IT1160899B - Procedimento per formare un rivestimento refrattario su un substrato,particolarmente a scopo di protezione o come sopporto per materiale catalitico - Google Patents

Procedimento per formare un rivestimento refrattario su un substrato,particolarmente a scopo di protezione o come sopporto per materiale catalitico

Info

Publication number
IT1160899B
IT1160899B IT69505/78A IT6950578A IT1160899B IT 1160899 B IT1160899 B IT 1160899B IT 69505/78 A IT69505/78 A IT 69505/78A IT 6950578 A IT6950578 A IT 6950578A IT 1160899 B IT1160899 B IT 1160899B
Authority
IT
Italy
Prior art keywords
substrate
gel
procedure
protection
forming
Prior art date
Application number
IT69505/78A
Other languages
English (en)
Italian (it)
Other versions
IT7869505A0 (it
Original Assignee
Atomic Energy Authority Uk
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Atomic Energy Authority Uk filed Critical Atomic Energy Authority Uk
Publication of IT7869505A0 publication Critical patent/IT7869505A0/it
Application granted granted Critical
Publication of IT1160899B publication Critical patent/IT1160899B/it

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/02—Impregnation, coating or precipitation
    • B01J37/0215—Coating
    • G—PHYSICS
    • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
    • G21C—NUCLEAR REACTORS
    • G21C3/00—Reactor fuel elements and their assemblies; Selection of substances for use as reactor fuel elements
    • G21C3/02—Fuel elements
    • G21C3/04—Constructional details
    • G21C3/16—Details of the construction within the casing
    • G21C3/20—Details of the construction within the casing with coating on fuel or on inside of casing; with non-active interlayer between casing and active material with multiple casings or multiple active layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/74—General processes for purification of waste gases; Apparatus or devices specially adapted therefor
    • B01D53/86—Catalytic processes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J13/00—Colloid chemistry, e.g. the production of colloidal materials or their solutions, not otherwise provided for; Making microcapsules or microballoons
    • B01J13/0004—Preparation of sols
    • B01J13/0047—Preparation of sols containing a metal oxide
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/02—Impregnation, coating or precipitation
    • B01J37/024—Multiple impregnation or coating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
    • C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
    • C23C18/125—Process of deposition of the inorganic material
    • C23C18/1254—Sol or sol-gel processing
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23D—ENAMELLING OF, OR APPLYING A VITREOUS LAYER TO, METALS
    • C23D5/00—Coating with enamels or vitreous layers
    • C23D5/02—Coating with enamels or vitreous layers by wet methods
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23D—ENAMELLING OF, OR APPLYING A VITREOUS LAYER TO, METALS
    • C23D5/00—Coating with enamels or vitreous layers
    • C23D5/10—Coating with enamels or vitreous layers with refractory materials
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/10—Solid density
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E30/00—Energy generation of nuclear origin
    • Y02E30/30—Nuclear fission reactors
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10S376/00—Induced nuclear reactions: processes, systems, and elements
    • Y10S376/90—Particular material or material shapes for fission reactors

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Physics & Mathematics (AREA)
  • General Chemical & Material Sciences (AREA)
  • Environmental & Geological Engineering (AREA)
  • Dispersion Chemistry (AREA)
  • Thermal Sciences (AREA)
  • High Energy & Nuclear Physics (AREA)
  • General Engineering & Computer Science (AREA)
  • Plasma & Fusion (AREA)
  • Health & Medical Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Analytical Chemistry (AREA)
  • Biomedical Technology (AREA)
  • Catalysts (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Paints Or Removers (AREA)
  • Chemically Coating (AREA)
IT69505/78A 1977-11-01 1978-10-31 Procedimento per formare un rivestimento refrattario su un substrato,particolarmente a scopo di protezione o come sopporto per materiale catalitico IT1160899B (it)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB4547177 1977-11-01

Publications (2)

Publication Number Publication Date
IT7869505A0 IT7869505A0 (it) 1978-10-31
IT1160899B true IT1160899B (it) 1987-03-11

Family

ID=10437343

Family Applications (1)

Application Number Title Priority Date Filing Date
IT69505/78A IT1160899B (it) 1977-11-01 1978-10-31 Procedimento per formare un rivestimento refrattario su un substrato,particolarmente a scopo di protezione o come sopporto per materiale catalitico

