IN2014KN01673A - - Google Patents
Info
- Publication number
- IN2014KN01673A IN2014KN01673A IN1673KON2014A IN2014KN01673A IN 2014KN01673 A IN2014KN01673 A IN 2014KN01673A IN 1673KON2014 A IN1673KON2014 A IN 1673KON2014A IN 2014KN01673 A IN2014KN01673 A IN 2014KN01673A
- Authority
- IN
- India
- Prior art keywords
- steel sheet
- rolled steel
- cold rolled
- tempered martensite
- volume fraction
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
- C21D1/25—Hardening, combined with annealing between 300 degrees Celsius and 600 degrees Celsius, i.e. heat refining ("Vergüten")
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/26—Methods of annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
- C21D8/0473—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
- C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/002—Bainite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
- C21D8/0436—Cold rolling
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Heat Treatment Of Sheet Steel (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2012050591A JP5348268B2 (ja) | 2012-03-07 | 2012-03-07 | 成形性に優れる高強度冷延鋼板およびその製造方法 |
PCT/JP2013/001217 WO2013132796A1 (ja) | 2012-03-07 | 2013-02-28 | 高強度冷延鋼板及びその製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
IN2014KN01673A true IN2014KN01673A (ko) | 2015-10-23 |
Family
ID=49116292
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
IN1673KON2014 IN2014KN01673A (ko) | 2012-03-07 | 2013-02-28 |
Country Status (11)
Country | Link |
---|---|
US (1) | US9631250B2 (ko) |
EP (1) | EP2824210B1 (ko) |
JP (1) | JP5348268B2 (ko) |
KR (1) | KR101530835B1 (ko) |
CN (1) | CN104160055B (ko) |
BR (1) | BR112014022007B1 (ko) |
CA (1) | CA2866130C (ko) |
IN (1) | IN2014KN01673A (ko) |
MX (1) | MX335961B (ko) |
RU (1) | RU2557035C1 (ko) |
WO (1) | WO2013132796A1 (ko) |
Families Citing this family (31)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5888471B1 (ja) * | 2014-03-31 | 2016-03-22 | Jfeスチール株式会社 | 高降伏比高強度冷延鋼板及びその製造方法 |
CN106133173B (zh) * | 2014-03-31 | 2018-01-19 | 杰富意钢铁株式会社 | 材质均匀性优异的高强度冷轧钢板及其制造方法 |
EP3178953A4 (en) * | 2014-08-07 | 2017-07-05 | JFE Steel Corporation | High-strength steel sheet and production method for same, and production method for high-strength galvanized steel sheet |
CN106574340B (zh) | 2014-08-07 | 2018-04-10 | 杰富意钢铁株式会社 | 高强度钢板及其制造方法、以及高强度镀锌钢板的制造方法 |
EP3178956A4 (en) * | 2014-08-07 | 2017-06-28 | JFE Steel Corporation | High-strength steel sheet and production method for same, and production method for high-strength galvanized steel sheet |
CN106574342B (zh) | 2014-08-07 | 2018-10-12 | 杰富意钢铁株式会社 | 高强度钢板及其制造方法、以及高强度镀锌钢板的制造方法 |
CN104388652B (zh) * | 2014-10-29 | 2016-11-02 | 攀钢集团江油长城特殊钢有限公司 | 一种高速钢冷轧薄板的制造方法和高速钢冷轧薄板 |
JP6179676B2 (ja) * | 2014-10-30 | 2017-08-16 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
EP3214199B1 (en) * | 2014-10-30 | 2019-06-12 | JFE Steel Corporation | High-strength steel sheet, high-strength hot-dip galvanized steel sheet, high-strength hot-dip aluminum-coated steel sheet, and high-strength electrogalvanized steel sheet, and methods for manufacturing same |
US10626485B2 (en) | 2015-02-17 | 2020-04-21 | Jfe Steel Corporation | Thin high-strength cold-rolled steel sheet and method of producing the same |
