ES2296002T3 - Poliestireno expansible. - Google Patents

Poliestireno expansible. Download PDF

Info

Publication number
ES2296002T3
ES2296002T3 ES05009648T ES05009648T ES2296002T3 ES 2296002 T3 ES2296002 T3 ES 2296002T3 ES 05009648 T ES05009648 T ES 05009648T ES 05009648 T ES05009648 T ES 05009648T ES 2296002 T3 ES2296002 T3 ES 2296002T3
Authority
ES
Spain
Prior art keywords
waxes
expandable polystyrene
zirconium
polyolefin waxes
bis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES05009648T
Other languages
English (en)
Inventor
Christian Lechner
Gerd Dr. Hohner
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Clariant Produkte Deutschland GmbH
Original Assignee
Clariant Produkte Deutschland GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Clariant Produkte Deutschland GmbH filed Critical Clariant Produkte Deutschland GmbH
Application granted granted Critical
Publication of ES2296002T3 publication Critical patent/ES2296002T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Poliestireno expansible, que contiene entre 0, 01 y 10 % en peso de ceras poliolefínicas, siendo preparadas las ceras poliolefínicas con ayuda de catalizadores del tipo de metalocenos y teniendo un punto de goteo o de reblandecimiento de anillo y bola comprendido entre 80 y 165ºC y una viscosidad de las masas fundidas, medida a una temperatura situada a 10ºC por encima del punto de goteo o de reblandecimiento, comprendida entre 20 y 10.000 mPaus.

Description

Poliestireno expansible.
El invento se refiere a un poliestireno expansible (EPS), que contiene ceras poliolefínicas, las cuales se habían preparado con ayuda de catalizadores de metalocenos.
Presenta una importancia especial en el caso de la preparación de un poliestireno expansible la estructura de una espuma. La homogeneidad y el tamaño de las celdas individuales determinan las propiedades de una espuma, es decir la expansibilidad y el período de tiempo de descomposición de la presión así como las propiedades de los materiales espumados, tales como por ejemplo la calidad superficial, las propiedades mecánicas (rigidez) y las ópticas. Con un número creciente de celdas, es decir celdas más finas, los períodos de tiempo de desmoldeo (períodos de tiempo de descomposición de la presión) disminuyen drásticamente, una elevación de los números de celdas de 6 a 12 por mm produce aproximadamente una división por la mitad del período de tiempo de desmoldeo. De esta manera se aumenta esencialmente la rentabilidad en el caso de la preparación. Unas estructuras más finas de las celdas dan lugar además a una rigidez elevada así como a un aspecto ópticamente "más blanco".
Esta estructura celular homogénea y más fina, que se ha de pretender, se consigue con ayuda de los denominados agentes formadores de núcleos (agentes de nucleación), que se añaden al realizar la polimerización de un poliestireno expansible. En ausencia de estos agentes formadores de núcleos se forman celdas de diversos tamaños. Esto repercute negativamente sobre las propiedades mecánicas y ópticas, arriba descritas, de la espuma.
Como posibles agentes formadores de núcleos se conocen polietilenos o respectivamente ceras poliolefínicas, parafinas y ceras de Fischer-Tropsch. Por regla general se utilizan ceras polietilénicas no ramificadas, no polares, es decir no modificadas.
En los documentos de patentes de los EE.UU. US-A-3.224.984 y US-A-3.398.105 se describe el empleo de ceras polietilénicas o respectivamente de polietilenos con un peso molecular de 1.000 a 4.000 en una concentración de 0,01 a 0,5%.
El documento US-A-3.060.138 describe la utilización de ceras parafínicas con unas longitudes de cadenas de 16 a 46 átomos de carbono como agentes formadores de núcleos para un poliestireno expansible.
En el documento de solicitud de patente alemana DE-A-324.38.85 se describe la utilización de unas ceras polietilénicas lineales en unas concentraciones de 0,05 a 0,5% en peso, con un peso molecular de 700 a 1.500 g/mol, con un punto de fusión de por lo menos 102ºC, con una densidad de por lo menos 15,4 g/cm^{3} así como con una polidispersidad menor que 1,2 (polidispersidad = el cociente del peso molecular medio ponderado y del peso molecular medio numérico).