Country Status (10)

Country Link
US (2) US4297246A (US07534539-20090519-C00104.png)
JP (1) JPH024677B2 (US07534539-20090519-C00104.png)
CA (1) CA1118301A (US07534539-20090519-C00104.png)
DE (1) DE2857147C2 (US07534539-20090519-C00104.png)
FR (1) FR2416743A1 (US07534539-20090519-C00104.png)
GB (3) GB2087632B (US07534539-20090519-C00104.png)
IT (1) IT1160899B (US07534539-20090519-C00104.png)
NL (1) NL7810883A (US07534539-20090519-C00104.png)
SE (2) SE431233B (US07534539-20090519-C00104.png)
WO (1) WO1979000247A1 (US07534539-20090519-C00104.png)

Families Citing this family (57)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5687604A (en) * 1979-12-05 1981-07-16 Atomic Energy Authority Uk Particle coating
DE3010950A1 (de) * 1980-03-21 1981-10-01 Hoechst Ag, 6000 Frankfurt Verfahren zur herstellung und verwendung eines katalysatortraeger
US4356106A (en) * 1980-05-09 1982-10-26 United Kingdom Atomic Energy Authority Cerium compounds
US4528212A (en) * 1982-07-22 1985-07-09 International Business Machines Corporation Coated ceramic substrates for mounting integrated circuits
GB8300554D0 (en) * 1983-01-10 1983-02-09 Atomic Energy Authority Uk Catalyst preparation
US4555275A (en) * 1984-10-19 1985-11-26 Grumman Aerospace Corporation Hydrogen permeation protection for metals
US4677095A (en) * 1985-01-31 1987-06-30 Engelhard Corporation Stabilized alumina catalyst support coatings
CA1331939C (en) * 1985-02-27 1994-09-13 Kazuo Tsuchitani Method for coating a metal covered with metal oxide film with refractory metal oxide
FR2583737B1 (fr) * 1985-06-20 1987-08-14 Rhone Poulenc Spec Chim Nouveau compose de cerium iv et son procede de preparation.
US4636440A (en) * 1985-10-28 1987-01-13 Manville Corporation Novel process for coating substrates with glass-like films and coated substrates
US4704299A (en) * 1985-11-06 1987-11-03 Battelle Memorial Institute Process for low temperature curing of sol-gel thin films
US4789563A (en) * 1986-09-26 1988-12-06 Advanced Technology Materials, Inc. Sol gel formation of polysilicate, titania, and alumina interlayers for enhanced adhesion of metal films on substrates
US4839402A (en) * 1986-09-26 1989-06-13 Advanced Technology Materials, Inc. Sol gel formation of polysilicate, titania, and alumina interlayers for enhanced adhesion of metal films on substrates
US4738896A (en) * 1986-09-26 1988-04-19 Advanced Technology Materials, Inc. Sol gel formation of polysilicate, titania, and alumina interlayers for enhanced adhesion of metal films on substrates
US4935296A (en) * 1986-09-26 1990-06-19 Advanced Technology Materials, Inc. Metal coated fibers containing a sol gel formed porous polysilicate, titania or alumina interlayer and composite material articles reinforced therewith
CA1292155C (en) * 1987-03-03 1991-11-19 Lance Wilson Method of forming a corrosion resistant coating
DE3719077A1 (de) * 1987-06-06 1988-12-22 Daimler Benz Ag Beschichtetes ventil fuer verbrennungsmotoren
DE3813946A1 (de) * 1988-04-26 1989-11-09 Asea Brown Boveri Verfahren zum aufbringen einer aus edelmetallen und/oder edelmetallverbindungen bestehenden katalysatorschicht auf einen traeger aus keramischem material
US4990303A (en) * 1988-06-24 1991-02-05 Combustion Engineering, Inc. Element with burnable poison coating
US5360634A (en) * 1988-12-05 1994-11-01 Adiabatics, Inc. Composition and methods for densifying refractory oxide coatings
US4962264A (en) * 1989-10-23 1990-10-09 Betz Laboratories, Inc. Methods for retarding coke formation during pyrolytic hydrocarbon processing
US5015358A (en) * 1990-08-30 1991-05-14 Phillips Petroleum Company Antifoulants comprising titanium for thermal cracking processes
DE4105235A1 (de) * 1991-02-20 1992-08-27 Merck Patent Gmbh Beschichtetes system
US5182077A (en) * 1991-04-15 1993-01-26 Gamma Engineering Corporation Water cooled nuclear reactor and fuel elements therefor
FR2683373B1 (fr) * 1991-10-31 1994-03-04 Pechiney Uranium Elements combustibles nucleaires comportant un piege a produits de fission a base d'oxyde.
US5324544A (en) * 1991-12-20 1994-06-28 United Technologies Corporation Inhibiting coke formation by coating gas turbine elements with alumina-silica sol gel
