ES2143596T3 - Una composicion de polvo a base de hierro. - Google Patents
Una composicion de polvo a base de hierro.Info
- Publication number
- ES2143596T3 ES2143596T3 ES95307340T ES95307340T ES2143596T3 ES 2143596 T3 ES2143596 T3 ES 2143596T3 ES 95307340 T ES95307340 T ES 95307340T ES 95307340 T ES95307340 T ES 95307340T ES 2143596 T3 ES2143596 T3 ES 2143596T3
- Authority
- ES
- Spain
- Prior art keywords
- sub
- iron
- particles
- oxygen
- degrees
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
UN POLVO METALICO BASADO EN HIERRO O COBRE UTIL PARA LA DEPOSICION POR PLASMA DE UN REVESTIMIENTO QUE TIENE UN COEFICIENTE DE FRICCION EN SECO DE 0,75 O INFERIOR Y QUE CONDUCE CALOR EN SEGUIDA A TRAVES DEL REVESTIMIENTO. EL POLVO CONTIENE (A) PARTICULAS ATOMIZADAS O RECOCIDAS DE H{SUB,2}O QUE CONSISTEN ESENCIALMENTE EN (EN PESO) DE UN 0,15 A UN 0,85% DE CARBONO, DE UN 0,1 A UN 0,45% DE OXIGENO, DE UN 0,1 A UN 6,5% DE UN AGENTE DE ENDURECIMIENTO AL AIRE SELECCIONADO DEL MANGANESO Y DEL NIQUEL, Y EL RESTO HIERRO O COBRE, EN DONDE AL MENOS EL 90% DE LAS PARTICULAS TIENEN OXIGENO E HIERRO O COBRE COMBINADOS EN LA FORMA DE OXIGENO ATOMICO MAS BAJA PARA UN OXIDO DE TAL METAL. UN METODO PARA LA PRODUCCION DE POLVO DE HIERRO ANTIFRICCION QUE ES ECONOMICO, SE OBTIENE SELECTIVAMENTE FEO Y FOMENTA LAS PARTICULAS FINAS FLUIBLES. EL METODO CONSISTE EN (A) ATOMIZAR AL VAPOR UN ACERO FUNDIDO QUE EXCLUYA OTRO OXIGENO, EN DONDE EL ACERO CONTIENE HASTA UN 0,4% EN PESO DE CARBONO PARA LA PRODUCCION DE UN CONJUNTO DE PARTICULAS TRITURADAS Y (B) RECOCER LAS PARTICULAS EN UNA ATMOSFERA DE AIRE DURANTE UN PERIODO DE TIEMPO DE 0,25 A 2,00 HORAS A UNA TEMPERATURA DE 427 A 760 (GRADOS) C (800 (GRADOS) -1400 (GRADOS) F) PARA REDUCIR EL CARBONO DE LAS PARTICULAS A UN 0,2% APROXIMADAMENTE O ESPONJA DE HIERRO REDUCIENDO FE{SUB,3}O{SUB,4} O FE{SUB,2}O{SUB,3} EN CO Y (VAPOR DE H{SUB,2}O) PARA OBTENER CASI TODO HIERRO CON CASI TODO FEO Y DE 0,1 A 0,85 C.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US08/352,666 US5663124A (en) | 1994-12-09 | 1994-12-09 | Low alloy steel powder for plasma deposition having solid lubricant properties |
Publications (1)
Publication Number | Publication Date |
---|---|
ES2143596T3 true ES2143596T3 (es) | 2000-05-16 |
Family
ID=23386009
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ES95307340T Expired - Lifetime ES2143596T3 (es) | 1994-12-09 | 1995-10-16 | Una composicion de polvo a base de hierro. |
Country Status (5)
Country | Link |
---|---|
US (3) | US5663124A (es) |
EP (1) | EP0715916B1 (es) |
CA (1) | CA2164139A1 (es) |
DE (1) | DE69515603T2 (es) |
ES (1) | ES2143596T3 (es) |
Families Citing this family (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5663124A (en) * | 1994-12-09 | 1997-09-02 | Ford Global Technologies, Inc. | Low alloy steel powder for plasma deposition having solid lubricant properties |
