DE801352C - Verfahren zur Herstellung von Magnetogrammtraegern - Google Patents
Verfahren zur Herstellung von MagnetogrammtraegernInfo
- Publication number
- DE801352C DE801352C DE1949P0043450 DEP0043450D DE801352C DE 801352 C DE801352 C DE 801352C DE 1949P0043450 DE1949P0043450 DE 1949P0043450 DE P0043450 D DEP0043450 D DE P0043450D DE 801352 C DE801352 C DE 801352C
- Authority
- DE
- Germany
- Prior art keywords
- production
- iron oxide
- heating
- magnetogram
- carriers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
- Verfahren zur Herstellung von Magnetogrammträgern Zur Herstellung von Tonträgern für das magnetographische Tonaufzeichnungs- und -wiedergabeverfahren benötigt inan magnetisierbare Stoffe, an die hinsichtlich Reinanenz und Koerzitivkraft besondere Anforderungen gestellt «-erden.
- Es wurde gefunden, <laß sich für diese Zwecke solche magnetisierbaren Eisenoxyde besonders gut eignen, welche durch Umsetzung von unmagnetischem Eisenoxv<i finit Salzen organischer Carbonsäuren, z. 13. Salzen der Essigsäure, Propionsäure oder Buttersäure, bei erhöhter Temperatur erhalten sind. Das Eisenoxvd kann nach einem bekannten Verfahren in der Weise gewonnen sein, daß man das unmagnetische Oxyd mit Alkaliacetat längere Zeit auf Schmelztemperatur erhitzt, wobei wegen der gleichzeitigen Bildung brennbarer, flüchtiger, organischer Verbindungen zweckmäßig für Ausschluß des Luftsauerstoffs gesorgt wird. Die so erhaltene schwarze Masse stellt nach dein Auswaschen des beim Erhitzen entstandenen Alkalicarbonats ein ferromagnetisches Eisenoxyd dar, das sich durch hohe Remanenz und hohe Koerzitivkraft auszeichnet. Diese kann noch gesteigert werden, wenn man das Produkt nachträglich einer Oxydation durch Erhitzen an der Luft unterwirft. Die gewünschten magnetischen Werte lassen sich durch `Fahl einer bestimmten Erhitzungsdauer und einer bestimmten Temperatur, die im allgemeinen zwischen 200 und .f00° liegt, beeinflussen.
- Beispiel i 7,2 Teile feinverteiltes unmagnetisches Eisenoxyd (sog. Eisenrot) werden mit 5,1 Teilen Natriumacetat in einer Stickstoffatmosphäre q. Stunden lang auf 450° erhitzt. Nach dem Erkalten wird die schwarze hasse durch Waschen mit Wasser von der gebildeten Soda befreit und getrocknet.
- Das so erhaltene Pulver wird entweder unmittelbar oder nach Erhitzen auf 2oo° an der Luft für die Herstellung von Magnetogrammträgern in der bekannten Weise mit Hilfe eines Bindemittels auf eine Trägerfolie aufgebracht. Beispiel e 55 Teile feinverteiltes Eisenoxyd werden mit ig Teilen Natriumpropionat innig gemischt und in einem mit Gasableitungsrohr versehenen Gefäß auf etwa 4oo° eine Stunde lang erhitzt. Das schwarze Reaktionsprodukt wird aus dem Gefäß mit Wasser herausgespült, von dem Wasser getrennt, neutral gewaschen und getrocknet. Durch Verkneten des Pulvers mit geeigneten Lackrohstoffen, z. B. Acetylcellulose, Nitrocellulose, Polyvinylchlorid o. dgl., und Vermischen der erhaltenen Massen mit Lösungsmitteln werden Dispersionen von magnetisierbarern Eisenoxyd erhalten, die nach Aufbringen auf eine Trägerfolie einen sehr guten Magnetogrammträger ergeben.
Claims (2)
- PATENTANSPRÜCHE: i. Verfahren zur Herstellung von Magnetogrammträgern unter Verwendung von magnetisierbaren Eisenoxyden, dadurch gekennzeichnet, daß man Eisenoxyde verwendet, welche durch Erhitzen von unmagnetischem Eisenoxyd mit Salzen organischer Carl)onsäuren, vorzugsweise unter Ausschluß des Luftsauerstoffs, erhalten sind.
- 2. Verfahren nach Anspruch i, dadurch gekennzeichnet, daß man ein Eisenoxyd verwendet, das durch Erhitzen von unmagnetischem Eisenoxyd mit Alkaliacetat auf Schmelztemperaturen unter Ausschluß des Luftsauerstoffs, Auswaschen und Trocknen und Erhitzen des erhaltenen Oxyds in Gegenwart von Sauerstoff erhalten ist.