US20180127856A1 (en) * | 2015-02-27 | 2018-05-10 | Jfe Steel Corporation | High-strength cold-rolled steel sheet and method for manufacturing the same |
MX2017012875A (es) | 2015-04-08 | 2018-02-21 | Nippon Steel & Sumitomo Metal Corp | Miembro de lamina de acero con tratamiento termico y metodo para producir el mismo. |
WO2016163468A1 (ja) * | 2015-04-08 | 2016-10-13 | 新日鐵住金株式会社 | 熱処理鋼板部材およびその製造方法 |
ES2782077T3 (es) | 2015-04-08 | 2020-09-10 | Nippon Steel Corp | Lámina de acero para tratamiento térmico |
KR101736619B1 (ko) | 2015-12-15 | 2017-05-17 | 주식회사 포스코 | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 |
WO2017109540A1 (en) * | 2015-12-21 | 2017-06-29 | Arcelormittal | Method for producing a high strength steel sheet having improved ductility and formability, and obtained steel sheet |
WO2017109538A1 (en) * | 2015-12-21 | 2017-06-29 | Arcelormittal | Method for producing a steel sheet having improved strength, ductility and formability |
US20190276907A1 (en) * | 2016-04-19 | 2019-09-12 | Jfe Steel Corporation | Steel sheet, coated steel sheet, and methods for manufacturing same |
JP6210183B1 (ja) * | 2016-04-19 | 2017-10-11 | Jfeスチール株式会社 | 鋼板、めっき鋼板、およびそれらの製造方法 |
CN106222550A (zh) * | 2016-08-03 | 2016-12-14 | 宁波宏协承汽车部件有限公司 | 一种高强度汽车防撞梁及其制备方法 |
CN108018484B (zh) | 2016-10-31 | 2020-01-31 | 宝山钢铁股份有限公司 | 抗拉强度1500MPa以上成形性优良的冷轧高强钢及其制造方法 |
WO2018115933A1 (en) * | 2016-12-21 | 2018-06-28 | Arcelormittal | High-strength cold rolled steel sheet having high formability and a method of manufacturing thereof |
US11208704B2 (en) | 2017-01-06 | 2021-12-28 | Jfe Steel Corporation | High-strength cold-rolled steel sheet and method of producing the same |
KR102243985B1 (ko) * | 2017-01-06 | 2021-04-22 | 제이에프이 스틸 가부시키가이샤 | 고강도 냉연 강판 및 그 제조 방법 |
WO2019092482A1 (en) * | 2017-11-10 | 2019-05-16 | Arcelormittal | Cold rolled heat treated steel sheet and a method of manufacturing thereof |
KR102375340B1 (ko) * | 2018-02-19 | 2022-03-16 | 제이에프이 스틸 가부시키가이샤 | 고강도 강판 및 그 제조 방법 |
MX2020008637A (es) | 2018-03-30 | 2020-09-21 | Nippon Steel Corp | Lamina de acero. |
KR102109265B1 (ko) * | 2018-09-04 | 2020-05-11 | 주식회사 포스코 | 항복강도비가 우수한 초고강도 고연성 강판 및 그 제조방법 |
US20230304119A1 (en) | 2020-10-15 | 2023-09-28 | Nippon Steel Corporation | Steel sheet and method for manufacturing same |
CN112553527B (zh) * | 2020-11-27 | 2021-11-23 | 中天钢铁集团有限公司 | 一种电炉流程生产高废钢比的20CrMnTi系列齿轮钢氮含量的控制方法 |
DE102021108448A1 (de) * | 2021-04-01 | 2022-10-06 | Salzgitter Flachstahl Gmbh | Stahlband aus einem hochfesten Mehrphasenstahl und Verfahren zur Herstellung eines derartigen Stahlbandes |
Family Cites Families (28)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6159312A (en) * | 1997-12-19 | 2000-12-12 | Exxonmobil Upstream Research Company | Ultra-high strength triple phase steels with excellent cryogenic temperature toughness |
DZ2530A1 (fr) * | 1997-12-19 | 2003-02-01 | Exxon Production Research Co | Procédé de préparation d'une tôle d'acier cette tôle d'acier et procédé pour renforcer la resistanceà la propagation des fissures d'une tôle d'acier. |
FR2790009B1 (fr) * | 1999-02-22 | 2001-04-20 | Lorraine Laminage | Acier dual-phase a haute limite d'elasticite |
