JP2008173856A - ハードコートフィルム - Google Patents
ハードコートフィルム Download PDFInfo
- Publication number
- JP2008173856A JP2008173856A JP2007009361A JP2007009361A JP2008173856A JP 2008173856 A JP2008173856 A JP 2008173856A JP 2007009361 A JP2007009361 A JP 2007009361A JP 2007009361 A JP2007009361 A JP 2007009361A JP 2008173856 A JP2008173856 A JP 2008173856A
- Authority
- JP
- Japan
- Prior art keywords
- hard coat
- film
- active energy
- energy ray
- coat film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】基材フィルム上に、(A)分子内に3個以上のエチレン性不飽和基を有し、かつイソシアヌレート誘導体以外の活性エネルギー線硬化型化合物と、その100質量部に対して、(B)分子内に3個以上のエチレン性不飽和基を有する、活性エネルギー線硬化型のイソシアヌレート誘導体150〜550質量部を含むハードコート層形成材料を用いて形成された、活性エネルギー線硬化樹脂層からなるハードコート層を有するハードコートフィルムである。
【選択図】なし
Description
一方、近年、画像表示装置の薄型化が要求されている。この場合、ハードコートフィルムには従来の厚さ(80〜125μm程度)の半分程度の厚さを有する基材フィルムの使用が望まれる。しかしながら、このような厚さの薄い基材フィルムに、従来通りのハードコート層を形成すると、ハードコート層の硬化収縮により、ハードコートフィルムにカールが発生し、その結果、表面保護フィルムとしての使用が困難となるなど、好ましくない事態を招来する。
そこで、硬化収縮を抑え、カールの発生を抑制するために、同一分子内に3個以上のエチレン性不飽和基及び1個以上のイソシアヌレート環を有する化合物を含む硬化性組成物を基材上に塗設して硬化させた、硬化後のハードコート層の膜厚が15μm以上200μm以下であるハードコート処理物品が開示されている(例えば、特許文献1参照)。しかしながら、この場合、十分な硬度を得るためには、ハードコート層の厚さを大きく設定しなければならないという問題がある。
また、2個のエチレン性不飽和基を有するイソシアヌレート誘導体と、ペンタエリスリトールアクリレートを含む組成物を硬化させてハードコート層とする技術が開示されている(例えば、特許文献2参照)。しかしながら、この技術においては、前記イソシアヌレート誘導体単体の硬化物の硬度が不十分であるため、組成物を硬化させたハードコート層の硬度に関して、さらなる改良の余地がある。
すなわち、本発明は、
[1]基材フィルム上に、(A)分子内に3個以上のエチレン性不飽和基を有し、かつイソシアヌレート誘導体以外の活性エネルギー線硬化型化合物と、その100質量部に対して、(B)分子内に3個以上のエチレン性不飽和基を有する、活性エネルギー線硬化型のイソシアヌレート誘導体150〜550質量部を含むハードコート層形成材料を用いて形成された、活性エネルギー線硬化樹脂層からなるハードコート層を有することを特徴とするハードコートフィルム、
[2](B)成分のイソシアヌレート誘導体が、イソシアヌル酸骨格の3つの窒素原子の全てに、エチレン性不飽和基が結合した構造を有する上記[1]項に記載のハードコートフィルム、
[3]10cm四方に裁断されたハードコートフィルムを平板上に載置した際に生じる4角のカール高さの合計が100mm以下であり、かつ鉛筆硬度が2H以上である上記[1]又は[2]項に記載のハードコートフィルム、
