FR2510547A1 - Verre optique depourvu de cdo et de tho2 et ayant un indice de refraction eleve - Google Patents

Verre optique depourvu de cdo et de tho2 et ayant un indice de refraction eleve Download PDF

Info

Publication number
FR2510547A1
FR2510547A1 FR8213168A FR8213168A FR2510547A1 FR 2510547 A1 FR2510547 A1 FR 2510547A1 FR 8213168 A FR8213168 A FR 8213168A FR 8213168 A FR8213168 A FR 8213168A FR 2510547 A1 FR2510547 A1 FR 2510547A1
Authority
FR
France
Prior art keywords
weight
glasses
cdo
tho2
optical glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR8213168A
Other languages
English (en)
Other versions
FR2510547B1 (fr
Inventor
Karl Mennemann
Volkmar Geiler
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
Original Assignee
Schott Glaswerke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schott Glaswerke AG filed Critical Schott Glaswerke AG
Publication of FR2510547A1 publication Critical patent/FR2510547A1/fr
Application granted granted Critical
Publication of FR2510547B1 publication Critical patent/FR2510547B1/fr
Granted legal-status Critical Current

Abstract

L'INVENTION CONCERNE DES VERRES OPTIQUES TRES REFRINGENTS QUI SONT DEPOURVUS DE CDO ET DE THO. LEURS INDICES DE REFRACTION SONT COMPRIS ENTRE 1,85 ET 2,05 ET LEURS INDICES D'ABBE SONT COMPRIS ENTRE 25 ET 43. LEURS COMPOSITIONS SE SITUENT DANS LA GAMME SUIVANTE:SIO, DE 5 A 15; BO, DE 2,5 A 8; SIOBO, DE 7,5 A 23; SIOBO, DE 1,3 A 2,1; LAO, DE 43 A 56; GDO, DE 0 A 14; LAOGDO DE 43 A 60; ZRO, DE 3 A 10; NBO, DE 0 A 15; TAO, DE 0 A 20; NBO TAO, DE 11 A 22.