De modo sorprendente, se encontró por fin que unas ceras poliolefínicas, preparadas con ayuda de catalizadores de metalocenos, son idóneas de un modo especialmente ventajoso como agentes de nucleación para un EPS. En particular, se estableció que un poliestireno expansible que contiene ceras obtenidas con metalocenos posee propiedades sorprendentemente positivas en lo que se refiere a la finura y a la homogeneidad de la estructura de las celdas del poliestireno expansible. El número de celdas de un poliestireno expansible en comparación con los agentes formadores de núcleos empleados habitualmente, referido a un área definida de superficie, se aumenta manifiestamente mediante la utilización de ceras poliolefínicas, que se habían preparado mediante una catálisis con metalocenos, lo cual se pone de manifiesto en unas propiedades mecánicas mejores (rigidez, posibilidad disminuida de aplastamiento) de la espuma, un aspecto ópticamente "más blanco" así como una disminución de la presión manifiestamente acelerada, es decir una velocidad de desmoldeo elevada. Además, el tamaño de las celdas se regula en el sentido de que se forman celdas homogéneas sin diferencias esenciales de tamaños entre ellas.
Es objeto de la solicitud, por lo tanto, un poliestireno expansible, que contiene ceras poliolefínicas, habiendo sido preparadas estas últimas con ayuda de catalizadores de metalocenos, y con un punto de goteo o de reblandecimiento de anillo y bola comprendido entre 80 y 165ºC y con una viscosidad de las masas fundidas, medida a una temperatura situada a 10ºC por encima del punto de goteo o de reblandecimiento, comprendida entre 20 y 10.000 mPa.s.
En este caso, las viscosidades de las masas fundidas se determinaron de acuerdo con la norma DIN 53019 con un viscosímetro rotatorio, los puntos de goteo de acuerdo con la norma DIN 51801/2, y los puntos de reblandecimiento de anillo y bola de acuerdo con la norma DIN EN 1427.
De manera preferida, las ceras poliolefínicas tienen un punto de goteo o de reblandecimiento de anillo y bola comprendido entre 90 y 160ºC y una viscosidad de las masas fundidas, medida a una temperatura situada a 10ºC por encima del punto de goteo o de reblandecimiento, comprendida entre 30 y 8.000 mPa.s.
De manera preferida, las ceras poliolefínicas tienen una masa molecular media ponderada Mw comprendida entre 1.000 y 30.000 g/mol y una masa molecular media numérica Mn comprendida entre 500 y 20.000 g/mol.
\newpage
De manera especialmente preferida, las ceras poliolefínicas tienen una masa molecular media ponderada Mw comprendida entre 2.000 y 10.000 g/mol y una masa molecular media numérica comprendida entre 800 y 3.000.
De manera preferida, como ceras poliolefínicas están contenidas unas ceras de homopolímeros de etileno.
De manera preferida, como ceras poliolefínicas están contenidas unas ceras de copolímeros de etileno y de 0,1 a 30% en peso de por lo menos un 1-alqueno ramificado o sin ramificar con 3 a 20 átomos de C.
De manera preferida, también como ceras poliolefínicas están contenidas unas ceras de homopolímeros de propileno.
De manera preferida, como ceras poliolefínicas están contenidas unas ceras de copolímeros de propileno y de 0,1 a 30% en peso de etileno y/o de por lo menos un 1-alqueno ramificado o sin ramificar con 4 a 20 átomos de C.
De manera preferida, están contenidos además materiales de carga o materiales coadyuvantes tales como agentes de expansión, pigmentos y antioxidantes así como agentes protectores contra la luz, agentes ignifugantes o antiestáticos.
Como ceras poliolefínicas entran en cuestión homopolímeros del etileno o de 1-olefinas superiores o sus copolímeros entre sí. Como 1-olefinas se emplean olefinas lineales o ramificadas con 3 a 18 átomos de C, de manera preferida con 3 a 6 átomos de C. Estas olefinas pueden tener una sustitución aromática que está en conjugación con el doble enlace olefínico. Ejemplos de ellas son propeno, 1-buteno, 1-hexeno, 1-octeno o 1-octadeceno así como estireno. Se prefieren homopolímeros del etileno o del propeno o sus copolímeros entre ellos. Los copolímeros se componen en un 70 a 99,9, de manera preferida en un 80 a 99% en peso, de un tipo de olefina.
