CS215886B1 - Pure alumina producing method - Google Patents
Pure alumina producing method Download PDFInfo
- Publication number
- CS215886B1 CS215886B1 CS788431A CS843178A CS215886B1 CS 215886 B1 CS215886 B1 CS 215886B1 CS 788431 A CS788431 A CS 788431A CS 843178 A CS843178 A CS 843178A CS 215886 B1 CS215886 B1 CS 215886B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- leaching
- stage
- hydrolysis
- process according
- temperature
- Prior art date
Description
METOfl nOJďWiHB >meř6B OK^jatBtlBfa 213 886 UOJiaCTB ΠρΗΜβΗβΗΗΗ ΗδΟό^ΤβΙΚΗ»"
HacTOíímae Η300ρβτβΗΗβ othochtch k npoMumjieHHOMy Maiosy cepHO-KHCJlOTHOrO BWJianHBaHHfl rJlHH OH ΟΗΗΟΒβΜΗΟΤΗΧ MHHepaJIOBAJifl nojiyqeHHH *imctoíí okhch aJHOMHHHH Hepe3 ochobhuíí npoMesyToq-Huíí npoayKT.
XapaKTepucTHKa οβθοτηηχ τθχηηηθοκηχ pemeHHÍÍ H3BecieH μθτοα nojiyqeHHH okhch aJHOMHHHH, 3aKJHoqaiomHíícH bΒΗΙΙξβΗβΊΜΒβΗΗΗ AlgO^ -COjepKaiHHX MHHepaJIOB CepHOft KHCJIOTOÍi ΠρΗΠΟΒΜΠΙβΗΗΜΧ £(8ΒΒ6ΗΗΗ H TeMnapaType, ΟΤΤξβΛΘΗΗΗ ΗβρβΟΤΒΟρΗΜΟΓΟKeňa, BOccTaHOBJíeHHM coflepacamarocn β pacTBopa «ejiaea bo H30a-Κ3ΗΗ6 ΘΓΟ OCaOeHHfl, ΓΗΑρ03ΐΜ3β paCTBOpa CyJIB$aTa aJHOMHHHH ηΤβρΜΜΗθΟΚΟΜ pd3JI0X6HHH OCaWHHOrO ΟΟΗΟΒΗΟΓΟ CyjIBiaia aJHOMHHHH(AS I 179 919). B CBH3H C 3THM Η3ΒΘ0ΤΗ0, ΨΓ0 BUXOfl ΤΒβρΑΟΓΟ IipO^KTa ΓΜ£ρθΛΗ33B6CBM3 CHJIBHO 33PHCHT OT OCHOBHOCTH paCTBOpa» K3K 3T0 Bbipa-KaeTCH, HanpHMeft b othoui6hhh MaccSO^tAlgO^.fljiH ycTaHOBjíeHHHB03M0KH0 ΗΗ3Κ0Γ0 ΟΤΗΟΙΙΙβΗΗΗ ΠρβρίΙβΓΘΘΤΟΗ flOÓaBHTB OCHOBHUÍÍCyJIÍ>$aT aJHOMHHHH HJIH 3KTHBHUÍÍ rJIHH036U. flJIH 3T0ÍÍ HOJIH HCnOJlh-3yeTCH hjih ochobhuíí cyjn>$aT, nojiyqaaMuíi b npoiiacce BuqajiaHHBa-HHH nofl flaBJl6HH6M, HJIH aKTHBHUÍt ΟΗΗ03ΘΜ H3 ΠρΟίφΟΟβ ΤβρΜΗ^ΙβΟ-ΚΟΓΟ pa3JIOK0HHH. Β pe3yjIBTaTe T8K0ÍÍ ΚΟρρβΚΙξΗΗ ΟΤΗΟΙΙΙβΗΗΗ MacecorjiacHO πρβΛΛΟ^θΗΗΐο flo 30 % nojiyqaHHoro οοηοβηογο cyjiB$aTaHJIH 3ΚΤΜΒΗ0Γ0 ΟΗΗ03ΘΜβ Ββ^θΤΟΗ Β Ο<5θρθΤΘ. ΤβΚΟβ Β03Βρ3ΙΙΙβΗΗΘqacTH οοηοβηογο cyjiB$iaTa hjih βκτηβηογο rjiHH03aMa BecBMa chjibhoHarpyaaeT οδοροτ Maiepnajia. 3το ηηχολητ οβοθ BupaaeHHe β ποβη-IH6HHH saTpaT Ha βηθργηιο η annapaTypy, uto βηθ^ητθιιβηο yaopojKaeinpouecc.
CymecTByai ema spyran bo3moxhoctb ποβηπιθηηη ochobhocth paciBO-pa - sto aočaBKa rHapooKHcafi mejioqHux MaTajuiOB hjih hx cojielt.floóaBKa 3THx χημηοτοβ β τθχιθηηθ 0onee zuíMTejiBHoro βρθμθηη πρκ-BOflHT K HeflOnyCTHMOMy 33ΓρΗ3ΗΘΗΜΒ ΚΟΗΘΗΗΟΓΟ npOflyKTa, Τ.Θ. OKH-CH aJHOMHHHH. fljIH ΤΟΓΟ, 4T0ÚU POCTH^B ΠρΗΓΟΛΗΟΓΟ JJIH SJíeKTpO-jiH3a pacnjiaBa nposyKTa HaMeqenu cooTBeTCTByiomHe CTaflHH ooctrh,narpyaaioiuHa npouacc b annapaTypHOM η θηθργθτηηθοκομ οτηοιιιθηηηχ. - i - 21S 886 H3B6CTHO0 ΠρβΑΛΟΚβΗΗβ ΜβΤΟΑβ AJIH ΟθρΗΟΚΗΟΛΟΤΗΟΓΟ BHmeEa^HBa— HHH ΓΟΗ Η ΓΗΗΗ03βΜΗ0ΤΗΧ ΜΗΗβρβΧΟΒ, BKJIlDWí ΠΟΟΛβΛγίΟΙίξΗβ Onepa-UHH, TpečyeT bncokhx annapaTypHOft, SHepreTHqecKHx η τθμ οομνμSKOHOMHUeCKHX 3aTpaT. Πο 3ΤθΚ ΠρίΠΗΗβ 3Τ0 Η3Ββ0ΤΗ0β npeflJIO-χβΗΗβ MeTOsa ne Hauuio θπξθ ηηκβκοΑ npoMhinuieHHOft peao3auHH.flpyrne HeflOCTaTKK Η3βθοτηογο npouecca - HeH3<5eacHaH Harpy3KaUHoa οόοροτΗΗΜ MaTepMOM, trro 03HaqaeT HeaonycTHMoe šarpH3-H6HH6 κοηθίηογο nposyKTa h yMeHBiueHHe ero yaejiBHoro Beca bΟόίΙξθΜ ΒΗΧΟΛθ.