[4]基材フィルムが、厚さ80μm以下のトリアセチルセルロースフィルムである上記[1]〜[3]項のいずれかに記載のハードコートフィルム、及び
[5]ハードコート層の厚さが3〜10μmである上記[1]〜[4]項のいずれかに記載のハードコートフィルム、
を提供するものである。
本発明のハードコートフィルムにおいて用いられる基材フィルムに特に制限はなく、従来光学用ハードコートフィルムの基材として公知のプラスチックフィルムの中から適宣選択して用いることができる。このようなプラスチックフィルムとしては、例えば、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレートなどのポリエステルフィルム、ポリエチレンフィルム、ポリプロピレンフィルム、セロファン、ジアセチルセルロースフィルム、トリアセチルセルロースフィルム、アセチルセルロースブチレートフィルム、ポリ塩化ビニルフィルム、ポリ塩化ビニリデンフィルム、ポリビニルアルコールフィルム、エチレン−酢酸ビニル共重合体フィルム、ポリスチレンフィルム、ポリカーボネートフィルム、ポリメチルペンテンフィルム、ポリスルホンフィルム、ポリエーテルエーテルケトンフィルム、ポリエーテルスルホンフィルム、ポリエーテルイミドフィルム、ポリイミドフィルム、フッ素樹脂フィルム、ポリアミドフィルム、アクリル樹脂フィルム、ノルボルネン系樹脂フィルム、シクロオレフィン樹脂フィルム等を挙げることができる。
これらの基材フィルムは、透明、半透明のいずれであってもよく、また、着色されていてもよいし、無着色のものでもよく、用途に応じて適宜選択すればよい。例えば液晶表示体の偏光子保護用として用いる場合には、無色透明のトリアセチルセルロースフィルムが好適である。
本発明のハードコートフィルムにおいて、前記の基材フィルム上に積層されるハードコート層は、(A)分子内に3個以上のエチレン性不飽和基を有し、かつイソシアヌレート誘導体以外の活性エネルギー線硬化型化合物と、(B)分子内に3個以上のエチレン性不飽和基を有する、活性エネルギー線硬化型のイソシアヌレート誘導体を含むハードコート層形成材料によって形成される。
この(A)成分の活性エネルギー線硬化型化合物は、分子内に3個以上のエチレン性不飽和基を有し、かつイソシアヌレート誘導体以外の化合物である。このような化合物としては、例えばトリメチロールプロパントリ(メタ)アクリレート、ジペンタエリスリトールトリ(メタ)アクリレート、プロピオン酸変性ジペンタエリスリトールトリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、プロピレンオキシド変性トリメチロールプロパントリ(メタ)アクリレート、プロピオン酸変性ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、カプロラクトン変性ジペンタエリスリトールヘキサ(メタ)アクリレートなどの3官能以上の(メタ)アクリレートが挙げられる。これらは1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。エチレン性不飽和基の数は3個以上であれば、特に制限はないが、カール抑制の観点から3〜6個が好ましい。
で表されるトリス[(メタ)アクリロイルオキシアルキル]イソシアヌレートを挙げることができる。
前記一般式(I)において、R1〜R3で示されるアルキレン基は直鎖状、分岐鎖状のいずれであってもよく、具体的にはエチレン基、プロピレン基、トリメチレン基、各種ブチレン基が挙げられる。また、3つの窒素原子に結合した(メタ)アクリロイルオキシアルキル基は、たがいに同一であってもよく、異なっていてもよい。
前記一般式(I)で表されるトリス[(メタ)アクリロイルオキシアルキル]イソシアヌレートとしては、例えばトリス(2−アクリロイルオキシエチル)イソシアヌレート、トリス(3−アクリロイルオキシプロピル)イソシアヌレート、トリス(2−メタクリロイルオキシエチル)イソシアヌレート、トリス(3−メタクリロイルオキシプロピル)イソシアヌレートなどを好ましく挙げることができる。
