウム含有量が表1に示す値となるように調整したコンパウンド樹脂チップを用いて、紡糸温度210℃で溶融した以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
熱可塑性樹脂としてASTM D−1238法によるMFRが8g/10分(温度230℃、荷重2.16kg)のポリエステルエラストマー(アルケマ社製Pebax 533SN01、デュロメータ硬さD55) を用い、モノフィラメント中の硫酸バリウム含有量が表1に示す値となるように調整したコンパウンド樹脂チップを用いて、紡糸温度220℃で溶融した以外は、実施例1と同様の方法でX線造影性モノフィラメントを得た。そして、得られたX線造影性モノフィラメントを用いて実施例1と同様の方法で不織布を得た。
熱可塑性樹脂として相対粘度1.37のポリエチレンテレフタレート(ロックウェル硬さR120)を用い、モノフィラメント中の硫酸バリウム含有量が60質量%となるように調製したコンパウンド樹脂チップをエクストルーダー型溶融押出機に供給し、溶融紡糸を行った。紡糸温度260℃で溶融し、孔径3.0mmの紡糸孔を有する紡糸口金より吐出させて、20℃の水浴により冷却固化し、実質的に延伸することなく、巻取速度40m/分で巻き取り、3800dtex/1fのX線造影性モノフィラメントを得た。そして、得られたモノフィラメントを用いて実施例1と同様の方法で不織布を得た。
熱可塑性樹脂として相対粘度2.4のナイロン6(ロックウェル硬さR110)を用い、モノフィラメント中の硫酸バリウム含有量が60質量%となるように調製したコンパウンド樹脂チップをエクストルーダー型溶融押出機に供給し、溶融紡糸を行った。紡糸温度260℃で溶融し、孔径3.0mmの紡糸孔を有する紡糸口金より吐出させて、20℃の水浴により冷却固化し、実質的に延伸することなく、巻取速度40m/分で巻き取り、3800dtex/1fのX線造影性モノフィラメントを得た。そして、得られたモノフィラメントを用いて実施例1と同様の方法で不織布を得た。
一方、比較例1のX線造影性モノフィラメントは硫酸バリウムの含有量が少なかったため、比較例3のX線造影性モノフィラメントは、繊度が小さすぎたため、ともに造影性に乏しいものであった。また、比較例2のX線造影性モノフィラメントは硫酸バリウムの含有量が多かったため、比較例4のX線造影性モノフィラメントは繊度が大きすぎたため、ともにヤング率が高く、柔軟性に乏しく、得られた不織布は硬く手術用ガーゼとして不適なものであった。比較例5、6のX線造影性モノフィラメントは、デュロメータ硬さがD70以上の熱可塑性樹脂を用いたものであったため、ヤング率が高く、柔軟性に乏しく、得られた不織布は硬く手術用ガーゼとして不適なものであった。
Claims (3)
- 放射線不透過剤を含有する熱可塑性樹脂からなるモノフィラメントであって、モノフィラメント中の放射線不透過剤の含有量が30〜80質量%、ヤング率が3.0cN/dtex以下、繊度が1000〜20000dtexであることを特徴とするX線造影性モノフィラメント。
- 熱可塑性樹脂がエラストマーである請求項1記載のX線造影性モノフィラメント。
- 熱可塑性樹脂のJIS K6253法によるデュロメータ硬さがD70未満である請求項1又は2記載のX線造影性モノフィラメント。