DE3114020C2 - Verwendung eines Stahls zur Herstellung von kaltgewalztem Tiefzieh-Stahlblech - Google Patents

Verwendung eines Stahls zur Herstellung von kaltgewalztem Tiefzieh-Stahlblech

Info

Publication number
DE3114020C2
DE3114020C2 DE3114020A DE3114020A DE3114020C2 DE 3114020 C2 DE3114020 C2 DE 3114020C2 DE 3114020 A DE3114020 A DE 3114020A DE 3114020 A DE3114020 A DE 3114020A DE 3114020 C2 DE3114020 C2 DE 3114020C2
Authority
DE
Germany
Prior art keywords
steel
cold
strength
rolled
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE3114020A
Other languages
German (de)
English (en)
Other versions
DE3114020A1 (de
Inventor
Yoshikuni Kitakyusyu Fukuoka Furuno
Masaaki Shibata
Nobuyuki Takahashi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of DE3114020A1 publication Critical patent/DE3114020A1/de
Application granted granted Critical
Publication of DE3114020C2 publication Critical patent/DE3114020C2/de
Expired legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
    • C21D8/0426—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
    • C21D8/0436—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0478—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing involving a particular surface treatment

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
DE3114020A 1980-04-09 1981-04-07 Verwendung eines Stahls zur Herstellung von kaltgewalztem Tiefzieh-Stahlblech Expired DE3114020C2 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP55046473A JPS5942742B2 (ja) 1980-04-09 1980-04-09 降伏比の低い深絞り用高強度冷延鋼板

Publications (2)

Publication Number Publication Date
DE3114020A1 DE3114020A1 (de) 1982-02-18
DE3114020C2 true DE3114020C2 (de) 1985-08-08

Family

ID=12748153

Family Applications (1)

Application Number Title Priority Date Filing Date
DE3114020A Expired DE3114020C2 (de) 1980-04-09 1981-04-07 Verwendung eines Stahls zur Herstellung von kaltgewalztem Tiefzieh-Stahlblech

Country Status (8)

Country Link
US (1) US4441936A (enExample)
JP (1) JPS5942742B2 (enExample)
BE (1) BE888322A (enExample)
DE (1) DE3114020C2 (enExample)
FR (1) FR2480311A1 (enExample)
GB (1) GB2074605B (enExample)
IT (1) IT1142482B (enExample)
SE (1) SE457801B (enExample)

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5839766A (ja) * 1981-09-01 1983-03-08 Kobe Steel Ltd 焼付硬化性及び深絞り性のすぐれた高強度冷延鋼板
JPS5867827A (ja) * 1981-09-18 1983-04-22 Nippon Steel Corp 深紋り用冷延鋼板の製造方法
JPS5989727A (ja) * 1982-11-12 1984-05-24 Kawasaki Steel Corp プレス成形性の優れた超深絞り用冷延鋼板の製造方法
JPS59177327A (ja) * 1983-03-25 1984-10-08 Sumitomo Metal Ind Ltd プレス加工用冷延鋼板の製造法
JPS6013053A (ja) * 1983-07-04 1985-01-23 Nisshin Steel Co Ltd 高温強度と耐熱性の優れたアルミニウムめつき鋼板
US4542048A (en) * 1983-07-07 1985-09-17 Inland Steel Company Powder metal and/or refractory coated ferrous metals
US4624895A (en) * 1984-06-04 1986-11-25 Inland Steel Company Aluminum coated low-alloy steel foil
JPS6043476A (ja) * 1983-08-17 1985-03-08 Nippon Steel Corp 連続溶融アルミメツキ法
JPS6383230A (ja) * 1986-09-27 1988-04-13 Nkk Corp 焼付硬化性およびプレス成形性の優れた高強度冷延鋼板の製造方法
JPS63190141A (ja) * 1987-02-02 1988-08-05 Sumitomo Metal Ind Ltd 成形性の良好な高張力冷延鋼板とその製法
US4931106A (en) * 1987-09-14 1990-06-05 Kawasaki Steel Corporation Hot rolled steel sheet having high resistances against secondary-work embrittlement and brazing embrittlement and adapted for ultra-deep drawing and a method for producing the same
JP2599466B2 (ja) * 1989-10-17 1997-04-09 新日本製鐵株式会社 非時効性に優れた低降状比構造用鋼材およびその製造方法
ES2125856T5 (es) * 1990-08-17 2004-09-16 Jfe Steel Corporation Lamina de acero de alta resistencia para formado en prensa y metodo de produccion de la misma.
WO1992016669A1 (en) * 1991-03-13 1992-10-01 Kawasaki Steel Corporation High-strength steel sheet for forming and production thereof
WO1992016668A1 (en) * 1991-03-15 1992-10-01 Nippon Steel Corporation High-strength, cold-rolled steel sheet excellent in formability, hot-dip zinc coated high-strength cold rolled steel sheet, and method of manufacturing said sheets
US5690755A (en) * 1992-08-31 1997-11-25 Nippon Steel Corporation Cold-rolled steel sheet and hot-dip galvanized cold-rolled steel sheet having excellent bake hardenability, non-aging properties at room temperature and good formability and process for producing the same
JPH07179946A (ja) * 1993-12-24 1995-07-18 Kawasaki Steel Corp 耐二次加工ぜい性に優れる高加工性高張力冷延鋼板の製造方法
EP1026278B2 (en) † 1998-07-27 2014-04-30 Nippon Steel & Sumitomo Metal Corporation Use of a ferritic steel sheet having excellent shape fixability and manufacturing method thereof
US6488790B1 (en) 2001-01-22 2002-12-03 International Steel Group Inc. Method of making a high-strength low-alloy hot rolled steel
JP5272714B2 (ja) * 2008-12-24 2013-08-28 Ｊｆｅスチール株式会社 製缶用鋼板の製造方法