US5264244A (en) * 1991-12-20 1993-11-23 United Technologies Corporation Inhibiting coke formation by coating gas turbine elements with alumina
US5266360A (en) * 1991-12-20 1993-11-30 United Technologies Corporation Inhibiting coke formation by coating gas turbine elements with silica
US5269137A (en) * 1991-12-20 1993-12-14 United Technologies Corporation Gas turbine elements bearing coke inhibiting coatings of alumina
US5240741A (en) * 1991-12-20 1993-08-31 United Technologies Corporation Inhibiting coke formation by coating gas turbine elements with tungsten disulfide
US5336560A (en) * 1991-12-20 1994-08-09 United Technologies Corporation Gas turbine elements bearing alumina-silica coating to inhibit coking
US5591380A (en) * 1991-12-20 1997-01-07 United Technologies Corporation Preparation of alumina-silica sol gel compositions
ES2104991T3 (es) * 1992-04-14 1997-10-16 Ebara Corp Dispositivo de cojinete para uso en un motor de tipo hermetico.
US5461648A (en) * 1994-10-27 1995-10-24 The United States Of America As Represented By The Secretary Of The Navy Supercritical water oxidation reactor with a corrosion-resistant lining
DE4441591C2 (de) * 1994-11-11 2001-05-03 Peter Goerzen Verfahren zum Korrosionsschutz der Auspuffröhren und Schalldämpfer für Abgase der Kraftfahrzeuge mit Verbrennungsmotoren
DE19600684A1 (de) * 1995-02-17 1996-08-22 Linde Ag Verfahren zum Spalten von Kohlenwasserstoffen und Vorrichtung
SE504795C2 (sv) * 1995-07-05 1997-04-28 Katator Ab Nätbaserad förbränningskatalysator och framställning av densamma
US5626923A (en) * 1995-09-19 1997-05-06 Mcdonnell Douglas Corporation Method of applying ceramic coating compositions to ceramic or metallic substrate
DE19607979A1 (de) * 1996-03-01 1997-09-04 Asea Brown Boveri Abgastrakt einer insbesondere zur Verbrennung von Schweröl einsetzbaren Verbrennungsvorrichtung
US5766562A (en) * 1997-03-10 1998-06-16 Ford Global Technologies, Inc. Diesel emission treatment using precious metal on titania aerogel
FR2765492B1 (fr) * 1997-07-03 1999-09-17 Rhodia Chimie Sa Procede de traitement de gaz pour la reduction des emissions des oxydes d'azote utilisant une composition catalytique avec un support a base de silice et d'oxyde de titane
NL1006638C2 (nl) 1997-07-21 1999-01-25 Univ Utrecht Dunne keramische deklagen.
NL1011098C2 (nl) * 1999-01-21 2000-07-24 Univ Utrecht Keramische deklaag.
DE10013865A1 (de) * 2000-03-21 2001-10-04 Siemens Ag Verfahren zur Verminderung der Korrosion eines Bauteils einer kerntechnischen Anlage und Bauteil einer kerntechnischen Anlage
KR100415265B1 (ko) * 2001-03-26 2004-01-16 한국전력공사 원자력발전소 증기발생기 전열관의 2차측 응력부식균열억제 방법
US6455182B1 (en) * 2001-05-09 2002-09-24 Utc Fuel Cells, Llc Shift converter having an improved catalyst composition, and method for its use
US20030186805A1 (en) * 2002-03-28 2003-10-02 Vanderspurt Thomas Henry Ceria-based mixed-metal oxide structure, including method of making and use
US6808816B2 (en) * 2002-09-13 2004-10-26 General Electric Company Method and coating system for reducing carbonaceous deposits on surfaces exposed to hydrocarbon fuels at elevated temperatures
US6932848B2 (en) * 2003-03-28 2005-08-23 Utc Fuel Cells, Llc High performance fuel processing system for fuel cell power plant
DE102004052135A1 (de) * 2004-06-07 2005-12-29 Fachhochschule Schmalkalden Beschichtetes Metallsubstrat und Verfahren zu seiner Herstellung
US7553517B1 (en) 2005-09-15 2009-06-30 The United States Of America As Represented By The United States Department Of Energy Method of applying a cerium diffusion coating to a metallic alloy
US20070160759A1 (en) * 2006-01-10 2007-07-12 General Electric Company Method for coating surfaces exposed to hydrocarbon fluids
CN101168683B (zh) * 2006-10-26 2011-05-04 中国石油化工股份有限公司 一种抑制烃类蒸汽裂解装置和急冷锅炉结焦的方法
JP2008188542A (ja) 2007-02-06 2008-08-21 Mitsubishi Heavy Ind Ltd 排ガス処理用触媒、その製造方法および排ガス処理方法
DE102007015635A1 (de) * 2007-03-31 2008-10-02 Schaeffler Kg Beschichtung eines Bauteils aus gehärtetem Stahl und Verfahren zum Aufbringen der Beschichtung
CN101294100B (zh) * 2007-04-28 2012-05-30 中国石油化工股份有限公司 一种抑制烃类蒸汽裂解炉结焦的方法
US10807071B2 (en) * 2016-05-05 2020-10-20 University Of Connecticut Mesoporous metal doped cerium oxide catalyst