本発明においては、(B)成分として、これらの化合物は1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。また、ハードコート層形成材料における当該(B)成分の含有量は、前記(A)成分100質量部に対して、150〜550質量部の範囲で選定される。この含有量が150質量部未満では、得られるハードコートフィルムのカール抑制効果が十分に発揮されないし、550質量部を超えるとハードコートフィルムの表面硬度が低下する。カール発生の抑制効果及び表面硬度のバランスなどの観点から、(B)成分の好ましい含有量は、180〜520質量部の範囲である。
他の活性エネルギー線硬化型化合物としては、例えば活性エネルギー線重合性プレポリマー及び/又は活性エネルギー線重合性単官能モノマーや2官能モノマーを挙げることができる。
活性エネルギー線重合性プレポリマーとしては、例えばポリエステルアクリレート系、エポキシアクリレート系、ウレタンアクリレート系、ポリオールアクリレート系などが上げられる。
一方、活性エネルギー線重合性単官能モノマーとしては、例えばメチル(メタ)アクリレート、エチル(メタ)アクリレート、ブチル(メタ)アクリレート、ヘキシル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、ラウリル(メタ)アクリレート、ステアリル(メタ)アクリレート、イソボルニル(メタ)アクリレートなどの中から少なくとも1種を適宜選択して用いることができる。
また、活性エネルギー線重合性2官能モノマーとしては、例えば1,4−ブタンジオールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、ポリエチレングリコールジ(メタ)アクリレート、ヒドロキシピバリン酸ネオペンチルグリコールジ(メタ)アクリレート、ジシクロペンタニルジ(メタ)アクリレート、カプロラクトン変性ジシクロペンテニルジ(メタ)アクリレート、エチレンオキシド変性リン酸ジ(メタ)アクリレート、アリル化シクロヘキシルジ(メタ)アクリレート、ビス[2−(メタ)アクリロキシエチル]イソシアヌレート、ビス[2−(メタ)アクリロキシエチル]2−ヒドロキシエチルイソシアヌレートなどの中から選ばれる少なくとも1種を適宜選択して用いることができる。
さらに、各種添加成分、例えばアンチグレア性を付与するための充填剤、反応性シリコーン化合物、光増感剤、重合禁止剤、架橋剤、酸化防止剤、紫外線吸収剤、光安定剤、レベリング剤、消泡剤などを適宜含有させることができる。
また、反応性シリコーン化合物としては、分子内にラジカル重合性不飽和基を有するシリコーン化合物を用いることができる。このシリコーン化合物は、活性エネルギー線の照射により架橋、硬化し、ハードコート層に耐汚染性や低摩擦性などを付与する作用を有している。
活性エネルギー線としては、例えば紫外線や電子線などが挙げられる。上記紫外線は、高圧水銀ランプ、ヒュージョンHランプ、キセノンランプなどで得られ、照射量は、通常100〜500mJ/cm2であり、一方電子線は、電子線加速器などによって得られ、照射量は、通常150〜350kVである。この活性エネルギー線の中では、特に紫外線が好適である。なお、電子線を使用する場合は、光重合開始剤を添加することなく、硬化膜を得ることができる。
ハードコート層の厚さは、通常3〜10μm程度である。このようにして得られたハードコートフィルムにおいては、通常、10cm四方に裁断されたハードコートフィルムを平板上に載置した際に生じる4角のカール高さの合計は100mm以下であり、また、鉛筆硬度は2H以上である。なお、カールの高さ及び鉛筆硬度の測定方法については、後で詳述する。
なお、透明導電性薄膜の材料としては、例えば酸化インジウム、酸化スズ、酸化亜鉛、インジウム−スズ酸化物、スズ−アンチモン酸化物、亜鉛−アルミニウム酸化物、インジウム−亜鉛酸化物などが挙げられる。