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1022256A (en) * 1961-12-11 1966-03-09 Yawata Iron & Steel Co Atmospheric corrosion-resistant cold-rolled steel sheet of deep drawing quality
FR1359542A (fr) * 1962-06-05 1964-04-24 Yawata Iron & Steel Co Tôles d'acier pour emboutissage profond résistant à la corrosion atmosphérique
FR1339970A (fr) * 1962-11-27 1963-10-11 Yawata Iron & Steel Co Tôle d'acier laminée à froid résistant à la corrosion atmosphérique de qualité pour emboutissage profond
US3598658A (en) * 1967-05-20 1971-08-10 Yawata Iron & Steel Co Method for manufacturing cold-rolled steel sheet
US3607456A (en) * 1969-04-15 1971-09-21 Bethlehem Steel Corp Deep drawing steel and method of manufacture
US3827924A (en) * 1971-05-21 1974-08-06 Nippon Steel Corp High-strength rolled steel sheets
DE2133744B2 (de) * 1971-07-07 1973-07-12 August Thyssen-Hütte AG, 4100 Duisburg Die verwendung eines vollberuhigten stahles fuer gegenstaende aus warmgewalztem band
DE2316324C2 (de) * 1972-04-03 1988-05-05 Nippon Steel Corp., Tokyo Verfahren zum Herstellen von alterungsbeständigem Stahlblech
US3988173A (en) * 1972-04-03 1976-10-26 Nippon Steel Corporation Cold rolled steel sheet having excellent workability and method thereof
US3988174A (en) * 1972-04-03 1976-10-26 Nippon Steel Corporation Hot rolled steel sheet having excellent workability and method thereof
US3897280A (en) * 1972-12-23 1975-07-29 Nippon Steel Corp Method for manufacturing a steel sheet and product obtained thereby
US3926692A (en) * 1974-09-30 1975-12-16 United States Steel Corp Drawability of deoxidized steels by the addition of phosphorus and silicon
JPS5271327A (en) * 1975-12-12 1977-06-14 Nisshin Steel Co Ltd Good cold workability stabilized nontempering high strength hot rolling steel and production of it
JPS54104417A (en) * 1978-02-06 1979-08-16 Kobe Steel Ltd Cold rolled steel sheet with superior surface properties and deep drawability
JPS54132421A (en) * 1978-04-05 1979-10-15 Nippon Steel Corp Manufacture of high toughness bainite high tensile steel plate with superior weldability
JPS5818973B2 (ja) * 1978-08-11 1983-04-15 日本鋼管株式会社 プレス成形性の優れた高張力冷延鋼板の製造方法
JPS5669359A (en) * 1979-10-16 1981-06-10 Kobe Steel Ltd Composite structure type high strength cold rolled steel sheet
US4397699A (en) * 1980-05-27 1983-08-09 Nippon Steel Corporation Process for producing deep-drawing cold rolled steel strip by continuous annealing

