EA022720B1 - Огнеупорный продукт с высоким содержанием диоксида циркония - Google Patents
Огнеупорный продукт с высоким содержанием диоксида циркония Download PDFInfo
- Publication number
- EA022720B1 EA022720B1 EA201200971A EA201200971A EA022720B1 EA 022720 B1 EA022720 B1 EA 022720B1 EA 201200971 A EA201200971 A EA 201200971A EA 201200971 A EA201200971 A EA 201200971A EA 022720 B1 EA022720 B1 EA 022720B1
- Authority
- EA
- Eurasian Patent Office
- Prior art keywords
- less
- product according
- mass content
- oxides
- content
- Prior art date
Links
- MCMNRKCIXSYSNV-UHFFFAOYSA-N Zirconium dioxide Chemical compound O=[Zr]=O MCMNRKCIXSYSNV-UHFFFAOYSA-N 0.000 title description 38
- 238000002844 melting Methods 0.000 claims abstract description 21
- 230000008018 melting Effects 0.000 claims abstract description 21
- 239000011521 glass Substances 0.000 claims abstract description 18
- 239000000047 product Substances 0.000 claims description 86
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims description 40
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims description 7
- ODINCKMPIJJUCX-UHFFFAOYSA-N calcium oxide Inorganic materials [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 claims description 5
- 235000012255 calcium oxide Nutrition 0.000 claims description 5
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 claims description 4
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 claims description 4
- 229910052788 barium Inorganic materials 0.000 claims description 4
- DSAJWYNOEDNPEQ-UHFFFAOYSA-N barium atom Chemical compound [Ba] DSAJWYNOEDNPEQ-UHFFFAOYSA-N 0.000 claims description 4
- 229910052749 magnesium Inorganic materials 0.000 claims description 4
- 239000011777 magnesium Substances 0.000 claims description 4
- 239000006060 molten glass Substances 0.000 claims description 4
- 229910052712 strontium Inorganic materials 0.000 claims description 4
- CIOAGBVUUVVLOB-UHFFFAOYSA-N strontium atom Chemical compound [Sr] CIOAGBVUUVVLOB-UHFFFAOYSA-N 0.000 claims description 4
- 229910052725 zinc Inorganic materials 0.000 claims description 4
- 239000011701 zinc Substances 0.000 claims description 4
- BRPQOXSCLDDYGP-UHFFFAOYSA-N calcium oxide Chemical class [O-2].[Ca+2] BRPQOXSCLDDYGP-UHFFFAOYSA-N 0.000 claims description 3
- 229910052760 oxygen Inorganic materials 0.000 claims description 3
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N iron oxide Inorganic materials [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 claims description 2
- SOQBVABWOPYFQZ-UHFFFAOYSA-N oxygen(2-);titanium(4+) Chemical class [O-2].[O-2].[Ti+4] SOQBVABWOPYFQZ-UHFFFAOYSA-N 0.000 claims description 2
- OGIDPMRJRNCKJF-UHFFFAOYSA-N titanium oxide Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 claims description 2
- 229910052814 silicon oxide Inorganic materials 0.000 claims 3
- 229910004298 SiO 2 Inorganic materials 0.000 claims 1
- 230000000295 complement effect Effects 0.000 claims 1
- 239000013589 supplement Substances 0.000 claims 1
- PBCFLUZVCVVTBY-UHFFFAOYSA-N tantalum pentoxide Inorganic materials O=[Ta](=O)O[Ta](=O)=O PBCFLUZVCVVTBY-UHFFFAOYSA-N 0.000 claims 1
- 239000012530 fluid Substances 0.000 abstract 1
- 239000000377 silicon dioxide Substances 0.000 description 18
- 235000012239 silicon dioxide Nutrition 0.000 description 13
- 239000012535 impurity Substances 0.000 description 9
- 239000007858 starting material Substances 0.000 description 9
- 230000015572 biosynthetic process Effects 0.000 description 8
- 239000000203 mixture Substances 0.000 description 8
- 238000001816 cooling Methods 0.000 description 6
- 230000007797 corrosion Effects 0.000 description 6
- 238000005260 corrosion Methods 0.000 description 6
- 239000012768 molten material Substances 0.000 description 6