Son apropiadas las ceras de homopolímeros y copolímeros de olefinas con una masa molecular media ponderada M_{w} comprendida entre 1.000 y 30.000 g/mol, de manera preferida entre 2.000 y 10.000 g/ml, con una masa molecular media numérica M_{n} comprendida entre 500 y 20.000 g/mol, de manera preferida entre 800 y 3.000 g/mol, con un punto de goteo o respectivamente de reblandecimiento de anillo y bola comprendido entre 80 y 165ºC, de manera preferida entre 90 y 160ºC y con una viscosidad de las masas fundidas, medida a una temperatura situada a 10ºC por encima del punto de goteo o respectivamente de reblandecimiento, comprendida entre 20 y 10.000 mPa.s, de manera preferida entre 30 y 8.000 mPa.s.
El poliestireno expansible conforme al invento puede contener adicionalmente materiales de carga o materiales coadyuvantes tales como pigmentos, agentes de expansión y antioxidantes, así como otros aditivos para polímeros, tales como agentes ignifugantes, antiestáticos y agentes protectores contra la luz.
Para la preparación de las ceras poliolefínicas utilizadas conforme al invento, se emplean compuestos de metalocenos de la fórmula I
1
Esta fórmula abarca también compuestos de la fórmula Ia
2
de la fórmula Ib
3
y de la fórmula Ic
4
En las fórmulas I, Ia y Ib M^{1} es un metal del grupo IVb, Vb o Vlb del sistema periódico de los elementos, por ejemplo titanio, zirconio, hafnio, vanadio, niobio, tántalo, cromo, molibdeno, wolframio, preferiblemente titanio, zirconio y hafnio.
R^{1} y R^{2} son iguales o diferentes y significan un átomo de hidrógeno, un grupo alquilo de C_{1}-C_{10}, de manera preferida de C_{1}-C_{3}, en particular metilo, un grupo alcoxi de C_{1}-C_{10}, preferiblemente de C_{1}-C_{3}, un grupo arilo de C_{6}-C_{10}, preferiblemente de C_{6}-C_{8}, un grupo ariloxi de C_{6}-C_{10}, preferiblemente de C_{6}-C_{8}, un grupo alquenilo de C_{2}-C_{10}, preferiblemente de C_{2}-C_{4}, un grupo arilalquilo de C_{7}-C_{40}, preferiblemente de C_{7}-C_{10}, un grupo alquilarilo de C_{7}-C_{40}, preferiblemente de C_{7}-C_{12}, un grupo arilalquenilo de C_{8}-C_{40}, preferiblemente de C_{8}-C_{12}, o un átomo de un halógeno, preferiblemente un átomo de cloro.
R^{3} y R^{4} son iguales o diferentes y significan un radical hidrocarbilo mono- o plurinuclear, que puede formar con el átomo central M^{1} una estructura en emparedado. De manera preferida, R^{3} y R^{4} son ciclopentadienilo, indenilo, tetrahidroindenilo, benzoindenilo o fluorenilo, pudiendo los entramados fundamentales llevar todavía sustituyentes adicionales o estar puenteados unos con otros. Además, uno de los radicales R^{3} y R^{4} puede ser un átomo de nitrógeno sustituido, teniendo R^{24} el significado el significado de R^{17} y siendo de manera preferida metilo, terc.-butilo o ciclohexilo.