US5592927A (en) * | 1995-10-06 | 1997-01-14 | Ford Motor Company | Method of depositing and using a composite coating on light metal substrates |
US5723187A (en) * | 1996-06-21 | 1998-03-03 | Ford Global Technologies, Inc. | Method of bonding thermally sprayed coating to non-roughened aluminum surfaces |
US6042949A (en) * | 1998-01-21 | 2000-03-28 | Materials Innovation, Inc. | High strength steel powder, method for the production thereof and method for producing parts therefrom |
US6036839A (en) * | 1998-02-04 | 2000-03-14 | Electrocopper Products Limited | Low density high surface area copper powder and electrodeposition process for making same |
US6316393B1 (en) * | 1998-11-04 | 2001-11-13 | National Research Council Of Canada | Modified lubricated ferrous powder compositions for cold and warm pressing applications |
US6140278A (en) * | 1998-11-04 | 2000-10-31 | National Research Council Of Canada | Lubricated ferrous powder compositions for cold and warm pressing applications |
EP1507020B1 (de) * | 1999-01-19 | 2007-06-27 | Sulzer Metco AG | Durch Plasmaspritzen aufgebrachte Schicht für Zylinderlaufflächen von Motorblöcken und Verfahren zu deren Herstellung |
SE517485C2 (sv) * | 1999-10-15 | 2002-06-11 | Avesta Polarit Ab Publ | Sätt vid separering av värdefull metall från en smältblanding, samt anordning härför |
SE517487C2 (sv) * | 1999-10-15 | 2002-06-11 | Avesta Polarit Ab Publ | Sätt vid tillverkning av fasta partiklar av en smälta, samt anordning härför |
US6756083B2 (en) * | 2001-05-18 | 2004-06-29 | Höganäs Ab | Method of coating substrate with thermal sprayed metal powder |
US6595263B2 (en) * | 2001-08-20 | 2003-07-22 | Ford Global Technologies, Inc. | Method and arrangement for utilizing a psuedo-alloy composite for rapid prototyping and low-volume production tool making by thermal spray form techniques |
CH695339A5 (de) | 2002-02-27 | 2006-04-13 | Sulzer Metco Ag | Zylinderlaufflächenschicht für Verbrennungsmotoren sowie Verfahren zu deren Herstellung. |
US6830815B2 (en) | 2002-04-02 | 2004-12-14 | Ford Motor Company | Low wear and low friction coatings for articles made of low softening point materials |
CA2514493C (en) * | 2004-09-17 | 2013-01-29 | Sulzer Metco Ag | A spray powder |
GB2426010B (en) * | 2005-05-14 | 2011-04-06 | Jeffrey Boardman | semiconductor materials and methods of producing them |
CN100372638C (zh) * | 2005-06-03 | 2008-03-05 | 北京科技大学 | 一种用于激光烧结成型的镍基合金粉末及其制备方法 |
FR2974610B1 (fr) * | 2011-04-26 | 2013-05-17 | Peugeot Citroen Automobiles Sa | Procede de realisation des surfaces de chambres a combustion d'un bloc moteur en alliage d'aluminium |
EP3134560B1 (de) * | 2014-04-24 | 2021-04-21 | Daimler AG | Thermisch beschichtetes bauteil |
CN106399901A (zh) * | 2016-11-18 | 2017-02-15 | 无锡明盛纺织机械有限公司 | 一种铝合金超音速火焰喷涂SiC‑Si‑Cr‑Mn‑Al耐磨涂层的方法 |
CN106399900A (zh) * | 2016-11-18 | 2017-02-15 | 无锡明盛纺织机械有限公司 | 一种铝合金超音速火焰喷涂Si‑Cr‑B‑W‑Al耐磨涂层的方法 |
CN110129715B (zh) * | 2019-05-14 | 2021-11-23 | 昆明理工大学 | 一种原位纳米金属-陶瓷复合涂层及其制备方法 |
Family Cites Families (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US991404A (en) * | 1909-11-10 | 1911-05-02 | Lyman Woodworth | Gas or combustion engine. |
US1347476A (en) * | 1915-03-29 | 1920-07-20 | Aluminum Castings Company | Process of making cylinders for internal-combustion engines |
GB484662A (en) * | 1935-11-04 | 1938-05-04 | Ivar Rennerfelt | Improvements in or relating to the decarbonising of carbon-containing iron or iron alloys |
US2534408A (en) * | 1947-10-17 | 1950-12-19 | Jr Harry M Bramberry | Relieved and filled cylinder surface |
US3390071A (en) * | 1964-10-26 | 1968-06-25 | Reynolds Metals Co | Cathode construction for aluminum reduction cell |
GB1136900A (en) * | 1964-12-22 | 1968-12-18 | Wellworthy Ltd | Improvements in or relating to cylinders or cylinder liners for internal combustion engines |
GB1252693A (es) * | 1969-01-13 | 1971-11-10 | ||
US3620137A (en) * | 1969-10-06 | 1971-11-16 | Ramsey Corp | Piston sleeve |
JPS5219823B2 (es) * | 1972-12-25 | 1977-05-31 | ||
JPS58481B2 (ja) * | 1976-03-12 | 1983-01-06 | 川崎製鉄株式会社 | 低酸素鉄系金属粉末の製造方法および装置 |
JPS5341621A (en) * | 1976-09-27 | 1978-04-15 | Honda Motor Co Ltd | Cylinders for internal combustion engine |
CH632013A5 (de) * | 1977-09-22 | 1982-09-15 | Ipsen Ind Int Gmbh | Verfahren zur gasaufkohlung von werkstuecken aus stahl. |
US4473481A (en) * | 1982-04-14 | 1984-09-25 | Kabushiki Kaisha Kobe Seiko Sho | Lubricant film for preventing galling of sliding metal surfaces |
US4495907A (en) * | 1983-01-18 | 1985-01-29 | Cummins Engine Company, Inc. | Combustion chamber components for internal combustion engines |
US4721599A (en) * | 1985-04-26 | 1988-01-26 | Hitachi Metals, Ltd. | Method for producing metal or alloy articles |
US5131577A (en) * | 1988-05-17 | 1992-07-21 | Ford Motor Company | Apparatus for making a powder metal connecting rod |
FR2660922B1 (fr) * | 1990-04-13 | 1992-09-04 | Centre Ntl Recherche Scient | Procede de preparation par broyage de materiaux composites comportant une phase oxyde et une phase metallique . |
JPH0483813A (ja) * | 1990-04-16 | 1992-03-17 | Kawasaki Steel Corp | 水アトマイズ鉄粉の製造方法 |
DE4019563A1 (de) * | 1990-06-15 | 1991-12-19 | Mannesmann Ag | Verfahren zur herstellung von metallpulver |
US5108493A (en) * | 1991-05-03 | 1992-04-28 | Hoeganaes Corporation | Steel powder admixture having distinct prealloyed powder of iron alloys |
JPH0643150A (ja) * | 1991-05-29 | 1994-02-18 | Wako Pure Chem Ind Ltd | 尿中成分の定量方法 |
US5239955A (en) * | 1993-01-07 | 1993-08-31 | Ford Motor Company | Low friction reciprocating piston assembly |
CN1104570A (zh) * | 1993-05-18 | 1995-07-05 | 川崎制铁株式会社 | 粉末冶金用的水雾化铁粉及其制造方法 |
US5385789A (en) * | 1993-09-15 | 1995-01-31 | Sulzer Plasma Technik, Inc. | Composite powders for thermal spray coating |
US5663124A (en) * | 1994-12-09 | 1997-09-02 | Ford Global Technologies, Inc. | Low alloy steel powder for plasma deposition having solid lubricant properties |
