FI95713B - Partikel av kärn/hölje-polymer och förfarande för framställning av den - Google Patents
Partikel av kärn/hölje-polymer och förfarande för framställning av den Download PDFInfo
- Publication number
- FI95713B FI95713B FI885842A FI885842A FI95713B FI 95713 B FI95713 B FI 95713B FI 885842 A FI885842 A FI 885842A FI 885842 A FI885842 A FI 885842A FI 95713 B FI95713 B FI 95713B
- Authority
- FI
- Finland
- Prior art keywords
- core
- polymer
- monomer
- acid
- envelope
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F267/00—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated polycarboxylic acids or derivatives thereof as defined in group C08F22/00
- C08F267/02—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated polycarboxylic acids or derivatives thereof as defined in group C08F22/00 on to polymers of acids or salts
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F265/00—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00
- C08F265/02—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00 on to polymers of acids, salts or anhydrides
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F265/00—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00
- C08F265/04—Macromolecular compounds obtained by polymerising monomers on to polymers of unsaturated monocarboxylic acids or derivatives thereof as defined in group C08F20/00 on to polymers of esters
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F285/00—Macromolecular compounds obtained by polymerising monomers on to preformed graft polymers
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S525/00—Synthetic resins or natural rubbers -- part of the class 520 series
- Y10S525/902—Core-shell
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Graft Or Block Polymers (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
Claims (27)
1. Partikel av käm/hölje-polymer ömfattande en kärna av en polymer bildad av ätminstone en etyleniskt omättad monomer som innehäller syrafunktionalitet och ett härt hölje som väsentli- 5 gen inkapslar kärnan och omfattar en kopolymer av en nonjonisk, monoetyleniskt omättad alifatisk monomer, varvid partikeln in-nefattar ätminstone ett hälrum som härrör frän reaktion med en icke-flyktig fast eller permanent bas, kännetecknad av att i polymeren som bildar hoi j et ingär även ätminstone 2 viktprocent 10 av en esterhaltig, omättad monomer som har valts sä att dess homopolymer har en glasövergängstemperatur som är högst 15°C samt frän 0 tili 25 molprocent av en nonjonisk, monoetyleniskt omättad aromatisk monomer, att de för bildande av höljet använ-da monomererna har valts sä att de är fria frän funktionella 15 syragrupper och att kopolymeren som bildar höljet har en glasövergängstemperatur som är minst 40°C.
2. Partikel av käm/hölje-polymer enligt patentkrav 1, kanne-tecknad av att den nonjoniska, monoetyleniskt omättade aroma- 20 tiska monomeren är vald ur gruppen som bestär av styren, alfa-metylstyren, vinyltoluen, ringsubstituerade derivat av alfame-tylstyren och vinyltoluen och blandningar därav.
3. Partikel av käm/hölje-polymer enligt patentkrav 1 eller 25 2, kännetecknad av att höljekopolymerens glasövergängstempera tur är högst 120°C.
4. Partikel av käm/hölje-polymer enligt patentkrav 1, 2 eller 3, kännetecknad av att höljekopolymerens glasövergängstem- 30 peratur är frän 60°C tili 100°C.
5. Partikel av käm/hölje-polymer enligt nägot av de före- : gäende patentkraven, kännetecknad av att höljekopolymeren har bildats av en nonjonisk, monoetyleniskt omättad, alifatisk mo-35 nomer som är vald ur gruppen som bestär av estrar av metakryl-syra, vinylklorid, vinyldenklorid och akrylonitril.
6. Partikel av kärn/hölje-polymer enligt nägot av de före-gäende patentkraven, kännetecknad av att den esterhaltiga, 40 omättade monomeren är vald ur gruppen som bestär av alkyl- 22 9 5 7 1 3 akrylat, alkylmetakrylat, längkedjiga estrar av akrylsyra, längkedjiga estrar av metakrylsyra och estrar av maleinsyra.
7. Partikel av kärn/hölje-polymer enligt nägot av patentkra-5 ven 1-5, kännetecknad av att den esterhaltiga, omättade monome- ren är vald ur gruppen som bestär av butylakrylat, etylakrylat, isobutylakrylat, etylhexylakrylat och dibutylmaleat.
8. Partikel av kärn/hölje-polymer enligt nägot av de före-10 gäende patentkraven, kannetecknad av att den etyleniskt omättade monomer, som innehäller syrafunktionalltet, är vald ur gruppen som bestär av akrylsyra, metakrylsyra, itakonsyra, akonit-syra, maleinsyra, maleinsyraanhydrid, fumarsyra, krotonsyra och monoestrar av dessa syror. 15
9. Partikel av kärn/hölje-polymer enligt nägot av de före-gäende patentkraven, kännetecknad av att kärnan är en kopolymer av den etyleniskt omättade monomer som innehäller syrafunk-tionalitet och en eteniskt omättad monomer som icke innehäller 20 nägra joniserbara grupper.