R^{5}, R^{6}, R^{7}, R^{8}, R^{9} y R^{10} son iguales o diferentes y significan un átomo de hidrógeno, un átomo de halógeno, de manera preferida un átomo de flúor, cloro o bromo, un grupo alquilo de C_{1}-C_{10}, de manera preferida de C_{1}-C_{4}, un grupo arilo de C_{6}-C_{10}, de manera preferida de C_{6}-C_{8}, un grupo alcoxi de C_{1}-C_{10}, de manera preferida de C_{1}-C_{3}, un radical -NR^{16}_{2}-, -SR^{16}-, -OSiR^{16}_{3}-, -SiR^{16}_{3}- o -PR^{16}_{2}-, en el que R^{16} es un grupo alquilo de C_{1}-C_{10}, preferiblemente de C_{1}-C_{3} o un grupo arilo de C_{6}-C_{10}, preferiblemente de C_{6}-C_{8}, o en el caso de radicales que contienen Si o P, también es un átomo de halógeno, preferiblemente un átomo de cloro, o en cada caso dos radicales R^{5}, R^{6}, R^{7}, R^{8}, R^{9} o R^{10} contiguos forman un anillo con los átomos de C que los une. Ligandos especialmente preferidos son los compuestos sustituidos de las estructuras fundamentales de ciclopentadienilo, indenilo, tetrahidroindenilo, benzoindenilo o fluorenilo.
\newpage
R^{13} es
\vskip1.000000\baselineskip
5 
\vskip1.000000\baselineskip
\vskip1.000000\baselineskip
6 
\vskip1.000000\baselineskip
=BR^{17}, =AIR^{17}, -Ge-, -Sn-, -O-, -S-, =SO, =SO_{2}, =NR^{17}, =CO, =PR^{17} o =P(OR^{17}, siendo R^{17}, R^{18} y R^{19} iguales o diferentes y significando un átomo de hidrógeno, un átomo de halógeno, preferiblemente un átomo de flúor, cloro o bromo, un grupo alquilo de C_{1}-C_{30}, preferiblemente de C_{1}-C_{4}, en particular un grupo metilo, un grupo fluoro-alquilo de C_{1}-C_{10}, preferiblemente un grupo CF_{3}, un grupo fluoro-arilo de C_{6}-C_{10}, preferiblemente un grupo pentafluorofenilo, un grupo arilo de C_{6}-C_{10}, preferiblemente de C_{6}-C_{8}, un grupo alcoxi de C_{1}-C_{10}, preferiblemente de C_{1}-C_{4}, en particular un grupo metoxi, un grupo alquenilo de C_{2}-C_{10}, preferiblemente de C_{2}-C_{4}, un grupo aralquilo de C_{7}-C_{40}, preferiblemente de C_{7}-C_{10}, un grupo arilalquenilo de C_{8}-C_{40}, preferiblemente de C_{8}-C_{12} o un grupo alquilarilo de C_{7}-C_{40}, preferiblemente de C_{7}-C_{12}, o R^{17} y R^{18} o R^{17} y R^{19} forman un anillo en cada caso en común con los átomos que los unen.
M^{2} es silicio, germanio o estaño, de manera preferida silicio y germanio. R^{13} es preferiblemente =CR^{17}R^{18}, =SiR^{17}
R^{18}, =GeR^{17}R^{18}, -O-, -S-, =SO, =PR^{17} o =P(O)R^{17}.
R^{11} y R^{12} son iguales o diferentes y tienen los significados mencionados para R^{17}.
m y n son iguales o diferentes y significan cero, 1 ó 2, de manera preferida cero o 1, siendo m más n cero, 1 ó 2, de manera de manera preferida cero o 1.
R^{14} y R^{15} tienen los significados de R^{17} y R^{18}.