UeJIL· Η300ΡΘΤΘΗΗΗ
Hejli Η300ρβΤΘΗΗΗ 38ΚΛΙ0ηθβΤΟΗ BO ΒΒΘΛβΗΗΗ B ΤβΧΗΟΛΟΓΗΚ) pHflaOTUaCTH CymeCTBeHHHX Η3ΜβΗβΗΗΗ ZWIfl ΟΗΗΚβΗΗΗ BNCOKHX TeXHHqeCKHXm sHepreTircecKHx 3aTpaT, B03HHKaiomnx πρκ Η3βθοτηομ MeTose πο-JiytieHHH OKHCH aJIIOMHHHfl CepHOKHCJIOTHNM BUmeJia^HBaHHeM rjIMH03e-Mhcthx MHHepajiOB, a TaKsce sjia co3saHHfl TexHOJioroecKM npocToro,3K0H0MHqeCKM ΒφφθΚΤΜΒΗΟΓΟ H 0CyiH6CTBMM0r0 B npOMNIUJieHHOCTHnpouecca, oÓecneunBaioinero nojiyqeHHe okhch 3ηιομηηηα Taicoft mc-totn, KOTopan π03Β0ΗΗβτ ee πρημθηθηηθ sjih npoH3BoscTBa MeTan-JlHUeCKOrO aSIOMMHHfl H3B6CTHNMH HeTOJiaMH.
CymHOCTB Η300ρβΤβΗΗΗ
Basana Η30όρβτβΗΗΗ 3aoiouaeTCH b co3saHHH MeTosa nojiywHflOKHCH aJIIOMHHHfl SByCTaSHftHNM BNHiejiatlHBaHHeM MexaHHneCKH h/hjih•τβρΜΗΗβοκΗ oópatfoiaHHNx tjihh hjih γηηηο3Θμηοτηχ MHHepaJioB cep-HO0 KHCJIOTOÍi nos ΛΘΒΗΘΗΗβΜ Η ΠρΗ ΠΟΒΝΙϋβΗΗΟβ TeMnepaType, OT-seneHHeM HepacTBopHMoro κβκβ, BoccTaHOBJíeHHeM acejie3a, rnspo-SHTHUeCKHM OCaWHHeM TBepSOrO ΟΟΗΟΒΗΟΓΟ CyJIB0aTa aJUOMHHHfl Hero nocjiesyiomHM τθρμη^θοκημ pašJioseHHeM b γληηο3ΘΜ, BKjnoqaflperenepaunio oÓopoTHoit khcjiotn H3 ra30B npouecca pa3JioaeHHH. Μθτολ corsacHO Μ3θ6ρβτβΗΗΐο npescTaBJíneT coóott oóO3pHMHtt npouecc,COCTOflmHftCfl H3 ΗβΜΗΟΓΗΧ CTaSHt! H SaKJHOUaiOIHHÍlCfl B BbímejiaUHBaHHMrjiHHN, nojiyweuHH οοηοβηογο pacTBopa cyjn>$aTa aJUOMHHHfl, a TaoeB ΒΗΒΟΑΘ 3arpfl3HeHMÍÍ c ΚρθΜΗΗΟΤΝΜ ΚΘΚΟΜ ΒΟΘΓΟ B SByX CT3SMflX, B BOCCTaHOBJíeHHH HCXOSHOrO paCTBOpa SJIfl rHSpOJIH3a, B THSpO-3iH3auHH pacTBopa h nocjiesyromeíí KpHCTaJiJiHeauHH b τβθρλνΗ ochob-hnK cyjn>$aT aJUOMHHHfl b oshoM οτθληη. 3to πο3βοληθτ βπθρβηθB ηρΟΜΗΙΠΛβΗΗΟΟΤΗ B BKOHOMMqeCKH Η ΤβΧΗΟΛΟΓΗ^βΟΚΜ ΒΝΓΟβΗΝΧ yCJIO-BHHX ΠρΗΜΘΗΗΤΒ KHCJIOTHNÍÍ ΠρΟΙξθΟΟ ΒΗΠΙΘΛ3^ΗΒ3ΗΗΗ ΓΗΜΗ03ΘΜ3· 2 215 886 Μθτολ comacEO Η30όρβτθΗΗΐ> OTJinqaeTCH HenpepusHOtt nocaesoBa-TeJIBHOCTLIO ΟΤβθΠΒΗΗΧ OnepaUHti B UHKJie, ΟΠρβΛΘΗΗΘΤΟΗ CGCT3B0MiíHpKyjiHpyDmnx ηηακοοτθΚ, nyjiin h odopoTHux pacTBopoB, xapaKTe-pH3yeTCfl ΒΒβββΗΜΘΜ MJIH OTÓOpOM ΒΘΚΗΗΧ Πρ0ΜΘ^Τ0*ΙΗΗΧ npOflyKTOBHa onpesejieHHhíx Meciax pnoa, a τβκχβ ycjiOBHHMH peaKijHH, KaKsaBJíeHHeM, TeMnepaTypott h 3aflepxK0ft. ΜβτοΛ corjiacHO Η30όρβτβΗΗΚ) coctoht m3 caeayioqHx onepaiwft:MexaHMqecKH h/hjih τβρΜκηβοκΗ odpaÓOTaHHafl ranna hjih γηηηο3Θ-mmctlis mhh θ pa jih Bhimejia^iMBaioTCH b nepBOtt cTaw προyecca c$OBTpaTOM Βτοροϋ CTaflO BtiinejianHBaHMH npw τβΜΠβρβτγρβ 110 -150 °C b τβ^βΗΗθ 15 - 60 mhh. IlepBafl οτθληη βηιιιθπθηηβθηηηnpOBOflHTCH npM yCJIOBHH ftOCTM3K6HHH ΟΟβ«ΛΘΗΗΗ «ΘΛΘββ, C00TB6T-CTByiomero KOjinnecTBy BbiqejiaqeHHoro b nponecce aene3a, b BH^eHepacTBopHMoro b KHcaoft oójiacTH κομππθκοηογο οοβΛΗΗβΗΗπ cyjiB$a-Ta TpexBajieHTHoro»eJie3a πρκ bo3mo»ho Biicniefl οτθπθηη pacTBope-ΗΗΗ ΓΛΗΗΗ. £jih nepBOíí CTaflHH βηι^θπθηηβθηηη (HeiíTpaJiBHOQ BiimejiawHBaHMa)HarnjiH, hto npeMMymecTBeHHO ηθοΡχολημηΜ snana30H TQMnopaTypuΠΟ CpaBHeHHD C H3B0CTHÍJM, ρβΗΘΘ ΠρβΖΡΙΟΚβΗΗΗΜ MOTOflOM flOJIMOHČHTB ΟΗΗ3ΚΘΗ flO 115 - 125 °C, HTOČU npeflOTBpaTHTB yM6HBU16HHeBHXOaa Η ΠΟΒΜΠΙΘΗΗβ ΟΟΛθρΚΘΗΗΗ ΠρΗΜβΟθίί B OCHOBHOM ΟγΠΒφΕΤΘ.Padonee αθβηθηηθ, cooTBeTCTByiomee 3T0My 4Hana30Hy TGMnepaTypu,οοοτθβληθτ Bcero jihuib 2-3 aTM. Κβκ οτ nepBOň οτθληη Bhimena- wHBaHHH οτφοι»τροΒΗΒ3Κ)τ η προΜΗΒ3κ>τ BOfloli, a coflepxamyiocH BΗΘΜ paCTBOpHMyiO flOJIIQ AlgO^ ΠΟΗΤΗ ΠΟΛΗΟΟΤΒΜ ΠθρβΒΟΛΗΤ B paCT-BOp OOopOTHUM paCTBOpOM, COflep«afllHM 10 - 15% CBOdOflHOtt CapHOttKMCJiOTbi» npw TGMnepaType 100 - 140 °C η προλοοητθπβηοοτηBbímejia^HBaHMH 15 - 60 mhh· Bo bt opotí οτηληη Bumojia^HBaHHH mokhopaÓOTaTB npn HOpM3JIBHOM SaBJIQHHH, ΠρΗΠβΜ Cylll6CTB6HHU6 Η3ΜΘΗβΗΗΗΗ3ΒΛΘΗΘΗΗΗ AlgO^ H COCiaBa paCTBOpa ΗΘ HaÓJIlOflaXyrCH. Ηηκθ πρπΒθΑθΗΜ padoqHa ycjiOBHH h pesyxBTaTH nepBOíí m bt opotícTasHtt BhimejiawHBaHHH: npOflOJIHHTejIBHOCTB ΒΗ12{ΘΗ8ΗΗΒ3ΗΗΗ
TeMnepaiypa b nepBOíí CTasHHTeMnepaiypa bo Βτοροϋ οτθληηKOHIíeHTpailHH H2SO4
B nepBOíí CTaflHHBO BTOpOÍÍ CTaflHH 15 - XI5 -100 -
60 MHH B KaXAOttn CTaflHH
125 °C140 °C 5-7%10 - 15% Η3ΒΛβ^βΗΗβ AlgO^ (β nepBOtt h Βταροκ CTaaHflx βμθοτθ) λο 90 % οτ coflepxaHHa αι2ο, β ηοχοληομMaTepaajie. 3τη paóoqiie ycjiOBHH oóeax CTaauft BHJnejiaHMBaHiiH πο3βοληιοτπροοτοβ annapaTypHoe οφορΜπβΗΗβ npoueoca. lípu nocjieayionieíí cTaflo rHApojuraa ηθοΟχοαημο H3<5esaTi> coocaw-hhh aejie3a β BHje Ρβ^+. JUh βτογο nepea ropojiH30M προβο^ητ-Cfl ΒΟΟΟΤβΗΟΒΛΘΗΗΘ Ρβ3+ Β Ρθ2+ ΠρΗ ΠΟΜΟ1ΜΪ ΒΟΟΟΤ3ΗΟΒΗΤΘ7ΙΗ,npeHMymecTBeHHO S02 , ββολημογο npa TeMnepaType ~ 20 -6u °C b pacTBop, nocTynaioinHJt Ha γηλροηιϊ3· Β προτηβηομ cjiynaeTpexBaneHTHoe χβπββο b ycjiOBHHx ropojiH3a noa ^3βηθηη6μ ocax-SaeTCH Β ΒΗΛΘ ΟΟΗΟΒΗΟΓΟ CyjIB^aTa aHaJIOrHHHO ηλιομηηηιο· ΦΟΒτρβτ nepBOft οτθληη BumejiaHHBaHHH, nocTynawiíl fia γηλρολμ3,cojiepxHT 50 - Π0 r/n Al2o3 H rHflponH3HpyeTCH npn Teunepa-Type ^24u °C npw HCKJi»qeHHH KHCJiopofla bo H3ÓexaHHe oópaTHoro0KMCJI6HMH flByxBaneHTHoro xejie3a. HeoóxoauMafl λβη npoijecca riwpo-jM3a TeMnepaTypa βηθηητθλβηο onpesejifleTCH MaiepnajioM πρημθηηθ-Moft annapaiypH, a Taoe θηοηομμηθοκημη pe3yjn>TaTaMM. H3 9τογοmojkho 3aKJiioHHTB, hto sHana30H padoweM TeMnepaTypu οοοτβΒΒΗβτnpeHMymecTB0HHO 220 - 280 °C.
Hase πρΗΒθΛθΗϋ οοηοβημθ ycaoBHH h pesyjiBTaTH rsmpojiH3a noa3aBJI6HH6U:
npOSOJiailTeJIBHOCTB rHflpOJIHSa 30 MHH ΒβΟΟΒΟβ 0TH0H16HH6 SO^ í 2,0 - 2,86
TeMnepaTypa 220 - 280 ° BHxofl npw raapojinae 50 - 7u %
CociaB ocHOBHoro cyjii>$aTa: 38,5 38,7 Jí A12O, 39,5 - 40,0 % S03 0,01 - 0,03 % Feg0} 0,01 - 0,02%T102 0,01 - 0,015 % K20 0,01 - 0,02 % Na20 ο,οι sio2 < 0,01 % MsO 0,1 - 0,2 % 0*0 4 215 886
Pemaiomea SHa^eHHe b ΜβτοΑβ cornacHO η30(5ρθτθηηιο ΗΜββτ χοτφθκτ, ητο BHCOKoa Η3βαθ*ιθηηθ AigO^ npn γηαροαηβθ b yica-33ΗΗΗΧ yCJIOBHHX AOCTMrHyTO 0Θ3 flOÓaBKH 3ΚΤΗΒΗ0Γ0 ΓΑΗΗ03ΘΜ3HJIH flpyrnx XHMHK3T0Bf KOTOpafl ΠΟ W3B6CTHHM ρθΗθβ ΠρβΑΑΟΧΘΗ-HiiM ueToaau cnMTajiacB óaaycjioBHO ηθο6χοαημοΚ.