- RVTZCBVAJQQJTK-UHFFFAOYSA-N oxygen(2-);zirconium(4+) Chemical compound [O-2].[O-2].[Zr+4] RVTZCBVAJQQJTK-UHFFFAOYSA-N 0.000 description 6
- 239000000126 substance Substances 0.000 description 6
- 238000004519 manufacturing process Methods 0.000 description 5
- 238000000034 method Methods 0.000 description 5
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 4
- 238000010891 electric arc Methods 0.000 description 4
- 239000000155 melt Substances 0.000 description 4
- 238000002156 mixing Methods 0.000 description 4
- 230000007547 defect Effects 0.000 description 3
- JKWMSGQKBLHBQQ-UHFFFAOYSA-N diboron trioxide Chemical compound O=BOB=O JKWMSGQKBLHBQQ-UHFFFAOYSA-N 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 229910000449 hafnium oxide Inorganic materials 0.000 description 3
- WIHZLLGSGQNAGK-UHFFFAOYSA-N hafnium(4+);oxygen(2-) Chemical compound [O-2].[O-2].[Hf+4] WIHZLLGSGQNAGK-UHFFFAOYSA-N 0.000 description 3
- 229910052738 indium Inorganic materials 0.000 description 3
- 239000000463 material Substances 0.000 description 3
- 230000001590 oxidative effect Effects 0.000 description 3
- 230000001603 reducing effect Effects 0.000 description 3
- 239000010936 titanium Substances 0.000 description 3
- 229910052845 zircon Inorganic materials 0.000 description 3
- GFQYVLUOOAAOGM-UHFFFAOYSA-N zirconium(iv) silicate Chemical compound [Zr+4].[O-][Si]([O-])([O-])[O-] GFQYVLUOOAAOGM-UHFFFAOYSA-N 0.000 description 3
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 2
- 229910052782 aluminium Inorganic materials 0.000 description 2
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 2
- 238000004458 analytical method Methods 0.000 description 2
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 2
- 229910052810 boron oxide Inorganic materials 0.000 description 2
- 238000005266 casting Methods 0.000 description 2
- 238000005336 cracking Methods 0.000 description 2
- 239000013078 crystal Substances 0.000 description 2
- 239000002019 doping agent Substances 0.000 description 2
- 238000005516 engineering process Methods 0.000 description 2
- 239000012467 final product Substances 0.000 description 2
- 239000008187 granular material Substances 0.000 description 2
- 229910052742 iron Inorganic materials 0.000 description 2
- -1 iron ions Chemical class 0.000 description 2
- 150000001247 metal acetylides Chemical class 0.000 description 2
- 150000004767 nitrides Chemical class 0.000 description 2
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 2
- 239000001301 oxygen Substances 0.000 description 2
- 230000008092 positive effect Effects 0.000 description 2
- 239000011734 sodium Substances 0.000 description 2
- KKCBUQHMOMHUOY-UHFFFAOYSA-N sodium oxide Chemical compound [O-2].[Na+].[Na+] KKCBUQHMOMHUOY-UHFFFAOYSA-N 0.000 description 2
- 229910001948 sodium oxide Inorganic materials 0.000 description 2
- 238000010186 staining Methods 0.000 description 2
- 229910052719 titanium Inorganic materials 0.000 description 2
- 229910018072 Al 2 O 3 Inorganic materials 0.000 description 1
- OYPRJOBELJOOCE-UHFFFAOYSA-N Calcium Chemical compound [Ca] OYPRJOBELJOOCE-UHFFFAOYSA-N 0.000 description 1
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 1
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 description 1
- QCWXUUIWCKQGHC-UHFFFAOYSA-N Zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 description 1
- 230000002411 adverse Effects 0.000 description 1
- 230000009286 beneficial effect Effects 0.000 description 1
- 229910052796 boron Inorganic materials 0.000 description 1
- 230000005587 bubbling Effects 0.000 description 1
- 238000001354 calcination Methods 0.000 description 1
- 229910052791 calcium Inorganic materials 0.000 description 1
- 239000011575 calcium Substances 0.000 description 1
- 239000000292 calcium oxide Substances 0.000 description 1
- 230000015556 catabolic process Effects 0.000 description 1
