FI109351B - Förfarande för framställning av cellulosasuspension - Google Patents
Förfarande för framställning av cellulosasuspension Download PDFInfo
- Publication number
- FI109351B FI109351B FI965075A FI965075A FI109351B FI 109351 B FI109351 B FI 109351B FI 965075 A FI965075 A FI 965075A FI 965075 A FI965075 A FI 965075A FI 109351 B FI109351 B FI 109351B
- Authority
- FI
- Finland
- Prior art keywords
- cellulose
- amine oxide
- tertiary amine
- liquid aqueous
- solution
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08B—POLYSACCHARIDES; DERIVATIVES THEREOF
- C08B1/00—Preparatory treatment of cellulose for making derivatives thereof, e.g. pre-treatment, pre-soaking, activation
- C08B1/003—Preparation of cellulose solutions, i.e. dopes, with different possible solvents, e.g. ionic liquids
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J3/00—Processes of treating or compounding macromolecular substances
- C08J3/02—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques
- C08J3/09—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in organic liquids
- C08J3/11—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in organic liquids from solid polymers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L1/00—Compositions of cellulose, modified cellulose or cellulose derivatives
- C08L1/02—Cellulose; Modified cellulose
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
- D01D1/00—Treatment of filament-forming or like material
- D01D1/02—Preparation of spinning solutions
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F2/00—Monocomponent artificial filaments or the like of cellulose or cellulose derivatives; Manufacture thereof
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2301/00—Characterised by the use of cellulose, modified cellulose or cellulose derivatives
- C08J2301/02—Cellulose; Modified cellulose
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Medicinal Chemistry (AREA)
- Textile Engineering (AREA)
- Materials Engineering (AREA)
- Life Sciences & Earth Sciences (AREA)
- General Chemical & Material Sciences (AREA)
- Biochemistry (AREA)
- Mechanical Engineering (AREA)
- Dispersion Chemistry (AREA)
- Polysaccharides And Polysaccharide Derivatives (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Artificial Filaments (AREA)
- Manufacture Of Macromolecular Shaped Articles (AREA)
- Cephalosporin Compounds (AREA)
Claims (10)
1. Förfarande för framställning av en cellulosasuspension i en flytande, vattenhaltig tertiär 5 aminoxid, varvid finfördelad cellulosa blandas i en flytande, vattenhaltig tertiär aminoxid, kanne-t e c k n a t av att (A) den finfördelade cellulosan bringas i kontakt med flytande, vattenhaltig tertiär aminoxid, varvid en 10 första blandning bildas och (B) denna första blandning utbreds mekaniskt som ett skikt pä en yta och transporteras under intensiv omrörning över denna yta, tills en homogen suspension bildas, vilken avlägsnas frän ytan, varvid 15 (C) stegen (A) och (B) utförs kontinuerligt.
2. Förfarande enligt patentkrav 1, k ä n n e -tecknat av att som flytande, vattenhaltig tertiär aminoxid används en vattenlösning av den tertiära aminoxiden. 20
3. Förfarande enligt patentkrav 1, k ä n n e - tecknat av att som flytande, vattenhaltig tertiär aminoxid används en smält tertiär aminoxidhydrat.
4. Förfarande enligt nägot av patentkraven 2 eller 3, kännetecknat av att man « « •·: : 25 använder en flytande, vattenhaltig tertiär aminoxid, vars • ’·· temperatur är inom omrädet 50-85 °C.
, : 5. Förfarande enligt nägot av patentkraven 1-4, ; ;'j kännetecknat av att cellulosan som » v » * , bringats i kontakt med den flytande, vattenhaltiga !!! 30 tertiära aminoxiden transporteras över ytan under en ' tidsperiod av 1-5 minuter.
6. Användning av en anordning för att utföra ett :/·> förfarande enligt nägot av patentkraven 1-5, k ä n- ·’: netecknad av att anordningen är ett . 35 indirekt uppvärmbart eller kylbart, med ett omrörningsor- t t * 109351 ί gan försett kärl, som bildas av en cylindrisk behällare (1), som är försedd med en centriskt lagrad rotor (2) och med därtill fästa omrörningselement (3, 4), som bildar en lutningsvinkel <χ med rotorns (2) axel för omrörning och 5 transportering av cellulosa som bringats i kontakt med den flytande, vattenhaltiga tertiära aminoxiden, varvid omrörningselementens (3, 4) radiala maximiavständ frän behällarens innervägg är 20 mm och behällarens (1) övre del är försedd med inloppsöppningar (6, 7) för den 10 finfördelade cellulosan och den flytande, vattenhaltiga tertiära aminoxiden och behällarens nedre del är försedd med en utloppsöppning (8) för den homogena suspensionen.
7. Användning av en anordning enligt patentkrav 6, kännetecknad av att lutnings- 15 vinkein a är reglerbar.
8. Förfarande för framställning av en formbar cellulosalösning, kännetecknat av att en enligt patentkraven 1-7 framställd homogen suspension genom avdunstning av vatten bearbetas tili en 20 formbar cellulosalösning.
9. Förfarande enligt patentkrav 8, kännetecknat av att det utförs i en tunnskiktsbe-handlingsanordning.
10. Förfarande för framställning av cellulosa- j : 25 formstycken, kännetecknat av att en enligt patentkrav 8 framställd formbar cellulosalös- ···. ning bearbetas pä ett i och för sig känt sätt tili « · folier, fibrer, membran eller andra formstycken. t t t t « i t • » > • t · • * · • · · I * » » · • tl I · I I « I * I • I t > t I lit I t I I I » • » » » »tl * » ·