HaflAQHO, ητο mohu μθγηηη ao KOHneHTpauHft 30 - 90 r/x Mgso^npHBOAHT κ CHJIBHOMy ΠΟΒΗΒΙΘΗΗΙΟ BHXOA3 ΠρΗ ΓΗΑΡ0ΑΗ3Θ, Ηθ 3a-ΓΡΗ3ΗΗΗ ΠρΗ 3Τ0Μ TBepAUft OCHOBHhlft CyjIB$aT δΡΙΙΟΜΗΗΗΗ, 0<5pa3yiO-mnilcfl b npoijecce rHflpojiMea, κβκ αοκθ3ηβ36τ πρηβθα6ηην$ βηιπθcociaB οοηοβηογο cyjn>$ao?a θημμηηηη. HoaTOMy cornaCHO H30(Spe-ΤΘΗΗΙ0 MOSHO OTKa3aTBCfl OT ΠρΜΜβΗΘΗΗΗ AOÓaBOK, ΠΟΒΗΙΠΘΙΟΙΙΙΗΧochobhoctb rHApojiH3Hpy6Moro pacTBopa· Ha npaKTHKe 9το 03Ha-naeT 3HannTeiiBHoe ynpoujeHHe npouecca, t.k. OTnaaaeT Harpy3-xa MaTepHaxBHoro oóopoTa B03BpaiH6HneM 9κτηβηογο rnHH03eMaHJIH ΟΟΗΟΒΗΟΓΟ CyjIB$aTa aJHOMHHHH Η ΤΘΜ CaMUM 3HanHT6JIBH0 CHH-xaioTCH 3aTpaTH Ha annapaTypy h sHepmio· B ΠρΟΤΗΒΟΠΟΑΟΚΗΟΟΤΒ UiejIOnHHM ΚΟΜΠΟΗΘΗΤΟΜ ΗΟΧΟΑΗΟΓΟ Μ3ΤθρΗ3Α8>BHBOAHHIHMCH C ΚΘΚΟΜ B ΒΗΑθ TpyAHOpaCTBOpHMHX ΟΟΘΑΗΗΘΗΗΜ, Μ3ΓΗΗβ,coAepaamHacH b chpbo, b npeotfjiaAaiomeM κοληηθοτβθ ocTaeTcn bpacTBopa. IIoaTOMy πρκ nepepaÓOTKe MarHHttcoAepaamero cupBH ηθTpeóyetrcH AOÓaBKH οοθαηηθηηΜ μθγηηη, qToóu AOCTMrHyTB βηοοκογοBHXOAa ΠρΗ ΓΗΑΡ0ΑΗ3Θ.
ΠρΗ nepepaóoTKe μθτθρηθαοβ, ηθ coAepaamHx μθγηηη, AOCTaTonHapa3OBan noAana μθγηηη aah ycTaHOBjíeHHH οπτημθλβηογο coAepaaHHH
Mg . ΠΟΒΒΠΠΘΗΗΘ ypOBHfl Μ3ΓΗΗΗ, ΒΟ3ΗΗΚ3Ι01ΙΙΘΘ B p63yjIBTaTé Πθρβ-paÓOTKH MarHHÍÍCOflepHamerO CtipBH, ΜΟΚΘΤ ÓLITB ΟΤΚΟρρθΚΤΗρΟΒΘΗΟbuboaom He3HanHT6JiBHHx κοπηίθοτβ pacTBopa c nocjieAyiomea ot-AQJiBHoft ero nepepačOTKOft.
HařtaeHO, ητο b ηθ0α8γοπρηητηηχ ycjiOBHHx oxjiaatfleHHH ao 25% ocaa-ΑΘΗΗΟΓΟ ΟΟΗΟΒΗΟΓΟ CyJIB$aTa aJUOMHHHH OÓpaTHO paCTBOpfleTCfl BΓΗΑροχΗ3Ηθϋ nyjiBne. B peeyjiBTaTe θτογο βηχοα πρΗ γκαροημ3Θ 3Ha-οτθχβηο CHHsaeTCH, coAepaaHHe AlgOj b oóopothom pacTBopenoBbímaeTCH, a BunycK AlgO-j Ha θαμηκι^γ oóBeMa annapaTypu yMQHB—niaeTCH. Μοοιιθαοβθηηη ποκθβθιιη, ψγο πρΗ οχλθμαθηηη ηθοΟχοαημοοηθηβ όιιοτρο npoxoAHTB AHana30H TeMnepaTypu 140 - 80 °C cΤΘΜ, TíTOObl θφφβΚΤ OdpaTHOrO paCTBOp0HHH OUJI Β03Μ0»Η0 HH3KHM.3φφθκτ OÓpaTHOrO paCTBOpeHHfl ΟΟΟϊΘΒΑΗΘΤ AAH npOAOJiaHTeJIBHOCTMoxjiaaASHHH -> 90 mmh > 18 %, a aah προαολχμτθλβηοοτμ oxjiaaAe- 5 21S 886 ΗΒΗ < 10 mhh < 4 % no OTHomeHino r KojímeCTBy oOpa30-BaBmerocH οοηοβηογο cyjiB$aTa 8λκ>μηηηη· Μθτολ corjiacHO M3o0pe~T6HHD n03B0JIH6T Λ7ΙΗ CTaflHH rHSpOJIM3a ΠΟΛ #8Β3Ι6ΗΗ6Μ flOCTHHBΒΘ0ΒΜ3 HH3KHX npOflOJIJKHTeJIBHOCTett OXJiaRSeHHfl, npeMMyiHeCTBeHHO10 MHH. ΟτφΜΤΙΒΤρΟΒΘΗΗΗίΙ ΠΟΟΗΘ ΓΜβρθΗΗ38 IlOfl Η3ΒΗ6ΗΗΘΜ OCHOBHMft CyJIB-$ai aJiBMHHHfl no^Bepraeicfl CTasHftHOMy pa3Jio»eHHD, a 3aieiiKajiBííHHaiíHH <ιβρβ3 y*- ai2o3 b oC - ai2o^ npa TeiinepaType1100 - 1300 °C. fljifl pereHepannH khcjioth ot βηπιθλθηιιβθηηη οτχοηηι^ηθ ra3H,coaep»aw cm6cb sOg/so^ h oópasyiomHecH b nponecce τθρμη-qecKoro Ρ33Η0κθηηη οοηοβηογο cyjiB$aTa θηιομηηηη b γηηηο3Θμ,noflBepraioT npeBpameHMio c μ3τοίηνμ pacTBopoM rnspojiH3a, co^ep-samMM mohu sene3a b Ka^iecTBe KaTaHH3aT0pa, npn TeiinepaType60 - 80, npaHMymecTBaHHO 70 °C, πρΜ ηητθηοηβηομ πθρθμθιιιηβθημμH noaa<í0 BO3flyxa. 9τμ ΗΙί3Κ0Κ0ΗηθΗΤρΗρ0Β3ΗΗΗΘ KHCJIOTH, nOJiyqeH-Htie T3KHM βηγοληημ b annapaTypHOM η τθχηολογηηθοκομ οτηοιπθημηχnyTOM, npMrOflHH Λ JIH BhimejiaUHBaHHH CHpBH B ΟΠΗΟΘΗΗΗΧ yCJIOBHHX* nonyqaeMHií nocjie BTopoft cia^HM Bumejia*niBaHJiH κρβΜΗΗοτΗίί κθκnocjia HaflJieaameK odpaóOTKH μοκηο πρημθηητβ, HanpuMep, b npoMbiin-JI6HH0CTH CT6KJIHHHOÍ4 TapH B ΚΟ^ΙΘΟΤΒΘ ΟΤΘΚΛβ-ΟΗρίξβ, B OTpOHTeJIB-ΗΟίί npOMHIilJieHHOCTH flJIH Πρ0Η3Β030ΤΒ3 ΟΤρΟΗΤΘΤΙΒΗΗΧ Μ3ΤβρΜ3Λ0Β, BΒΗΤβίίΗΟΜ ΠΡ0Η3Β0Λ0ΤΒΘ B ΚΘ^ΙΘΟΤΒΘ ΟΤβίίΗΟΓΟ ΚρβΠΗΤΘΗΗ, a Τ3Κ3ΚΘΚ3Κ HanOJIHHTGJIB flJIH np0H3B0flCTBa pa3JIMHHNX ΗΘΟρΓΘΗΗ’ΊΘΟΚΗΧ ΗopraHHHecKHx MaTepnanoB h h ji η apymx nejieíí.