- 229910052729 chemical element Inorganic materials 0.000 description 1
- 238000006243 chemical reaction Methods 0.000 description 1
- 229910052804 chromium Inorganic materials 0.000 description 1
- 239000011651 chromium Substances 0.000 description 1
- 230000000052 comparative effect Effects 0.000 description 1
- 238000007796 conventional method Methods 0.000 description 1
- RKTYLMNFRDHKIL-UHFFFAOYSA-N copper;5,10,15,20-tetraphenylporphyrin-22,24-diide Chemical compound [Cu+2].C1=CC(C(=C2C=CC([N-]2)=C(C=2C=CC=CC=2)C=2C=CC(N=2)=C(C=2C=CC=CC=2)C2=CC=C3[N-]2)C=2C=CC=CC=2)=NC1=C3C1=CC=CC=C1 RKTYLMNFRDHKIL-UHFFFAOYSA-N 0.000 description 1
- 238000012926 crystallographic analysis Methods 0.000 description 1
- 238000006731 degradation reaction Methods 0.000 description 1
- 230000000593 degrading effect Effects 0.000 description 1
- 238000013461 design Methods 0.000 description 1
- 238000011161 development Methods 0.000 description 1
- 230000005611 electricity Effects 0.000 description 1
- 239000007789 gas Substances 0.000 description 1
- 239000007788 liquid Substances 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 229910021645 metal ion Inorganic materials 0.000 description 1
- 238000000465 moulding Methods 0.000 description 1
- 229910000484 niobium oxide Inorganic materials 0.000 description 1
- URLJKFSTXLNXLG-UHFFFAOYSA-N niobium(5+);oxygen(2-) Chemical compound [O-2].[O-2].[O-2].[O-2].[O-2].[Nb+5].[Nb+5] URLJKFSTXLNXLG-UHFFFAOYSA-N 0.000 description 1
- 150000002823 nitrates Chemical class 0.000 description 1
- 238000007254 oxidation reaction Methods 0.000 description 1
- SIWVEOZUMHYXCS-UHFFFAOYSA-N oxo(oxoyttriooxy)yttrium Chemical compound O=[Y]O[Y]=O SIWVEOZUMHYXCS-UHFFFAOYSA-N 0.000 description 1
- BPUBBGLMJRNUCC-UHFFFAOYSA-N oxygen(2-);tantalum(5+) Chemical compound [O-2].[O-2].[O-2].[O-2].[O-2].[Ta+5].[Ta+5] BPUBBGLMJRNUCC-UHFFFAOYSA-N 0.000 description 1
- 239000013618 particulate matter Substances 0.000 description 1
- 150000002978 peroxides Chemical class 0.000 description 1
- 229910052698 phosphorus Inorganic materials 0.000 description 1
- 239000011574 phosphorus Substances 0.000 description 1
- 239000002243 precursor Substances 0.000 description 1
- 239000002994 raw material Substances 0.000 description 1
- 230000002441 reversible effect Effects 0.000 description 1
- 239000004576 sand Substances 0.000 description 1
- 238000000926 separation method Methods 0.000 description 1
- 229910052708 sodium Inorganic materials 0.000 description 1
- 230000002195 synergetic effect Effects 0.000 description 1
- 229910001936 tantalum oxide Inorganic materials 0.000 description 1
- 238000012360 testing method Methods 0.000 description 1
- 230000009466 transformation Effects 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
- 229910052720 vanadium Inorganic materials 0.000 description 1
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 description 1
- 229910052726 zirconium Inorganic materials 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B5/00—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture
- C03B5/16—Special features of the melting process; Auxiliary means specially adapted for glass-melting furnaces
- C03B5/42—Details of construction of furnace walls, e.g. to prevent corrosion; Use of materials for furnace walls
- C03B5/43—Use of materials for furnace walls, e.g. fire-bricks
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
- C04B35/48—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zirconium or hafnium oxides, zirconates, zircon or hafnates
- C04B35/481—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zirconium or hafnium oxides, zirconates, zircon or hafnates containing silicon, e.g. zircon
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
- C04B35/48—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on zirconium or hafnium oxides, zirconates, zircon or hafnates