CA2387322C (en) | 2001-06-06 | 2008-09-30 | Kawasaki Steel Corporation | High-ductility steel sheet excellent in press formability and strain age hardenability, and method for manufacturing the same |
JP4306202B2 (ja) | 2002-08-02 | 2009-07-29 | 住友金属工業株式会社 | 高張力冷延鋼板及びその製造方法 |
JP4268079B2 (ja) | 2003-03-26 | 2009-05-27 | 株式会社神戸製鋼所 | 伸び及び耐水素脆化特性に優れた超高強度鋼板、その製造方法、並びに該超高強度鋼板を用いた超高強度プレス成形部品の製造方法 |
JP4362319B2 (ja) | 2003-06-02 | 2009-11-11 | 新日本製鐵株式会社 | 耐遅れ破壊特性に優れた高強度鋼板およびその製造方法 |
JP4109619B2 (ja) | 2003-12-16 | 2008-07-02 | 株式会社神戸製鋼所 | 伸び、及び伸びフランジ性に優れた高強度鋼板 |
JP4445365B2 (ja) * | 2004-10-06 | 2010-04-07 | 新日本製鐵株式会社 | 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法 |
JP3889768B2 (ja) | 2005-03-31 | 2007-03-07 | 株式会社神戸製鋼所 | 塗膜密着性と延性に優れた高強度冷延鋼板および自動車用鋼部品 |
JP4164537B2 (ja) * | 2006-12-11 | 2008-10-15 | 株式会社神戸製鋼所 | 高強度薄鋼板 |
JP5223360B2 (ja) | 2007-03-22 | 2013-06-26 | Jfeスチール株式会社 | 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP2009068039A (ja) * | 2007-09-11 | 2009-04-02 | Nisshin Steel Co Ltd | エネルギー吸収特性に優れた高強度合金化溶融亜鉛めっき鋼板及びその製造方法 |
JP5365217B2 (ja) * | 2008-01-31 | 2013-12-11 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5167487B2 (ja) * | 2008-02-19 | 2013-03-21 | Jfeスチール株式会社 | 延性に優れる高強度鋼板およびその製造方法 |
JP5206244B2 (ja) | 2008-09-02 | 2013-06-12 | 新日鐵住金株式会社 | 冷延鋼板 |
JP2010065272A (ja) | 2008-09-10 | 2010-03-25 | Jfe Steel Corp | 高強度鋼板およびその製造方法 |
JP5365112B2 (ja) | 2008-09-10 | 2013-12-11 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5418047B2 (ja) * | 2008-09-10 | 2014-02-19 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5709151B2 (ja) | 2009-03-10 | 2015-04-30 | Jfeスチール株式会社 | 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5412182B2 (ja) | 2009-05-29 | 2014-02-12 | 株式会社神戸製鋼所 | 耐水素脆化特性に優れた高強度鋼板 |
JP5347739B2 (ja) | 2009-06-11 | 2013-11-20 | 新日鐵住金株式会社 | 析出強化型複相冷延鋼板の製造方法 |
JP5521444B2 (ja) * | 2009-09-01 | 2014-06-11 | Jfeスチール株式会社 | 加工性に優れた高強度冷延鋼板およびその製造方法 |
BR112012013042B1 (pt) * | 2009-11-30 | 2022-07-19 | Nippon Steel Corporation | Chapa de aço de alta resistência com resistência máxima à tração de 900 mpa ou mais e métodos de produção da mesma |
JP5487984B2 (ja) | 2010-01-12 | 2014-05-14 | Jfeスチール株式会社 | 曲げ性に優れた高強度冷延鋼板およびその製造方法 |
JP2011153336A (ja) * | 2010-01-26 | 2011-08-11 | Nippon Steel Corp | 成形性に優れた高強度冷延鋼板及びその製造方法 |
JP5327106B2 (ja) | 2010-03-09 | 2013-10-30 | Jfeスチール株式会社 | プレス部材およびその製造方法 |
JP5671391B2 (ja) | 2010-03-31 | 2015-02-18 | 株式会社神戸製鋼所 | 加工性および耐遅れ破壊性に優れた超高強度鋼板 |
-
2012
- 2012-03-07 JP JP2012050591A patent/JP5348268B2/ja not_active Expired - Fee Related
-
2013
- 2013-02-28 WO PCT/JP2013/001217 patent/WO2013132796A1/ja active Application Filing
- 2013-02-28 EP EP13758658.2A patent/EP2824210B1/en not_active Not-in-force
- 2013-02-28 US US14/383,008 patent/US9631250B2/en active Active
- 2013-02-28 CN CN201380012719.0A patent/CN104160055B/zh not_active Expired - Fee Related
- 2013-02-28 MX MX2014010648A patent/MX335961B/es unknown
- 2013-02-28 BR BR112014022007-7A patent/BR112014022007B1/pt not_active IP Right Cessation
- 2013-02-28 IN IN1673KON2014 patent/IN2014KN01673A/en unknown
- 2013-02-28 CA CA2866130A patent/CA2866130C/en not_active Expired - Fee Related
- 2013-02-28 KR KR1020147024900A patent/KR101530835B1/ko active IP Right Grant
- 2013-02-28 RU RU2014140310/02A patent/RU2557035C1/ru not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
