JP2008266108A - コンクリート混和材、水硬性結合材料、コンクリートおよびコンクリート構造物の構築方法 - Google Patents
コンクリート混和材、水硬性結合材料、コンクリートおよびコンクリート構造物の構築方法 Download PDFInfo
- Publication number
- JP2008266108A JP2008266108A JP2007115331A JP2007115331A JP2008266108A JP 2008266108 A JP2008266108 A JP 2008266108A JP 2007115331 A JP2007115331 A JP 2007115331A JP 2007115331 A JP2007115331 A JP 2007115331A JP 2008266108 A JP2008266108 A JP 2008266108A
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- mass
- admixture
- concrete admixture
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】生石灰粉末と無水石膏粉末とを含むコンクリート混和材であって、コンクリート混和材中、生石灰粉末が30〜70質量%、無水石膏粉末が70〜30質量%であり、生石灰粉末の強熱減量が6質量%以下であり、かつ生石灰粉末がCaOを90質量%以上含み、および生石灰粉末のブレーン比表面積が4000〜6000cm2/gであり、かつBET比表面積が1.5〜3.0m2/gである、早期脱型コンクリート用のコンクリート混和材である。
【選択図】なし
Description
Claims (5)
- 生石灰粉末と無水石膏粉末とを含むコンクリート混和材中、生石灰粉末が30〜70質量%、無水石膏粉末が70〜30質量%であり、
生石灰粉末の強熱減量が6質量%以下であり、かつ生石灰粉末がCaOを90質量%以上含み、および
生石灰粉末のブレーン比表面積が4000〜6000cm2/gであり、かつBET比表面積が1.5〜3.0m2/gである、
早期脱型コンクリート用のコンクリート混和材。 - コンクリート混和材が、温度20℃、封緘養生時の無拘束条件下において、基準モルタルに、セメントと、セメントおよびコンクリート混和材の合計量に対して3〜9質量%のコンクリート混和材とを含むとき、
材齢24時間の長さ変化率(ε24)が、800×10-6以上、
材齢24時間から48時間までの長さ変化率の増分(ε48−ε24)が、60×10-6以上、および
材齢48時間から72時間までの長さ変化増加率((ε72−ε48)/ε48)の絶対値が、0.01以下
である、請求項1記載のコンクリート混和材。 - セメントと、請求項1または2記載のコンクリート混和材と、を含み、コンクリート混和材の量が、セメントとコンクリート混和材との合計量に対して3〜9質量%である、早期脱型水硬性結合材料。
- 請求項3記載の早期脱型水硬性結合材料と、水と、を含み、水の量が、セメントとコンクリート混和材の合計量に対して45〜60質量%である、早期脱型コンクリート。
- 請求項4記載のコンクリートを用いて打設および養生し、材齢2日〜3日で脱型することを特徴とする、コンクリート構造物の構築方法。