- C04B35/484—Refractories by fusion casting
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/653—Processes involving a melting step
- C04B35/657—Processes involving a melting step for manufacturing refractories
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3201—Alkali metal oxides or oxide-forming salts thereof
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
- C04B2235/3215—Barium oxides or oxide-forming salts thereof
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
- C04B2235/3244—Zirconium oxides, zirconates, hafnium oxides, hafnates, or oxide-forming salts thereof
- C04B2235/3248—Zirconates or hafnates, e.g. zircon
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
- C04B2235/3251—Niobium oxides, niobates, tantalum oxides, tantalates, or oxide-forming salts thereof
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3409—Boron oxide, borates, boric acids, or oxide forming salts thereof, e.g. borax
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3418—Silicon oxide, silicic acids or oxide forming salts thereof, e.g. silica sol, fused silica, silica fume, cristobalite, quartz or flint
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
- C04B2235/72—Products characterised by the absence or the low content of specific components, e.g. alkali metal free alumina ceramics
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
- C04B2235/72—Products characterised by the absence or the low content of specific components, e.g. alkali metal free alumina ceramics
- C04B2235/727—Phosphorus or phosphorus compound content
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
- C04B2235/95—Products characterised by their size, e.g. microceramics
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Structural Engineering (AREA)
- Composite Materials (AREA)
- Inorganic Chemistry (AREA)
- Compositions Of Oxide Ceramics (AREA)
- Furnace Housings, Linings, Walls, And Ceilings (AREA)
- Glass Compositions (AREA)
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| FR1050600A FR2955577B1 (fr) | 2010-01-28 | 2010-01-28 | Produit refractaire a forte teneur en zircone. |
| PCT/IB2011/050389 WO2011092658A1 (fr) | 2010-01-28 | 2011-01-28 | Produit refractaire a forte teneur zircone |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| EA201200971A1 EA201200971A1 (ru) | 2013-01-30 |
| EA022720B1 true EA022720B1 (ru) | 2016-02-29 |
Family
ID=42145175
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| EA201200971A EA022720B1 (ru) | 2010-01-28 | 2011-01-28 | Огнеупорный продукт с высоким содержанием диоксида циркония |
Country Status (14)
| Country | Link |
|---|---|
| US (1) | US8822362B2 (enExample) |
| EP (1) | EP2528873B1 (enExample) |
| JP (2) | JP5889210B2 (enExample) |
| KR (1) | KR101779575B1 (enExample) |
| CN (1) | CN102741175B (enExample) |
| BR (1) | BR112012018405A2 (enExample) |
| CA (1) | CA2787649A1 (enExample) |
| EA (1) | EA022720B1 (enExample) |
| FR (1) | FR2955577B1 (enExample) |
| MX (1) | MX2012008599A (enExample) |
| MY (1) | MY158949A (enExample) |
| SG (1) | SG182722A1 (enExample) |
| TW (1) | TWI541216B (enExample) |
| WO (1) | WO2011092658A1 (enExample) |
Families Citing this family (12)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| FR2955578B1 (fr) | 2010-01-28 | 2014-06-13 | Saint Gobain Ct Recherches | Produit refractaire a forte teneur en zircone |
| FR2955577B1 (fr) * | 2010-01-28 | 2014-06-20 | Saint Gobain Ct Recherches | Produit refractaire a forte teneur en zircone. |
| FR2969145B1 (fr) * | 2010-12-16 | 2013-01-11 | Saint Gobain Ct Recherches | Produit refractaire a haute teneur en zircone. |
| FR2984878B1 (fr) * | 2011-12-21 | 2014-02-28 | Saint Gobain Ct Recherches | Produit refractaire a forte teneur en zircone. |