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
LU38182A1 (US07534539-20090519-C00104.png) *
US3133829A (en) * 1959-02-02 1964-05-19 Du Pont Method of applying protective coatings to metals
US3186867A (en) * 1962-10-12 1965-06-01 Gen Electric Process for coating ferrous material and material coated by such process
GB1181794A (en) * 1966-06-09 1970-02-18 Atomic Energy Authority Uk Improvements in or relating to Zirconium Compounds
US3762936A (en) * 1967-07-31 1973-10-02 Du Pont Manufacture of borosilicate glass powder essentially free of alkali and alkaline earth metals
US3761571A (en) * 1970-02-10 1973-09-25 Atomic Energy Authority Uk Production of ceria
US3894963A (en) * 1971-05-10 1975-07-15 Norton Co High surface area catalyst bodies
US3785998A (en) * 1971-06-30 1974-01-15 Universal Oil Prod Co Method of catalyst manufacture by impregnating honeycomb-type support
US3767453A (en) 1971-06-30 1973-10-23 Universal Oil Prod Co Method of depositing a high surface area alumina film on a relatively low surface area support
BE792075A (fr) 1971-11-30 1973-05-29 Union Carbide Corp Elements metalliques poreux a revetement ceramique et leur procede de realisation
DE2339338C3 (de) * 1973-02-06 1979-02-15 Deutsche Gold- Und Silber-Scheideanstalt Vormals Roessler, 6000 Frankfurt Verfahren zur Herstellung eines Katalysators für die oxidative Reinigung von Abgasen
UST956185I4 (US07534539-20090519-C00104.png) * 1972-12-28
JPS5320959B2 (US07534539-20090519-C00104.png) * 1973-05-14 1978-06-29
SE464798B (sv) * 1973-10-24 1991-06-17 Johnson Matthey Co Ltd Katalysator innefattande ett substrat, ett mellanliggande oxidskikt och ett katalytiskt skikt
US3957692A (en) * 1973-12-10 1976-05-18 United Kingdom Atomic Energy Authority Method of preparing a catalyst
US3966645A (en) * 1974-02-22 1976-06-29 United Kingdom Atomic Energy Authority Catalyst
GB1471138A (en) * 1974-05-06 1977-04-21 Atomic Energy Authority Uk Supports for catalyst materials
JPS5917521B2 (ja) 1975-08-22 1984-04-21 川崎製鉄株式会社 方向性けい素鋼板に耐熱性のよい上塗り絶縁被膜を形成する方法
IT1070310B (it) 1975-10-22 1985-03-29 Atomic Energy Authority Uk Catalizzatore particolarmente per il trattamento dei gas di scarico di autoveicoli..e procedimento per la sua preparazione
GB1568391A (en) * 1976-04-14 1980-05-29 Atomic Energy Authority Uk Catalysts having metallic substrates
US4070286A (en) * 1976-06-15 1978-01-24 E. I. Du Pont De Nemours And Company Macroporous microspheroids and a process for their manufacture

