DE3444712A1 - Stahlmatrix-hartstoff-verbundwerkstoff - Google Patents

Stahlmatrix-hartstoff-verbundwerkstoff

Info

Publication number
DE3444712A1
DE3444712A1 DE19843444712 DE3444712A DE3444712A1 DE 3444712 A1 DE3444712 A1 DE 3444712A1 DE 19843444712 DE19843444712 DE 19843444712 DE 3444712 A DE3444712 A DE 3444712A DE 3444712 A1 DE3444712 A1 DE 3444712A1
Authority
DE
Germany
Prior art keywords
weight
steel matrix
material composite
hot
sintered material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19843444712
Other languages
English (en)
Inventor
Helmut Dipl.-Ing. 8000 München Seilstorfer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Seilstorfer & Co Metallur GmbH
Original Assignee
Seilstorfer & Co Metallur GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Seilstorfer & Co Metallur GmbH filed Critical Seilstorfer & Co Metallur GmbH
Priority to DE19843444712 priority Critical patent/DE3444712A1/de
Publication of DE3444712A1 publication Critical patent/DE3444712A1/de
Withdrawn legal-status Critical Current

Description

  • Beschreibung
  • Die Erfindung betrifft einen Stahlmatrix-artstoff-Verbundwerkstoff, der durch heißisostatisches Pressen eines Pulvergemisches aus Stahlmatrix und Hartstoffphase gewonnen ist.
  • Solche Verbundwerkstoffe sind grundsätzlich bekannt (DE-OS 33 08 409).
  • Aufgabe der Erfindung ist es, einen Verbundwerkstoff zu schaffen, mit dem sich eine besonders geeignete Warmhärte und Warmfestigkeit sowie eine hohe Biegebruchfestigkeit erzielen lassen.
  • Diese Aufgabe wird erfindungsgemäß gelöst durch einen Stahlmatrix-Hartstoff-Verbundwerkstoff, gebildet durch heißisostatisches Pressen eines Pulvergemisches aus 50 bis 95 Vol.-% Warmarbeitsstahlmatrix der Zusammensetzung 0,01 bis 0,1 Gew.-% C, 0,5 bis 1,0 Gew.-% Si, 12,0 bis 20,0 Gew.-% Cr, 10,0 bis 15,0 Gew.-% Co, 1,0 bis 10,0 Gew.-E Mo, 20,0 bis 60,0 Gew.-% Ni, 0,1 bis 1,0 Gew.-% V, 1,0 bis 4,0 Gew.-% Ti, 1,0 bis 4,0 Gew.-% Al, Rest, abgesehen von unvermeidbaren Verunreinigungen, Eisen mit 50 bis 5 Vol.-% eines der Hartstoffe TiC, A1203, B4C und VC.
  • Ein solches Pulvergemisch mit in ihrer Zusammensetzung neuer Stahlmatrix ergibt beim heißisostatischen Pressen einen Werkstoff hoher Härte und Zähigkeit für erweiterte Warmarbeitsstahl-Einsatzmöglichkeiten.
  • Die Parameter des heißisostatischen Pressens sind typischer-und vorzugsweise 13500C, 1000 bar und 3 h. Das Pulver der Stahlmatrix hat vorzugsweise nur Anteile kleiner 45 Am Korngröße. Das Pulver der Hartstoffphase hat vorzugsweise eine Korngröße zwischen 5 und 10wem.

Claims (1)

  1. Stahlmatrix-HartstofE-Verbundwerkstoff Patentanspruch 1. Stahlmatrix-Hartstoff-Verbundwerkstoff gebildet durch heißisostatisches Pressen eines Pulveryemisches aus 50 bis 95 Vol.-% Warmarbeitsstahlmatrix der Zusammensetzung 0,01 bis 0,1 Gew.-% C, 0,5 bis 1,0 Gew.-% Si, 12,0 bis 20,0 Gew.-% Cr, 10,0 bis 15,0 Gew.-% Co, 1,0 bis 10,0 Gew.-% Mo, 20,0 bis 60,0 Gew.-9 Ni, 0,1 bis 1,0 Gew.-% V, 1,0 bis 4,0 Gew.-% Ti, 1,0 bis 4,0 Gew.-% Al, und unvermeidbare Verunreinigungen, Rest Eisen mit 50 bis 5 Vol.-% eines der Hartstoffe TiC, A1203, B4C und VC.
DE19843444712 1984-12-07 1984-12-07 Stahlmatrix-hartstoff-verbundwerkstoff Withdrawn DE3444712A1 (de)