| EP2835364B1 (en) * | 2012-04-06 | 2020-06-10 | AGC Inc. | High zirconia fused cast refractory |
| CN104128219A (zh) * | 2014-08-15 | 2014-11-05 | 长沙开元仪器股份有限公司 | 一种存取样装置 |
| JP5763823B1 (ja) * | 2014-10-07 | 2015-08-12 | サンゴバン・ティーエム株式会社 | 高ジルコニア電気溶融鋳造耐火物 |
| EP3453689B1 (en) * | 2017-09-08 | 2020-08-26 | AGC Ceramics Co., Ltd. | High-zirconia electrocast refractory and method for manufacturing the same |
| CN110183236A (zh) * | 2018-02-22 | 2019-08-30 | 高佑君 | 一种高温耐火复合材料及其制备方法 |
| JP7054683B2 (ja) * | 2019-02-28 | 2022-04-14 | サンゴバン・ティーエム株式会社 | 高アルミナ質溶融鋳造耐火物及びその製造方法 |
| CN115368118B (zh) * | 2022-09-21 | 2023-05-16 | 淄博艾杰旭刚玉材料有限公司 | 超低气泡析出率azs电熔砖及其制备方法 |
| CN121974723B (zh) * | 2026-04-09 | 2026-06-23 | 湖南泽尔顿新材料有限公司 | 一种利用玻璃粉渗透再生氧化锆及其制备方法 |
Citations (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| FR2897861A1 (fr) * | 2006-02-24 | 2007-08-31 | Saint Gobain Ct Recherches | Refractaire a forte teneur en zircone a grande resistivite |
| FR2897862A1 (fr) * | 2006-02-24 | 2007-08-31 | Saint Gobain Ct Recherches | Produit refractaire fondu et coule a forte teneur en zircone, presentant une resistivite electrique amelioree. |
| WO2008113949A2 (fr) * | 2007-02-23 | 2008-09-25 | Saint-Gobain Centre De Recherches Et D'etudes Europeen | Bloc refractaire fondu et coule a forte teneur en zircone |
| WO2009027610A2 (fr) * | 2007-08-24 | 2009-03-05 | Saint-Gobain Centre De Recherches Et D'etudes Europeen | Produit refractaire a forte teneur en zircone dope |
Family Cites Families (19)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| FR1208577A (fr) | 1958-07-07 | 1960-02-24 | Electro Refractaire | Perfectionnements à la fabrication de produits réfractaires électrofondus contenant des oxydes minéraux |
| JPH0694391B2 (ja) | 1987-05-18 | 1994-11-24 | 東芝モノフラックス株式会社 | 高ジルコニア鋳造耐火物 |
| FR2648455B1 (fr) | 1989-06-15 | 1993-04-23 | Produits Refractaires | Produits refractaires fondus et coules a forte teneur en zircone |
| FR2701022B1 (fr) | 1993-02-03 | 1998-07-10 | Asahi Glass Co Ltd | Refractaires coules par fusion a forte teneur en zircone. |
| JP4714697B2 (ja) * | 2004-01-02 | 2011-06-29 | レフラクトリー インテレクチュアル プロパティー ゲゼルシャフト ミット ベシュレンクテル ハフツング ウント コンパニー コマンディトゲゼルシャフト | 電気抵抗の高い溶融鋳込みジルコニア耐火物 |
| US10674570B2 (en) | 2006-02-21 | 2020-06-02 | Goji Limited | System and method for applying electromagnetic energy |
| US8839527B2 (en) | 2006-02-21 | 2014-09-23 | Goji Limited | Drying apparatus and methods and accessories for use therewith |
| WO2008102334A1 (en) | 2007-02-21 | 2008-08-28 | Rf Dynamics Ltd. | Rf controlled freezing |
| US8653482B2 (en) | 2006-02-21 | 2014-02-18 | Goji Limited | RF controlled freezing |
| CN101427605B (zh) | 2006-02-21 | 2013-05-22 | 戈吉有限公司 | 电磁加热 |
| US9131543B2 (en) | 2007-08-30 | 2015-09-08 | Goji Limited | Dynamic impedance matching in RF resonator cavity |
| US9078297B2 (en) | 2008-02-21 | 2015-07-07 | Goji Limited | Methods and systems for a modular processing device |
| ES2448216T3 (es) | 2008-11-10 | 2014-03-13 | Goji Limited | Dispositivo y método de calentamiento mediante el uso de energía de radiofrecuencia (RF) |
| US20110033584A1 (en) | 2009-08-03 | 2011-02-10 | Rf Dynamics Ltd. | Method and system for dielectric heating and cooking |
| FR2955577B1 (fr) * | 2010-01-28 | 2014-06-20 | Saint Gobain Ct Recherches | Produit refractaire a forte teneur en zircone. |
| FR2955578B1 (fr) | 2010-01-28 | 2014-06-13 | Saint Gobain Ct Recherches | Produit refractaire a forte teneur en zircone |
| JP5739516B2 (ja) | 2010-03-26 | 2015-06-24 | ユニオン カーバイド ケミカルズ アンド プラスティックス テクノロジー エルエルシー | ヘアカラーリング用のパーソナルケア組成物 |
| US20110266463A1 (en) | 2010-05-03 | 2011-11-03 | Pinchas Einziger | Partitioned cavity |
| US9992824B2 (en) | 2010-10-29 | 2018-06-05 | Goji Limited | Time estimation for energy application in an RF energy transfer device |
-
2010
- 2010-01-28 FR FR1050600A patent/FR2955577B1/fr not_active Expired - Fee Related