MeToa dojiee no^poÚHO ποηοηηθτοη «a npuMepe n οχθμθ. ϊκ333ηηηθxapaKTapHCTHKH βθπιθοτβ othochtch k paBHOBacHOMy coctohhhk), npakot op ou pacTBops η κθκη, BeflymHecfl b οόοροτβ, no CBoeiiy cocTaByÓOJIBUIQ Ηθ H3M0HHJIHCB. ΠρΗΜθρ ΒΗΠΟΉΗΘΗΗΗ B KanecTBG cuptn b nepBOít CTaao BumenanHBaHHH (3) aarpyxana I τMexaHHwecKH (I) h τθρμηηθοκη (2) oópaÓOTaHHOíi iohh nraecjie- 6 215 886 flyminero cociaBa: AX2°3 362,0 κγ TiO2 20,9 κγ Pe20^ 23,0 κγ so3 1,7 κγ MgO 4,1 κγ v2°5 0,3 κγ K20 9,0 kt Si02 ta nponaa 551,1 κγ
Ua2o 0,5 ΚΓ
OaO 4,2 ΚΓ Οκοπο 80 % A120.j HaxoflHjioct b βηαθ ΜβτβκβοπΗΗβ, xopomo noaaaiomerocH βηαθηθ^ιηβθηηι)· IOHy npw πθρθμθπηβθηηη cycneHAH-pOBaJIH B ΟΜβΟΜ paCTBOpOB OT BTopotí KHCJIOft CTaflMM BHmejiaqHBaHHH(5), COCTOHIHefl M3 3,9 U? φΟΒΤρβΤΘ H 0,5 M3 npOMLIBOHHOfl ΒΟΛΗcjie^yiomero cocTaBa: ai203 233,0 ΚΓ MgO 129,8 ΚΓ SO3 1246,0 κγ Na20 0,5 ΚΓ Ρθ2Ο3 47,8 κγ κ2 1,6 ΚΓ h oópaóaTHBajiH nos ΑθΒπβΗΗβΜ πρκ TaMnapaTypa 120 °C b τθ^θηηθ0,5 — I *ι· TaKHM oópa3OM yaajiocB πθρθβθοτη b pacTBop 61,3 %coflapxamerocfl b γπμηθ pacTBopMMoro Ai2o3 · Πρκ stom co^epscamMecnB rjIHHe ΠρΗΜΘΟΗ - 3ΚΘΛΘ3Ο, KaJIHÍl Μ ΗΘΤρΗίί - ÓOJIBlUeíí ΗΘΟΤΒΙΟ CHadojiiuiHM KOjinuectbom pacTBOpaHHoro 8Jik)mmhmh nepaBOAHTCH b Hapae-;TBOpHMUa OCHOBHUa CyJIB$aTH H OTfleJIfHQTCH C HepaCTBOpHMHMH uac-TffMH SÍO2 H TiOg B ΓΠΗΗΘ IlOCJie $HJIBTpaHHM (4) B κβκβ·CocTaB κβκβ nocjie προμηβκμ I m^ boaus
AlgO^ SO3 Ρβ2©3 187,4 κγ 85,5 κτ40,1 κγ MgO Ii02 ν205 4,9 κγ 26,0 κτ 0,2 κγ. 9τοτ κβκ HanpaBJíaH βοKHCJIOTOÍÍ Β ΟάΐβΜΘ 4 Μ' BTopyn ctbaho BiimejiaiiHBaHHH (5) οόοροτΗοίί* cjieflyioinero cociaBa: Α12°3 152,1 κγ MgO 126,2 κτ SO3 Ρβ2Ο3 1330,5 κτ43,0 κτ v205 0,2 κγ Γββ aHajiorirao napBOíí οτπαηη Bumajia^HBaHHH ΠΟΑ ΑθΒΠΘΗΗΘΜ npH 7 21S 886 130 °C H3 γπμηη BbmejiaHHBaJiocB 38,7 % pacTBopHMofi qacTHa12°3. nocaa $O5Tpaijo h προμηβκη κβκβ βολοΑ b ούι,βΜβ 4 m?qacTB KOTopofl y®a HcnojiB3OBaaaci> ajih προμηβκη npoayKTa γηλρο-jiH3a, nonynaioT 4,4 m^ pacTBopa, κοτορκίί - κθκ y®e onucaHO -HanpaBJíflioT Ha nepByro ciaw βηο(6Λ3?μβ8ΗΗπ, h 854,7 κγ κρβω-HHCToro κθκ3 cjieflymero cocTaBa: A12O3 77,8 κγ MgO 1,3 κγ SO3 51,5 ΚΓ TiO2 25,7 kp
Fe2o3 23,0 κγ V2O5< 0,2 κγ KOTOptlfl ΜΟΧΘΤ ΠρΗΜΘΗΗΤΒΟΗ, ΗβΠρΗΜθρ, B CTp0HT6JIBH0fl ΠρΟΜΗΠ-ΧΘΗΗΟΟΤΗ.