\vskip1.000000\baselineskip
Ejemplos de metalocenos apropiados son:
dicloruro de bis(1,2,3-trimetil-ciclopentadienil)zirconio,
dicloruro de bis(1,2,4-trimetil-ciclopentadienil)zirconio,
dicloruro de bis(1,2-dimetil-ciclopentadienil)zirconio,
dicloruro de bis(1,3-dimetil-ciclopentadienil)zirconio,
dicloruro de bis(1-metil-indenil)zirconio,
dicloruro de bis(1-n-butil-3-metil-ciclopentadienil) zirconio,
dicloruro de bis(2-metil-4,6-di-i-propil-indenil)zirconio,
dicloruro de bis(2-metil-indenil)zirconio,
dicloruro de bis(4-metil-indenil)zirconio,
dicloruro de bis(5-metil-indenil)zirconio,
dicloruro de bis(alquil-ciclopentadienil)zirconio,
dicloruro de bis(alquil-indenil)zirconio,
dicloruro de bis(ciclopentadienil) zirconio,
dicloruro de bis(indenil)zirconio,
dicloruro de bis(metil-ciclopentadienil)zirconio,
dicloruro de bis(n-butil-ciclopentadienil)zirconio,
dicloruro de bis(octadecil-ciclopentadienil)zirconio,
dicloruro de bis(pentametil-ciclopentadienil)zirconio,
dicloruro de bis(trimetil-silil-ciclopentadienil)zirconio,
bis-ciclopentadienil-zirconio-dibencilo
bis-ciclopentadienil-zirconio-dimetilo,
dicloruro de bis-tetrahidroindenil-zirconio,
dicloruro de dimetil-silil-9-fluorenil-ciclopentadienil-zirconio,
dicloruro de dimetil-silil-bis-1-(2,3,5-trimetil-ciclopentadienil)zirconio,
dicloruro de dimetil-silil-bis-1-(2,4-dimetil-ciclopentadienil)zirconio,
dicloruro de dimetil-silil-bis-1-(2-metil-4, 5-benzoindenil)zirconio,
dicloruro de dimetil-silil-bis-1-(2-metil-4-etil-indenil)zirconio,
dicloruro de dimetil-silil-bis-1-(2-metil-4-i-propil-indenil)zirconio,
dicloruro de dimetil-silil-bis-1-(2-metil-4-fenil-indenil)zirconio,
dicloruro de dimetil-silil-bis-1-(2-metil-indenil)zirconio,
dicloruro de dimetil-silil-bis-1-(2-metil-tetrahidroindenil)zirconio,
dicloruro de dimetil-silil-bis-1-indenil-zirconio,
dimetil-silil-bis-1-indenil-zirconio-dimetilo,
dicloruro de dimetil-silil-bis-1-tetrahidroindenil-zirconio,
dicloruro de difenil-metilen-9-fluorenil-ciclopentadienil-zirconio,
dicloruro de difenil-silil-bis-1-indenil-zirconio,
dicloruro de etilen-bis-1-(2-metil-4,5-benzoindenil)zirconio,
dicloruro de etilen-bis-1-(2-metil-4-fenil-indenil)zirconio,
dicloruro de etilen-bis-1-(2-metil-tetrahidroindenil)zirconio,
dicloruro de etilen-bis-1-(4,7-dimetil-indenil)zirconio,
dicloruro de etilen-bis-1-indenil-zirconio,
dicloruro de etilen-bis-1-tetrahidroindenil-zirconio,
dicloruro de indenil-ciclopentadienil-zirconio,
dicloruro de isopropiliden(1-indenil)(ciclopentadienil)zirconio,
dicloruro de isopropiliden(9-fluorenil)(ciclopentadienil)zirconio,
dicloruro de fenil-metil-silil-bis-1-(2-metil-indenil)zirconio,
así como en cada caso los derivados de alquilo o arilo de estos dicloruros de metalocenos.
\vskip1.000000\baselineskip
Para la activación de los sistemas de catalizadores de un sólo centro se emplean apropiados cocatalizadores. Apropiados cocatalizadores para metalocenos de la fórmula I son compuestos orgánicos de aluminio, en particular alumoxanos o también sistemas exentos de aluminio, tales como R^{20}_{x}NH_{4-x}BR^{21}_{4}, R^{20}_{x}PH_{4-x}BR^{21}_{4}, R^{20}_{3}CBR^{21}_{4} o BR^{21}_{3}. En estas fórmulas, x significa un número de 1 a 4, los radicales R^{20} son iguales o diferentes, de manera preferida iguales, y significan alquilo de C_{1}-C_{10} o arilo de C_{6}-C_{18} o dos radicales R^{20} forman un anillo en común con el átomo que los une, y los radicales R^{21} son iguales o diferentes, de manera preferida iguales, y representan arilo de C_{6}-C_{18}, que puede estar sustituido con alquilo, haloalquilo o fluoro. En particular R^{20} representa etilo, propilo, butilo o fenilo y R^{21} representa fenilo, pentafluoro-fenilo, 3,5-bis-trifluorometil-fenilo, mesitilo, xililo o tolilo.