表面に透明導電性薄膜層を設けたハードコート層を有する本発明のハードコートフィルムは、該ハードコート層の耐擦傷性が高いことから、このハードコートフィルムを、抵抗膜方式のタッチパネルにおけるタッチ側透明プラスチック基板に適用することにより、タッチ側透明プラスチック基板の透明導電性薄膜が摩耗したり、クラックが発生したり、さらには基材から剥離してしまうという問題を解消することができる。
本発明においては、基材フィルムのハードコート層とは反対側の面に、被着体に貼着させるための粘着剤層を形成させることができる。この粘着剤層を構成する粘着剤としては、光学用途用のもの、例えばアクリル系粘着剤、ウレタン系粘着剤、シリコーン系粘着剤が好ましく用いられる。この粘着剤層の厚さは、通常5〜100μm、好ましくは10〜60μmの範囲である。
さらに、この粘着剤層の上に、必要に応じて剥離シートを設けることができる。この剥離シートとしては、例えばグラシン紙、コート紙、ラミネート紙などの紙及び各種プラスチックフィルムに、シリコーン樹脂などの剥離剤を塗付したものなどが挙げられる。この剥離シートの厚さについては特に制限はないが、通常20〜150μm程度である。
本発明のハードコートフィルムは、各種画像表示装置の表面保護フィルムとして必要十分な表面硬度を有し、かつ硬化収縮による反りが小さい。
なお、各例で得られたハードコートフィルムの性能は、下記の方法に従って評価した。
(1)鉛筆硬度
鉛筆引掻塗膜硬さ試験機[(株)東洋精機製作所製、型式「NP」]を用いて、JIS K 5600−5−4に準拠して鉛筆法により測定した。
(2)カール
ハードコートフィルムを10cm四方角に裁断し試験片を作製し、23℃、相対湿度(RH)55%の環境下に24時間静置したのち、水平なガラス板上に試験片を上方が凹となるように載置し、4つの角の浮き上がりを定規にて測定し、その合計値を求めた。
(A)ペンタエリスリトールトリアクリレート[新中村化学工業(株)製、商品名「NKエステルA−TMM−3」、固形分濃度100%]100質量部に、(B)トリス(2−アクリロイルオキシエチル)イソシアヌレート[東亜合成化学工業(株)製、商品名「アロニックスM−315」、固形分濃度100%]200質量部、光重合開始剤として1−ヒドロキシ−シクロヘキシルフェニルケトン[チバ・スペシャルティ・ケミカルズ社製、商品名「イルガキュア184」]6質量部を添加し、固形分濃度が40質量%になるように、プロピレングリコールモノメチルエーテルで希釈し、塗工液Aを調製した。
調製例2 塗工液Bの調製
調製例1において、(B)トリス(2−アクリロイルオキシエチル)イソシアヌレートの量を500質量部に、1−ヒドロキシ−シクロヘキシルフェニルケトンの量を12質量部に変更した以外は、調製例1と同様にして塗工液Bを調製した。
調製例3 塗工液Cの調製
調製例1において、(A)ペンタエリスリトールトリアクリレートをペンタエリスリトールテトラアクリレート[新中村化学工業(株)製、商品名「NKエステルA−TMMT」、固形分濃度100%]に変更した以外は、調製例1と同様にして塗工液Cを調製した。
調製例4 塗工液Dの調製
調製例2において、(A)ペンタエリスリトールトリアクリレートをペンタエリスリトールテトラアクリレート(前出)に変更した以外は、調製例2と同様にして塗工液Dを調製した。
調製例5 塗工液Eの調製
調製例1において、(A)ペンタエリスリトールトリアクリレートをジペンタエリスリトールヘキサアクリレート[東亜合成化学工業(株)製、商品名「アロニックスM−400」、固形分濃度100%]に変更した以外は、調製例1と同様にして塗工液Eを調製した。
調製例6 塗工液Fの調製
調製例2において、(A)ペンタエリスリトールトリアクリレートをジペンタエリスリトールヘキサアクリレート(前出)に変更した以外は、調製例2と同様にして塗工液Fを調製した。
調製例7 塗工液Gの調製
調製例1において、(B)トリス(2−アクリロイルオキシエチル)イソシアヌレートの量を350質量部に変更した以外は、調製例1と同様にして塗工液Gを調製した。
調製例8 塗工液Hの調製