OcTaBIUHflCH Ofaeií B 3,5 M^ ΠρΟΜΗΒΟΠΗΟϋ ΒΟΛΗ COCTaBa A12O3 16,2 κγ S03 50,0 κγ
MgO 2,8 ΚΓ HCn0JIB30BaJIH TtflH ΠρΟΜΕΙΒΚΜ ΚΘΚ3 H3 ΠβρΒΟΑ ΟΤΟΛΗΗ BUliieJiaOSaHHH,a Taoe Win λοποληθηηη ποτβρι. βολή, B03HHKaromHx πρκ perenepa-ΠΗΗ S03 Η3 ΟΤΧΟΛΗΙΡΧ ΓΘ30Β ρθ3Π0®βΗΗΗ ΠpOΛyKTa ΓΗΛΡΟΛΗ33 Βnpouecce MOKporo KaTaJiHea, οπηοηβ36Μομ no3®e (10). IIOCJIQ $HJIBTpaiíHH nyjIBIHÍ nepBOň ΟΤΘΛΗΗ BLIlHejiaHMBaHHH (4) Μ προ-MblBKH K6K3 nOJiy<IHJIH 4,7 M^ ΟΟΗΟΒΗΟΓΟ paCTBOpa CyjIB^aTa aJIIOMHHHHCJI6ΛyIOI^6ΓO cociaBa: αι2ο3 407,6 κγ κ2ο 0,1 κγ SO3 1154,1 κγ Na20 0,2 κγ ρθ2ο3 30,7 κγ Si02 2,ϊ κγ MgO 129,0 κγ tío2 0,1 κγ v2o5 0,4 κγ 9tot κοηθ^ηηΚ pacTBop on »e ηοχοληηΑ paciBop λπη mpojiKaa· ΗΜΘΛ Κ8ΗΘΟΤΒβΗΗΟ6 ΟΤΗΟΙΠΘΗΗΘ SOj I AlgO^ · 2,84· K nOJiy-HCHHOMy T3KHM 0Ópa30M HCXOΛHOMy paCTBOpy ΛΛΗ ΓΗΛΡ0ΛΗ33 ΠρΗTCMnepaTypa 40 °C ΛΟόβΒΟΜ so2 λο TpexKpaTHoro κοληηθοτβο,ΗΘΟ0ΧΟΛΗΜΟΓΟ ΛΗΗ ΟΤΘΧΗΟΜβΤρΜΗΘΟΚΟΓΟ ΒΟΟΟΤΘΗΟΒΛΘΗΗΗ ΤρβΧΒΘΗβΗΤ-HUX ΗΟΗΟΒ Β Λ^ΧΒ9ΠΘΗΤΗΜΘ HOHtI ΧβΛθβθ, Μ Π0ΛBθpΓaJIHΓHΛP0JIH3y ΒΠΟΛΧΟΛΑΙΙίΗΧ annapaTypHHX yCJIOBHHX, C ΠΟΛΗΗΜ ΗΟΚίΙΚΓίβΗΗθΜ ΚΗΟΛΟρΟΛβ,Β ΤΘ^ΘΗΗΘ 30 ΜΗΗ ΠρΗ T0MIiepaType 240 °C Η ΛθΒίΙΘΗΗΗ 30 aTH. 8 215 886 B pQ3yjiLTaTe βτογο nonywiH τβθρληΑ KpncTaJuiH3aT οκοοηηθβογοaayHHTa, nerico πολλθιοπιηΑοη φΗΒΒτρβίξΜΗ, κοτορκΑ nocae pe3KorooxjiawHHH c uejiBK) npeflOTBpameHHH βφφβκτβ oópaTHoro pacTBope-HHH 0ΤφθΒΤρ0Β8ΒΗ OT ΜβΤΟΧΙΗΟΓΟ paCTBOpa ΓΜβρ0ΛΗ3&· ΠΟΟΛβ ΠρΟ-mhbkh lipovýma rnapojiMsa βολοΑ οΟβθμομ b 3 m^ h oyinKH npHTeMnepaType 150 °C οτλθληλη 692,9 κγ KpncTajuiH3aTa caeayionerococTaBa:
Xl2°3 SO3 Pe2°3 MgO 268,00 κγ274,00 κγ 0,08 κγ 0,06 κγ Ti©2 CrO3 NiO CuO < < < 0,09 kt0,03 κγ0,07 κγ0,07 kt k2o 0,07 ΚΓ MnO < 0,03 ΚΓ Ka20 0,14 ΚΓ V2°5 0,17 KT Si02 0,04 ΚΓ SnOg < 0,07 ΚΓ OaO 0,80 ΚΓ, 9tot flocTaToqHO ^hctuA npOMeayTonHuA npoayKT nocae pa3aoxeHHnH KaJIBIíHHaiíHH ΠρΗ T6MIiepaType 1100 °C - 1300 °C K3K ΓΛΗΗ03βΜc bhcokhm coaepKaHHeM oó -ai2o3 μοκθτ <$htb HanpaBJíeH Henocpea-ctb6hho b 3JieKTpoji«3 pacnaaBa ajih nojiyqeHna θλιομμηηη. K oTxoaamuM ra3aM pa3Jio»eHHH, coflepaamuM ~ 3 % so2 , flOtfaBJIHJIH B03flyX B Ο0ΒΘΜΗΟΜ ΟΤΗΟΠ1ΘΗΜΗ Og t SOg S» 4· 3aT6MHactimaJiH H3 npOMHBHoA bo^oA nponeccoB Φηλβτρθηηη (6) m (8) bοοοτΒβτοτΒΗΗ c napnMaaBHUM aaBJíeHMeM βο^ηηογο napa 0,32 aTMh b noflxoflnmeA annapaType (10) npn TeMnepaType 70 - 80 °C ηητθηΗchbho nepeMemajiH c MaTowíM pacTBopoM rM£pojiH3a b οΟβθμθ4,2 m^ cjie^yiomero cocTaBa: aipo3 123,4 ΚΓ MgO 126,2 κγ SO3 848,3 ΚΓ Ti02 0,1 κγ Pe2O3 30,3 KT v205 0,2 κγ» OKHCJieHMe so2 b cepHy® KHCJiOTy npoxoaHao nowrlOO ^-hotfjiaroflapíi KaTaornnecKOMy αθΑοτβη» oOpaeOBaBinMxcH hohob τρβχ-ΒθίΙΘΗΤΗΟΓΟ ΚΘΗΘ38Β CBH3H C KHCJIOpOflOM B03flyxa. BO Η3ΰθΚΘΗΗΘflaJiBHeAiaero ποβηιιιθηηη coaepKaHHH npuMeceA, b naciHOCTH MgO ,b nojiyueHHoA οόοροτκοΑ κηολοτθ, 3,3 % MaTomioro paCTBOpa rn#po-JIH3a ΒΜΒΟΛΟΗ Η ΟΤ^ΘΛΒΗΟ OOpaOaTHBaHH, ÍTO ΠρΗΒΘΗΟ K ΟΗΗΚβΗΗΙΟ 9 213 886 oómero HSBJíetieHHfl AigO^ no aaHHOMy MeToay Bcero jihibb Ha 1%. ΠοτθρΜ cepu, B03HHKaioinne BCJieACTBue βηλθτιθηηη μθτοήιογο paci-BOpa H ΚρβΜΗΗΟΤΟΓΟ ΚΘΚ8» nOnOJIHHJIMCL· CHHraHHeM Cepu BO BpeUHpů3JioseHHH aJiyHHTa okcohhh hjih floCaBKofí cepHOít khcjiotn kOČOpOTHOfl KHCJIOTa. OOntee ηββλθ^θηηθ ai2o3 no aaHHOMy MeTOfly cocTaBJíajio 82a Buxofl npu nmpojW3e - 66 10 21S 886 $opuyxa Η3Ο(5ρθΤ6ΗΗΗ (1) MeToa nojiyqeHHH tHicioft okhch araoMHHHH cepHOKHcjiOTHHitΒΗΙΙΙβΙΙβ'ΊΗΒδΗΗβΜ MexaHHtjeCKH H/HJIH TepMHqeCKH OČpaČOTaHHHX Γ3ΙΗΗHJIH ]?JIHH03eMHCTHX MHHepaJIOB C ΠρΗΜΘΗΘΗΗβΜ flaBJíeHHH Η ΠΟΒΗΙΙΙθΗ-Hoa TeunepaTypu, οταθηθηηθμ HepacTBopHMoro κβκβ, BOccTaHOBJíe-ηηθμ xejlasa, rnflpojiH3OM pacTBopa cyjiL$aTa ajnoMHHHH b τβθρληΗOCHOBEUÍÍ CyJIB$aT aJIKJMHHHH, ΡΘ3ΛΟ3ΚΘΗΜΘΜ npOflyKTa ΙΊΪΛΡ<ΗΙΗ3Θ BOKHCB