JP2006213959A - 生産性に優れたホットプレス高強度鋼製部材の製造方法 - Google Patents
生産性に優れたホットプレス高強度鋼製部材の製造方法 Download PDFInfo
- Publication number
- JP2006213959A JP2006213959A JP2005027080A JP2005027080A JP2006213959A JP 2006213959 A JP2006213959 A JP 2006213959A JP 2005027080 A JP2005027080 A JP 2005027080A JP 2005027080 A JP2005027080 A JP 2005027080A JP 2006213959 A JP2006213959 A JP 2006213959A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- hot
- steel
- steel sheet
- strength steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】質量%でC:0.05〜0.35%,Si:0.005〜1.0%,Mn:0〜4.0%,Cr:0〜3.0%,Cu:0〜4.0%,Ni:0〜3.0%,B:0.0002〜0.1%,Ti:0.001〜3.0%,P:0.1%以下,S:0.05%以下,Al:0.005〜0.1%,N:0.01%以下を含有し,かつMn+Cr/3.1+(Cu+Ni)/1.4≧2.5%を満たし残部がFeおよび不可避的不純物からなる鋼板を,750〜1300℃で10〜6000秒間加熱した後300℃以上でプレス成形し,金型から取り出して200〜1100℃から5〜40℃まで0.1℃/秒以上で冷却し,面積率で60%以上のマルテンサイト組織を有する部材を得る。
【選択図】なし
Description
S:0.05%以下,Al:0.005〜0.1%,N:0.01%以下,を含有し,かつ,Mn+Cr/3.1+(Cu+Ni)/1.4≧2.5%を満たし,残部がFeおよび不可避的不純物からなる鋼板を,750〜1300℃に昇温して10〜6000秒間維持した後,300℃以上にてプレス成形を行い,その後,成形品を金型から取り出して,200〜1100℃から5〜40℃まで0.1℃/秒以上の冷却速度で冷却し,面積率で60%以上のマルテンサイト組織を有する部材を得ることを特徴とする,生産性に優れたホットプレス高強度鋼製部材の製造方法が提供される。
まず,本発明における鋼の化学成分の限定理由について説明する。
ホットプレス成形は,質量%で,C:0.05〜0.35%,Si:0.005〜1.0%,Mn:0〜4.0%,Cr:0〜3.0%,Cu:0〜4.0%,Ni:0〜3.0%,B:0.0002〜0.1%,Ti:0.001〜3.0%,P:0.1%以下,S:0.05%以下,Al:0.005〜0.1%,N:0.01%以下,を含有し,かつ,Mn+Cr/3.1+(Cu+Ni)/1.4≧2.5%を満たし,さらに任意で,質量%でMo:0.01〜3.0%,または,質量%で,Nb:0.01〜3.0%,V:0.001〜3.0%,W:0.005〜3.0%,の1種または2種以上,または,質量%で,REM:0.0005〜0.01%,Y:0.0005〜0.01%,Ca:0.0005〜0.01%,Mg:0.0005〜0.01%,の1種または2種以上を含有し,残部がFeおよび不可避的不純物からなる鋼板を,750〜1300℃に昇温して10〜6000秒間維持した後,プレスダイスの上に置き,300℃以上にてプレス成形を行う。その後,成形品を金型から取り出して,200〜1100℃から5〜40℃まで0.1℃/秒以上の冷却速度で冷却する。
表1に示す成分の鋼を溶製し,常法に従い連続鋳造でスラブ鋼片とした。符号(鋼No.)A〜Iが本発明に従った成分の鋼で,符号J〜P(鋼No.)は成分が本発明から逸脱するものである。これらの鋼片を加熱炉中で1120℃〜1280℃に加熱し,熱間圧延を仕上げ温度850〜950℃で実施,その後620℃まで空冷し巻き取った。この熱延板を圧下率50%で冷延し,それぞれ冷延鋼板とし,ホットプレス用素材とした。
Claims (5)
- 質量%で,
C:0.05〜0.35%,
Si:0.005〜1.0%,
Mn:0〜4.0%,
Cr:0〜3.0%,
Cu:0〜4.0%,
Ni:0〜3.0%,
B:0.0002〜0.1%,
Ti:0.001〜3.0%,
P:0.1%以下,
S:0.05%以下,
Al:0.005〜0.1%,
N:0.01%以下,
を含有し,かつ,Mn+Cr/3.1+(Cu+Ni)/1.4≧2.5%を満たし,残部がFeおよび不可避的不純物からなる鋼板を,750〜1300℃で10〜6000秒間加熱した後,300℃以上にてプレス成形を行い,その後,成形品を金型から取り出して,200〜1100℃から5〜40℃まで0.1℃/秒以上の冷却速度で冷却し,面積率で60%以上のマルテンサイト組織を有する部材を得ることを特徴とする,生産性に優れたホットプレス高強度鋼製部材の製造方法。 - 前記鋼板は,さらに質量%で,Mo:0.01〜3.0%を含有することを特徴とする,請求項1に記載の生産性に優れたホットプレス高強度鋼製部材の製造方法。
- 前記鋼板は,さらに質量%で,
Nb:0.01〜3.0%,
V:0.001〜3.0%,
W:0.005〜3.0%,
の1種または2種以上を含有することを特徴とする,請求項1又は2に記載の生産性に優れたホットプレス高強度鋼製部材の製造方法。 - 前記鋼板は,さらに質量%で,
REM:0.0005〜0.01%,
Y:0.0005〜0.01%,
Ca:0.0005〜0.01%,
Mg:0.0005〜0.01%,
の1種または2種以上を含有することを特徴とする,請求項1〜3の何れかに記載の生産性に優れたホットプレス高強度鋼製部材の製造方法。 - 前記鋼板を,1〜100℃/秒の昇温速度で750〜1300℃に加熱することを特徴とする,請求項1〜4の何れかに記載の生産性に優れたホットプレス高強度鋼製部材の製造方法。