-
2011
- 2011-01-28 BR BR112012018405A patent/BR112012018405A2/pt not_active IP Right Cessation
- 2011-01-28 EA EA201200971A patent/EA022720B1/ru not_active IP Right Cessation
- 2011-01-28 MY MYPI2012003391A patent/MY158949A/en unknown
- 2011-01-28 JP JP2012550553A patent/JP5889210B2/ja active Active
- 2011-01-28 MX MX2012008599A patent/MX2012008599A/es not_active Application Discontinuation
- 2011-01-28 WO PCT/IB2011/050389 patent/WO2011092658A1/fr not_active Ceased
- 2011-01-28 SG SG2012055067A patent/SG182722A1/en unknown
- 2011-01-28 US US13/575,555 patent/US8822362B2/en active Active
- 2011-01-28 CN CN201180007757.8A patent/CN102741175B/zh active Active
- 2011-01-28 TW TW100103485A patent/TWI541216B/zh active
- 2011-01-28 CA CA2787649A patent/CA2787649A1/fr not_active Abandoned
- 2011-01-28 EP EP11705268.8A patent/EP2528873B1/fr active Active
- 2011-01-28 KR KR1020127020940A patent/KR101779575B1/ko active Active
-
2015
- 2015-10-21 JP JP2015207244A patent/JP2016074591A/ja active Pending
Patent Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| FR2897861A1 (fr) * | 2006-02-24 | 2007-08-31 | Saint Gobain Ct Recherches | Refractaire a forte teneur en zircone a grande resistivite |
| FR2897862A1 (fr) * | 2006-02-24 | 2007-08-31 | Saint Gobain Ct Recherches | Produit refractaire fondu et coule a forte teneur en zircone, presentant une resistivite electrique amelioree. |
| WO2007099253A2 (fr) * | 2006-02-24 | 2007-09-07 | Saint-Gobain Centre De Recherches Et D'etudes Europeen | Refractaire a forte teneur en zircone a grande resistivite |
| WO2008113949A2 (fr) * | 2007-02-23 | 2008-09-25 | Saint-Gobain Centre De Recherches Et D'etudes Europeen | Bloc refractaire fondu et coule a forte teneur en zircone |
| WO2009027610A2 (fr) * | 2007-08-24 | 2009-03-05 | Saint-Gobain Centre De Recherches Et D'etudes Europeen | Produit refractaire a forte teneur en zircone dope |
Also Published As
| Publication number | Publication date |
|---|---|
| JP5889210B2 (ja) | 2016-03-22 |
| KR20120127594A (ko) | 2012-11-22 |
| JP2013518027A (ja) | 2013-05-20 |
| MX2012008599A (es) | 2012-08-15 |
| EP2528873A1 (fr) | 2012-12-05 |
| US20130199244A1 (en) | 2013-08-08 |
| SG182722A1 (en) | 2012-08-30 |
| US8822362B2 (en) | 2014-09-02 |
| TW201136865A (en) | 2011-11-01 |
| EA201200971A1 (ru) | 2013-01-30 |
| CA2787649A1 (fr) | 2011-08-04 |
| CN102741175B (zh) | 2016-06-22 |
| KR101779575B1 (ko) | 2017-09-18 |
| MY158949A (en) | 2016-11-30 |
| WO2011092658A1 (fr) | 2011-08-04 |
| FR2955577A1 (fr) | 2011-07-29 |
| FR2955577B1 (fr) | 2014-06-20 |
| BR112012018405A2 (pt) | 2018-08-07 |
| CN102741175A (zh) | 2012-10-17 |
| TWI541216B (zh) | 2016-07-11 |
| JP2016074591A (ja) | 2016-05-12 |
| EP2528873B1 (fr) | 2017-05-10 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US8822362B2 (en) | Refractory product having high zirconia content | |
| US8268742B2 (en) | Highly zirconia-based refractory and melting furnace | |
| US8796167B2 (en) | Refractory product having high zirconia content | |
| CN102264667B (zh) | 用于玻璃熔炉的耐火块 | |
| KR101793244B1 (ko) | 높은 지르코니아 함량을 갖는 내화 생성물 | |
| EA017354B1 (ru) | Огнеупорное изделие с высоким содержанием диоксида циркония и диоксида кремния | |
| EA013484B1 (ru) | Огнеупор с высоким удельным сопротивлением, с высоким содержанием диоксида циркония | |
| EA021990B1 (ru) | Огнеупорный материал с высоким содержанием добавки диоксида циркония | |
| EA023785B1 (ru) | Огнеупорное изделие с высоким содержанием диоксида циркония | |
| US10239793B2 (en) | Melted product with a high zirconium content |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| MM4A | Lapse of a eurasian patent due to non-payment of renewal fees within the time limit in the following designated state(s) |
Designated state(s): AM AZ BY KZ KG MD TJ TM RU |