aJIIOMHHHfl, OTJIHRaiOIIIEífiCH TOM, ΨΓΟ ΜΘΧ8ΗΗ-qecKH h/hjih TepMoacKH oópatfoTaHHHlt ηοχοληηΗ MaTapHan nacTHHHOpacTBopneTCH b nepBofi CTamHH BbímeJia^HBaHHH npH TeMnepaType 115 - 125 °C B ΤΘΗΘΗΗβ 15 - 60 MHH C $HJIBTpaTOM H3 BTOpOÍi CT3—SHH BtimejiaHHBaHHfl, cosepaaiUHM 5 - 7 % cboóo^hoíí cepHOíi khcjioth,κθκ nepBOit cTamHH BumejianHBaHHfl nomaioT bo BTopyw οτθληιο Bume-Jia^HBaHMH H T3M ΠΟΨΕΗ nOJIHOCTBIO BHmeJianHBaMT paCTBOpHMyK) HaCTBnpn TeianapaTypa 100 - 140 °C b τβηβΗΗθ 15 - 60 mhh πρκ maBjíeHHH1-3 8TM OÓOpOTHHM paCTBOpOM, COflepJKamHM 10 - 15 % CBOÓOflHOftcepnott khcjioth, κ $HjiBTpaTy nepBOfó cTamHH BumejianHBaHHfl moáaB-jihiot S02 npeHMymecTBeHHO πρκ TeunepaType 20 - 60 °C b repMe-τκηβσκοΜ noMemeHHH h HarpeBaioT npeHMymecTBeHHO mo TeMnepaTypurHflpojiH3a 240 °C, nojiytieHHHíi ochobhhH cyjiB$aT ajnoMHHHH πρκ τθμ-nepaType 1100 - 1300 °C KajiBUHHHpyioT b γλμηο3Θμ, oópa3yiomyiocflnpH 3tom CM6CB sOg/so^ b Mecie c B03ayx0M npeBpamaioT npnTeMnepaType οκολο 60 - 80 °C, npeHMymecTBeHHO πρκ 70 °C, c$HjiLTpaTOM rMflpojiH3a, a nojiynaeMyio cepHyio KHCJioiy c bo3mojkhoHfloóaBKOft cBeaeít cepHOM khcjioth HcnojiB3yioT flJifl nonojiHeHHa ποτβρΒ ísOg/so^ b κθηθοτβθ oóopoTHoro pacTBopa mjifl ΒτοροΗ cTamHHBHmejiawHBaHHH. (2) Μθτοα nojiyueHHH <ihctoíí okhch 8jiiomhhhh corjiacHO nyHKTy I, OTjiHqaroniHíicfl τ e μ, ητο b nepBoň ciaflHH Bumejia^H-BaHHfl C HCXOflHHM Μ3ΤθρΗ37ΙΟΜ 3arpysaeTCH H30HTOK , COCTaB- jiHiomHtt 60 - 120 %, npeHMymecTBeHHO 80 %, b pacneie Ha Bumejia-nHBaeMyio mojno AlgO^. Číma othochtch I qepTex.
II 215 888
(3) MeTOfl nojiynaHHH tmciotl okhch qjixímhhhh corjiacHO nyHKTaM I 0 2, OTJIHHaDUHfiCfl Τ θ Μ , ΨΓΟ OÓOpOTHHft paCTTBOpcoXepxHT 30 - 90 r/jiMgSO. »5-50 τ/u ai2O3 5 0,01 - 0,1 r/x V2O5 ; 2 - 12 γ/ji Ρβ2ο3 ; ο,ΐ - 0»3 γ/ji ito H 0,01 - 0,1 r/jiTi02. (4) Μθτοα nojiyuQHHH ίηοτοΗ okhch ajnoMHHHH corjiacHO nyHKTaMI - 3, O T JI Η H a E m H ň C fl T a M , %CO BO BTOpOft CTaSHHBumeiiawaHHfl moxho paóoiaTB npn HopuaJiBHOu jiaBJíoHHH. (5) Μθτολ nojiyqeHMH ηΗοτοίΙ okhch θλιομηηηη corjiacHO nyHKTaM1-4, OTJiHqaKinHftcfl τ a μ , ητο nojiynaeMníí nocjiaBHinajiaOTaHHs κρβΜΗΗοτυϋ κθκ cooTBeTCTByioniHM oópa3ou napapaóa-ΤΗΒΒΘΤΟΗ C H6JIBK) ΘΓΟ HCn0JIB30BaHHH B CT6KOJIBHOM H CTpOHTejIBHOftΠρΟΜΗΠυίβΗΗΟΟΤΗ, ΠρΗ Πρ0Η3Β0β0ΤΒβ ΗΒΠΟΒΗΗΤβJiatl ΗΒΗ JIJIHSPyrHX ΙξβΒββ. (6) Μβτο# nojiyweHHH nucTOtt okhch ajnoMHHHH corjiacHO nyHKTaM ! 1-5, O T JI K ti a D m H ft C Η Τ β Μ, HTO rHflpOJIH3 ΠρΟΒΟ^ΗΤΟΗ !npn HCKJIK)ti6HHH KMCJIOpOfla ΠρΗ BOCOBOM ΟΤΗΟΠΙβΗΗΗ SO^ » AlgO^ “2,0 2,86, npaHMymacTBaHHO 2,65, h coflepstaHHH ai2<>3 = 50 - Π0 Γ/λ 0Θ3 ΒΒβΛθΗΗΗ ΘΚΤΗΒΗΟΓΟ rJIHHO3eMa ΟΟΗΟΒΗΟΓΟ CyJIB-$aTa aJIDMHHHH hjih apyrnx χημηκθτοβ· (7) Μθτολ nojiytiaHHfl ηΜοτοίί okhch θιιβμηηηη corjiacHO nyHKTaM1-6, o τ ji η n a » n h ti c η τ a u , ητο rnflpojiH3 npOBosHTCHB npHCyTCTBHH MgSO^ B KOJlHMaCTBO 30 - 90 r/jl. (8) Motoa nojiynaHHfl nncTOti okhch ajnoMHHHH corjiacHO nyHKTaM1-7, OTJiHnanniHftcft τ a m , wo hs ούοροτβ OTónpaiOToko ji o 2-5 ofoaMHHx % η napapaÓaTHBa»T, HanpHMep, b KauecTBa$jiOKyjiHHTa win BO^oxosnticTBa hjih ^jih flpyrnx nejietí. (9) Ubtoa nojiytiaHHH tmcTOti okhch ajnoMHHHH corjiacHO nyHKTaM1-8, OTJIHtiaiOmHtiCH ΤΘΜ, tjTO OXJiaWHHa rHflpOJIH3-hoíí nyjiBím npoBOjtHTcn npH MaKCHMajiBHOň peraHapanHM ea θητθιιβ—πηη b npaaajie TaMnapaiyp 140 - 80 °C b τθηθηηθ μθηθθ 10 MHHyT. 12 21S 886
AHHOTaiíHH
MeTOfl nOJiyqeHHH qUCTOK OKHCH aJIBMHHHH H3 Γ3ΙΗΗ H ΓΗΗΗ03ΘΜΗ0ΤΗΧMHHepaJIOB. Ιΐ3Ο(5ρθΤΘΗΜΘ OTHOCMTCfl K MeTOfly CapHOKHCJIOTHOrO BHHiana^HBaHHflΓ3ΙΗΗ H rjIMH036MMTCUX MHHepaJIOB flJIH ΠΟΗγΗΘΗΗΗ ^HCTOfi OKHCM aJIíO—MHHMH Ηβρθ3 OCHOBHbltt ΠρΟΜθΚγΤΟ^ΗΗίί IipOflyKT.