Also Published As

Publication number Publication date
JPS5942742B2 (ja) 1984-10-17
SE8101929L (sv) 1981-10-10
FR2480311A1 (fr) 1981-10-16
IT8148223A0 (it) 1981-04-07
SE457801B (sv) 1989-01-30
GB2074605A (en) 1981-11-04
IT1142482B (it) 1986-10-08
US4441936A (en) 1984-04-10
JPS56142852A (en) 1981-11-07
BE888322A (fr) 1981-07-31
GB2074605B (en) 1984-01-25
FR2480311B1 (enExample) 1985-04-12
DE3114020A1 (de) 1982-02-18

Similar Documents

Publication Publication Date Title
DE3114020C2 (de) Verwendung eines Stahls zur Herstellung von kaltgewalztem Tiefzieh-Stahlblech
DE3107276C2 (de) Verwendung eines nichtrostenden ferritischen Stahls als Werkstoff zur Herstellung von Tiefziehblechen
EP3504349B1 (de) Verfahren zur herstellung eines höchstfesten stahlbandes mit verbesserten eigenschaften bei der weiterverarbeitung und ein derartiges stahlband
EP2553133B1 (de) Stahl, stahlflachprodukt, stahlbauteil und verfahren zur herstellung eines stahlbauteils
DE69935125T3 (de) Hochfestes, kaltgewalztes Stahlblech und Verfahren zu dessen Herstellung
DE69221597T2 (de) Hochfestes warmgewalztes Stahlfeinblech mit niedrigem Strechgrenzenverhältnis und Verfahren zu seiner Herstellung
DE2607646C2 (de) Kaltgewalztes und geglühtes Stahlband und Stahlblech, dessen Verwendung und Verfahren zu seiner Herstellung
DE69002661T2 (de) Emaillierfähige Stahlbleche und Verfahren zu ihrer Herstellung.
DE3107490C2 (de) Verfahren zur Herstellung eines Niob enthaltenden, rostfreien Chromferrit-Stahlblechs
DE4219336C2 (de) Verwendung eines Stahls zur Herstellung von Konstruktionsrohren
DE69311393T2 (de) Verfahren zum Herstellen hochfester Stahlbleche für Dosen
DE10128544A1 (de) Höherfestes, kaltumformbares Stahlband oder -blech, Verfahren zu seiner Herstellung und Verwendung eines solchen Bands oder Blechs
DE69228403T2 (de) Hochfestes, kaltgewalztes, bei Raumtemperatur alterungsbeständiges, tiefziehbares Stahlblech und Herstellungsverfahren
DE69618263T2 (de) Kaltgewalztes Stahlblech mit hervorragender Pressverformbarkeit und Herstellungsverfahren
DE3126386C2 (de) Verfahren zur Herstellung von preßumformbarem, hochfestem Stahlblech mit einem Zweiphasengefüge
DE69713639T2 (de) Stahl, Stahlblech mit hervorragender Bearbeitbarkeit und dessen Herstellungsverfahren durch Elektrostahlofen und Vakuumentgasung
DE2324788A1 (de) Kohlenstoffarmer stahl und verfahren zu seiner herstellung
DE69021471T2 (de) Kaltgewalztes Tiefziehblech aus Stahl und Verfahren zu seiner Herstellung.
DE69130555T3 (de) Hochfestes Stahleinblech zur Umformung durch Pressen und Verfahren zur Herstellung dieser Bleche
DE69716518T2 (de) Stahlblech mit gut aussehender Oberfläche und Beulfestigkeit nach der Verformung
DE69329696T2 (de) Kaltgewalztes Stahlblech, gegebenenfalls feuerverzinkt, mit guter Einbrenn-härtbarkeit, gute Kaltalterungsbeständigkeit und Formbarkeit und Verfahrenzur Herstellung dieser Bleche
DE3045761C2 (de) Verfahren zur Herstellung eines hochfesten kaltgewalzten Stahlbands mit ausgezeichneter Preßformbarkeit
DE69521284T2 (de) Verfahren zum Herstellen von Stahlblechen hoher Schlagfestigkeit für den Automobilbau
DE69216503T2 (de) Kaltgewalztes hochfestes Stahlblech mit hervorragender Tiefziehfähigkeit
EP3512968B1 (de) Verfahren zur herstellung eines stahlflachprodukts aus einem manganhaltigen stahl und ein derartiges stahlflachprodukt

Legal Events

Date Code Title Description
OP8 Request for examination as to paragraph 44 patent law
8128 New person/name/address of the agent

Representative=s name: SCHWABE, H., DIPL.-ING. SANDMAIR, K., DIPL.-CHEM.

D2 Grant after examination
8364 No opposition during term of opposition