MX2014010648A (es) | 2014-11-21 |
EP2824210A4 (en) | 2015-04-29 |
EP2824210A1 (en) | 2015-01-14 |
US20150034219A1 (en) | 2015-02-05 |
JP2013185196A (ja) | 2013-09-19 |
CA2866130C (en) | 2016-04-26 |
KR20140112581A (ko) | 2014-09-23 |
JP5348268B2 (ja) | 2013-11-20 |
MX335961B (es) | 2016-01-05 |
KR101530835B1 (ko) | 2015-06-22 |
CN104160055B (zh) | 2016-05-04 |
CN104160055A (zh) | 2014-11-19 |
RU2557035C1 (ru) | 2015-07-20 |
US9631250B2 (en) | 2017-04-25 |
CA2866130A1 (en) | 2013-09-12 |
EP2824210B1 (en) | 2016-10-05 |
WO2013132796A1 (ja) | 2013-09-12 |
BR112014022007B1 (pt) | 2019-04-30 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
IN2014KN01673A (ko) | ||
MX2016007954A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
MX2015014099A (es) | Hoja de acero laminada en caliente y metodo de fabricacion de la misma. | |
MX339219B (es) | Lamina de acero de alta resistencia y lamina de acero revestida con zinc de alta resistencia que tiene excelente ductilidad y capacidad de embridado por estiramiento y metodo de fabricacion de las mismas. | |
MX2018009643A (es) | Lamina de acero de alta resistencia y metodo para la produccion de la misma. | |
MX2016001723A (es) | Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma. | |
UA117134C2 (uk) | Холоднокатаний сталевий лист, спосіб його виробництва і автотранспортний засіб | |
MX2015013579A (es) | Lamina de acero recocida despues de galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
MX357839B (es) | Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas. | |
MX2017001529A (es) | Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia. | |
MA32294B1 (fr) | Procede de fabrication de toles d'aciers dual phase laminees a froid a tres haute resistance et toles ainsi produites | |
MX2020003923A (es) | Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma. | |
IN2014DN03212A (ko) | ||
UA118036C2 (uk) | Високоміцна сталь та спосіб виготовлення | |
WO2009066734A1 (ja) | 高強度冷延鋼板 | |
MX2015011027A (es) | Hoja de acero laminada en caliente y metodo para fabricar la misma. | |
MX2015013516A (es) | Lamina de acero de alta resistencia y metodo para la produccion de la misma. | |
MX350016B (es) | Lámina de acero con altas propiedades de resistencia mecánica, ductilidad y de formación, método de producción de la misma y uso de dichas láminas. | |
MX2016012708A (es) | Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en inmersion en caliente de alta resistencia y chapa de acero galvanfusionado en inmersion en caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad. | |
GB201210376D0 (en) | High Strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof | |
MX2018007641A (es) | Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida. | |
PL2256224T3 (pl) | Blacha stalowa cienka walcowana na zimno o dużej wytrzymałości, blacha stalowa cienka ocynkowana o dużej wytrzymałości i blacha stalowa cienka stopowa cynkowana na gorąco o dużej wytrzymałości mające doskonałą odkształcalność i spawalność oraz sposoby ich wytwarzania | |
IN2014DN08590A (ko) | ||
GB2452231B (en) | High-strength steel sheet having excellent elongation, stretch flangeability, and weldability | |
MX2018009735A (es) | Lamina de acero de alta resistencia y metodo para fabricar la misma. |