Adicionalmente, se necesita con frecuencia un tercer componente, con el fin de conservar una protección contra venenos polares de catalizadores. Para esto son apropiados ciertos compuestos orgánicos de aluminio, tales como p.ej. trietil-aluminio, tributil-aluminio y otros, así como mezclas de ellos.
Según sea el procedimiento, se pueden pasar a utilizar catalizadores de un solo centro soportados. Se prefieren unos sistemas de catalizadores, en los cuales los contenidos residuales de material de soporte y de cocatalizador no sobrepasan una concentración de 100 ppm en el producto.
La preparación de tales ceras poliolefínicas se describe por ejemplo en los documentos de solicitudes de patentes europeas EP-A-0.321.851, EP-A-0.321.852 así como EP-A-0.384.264.
Las ceras poliolefínicas están contenidas en un poliestireno expansible con una proporción ponderal comprendida entre 0,01 y 10%, de manera preferida entre 0,03 y 5%.
Resultados técnicos de aplicaciones
Para la realización de la polimerización en suspensión se dispusieron previamente, dentro de un recipiente de acero, agua (totalmente desalinizada, como agente coadyuvante de suspensión DMS (\alpha-metil-estireno dímero) así como la cera que se había de ensayar. A continuación, se añadieron dosificadamente estireno y un agente iniciador (un peróxido). Después de haber agitado durante dos horas, la mezcla se calentó a 100ºC y la temperatura se mantuvo durante 5,5 horas. Después de esto, la temperatura se eleva a 130ºC y se mantiene durante 2 horas. Después de haber enfriado a aproximadamente 80-85ºC, se añade dosificadamente en primer lugar un agente estabilizador de suspensiones y después de ello n-pentano durante 1,5 horas.
Las perlas contenidas se separaron por centrifugación y se secaron y enfriaron con aire, se recubrieron con EBS (bis-estearoíl-etilendiamina) como agente de separación y se separó por tamizado una fracción de tamaños de perlas de 1-2 mm. Esta fracción se espumó previamente sin presión de una manera discontinua y a continuación se espumó para formar un paralelepípedo con una presión de vapor de 1,2 bar. En este caso se determinó la descomposición de la presión, es decir el período de tiempo que se precisa para el desmoldeo, así, como, junto a una superficie de corte, con un microscopio el número de celdillas por mm. Asimismo la estructura de la espuma se evaluó ópticamente y se valoró en qué grado la estructura celular es homogénea (iguales tamaños de celdas) o heterogénea (diferentes tamaños de celdas). En particular, las celdas uniformes pequeñas proporcionan un aspecto blanco de la superficie de corte, y unos diferentes tamaños de celdas generan un aspecto grisáceo.
La media ponderada de la masa molecular M_{w} y la M_{n} de las ceras empleadas se determinaron mediante cromatografía de penetrabilidad en gel a 135ºC en 1,2-dicloro-benceno.
Ejemplos
Ejemplo 1
(Comparativo)
La reacción arriba descrita se llevó a cabo sin la adición de ninguna cera.
Ejemplo 2
La reacción se llevó a cabo con 0,1% en peso de una cera polietilénica obtenida con un metaloceno (homopolímero) de la entidad Clariant, nombre comercial TP Licocene® PE 4201, (M_{n} = 1.200 g/mol, M_{w} = 2.400 g/mol, punto de goteo 123ºC, viscosidad a 140ºC 60 mPa.s).
Ejemplo 3
La reacción se llevó a cabo con 0,1% en peso de una cera polietilénica obtenida con un metaloceno (copolímero con 5% en peso de propeno) (M_{n} = 2.300 g/mol, M_{w} = 5.100 g/mol, punto de goteo 118ºC, viscosidad a 140ºC 900 mPa.s).
Ejemplo 4
La reacción se llevó a cabo con 0,1% de una cera polietilénica de Ziegler (M_{n} = 1.600 g/mol, M_{w} = 4.800 g/mol, punto de goteo 130ºC, viscosidad a 140ºC 550 mPa.s).