Also Published As

Publication number Publication date
US4427721A (en) 1984-01-24
JPH024677B2 (US07534539-20090519-C00104.png) 1990-01-30
SE431233B (sv) 1984-01-23
NL7810883A (nl) 1979-05-03
GB2087250A (en) 1982-05-26
DE2857147C2 (de) 1987-03-26
FR2416743A1 (fr) 1979-09-07
FR2416743B1 (US07534539-20090519-C00104.png) 1985-01-18
WO1979000247A1 (en) 1979-05-17
IT7869505A0 (it) 1978-10-31
DE2857147T1 (US07534539-20090519-C00104.png) 1980-12-11
GB2023453B (en) 1982-11-17
JPS54500020A (US07534539-20090519-C00104.png) 1979-09-06
GB2087632B (en) 1982-12-15
GB2087632A (en) 1982-05-26
CA1118301A (en) 1982-02-16
SE7905690L (sv) 1979-06-28
GB2023453A (en) 1980-01-03
GB2087250B (en) 1982-12-08
US4297246A (en) 1981-10-27
SE8201621L (sv) 1982-03-15

Similar Documents

Publication Publication Date Title
IT1160899B (it) Procedimento per formare un rivestimento refrattario su un substrato,particolarmente a scopo di protezione o come sopporto per materiale catalitico
BR8200189A (pt) Processo para preparar um polimero de silazana polimero de silazana assim obtido processo para preparar um material ceramico de carbureto de silicio processo para preparar um artigo revestido com ceramica e tal artigo
EP0228270A3 (en) Catalysts comprising silica supported on a boehmite-like surface, their preparation and use
DE3268909D1 (en) Process for the simultaneous production of fuel gas and thermal energy from carbonaceous materials
IT8220981A0 (it) All'abrasione, procedimento per la composizione per rivestimenti loro applicazione su substrati colorabili resistenti solidi e substrati solidi ottenuti con detto procedimento.
JPS5575506A (en) Support construction of ceramic elements for fixing gas turbine engine
YU47516B (sh) Perovskitni materijali, katalizatori i postupak dobijanja perovskita
ES490718A0 (es) Procedimiento para la fabricacion de paneles para revesti- miento, y paneles obtenidos con tal procedimiento
NO153180C (no) Katalytisk fremgangsmaate for fremstilling av etylen-kopolymerer i en hvirvelsjiktreaktor.
MX147847A (es) Panel de fibra ceramica mejorada y metodo para proteger substratos metalicos de temperaturas elevadas
ATA136879A (de) Verkleidung der aussenseite von baukonstruktion konstruktionen zur thermischen isolierung und abschirmung, insbesondere gegen wind
NO772729L (no) Fremgangsm}te ved belegning av glass eller keramiske overflater
IT1165392B (it) Processo per ridurre la porosita' e la scabrosita' superficiale di substrati ceramici
GB1535451A (en) Coating ceramic with silicon
SE8104496L (sv) Kiselkarbidkeram-forpolymerer som ger hogt utbyte
IT7830699A0 (it) Processo per la preparazione di leganti per vernici, modigicate al polisilossano, idrolosubili.
ES489610A0 (es) Procedimiento para proteger superficies de acero de la ac- cion oxidante de la atmosfera.
IT7926373A0 (it) Ad uno strato di pezzi sagomati in dotazione ausiliaria per la cottura ceramica su vagonetti di cottura.
IT1110265B (it) Barrotto di griglia per rivestimenti di griglia,specialmente di focolari
IT975860B (it) Procedimento per la protezione di parti di carbonio particolarmente di elettrodi di grafite contro l os sidazione ad elevate temperature
DE2964875D1 (en) Process for producing abradable metal/ceramic seal structures, particularly for application on turbine engine surfaces, and seal structures produced according to the process
IT7947991A0 (it) Processo per la desolforazione e calcinazione termica di coke di petrolio
FR2437678B1 (fr) Procede pour la fabrication de pastilles combustibles ceramiques pour reacteurs nucleaires
AT388722B (de) Spaltofen zur katalytischen hochtemperaturspaltung von gasen insbesondere mittels kernenergie
JPS5799340A (en) Thermal shock resistant honeycomb support and manufacture thereof