-
1994
- 1994-12-09 US US08/352,666 patent/US5663124A/en not_active Expired - Lifetime
-
1995
- 1995-10-16 DE DE69515603T patent/DE69515603T2/de not_active Expired - Fee Related
- 1995-10-16 ES ES95307340T patent/ES2143596T3/es not_active Expired - Lifetime
- 1995-10-16 EP EP95307340A patent/EP0715916B1/en not_active Expired - Lifetime
- 1995-11-30 CA CA002164139A patent/CA2164139A1/en not_active Abandoned
-
1997
- 1997-02-10 US US08/798,207 patent/US5846349A/en not_active Expired - Lifetime
- 1997-08-18 US US08/799,738 patent/US5863870A/en not_active Expired - Lifetime
Also Published As
Publication number | Publication date |
---|---|
EP0715916A3 (en) | 1996-09-04 |
EP0715916A2 (en) | 1996-06-12 |
US5846349A (en) | 1998-12-08 |
DE69515603T2 (de) | 2000-08-03 |
CA2164139A1 (en) | 1996-06-10 |
DE69515603D1 (de) | 2000-04-20 |
US5863870A (en) | 1999-01-26 |
EP0715916B1 (en) | 2000-03-15 |
US5663124A (en) | 1997-09-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ES2143596T3 (es) | Una composicion de polvo a base de hierro. | |
US4253874A (en) | Alloys steel powders | |
US10618110B2 (en) | Master alloy for producing sinter hardened steel parts and process for the production of sinter hardened parts | |
JPS5274509A (en) | Ni-base sintered alloy | |
ES2087933T3 (es) | Metodo para la formacion de una capa de nitruro o carbonitruro. | |
CN106498220B (zh) | 碳酸镍用于改善烧结锰铜阻尼合金性能的方法 | |
CN106424712A (zh) | 一种提高锰铜烧结阻尼合金组织和性能均匀性的工艺 | |
ES2183317T3 (es) | Pprocedimiento de fabricacion de piezas de reloj de aleacion de titanio. | |
JP6044492B2 (ja) | Mo含有海綿鉄およびMo含有還元鉄粉の製造方法 | |
ES2310427T3 (es) | Polvo metalico aleado no oxidante. | |
CN106392064B (zh) | 用草酸镍改善高锰锰铜阻尼合金烧结性能的方法 | |
JPH059501A (ja) | 焼結用鉄系粉末およびその製造方法 | |
JPH06122957A (ja) | フェライト系ステンレス材の表面処理方法 | |
US886349A (en) | Manufacture of railway-rails. | |
SE0203168D0 (sv) | Heat treatment of iron-based components | |
JP2003147405A (ja) | 鉄系焼結熱処理材料用合金鋼粉 | |
Sulowski | the effects of processing parameters on the structure and mechanical properties of structural PM steels containing Mn, Cr and Mo | |
Nestorović et al. | Influence of Powder Metallurgy on the Enviroment | |
McLelland et al. | Sintering furnace cycle influence on sinter hardened part parameters | |
German | An Overview of Enhanced Sintering Treatments for Iron | |
Chen et al. | Atmosphere Effects on Dimensional Control of Fe--Cu--C Powder Metal Compacts | |
GB802086A (en) | Improvements in or relating to the manufacture of composite bodies comprising a metallic component and a component of porous material | |
Zheng et al. | New high nitrogen wear and corrosion resistant steels from powder metallurgical process | |
CA1053488A (en) | Making articles from metallic powder | |
Krave | Carburization as a function of density and carbon potential |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
FG2A | Definitive protection |
Ref document number: 715916 Country of ref document: ES |