UeJIB Η300ρβΤβΗΗΗ 3aKJIK)HaeTCH B ΟΗΗΧβΗΗΜ BHCOKHX ΤβΧΗΗΗβΟΚΗΧ H3ΗθρΓ6ΤΟ60ΚΗΧ 38TpaT Η3ΒΘ0ΤΗΗΧ ΜβΤΟ^ΟΒ H C03flaHMH ΤΘΧΗΟΛΟΓΗ-H6CKH ΠρΟΟΤΟΓΟ Μ θΚΟΗΟΜΗΗΘΟΚΜ 3φφβΚΤΗΒΗ0Γ0 npouecca.
MexaHMqecKH h/hjih τβρΜΜΗβοκκ oópaáOTaHHoe čapte nojBepraeTCHflByxcTaaHiiHOMy BumejiawBaHMio οθρηοκηοηοτηημη pacTBopaMH no# saBηθηηθμ. K pacTBopy cyjii^aTa θιιιομηηηη aoáaBJíHioT so2 c uejiBioBOccTaHOBJíeHHH acejie3a, nocjie βτογο προβολμτοη rH^pojiHTMqecKoeocawHHe ocHOBHoro cyjiL$aTa aJiioMMHHH. Ilocjie BHsejieHHfi cojih KeuaToqnoro pacTBopa, BO3BpamaeMoro b npouecc, cyjii^aT ajiiOMMHHHTepMMuecKH pa3JiaraeTCH. 0<5pa3y »mHe ch npM stou ra3H pa3JioaceHHfl,coflepsamna so2/so3 cjiyxaT ajih nojiy^eHHH khcjioth ajihBamejiaoBaHHH· Η3θ6ρβΤβΗΜΘ ΠρΗΜΘΗΗβΤΟΗ flJIH IIOJiytieHHH HMCTOÍl OKHCM aJIIOMMHHHjuih nojiyweHHH amoMHHHH nyieM 3JieKTpojiH3a pacnjiaBa, a TaKace sjihnp0M3B0flCTBa CneiJHaJIBHHX MapOK rjIHH03eMa. 13
Claims (9)
1. Způsob získávání čistého kysličníku hlinitého louženímkyselinou sírovou mechanicky a/nebo tepelně zpracováva-ných jílů nebo minerálů obsahujících kysličník hlinitýs použitím tlaku .a zvýšené teploty, oddělením rozpust-ného loužence, redukcí železa, hydrolýzou roztoku síra-nu hlinitého na tuhý základní síran hlinitý a rozklademproduktu hydrolýzy na kysličník hlinitý, vyznačující setím, že mechanicky a/nebo tepelně zpracovaný výchozímateriál se částečně rozpouští v prvním stádiu vyluho-vání při teplotě 115 až 125 °C po dobu 15 až 60 minut sfiltrátem z druhého stádia vyluhováni, obsahujícího 5až 7 % volné kyseliny sírové, louženec prvního stádiavyluhování se podává do druhého stádia vyluhování a tamse téměř úplně vylouží rozpustitelná Část při teplotě100 až 140 °C po dobu 15 až 60 minut a při tlaku 0,1až 0,3 MPa vratným roztokem, obsahujícím 10 až 15 %volné kyseliny sírové, k filtrátu prvního stádia vylu-hování se přidá SOg převážně při teplotě 20 až 60 °C vhermeticky uzavřeném prostoru a ohřeje se převážně aždo teploty hydrolýzy 240 °C, získaný volný síran hlini-tý se při teplotě 1100 až 1300 °C kalcinuje s kysliční-kem hlinitým, a při tom vzniká-směs SO2/SO spolu sevzduchem uvádí do styku při teplotě přibližně 60 až80 °C, s výhodou při 70 °C, 3 filtrátem hydrolýzy a zí-skaná kyselina sírová s případnou přísadou čerstvé ky-seliny sírové se používá pro doplnění ztrát SOg/SQ^ jakovratného roztoku pro druhé stádium vyluhování. Předmět vynálezu č 15- 215 886
2. Způsob podle bodu 1, vyznačující se tím, že v prvnímstádia vyluhování se s výchozím materiálem vsází pře-bytek A12O3, představující 60 až 120 %, s výhodou 80 %,v přepočtu na vyloužený podíl AljOj.
3. Způsob podle bodů 1 a 2, vyznačující se tím, že vratnýroztok obsahuje 30 až 90 g/1 MgSO^, až 50 g/1 A12O3,0,01 až 0,1 g/1 V205, 2 až 12 g/1 Fe203, 0,1 až 0,3g/1 Mn a 0,01 až 0,1 g/1 TiO2.
4. Způsob podle bodů 1 až 3, vyznačující se tím, že vdruhém stádiu vyluhování je možno pracovati při normál-ním tlaku
5. Způsob podle bodů 1 až 4, vyznačující se tím, že po vy-loučení získaný křemíkový louženec se příslušným způso-bem nově zpracuje za účelem jeho využití ve sklářském a stavebním průmyslu a při výrobě plnidel.
6. Způsob podle bodů 1 až 5 vyznačující se tím, že hydro- lýza se provádí v nepřítomnosti kyslíku při hmotnostnímpoměru SO3:A12C>3 2 až 2,86, s výhodou 2,65, a obsahu A12C>3 50 až 110 g/1 bez zavedení aktivního kysličníkuhlinitého, základního síranu hlinitého anebo jinýchchemikálií.
7. Způsob podle bodů 1 až 6, vyznačující setím, že hydro-lýza se provádí za přítomnosti MgSO^ v množství 30 až90 g/1.
8. Způsob podle bodů 1 až 7, vyznačující se tím, že zvratného podílu se odebírá přibližně 2 až 5 % objemu,které se nově zpracovávají, například jako flokulační činidlo pro vodní hospodářství. *
9. Způsob podle bodů 1 až 8, vyznačující se tím,Že chlaze-ní hydrolýzové rozplavené zeminy se provádí při maxi-mální regeneraci její entalpie v mezích teplot 140 až80 °C po dobu méně než 10 minut. Uznáno vynálezem na základě výsledků expertizy,provedenétfřadem pro vynálezectví a patentnictví, Berlín, DD. Vytiskly Moravské tiskařské závody, Cena: 2,40 Kčs provoz 12, Leninova 21, Olomouc