Ejemplo 5
La reacción se llevó a cabo con 0,1% de una cera polietilénica, que se había preparado de acuerdo con el procedimiento a alta presión (M_{n} = 1.500 g/mol, M_{w} = 3.500 g/mol, punto de goteo 110ºC, viscosidad a 140ºC 700 mPa.s).
Ejemplo 6
La reacción se llevó a cabo con 0,1% de una cera polietilénica de Ziegler de alto peso molecular (M_{n} = 5.500 g/mol, M_{w} = 18.000 g/mol, punto de goteo 135ºC, viscosidad a 140ºC 23.000 mPa.s).
Valoración
7
Tal como se desprende de la Tabla, el empleo de ceras preparadas mediante catalizadores del tipo de metalocenos conduce a unos números de celdas comparativamente más altos, a unos períodos de tiempo de desmoldeo más pequeños y a una estructura de la espuma más ventajosa.

Claims (10)

1. Poliestireno expansible, que contiene entre 0,01 y 10% en peso de ceras poliolefínicas, siendo preparadas las ceras poliolefínicas con ayuda de catalizadores del tipo de metalocenos y teniendo un punto de goteo o de reblandecimiento de anillo y bola comprendido entre 80 y 165ºC y una viscosidad de las masas fundidas, medida a una temperatura situada a 10ºC por encima del punto de goteo o de reblandecimiento, comprendida entre 20 y 10.000 mPa\cdots.
2. Poliestireno expansible de acuerdo con la reivindicación 1, caracterizado porque las ceras poliolefínicas tienen un punto de goteo o reblandecimiento de anillo y bola comprendido entre 90 y 160ºC y una viscosidad de las masas fundidas, medida a una temperatura situada a 10ºC por encima del punto de goteo o de reblandecimiento, comprendida entre 30 y 8.000 mPa.s.
3. Poliestireno expansible de acuerdo con las reivindicaciones 1 ó 2, caracterizado porque las ceras poliolefínicas tienen una masa molecular media ponderada M_{w} comprendida entre 1.000 y 30.000 g/mol y una masa molecular media numérica M_{n} comprendida entre 500 y 20.000 g/mol.
4. Poliestireno expansible de acuerdo con las reivindicaciones 1 y 2, caracterizado porque las ceras poliolefínicas tienen una masa molecular media ponderada M_{w} comprendida entre 2.000 y 10.000 g/mol y una masa molecular media numérica comprendida entre 800 y 3.000 g/mol.
5. Poliestireno expansible de acuerdo con una o varias de las reivindicaciones 1 a 4, que como ceras poliolefínicas contiene ceras de homopolímeros de etileno.
6. Poliestireno expansible de acuerdo con una o varias de las reivindicaciones 1 a 4, que como ceras poliolefínicas contiene ceras de copolímeros de etileno y de 0,1 a 30% en peso de por lo menos un 1-alqueno ramificado o sin ramificar con 3 a 20 átomos de C.
7. Poliestireno expansible de acuerdo con una o varias de las reivindicaciones 1 a 4, que como ceras poliolefínicas contiene ceras de homopolímeros de propileno.
8. Poliestireno expansible de acuerdo con una o varias de las reivindicaciones 1 a 4, que como ceras poliolefínicas contiene ceras de copolímeros de propileno y de 0,1 a 30% en peso de etileno y/o de por lo menos un 1-alqueno ramificado o sin ramificar con 4 a 20 átomos de C.
9. Poliestireno expansible de acuerdo con una o varias de las reivindicaciones 1 a 8, caracterizado porque contiene además materiales de carga o materiales coadyuvantes.
10. Poliestireno expansible de acuerdo con la reivindicación 9, caracterizado porque como materiales coadyuvantes contiene agentes de expansión, pigmentos y antioxidantes, así como agentes de protección contra la luz, agentes ignifugantes o antiestáticos.
ES05009648T 2004-05-13 2005-05-03 Poliestireno expansible. Expired - Lifetime ES2296002T3 (es)