10. Partikel av kärn/höljepolymer enligt patentkrav 9, kän-netecknad av att den etyleniskt omättade monomer som icke innehäller nägra joniserbara grupper, är vald ur gruppen som bestär 25 av metylmetakrylat, styren vinyltoluen, alfametylstyren, ety-len, vinylacetat, vinylklorid, akrylnitril, metakrylamid, ak-rylamid, alkylestrar av metakrylsyra, alkenylestrar av metakrylsyra, alkylestrar av akrylsyra, alkenylestrar av akrylsyra och alkylestrar av vinylalkohol. 30
11. Partikel av kärn/hölje-polymer enligt nägot av de före-gäende patentkraven, kännetecknad av att kärnpolymeren är bil- • dad av ätminstone 10 viktprocent av den eteniskt omättade mono mer som innehäller syrafunktionalitet. 35
12. Partikel av kärn/hölj e-polymer enligt patentkrav 11, kännetecknad av att mängden av den etyleniskt omättade monomer, som innehäller syrafunktionalitet, är ätminstone 20 viktprocent ·’ av kärnpolymeren. 40 23 55713
13. Partikel av kärn/hölje-polymer enligt nägot av de före-gäende patentkraven, kannetecknad av att kärnpolymeren även är framställd av etyleniskt omättad monomer med ätminstone difunk-tionalitet. 5
14. Partikel av kärn/hölje-polymer enligt patentkrav 13, kännetecknad av att nämnda monomer är vald ur gruppen som bes-tär av etylenglykoldimetakrylat, etylenglykoldiakrylat, allyl-metakrylat, allylakrylat, 1,3-butandioldimetakrylat, 1,3-butan- 10 dioldiakrylat, divinylbensen och trimetylolpropantriakrylat.
15. Partikel av kärn/hölje-polymer enligt patentkrav 13 el-ler 14, kannetecknad av att mängden etyleniskt omättad monomer med ätminstone difunktionalitet är frän 0,1 % tili 5 viktpro- 15 cent av den totala monomermängd som ingär i kärnan.
16. Förfarande för framställning av partiklar av käm/hölje-polymer, vilket omfattar bildande av ett monomersystem innehäl-lande ätminstone en etyleniskt omättad monomer med syrafunk- 20 tionalitet, polymerisering av systemet i form av en vattenhal-tig emulsion för bildning av kärnpartiklar, bildande av en vat-tenhaltig dispersion av kärnpartiklama samt en blandning inne-hällande en nonjonisk, monoetyleniskt substituerad alifatisk monomer samt polymerisering för bildande av ett hölje kring 25 kärnpartiklama, blandande av en icke-flyktig fast eller permanent bas med de erhällna partiklarna av kärn/hölje-polymer : utan ett organiskt lösningsmedel och svällning av kämoma vid en temperatur av 50-120°C för alstring däri av ett eller flera hälrum, kannetecknat av att i blandningen som innehäller den 30 alifatiska monomeren ingär även ätminstone 2 viktprocent av en esterhaltig, omättad monomer som har valts bland de monomerer, vilka vid homopolymerisering ger en polymer med en glasöver-: gängstemperatur som är högst 15°C samt frän 0 tili 25 molpro- cent av en nonjonisk, monoetyleniskt omättad aromatisk monomer, 35 att de för bildande av höljet använda monomerema väljs sä att de är fria frän funktionella syragrupper och att monomerema kopolymeriseras sä att pä kärnpartiklama avsätts ett härt hölje med en glasövergängstemperatur som är minst 40°C.
17. Förfarande enligt patentkrav 16, kännetecknat av att kärnpartiklarna bildas genom polymerisation av erfordrade mo-nomerer pä i förväg bildade partiklar av ymppolymer dispergera-de i vatten. 5
18. Förfarande enligt patentkrav 17, kannetecknat av att ymppolymeren är en polymer av en vinylgrupphaltig monomer.
19. Förfarande enligt patentkravet 17 eller 18, kännetecknat 10 av att partiklarna av ymppolymer har mindre storlek än 100 nm.
20. Förfarande enligt nägot av patentkraven 16-19, kännetecknat av att kärnpartikeln har en storlek av 100-1000 nm när den är i osvällt tillständ. 15
21. Förfarande enligt patentkrav 20, kännetecknat av att kärnpartikeln har en storlek frän 100 tili 500 nm.
22. Förfarande enligt nägot av patentkraven 16-21, känne-20 tecknat av att kärn/höljepartiklarna efter bildning och före svällning har en storlek av 150-4000 nm.
23. Förfarande enligt patentkrav 22, kännetecknat av att partikeln har en storlek frän 200 tili 2000 nm. 25
24. Förfarande enligt nägot av patentkraven 16-23, kännetecknat av att basen är en alkalimetallhydroxid.
24. E 7 13
25. Förfarande enligt nägot av patentkraven 16-23, känne-30 tecknat av att basen är ett aikaiimetailbikarbonat.
26. Förfarande enligt nägot av patentkraven 16-25, känne- ' tecknat av att partiklarna bringas att svälla genom uppvärmning med basen vid förhöjd temperatur. 35
27. Förfarande enligt patentkrav 26, kännetecknat av att temperaturen är frän 85°C tili 98°C. II