Description

Verre optique dépourvu de Cd O et de Th O, et ayant un indice
de réfraction élevé.
La présente invention concerne des verres optiques très réfringents ou extrêmement réfringents,qui ont un indice d'Abbe élevé Grâce à la présente invention il est possible
de fabriquer des verres optiques ayant des indices de réfrac-
tion jusqu'à présent inégalés, puisqu'ils peuvent s'élever jus-
qu'à 2,05,et des indices d'Abbe supérieurs à 25.
Le premier fascicule publié de la demande de brevet
JP 79 133 506 décrit des verres ayant des indices de réfrac-
tion de 1,90 à 1,95 et des indices d'Abbe analogues à ceux des verres de la présente invention; la valeur maximale que peuvent atteindre les indices de réfraction, selon ce document,
n'est donc que de 1,95, et cela avec une proportion très impor-
tante de Ge O 2, corps très coûteux.
Des verres ayant des indices de réfraction allant jus-
qu'à 1,95 et des indices d'Abbe analogues sont également décrits dans le premier fascicule publié de la demande de brevet JP 79 90 218; mais ou bien ces verres connus contiennent de l'oxyde coûteux Ge O 2, ou bien ils ne résistent pas suffisamment bien à
la dévitrification.
Cela étant, la présente invention a pour objet des verres optiques dépourvus de Cd O et de Th O 2, à haut indice de réfraction, plus précisément à indice de réfraction compris entre 1,85 et 2,05, et à indice d'Abbe compris entre 25 et 43, verres caractérisés en ce qu'ils ont la composition suivante, en % en poids: Si O 2 de 5 à 15 B 203 de 2,5 à 8 Si O 2 2 3 de 7,5 à 23 Si O 2 / B 203 de 1,3 à 2,1 La 203 de 43 à 56 Gd 203 de O à 14 La 203 + Gd 203 de 43 à 60 Zr O 2 de 3 à 10 Nb 205 de O à 15 Ta 25 de O à 20 Nb 205 + Ta 205 de 11 à 22
Une particularité tout à fait essentielle de la pré-
sente invention est le rapport Si O 2/B 203 extrêmement élevé, qui, selon l'invention, est compris entre 1,3 et 2,1 En effet, tous les verres que l'on connaissait jusqu'à présent dans la zone indiquée du diagramme nd-vd nécessitent des com- positions dans lesquelles la proportion de B 203 dépasse celle de Si O 2 C'est ainsi que dans les verres du premier fascicule
publié de la demande de brevet DE 2 653 581,le maximum du rap-
port Si O 2/B 203 est de 1 Dans les verres que décrit le second fascicule publié de la demande de brevet DE 1 926 959 et pour lesquels nd est égal à 1,9 et vd à 40,le rapport Si O 2/B 203 est
d'environ 0,75; en outre ces verres contiennent l'oxyde coû-
teux Ge O 2 Ilen va de même pour les verres du premier fasci-
cule publié de la demande de brevet DE 20 57 706.
D-'autres verres optiques très réfringents à rapport
Si O 2/B 203 au moins égal à 1 sont décrits dans le second fasci-
cule publié de la demande de brevet DE 1 061 976 Tous les exemples à indice de réfraction supérieur à 1,85 qui sont cités dans ce document ont des teneurs en La 203 d'environ 63 % en poids Ces hautes teneurs en La 203 nuisent à la stabilité de ces verres; de plus ceux-ci contiennent obligatoirement Al O ou Y 203 Conformément à l'invention, le meilleur rapport Si O 2/
B 203 est compris entre 1,6 et 1,9 Pour obtenir les hauts indi-
ces de réfraction nécessaires, c'est-à-dire des indices au moins égaux à 1,86, il faut de 43 à 56 % en poids de La 203 ainsi que, au choix, de O à 14 % en poids de Gd 203, la somme de ces deux
composants étant comprise entre 43 et 60 % en poids.
La proportion de Zr O 2 est de 3 à 10 % en poids Il est absolument indispensable qu'il y ait une fraction de 11 à 22 % en poids des vitrifiants de remplacement pentavalents Ta 205 et Nb 205, la proportion de Nb 205 pouvant aller de 0 à 15 % en poids et celle de Ta 205 de O à 20 % en poids Ce n'est qu'avec ces hautes teneurs en Nb 205 et/ou Ta 205 que l'on peut fabriquer par fusion des verres ayant l'état optique requis et qui sont
suffisamment stables à la dévitrification; en outre ces compo-
santes augmentent beaucoup l'indice de réfraction Il peut éga-
lement y avoir Pb O (de O à 13 % en poids), Ti O 2 (de O à 13 % en poids), WO 3 (de O à 23 % en poids) et Zn O (de O à 3 % en poids).
On fabrique des verres conformes à la présente inven-
tion en opérant de la façon suivante.
On pèse les matières premières (c'est-à-dire les oxy-
des, nitrates et carbonates correspondants) conformément à la composition voulue; on ajoute une petite proportion d'un agent
d'affinage, tel As 2 3 ' par petitesquantités,et on mélange bien.
On fond ce mélange dans un creuset en platine à une température de 1450 à 1550 'C, on l'affine et on l'homogénéise bien au moyen d'un agitateur Ensuite on continue d'agiter jusqu'à ce que la température de coulée, soit environ 14000 C,soit atteinte,et on
coule dans un moule en fer.
Dans le tableau suivant on a rassemblé 11 compositions,
citées à titre d'exemples, dont-on indique les valeurs optiques.
9 1 go Iz q 1 si ', 1ZE ', TSL'T 691 T 9911 19,11 gli OL' T z OTS ot'ITE ozjsú OT'ze OT "OC 00 GE 09 'SE SL OE O 9 PE SL" 9 Z OT'LZ 09 9 ú PA Ot IP 6 "T Og Lgàl OC 99 'T Oút O"Z t'69 VT GZ 6 'T ZTL 6 T 68 T 6 "T úLúOiz 99 PO'Z TTT 6 'T pu Sz 4 z TOSIOT Sv'lz çz Izz O E ', O T E O z POú O z PE) ouz E om E om G 91 EWo oú 9 OLIO qu'o O 9 ', C)09 IZT W 9 99- 10 ZOTJJ ss,'ú 9 1l O 09 JE OEIT OL't, çzjz spiz GLIT 9611 T 001 T oqci SL O 1 SE l 9 t 06 l O T 00 'TT O 9 j O T 99 'L SE ', 9 SS'ZI SP'6 os,,úT go Z-ej, 9 z C 6 09 111 09 '6OL l 6 OSJ 9 Op Ig oi ll SEIS 99 ', q SE - P O q N z OGIL 90 'L 09 JL 591 E ot Ig 09 6 oz ', 9osls SCIS SLIS os 8 ozz OS' ES OE:'9 P 99 'St, 9 Z S O E 99 O T 09 08 " E GL'L 06 Lt, SP l 6 99 t S O z-erl oz 1 t,O T 06 9sz t, sels 08 "ç SE 1 ggig W 001 E SE 19 O E El op'IL ggle T OLIZT St,'L SL"L SEOI Súl L 06 OT 01 'L OP'g oeloi -Z OTS il OT 9 L 9 9 E z T O ldurexa N. : -r v CD le- Ln Cu nvzlrlavj,
2510547 '

Claims (4)

REVENDICATIONS
1 Verre optique très réfringent, dépourvu de et de Th O 2 et ayant un indice de réfraction de 1,85 à et un indice d'Abbe de 25 à 43, verre caractérisé par position suivante en % en poids: Si O 2 de 5 à 15 B 203 de 2,5 à 8 Si O 2 + B 203 de 7,5 à 23 Si O 2 / B 203 de 1,3 à 2,1 0 La 203 de 43 à 56 Gd 203 de O à 14 La 203 + Gd 203 de 43 à 60 Zr O 2 de 3 à 10 Nb 205 de O à 15 Ta 205 de O à 20 Nb 25 + Ta 205 de 11 à 22 2 Verre selon la revendication 1, la composition suivante en % en poids: Si O 2 de 5 à 15 B 203 de 2,5 à 8 Si O 2 + B 203 de 7,5 à 23 Si O 2 / B 203 de 1, 6 à 1,9 La 203 de 43 à 56 Gd 203 de O à 14 La 203 + Gd 203 de 43 à 60 Zr O 2 de 5 à 9 Nb 205 de O à 15 Ta 25 de O à 20 Nb 205 + Ta 205 de 11 à 22 caractérisé par
3 Verre selon l'une des revendications 1 et 2, carac-
térisé en ce qu'il contient en outre:
de O à 13 % en poids de Ti O 2.
4 Verre selon l'une quelconque des revendications 1 à
3, caractérisé en ce qu'il contient en outre: de O à 13 % en poids de Pb O. Cd O 2,05
la com-
Verre selon l'une quelconque des revendications 1 à
4, caractérisé en ce qu'il contient en outre:
de O à 23 % en poids de WO 3.
6 Verre selon l'une quelconque des revendications 1 à
5, caractérisé en ce qu'il contient en outre: de O à 3 % en poids de Zn O.
FR8213168A 1981-07-30 1982-07-28 Verre optique depourvu de cdo et de tho2 et ayant un indice de refraction eleve Granted FR2510547A1 (fr)