調製例1において、(B)トリス(2−アクリロイルオキシエチル)イソシアヌレートの量を100質量部に、1−ヒドロキシ−シクロヘキシルフェニルケトンの量を5質量部に変更した以外は、調製例1と同様にして塗工液Hを調製した。
調製例9 塗工液Iの調製
調製例8において、(A)ペンタエリスリトールトリアクリレートをジペンタエリスリトールヘキサアクリレート(前出)に変更した以外は、調製例8と同様にして塗工液Iを調製した。
調製例10 塗工液Jの調製
調製例1において、(B)トリス(2−アクリロイルオキシエチル)イソシアヌレートの量を600質量部に、1−ヒドロキシ−シクロヘキシルフェニルケトンの量を14質量部に変更した以外は、調製例1と同様にして塗工液Jを調製した。
調製例11 塗工液Kの調製
調製例10において、(A)ペンタエリスリトールトリアクリレートをジペンタエリスリトールヘキサアクリレート(前出)に変更した以外は、調製例10と同様にして塗工液Kを調製した。
基材フィルムとして厚さ40μmのトリアセチルセルロースフィルム[富士写真フィルム(株)製、商品名「T40UZ」]上に、調製例1〜7で調製した塗工液A〜Gを、バーコーターを用いて乾燥後の厚さが3μmになるように塗工し、70℃で1分間乾燥後、塗工面に紫外線を光量230mJ/cm2で照射して硬化させ、各ハードコートフィルムを作製した。ハードコート層の厚さは3μmであった。
各ハードコートフィルムの性能評価結果を第1表に示す。
実施例2
実施例1において、乾燥後の厚さが6μmになるように塗工した以外は、実施例1と同様にして、各ハードコートフィルムを作製した。ハードコート層の厚さは6μmであった。
各ハードコートフィルムの性能評価結果を第1表に示す。
実施例3
実施例1において、乾燥後の厚さが10μmになるように塗工した以外は、実施例1と同様にして、各ハードコートフィルムを作製した。ハードコート層の厚さは10μmであった。
各ハードコートフィルムの性能評価結果を第1表に示す。
基材フィルムとして厚さ40μmのトリアセチルセルロースフィルム(前出)上に、調製例8、9で調製した塗工液H、Iを、バーコーターを用いて乾燥後の厚さが6μmになるように塗工し、70℃で1分間乾燥後、塗工面に紫外線を光量230mJ/cm2で照射して硬化させ、各ハードコートフィルムを作製した。
各ハードコートフィルムの性能評価結果を第1表に示す。
比較例2
基材フィルムとして厚さ40μmのトリアセチルセルロースフィルム(前出)上に、調製例10、11で調製した塗工液J、Kを、バーコーターを用いて乾燥後の厚さが6μmになるように塗工し、70℃で1分間乾燥後、塗工面に紫外線を光量230mJ/cm2で照射して硬化させ、各ハードコートフィルムを作製した。
各ハードコートフィルムの性能評価結果を第1表に示す。
これに対し、比較例1は、鉛筆硬度が2H以上で高いものの、カール量が大きく、不合格であり、また比較例2は、カール量が小さいが、鉛筆硬度はHで不合格である。
Claims (5)
- 基材フィルム上に、(A)分子内に3個以上のエチレン性不飽和基を有し、かつイソシアヌレート誘導体以外の活性エネルギー線硬化型化合物と、その100質量部に対して、(B)分子内に3個以上のエチレン性不飽和基を有する、活性エネルギー線硬化型のイソシアヌレート誘導体150〜550質量部を含むハードコート層形成材料を用いて形成された、活性エネルギー線硬化樹脂層からなるハードコート層を有することを特徴とするハードコートフィルム。
- (B)成分のイソシアヌレート誘導体が、イソシアヌル酸骨格の3つの窒素原子の全てに、エチレン性不飽和基が結合した構造を有する請求項1に記載のハードコートフィルム。
- 10cm四方に裁断されたハードコートフィルムを平板上に載置した際に生じる4角のカール高さの合計が100mm以下であり、かつ鉛筆硬度が2H以上である請求項1又は2に記載のハードコートフィルム。
- 基材フィルムが、厚さ80μm以下のトリアセチルセルロースフィルムである請求項1〜3のいずれかに記載のハードコートフィルム。
- ハードコート層の厚さが3〜10μmである請求項1〜4のいずれかに記載のハードコートフィルム。