DE595809C - Herstellung von negativen Elektroden fuer alkalische Sammler aus Eisen - Google Patents

Herstellung von negativen Elektroden fuer alkalische Sammler aus Eisen

Info

Publication number
DE595809C
DE595809C DEI40677D DEI0040677D DE595809C DE 595809 C DE595809 C DE 595809C DE I40677 D DEI40677 D DE I40677D DE I0040677 D DEI0040677 D DE I0040677D DE 595809 C DE595809 C DE 595809C
Authority
DE
Germany
Prior art keywords
cadmium
iron
alkaline
manufacture
negative electrodes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEI40677D
Other languages
English (en)
Inventor
Dr Karl Ackermann
Dr Georg Pfleiderer
Dr Fritz Spoun
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
IG Farbenindustrie AG
Original Assignee
IG Farbenindustrie AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by IG Farbenindustrie AG filed Critical IG Farbenindustrie AG
Priority to DEI40677D priority Critical patent/DE595809C/de
Application granted granted Critical
Publication of DE595809C publication Critical patent/DE595809C/de
Expired legal-status Critical Current

Description

DEUTSCHES REICH
AUSGEGEBEN AM
2Q.APRIL.i934
REICHSPATENTAMT
PATENTSCHRIFT
KLASSE 21b GRUPPE 25 os
Zusatz zum Patent 491
Patentiert im Deutschen Reiche vom 13. Februar 1931 ab Das Hauptpatent hat angefangen am 6. Juli 1928.
Gemäß dem Hauptpatent werden Elektroden - für Sekundärelemente, insbesondere • solche mit alkalischem Elektrolyten, in· der Weise hergestellt, daß die aktive Masse in die Poren eines zusammenhängenden, porösen, metallisch leitenden Materials, z. B. aus Eisen, eingebracht wird. Als aktive Masse für die negativen· Elektroden alkalischer Akkumulatoren kann man z. B. Cadmium, gegebenenfalls zusammen mit Eisen, verwenden.
Es wurde nun. gefunden, daß man Elektroden dieser Art durch. Imprägnieren poröser Eisenkörper mit Cadmiumverbindungen besonders vorteilhaft herstellen) kann, wenn man den Eiaenkörper vorher formiert, d.h. ihm durch eine oder mehrere anodische und kathoäüsche elektrolytische Behandlungen, zweckmäßig in Alkalilauge als Elektrolyt, schon für sich allein ohne Cadmium eine
ao gewisse Kapazität verleiht und ihn erst dann mit Cadmium imprägniert. Es entstehen so negative Elektroden, die eine wesentlich höhere Kapazität besitzen als derselbe Eisenkörper, der unformiert in der gleichen Weise mit Cadmium imprägniert wurde.
Das Einbringen des Cadmiums in die poröse Elektrode geschieht vorzugsweise durch Tränken mit einer konzentrierten Cadmiumchloridlösung und darauffolgendes Ausfällen von Cadmiumhydroxyd in den Poren durch Alkalilauge. Nach der Imprägnierung geht die Kapazität der Elektrode zwar zunächst erheblich zurück, steigt aber schon nach wenigen Entladungen wieder ungefähr auf jdenselben Wert wie vorher, wobei sie nun aber die Vorteile der Cadmiumelektroden, geringe Abhängigkeit der Kapazität von der Temperatur und geringes Nachgasen beim Stehen in geladenem Zustand, besitzt.
Die Anwendung des Cadmiumchlorids zur Imprägnierung der Elektrodenkörper hat außer der großen Löslichkeit dieses Salzes in Wasser den Vorteil, daß sich mit der Cadmiumimprägnierung sehr leicht eine Quecksilberimprägnierung verbinden läßt. Es ist zweckmäßig, dem Eisen einen Zusatz von etwa 2 0/0 Quecksilber zu erteilen. Bei der geringen Löslichkeit der Quecksilbersalze in Wasser müßte die Imprägnierung mehrmals wiederholt werden, wobei die Platten nach
*) Von dem Patentsucher sind als die Erfinder angegeben worden:
Dr. Georg Pfleiderer, Dr. Frits Spoun in Ludwigshafen a. Rh. und Dr. Karl Ackermann in Mannheim.
jeder Imprägnierung getrocknet werden müßten. Es gelingt jedoch, schon mit einer Imprägnierung auszukommen, wenn man die Eigenschaft des Quecksilberchlorids, sich in Lösungen von Cadmiumchlorid sehr leicht unter Komplexsalzbildung zu lösen, verwertet. In vielen Fällen ist es zweckmäßig, die Haltbarkeit der Elektrodenkörper dadurch zu erhöhen, daß man Teile des letzteren von der ίο Tejlnahme an den elektrochemischen Vorgängen ausschließt, so daß diese Teile als schwer oder unangreifbares Gerüst dienen.
Beispiel
Eine 327,8 g schwere, durch Sintern von aus Eisencarbonyl gewonnenem Eisenpulver hergestellte und mit einem unangreifbaren Gitterwerk versehene poröse Platte wird mit alkoholischer Quecksilberchloridlösung getränkt, ι Stunde lang mit heißer 250/oiger Kalilauge behandelt und dami bei 400 in der gleichen Lauge elektrolytisch formiert. Die Platte hatte darauf bei den beiden ersten Entladungen eine Kapazität von 80 bis 90 Amperestunden.
Hierauf wurde die Elektrodenplatte im entladenen Zustand durch Waschen von dem in ihr enthaltenen Alkali befreit, in einer Cadmiumchloridlösung gebadet und dann wieder mit Kalilauge, wie oben angegeben, behandelt. Die nunmehr einen Gehalt von 3 0/0 Cadmium aufweisende Platte zeigte bei der Verwendung als negative Sammlerelektrode eine durchschnittliche Kapazität von 74 Am- 35' perestunden entsprechend einer spezifischen Kapazität von 0,22 Amperestunden pro Gramm. ■

Claims (2)

  1. Patentansprüche:
    ι. Herstellung von negativen Elektroden für alkalische Sammler aus Eisen nach Patent 491498 unter Verwendung von cadmiumhaltiger aktiver Masse, dadurch gekennzeichnet, daß der poröse Eisenkörper vor dem Einbringen der Cadmiumverbindungen formiert wird.
  2. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß man zur Imprägnierung des porösen Eisenkörpers ^0 eine wäßrige Lösung von Cadmiumchlorid und Quecksilberchlorid verwendet.
DEI40677D 1931-02-13 1931-02-13 Herstellung von negativen Elektroden fuer alkalische Sammler aus Eisen Expired DE595809C (de)