CN85104029A - 一防水、抗风雨和基本上无弹性的纺织品,生产它的方法,以及由它制造的组件 - Google Patents
一防水、抗风雨和基本上无弹性的纺织品,生产它的方法,以及由它制造的组件 Download PDFInfo
- Publication number
- CN85104029A CN85104029A CN198585104029A CN85104029A CN85104029A CN 85104029 A CN85104029 A CN 85104029A CN 198585104029 A CN198585104029 A CN 198585104029A CN 85104029 A CN85104029 A CN 85104029A CN 85104029 A CN85104029 A CN 85104029A
- Authority
- CN
- China
- Prior art keywords
- polyurethane
- textiles
- wind resistance
- coated
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一防水,抗风雨和基本无弹性的纺织品,它是用抗风雨合成物质涂渍的基本无弹性,抗拉力的织物。
依照本发明,一玻璃纤维织物首先用聚亚胺酯或聚丙烯酸酯浸渍以便形成一连续的作为抗风雨合成物质聚酰亚胺或氟化聚亚胺酯的涂层基底。
Description
本发明涉及一防水,抗风雨和基本上无弹性的纺织品,而且特别涉及涂渍以抗风雨合成物质的基本上无弹性,抗张的织物。
早先已知用某些适合此目的的合成物涂渍纺织品。在众多聚合物中,下列聚合物已用作纺织品的涂层物质:聚亚胺酯,聚氯乙烯及其共聚物,聚乙烯,乙烯和乙酸乙烯的共聚物,聚丙烯酸的酯类及共聚物,聚酰胺类,合成橡胶及其共聚物,以及硅橡胶。当溶液从系统中蒸发时,从溶解或分散在有机溶剂中的聚合物可生成一连续的聚合物薄膜,或者可以水分散体的形式将聚合物施用于纺织品,当水从分散体蒸发时在纺织品上生成一连续的聚合物薄膜。热塑聚合物亦可以熔融状态加上。
藉在纺织品上形成一连续的聚合物薄膜可使纺织品防水。涂渍纺织品的强度性质主要决定于选用作基底织物的质料,纱线的粗细,经纱和纬纱的纱线密度以及编织法。适当地选择这些,得到的纺织品具有所希望的强度值和使用时不会在载荷下有大的延伸。然而这类织物本身并不防水和抗风雨。防水性是由涂渍某些适宜的合成物质而获得以及,如果产品需要弹性,例如可轧制的性能,则用以涂渍的聚合物必须是挠性的,亦即可拉伸的。此种性质甚至可由一种单体类型生成的聚合物得到,但通常是用由不同样单体形成的共聚物达到所希望的性质。采用所谓的外部柔软剂可给予聚合物额外的柔软性和挠性。
从纺织品整理一书,国营书藉出版社,來比锡,1981,第一版(Textilveredlung,VEB Fachbuchverlag,Leipzig,1981.I·Auflage)已知为纺织品生成许多种涂层的方法,并且说明由聚亚胺酯的水分散体制备的涂层其性质不如用溶剂为基底的涂层为佳,但由于排除了溶剂所引起的不利因素它的重要性增加了。此外书中说明作为纺织品的涂层物质只有少数聚丙烯酯类具重要性。
先前亦已知道用聚亚胺酯的水分散体涂渍玻璃纤维织物,凭此获得高强度和防水的纺织品。对这类产物的抗风雨性能要求愈高则需用的聚亚胺酯分散体耗费愈大。那末产品的总价值将升得很高,因为需要相当大量的聚亚胺酯分散体來填补纺织品的微孔以便获得完全防水的产品。
亦已知用其他的合成物质产生特别良好的抗风两性。这类物质为芳族聚酰亚胺类,其制造,性质和应用已有叙述,例如在Kemian teollisuus(化学工业)刊物28(1971)2/97-101。
聚合物料的现代应用常常需要范围十分广阔的抗热和热稳定性,和特别长期而且在困难和极端条件下以及迅速变化的极端条件下的抗风雨性能。这对于专门的纺织品和由它们制造的产品,例如房屋和结构物,而特别是当它们用在极圈地带或热带的条件下时尤其是这样。
已知聚酰亚胺的机械性质在外部温度变化达600-700℃时通常仍保持不变。例如在500℃的温度下聚酰亚胺薄膜强度为室温下聚乙烯薄膜的二倍。它于室温下的强度和聚对苯二甲酸乙酯大约相同,但在0℃以下就大得多。聚酰亚胺薄膜不会软化或熔融,其弹性在-200℃和+400℃的温度间保持不变。
基于上述显然芳族聚酰亚胺特别适合于涂渍在十分困难和极端的条件下必须抗风雨的纺织品。然而,芳族聚酰亚胺十分昂贵,如要用以涂渍亦需防水的纺织品,就必须十分大量地使用,由此使产品的价格上升过高。
因而本发明的目的是提供一较廉价的防水又同时抗风雨的和基本无弹性的纺织品。此纺织品为一用比以前较少量的抗风雨合成物质涂渍的基本无弹性的,抗拉力的织物,以及用以生产此类纺织品的方法。
此外本发明的目的为提供一防水又同时抗风雨和基本无弹性的,可轧制的纺织品构件,打算用作房屋或结构物承受荷载的部分,此构件为一用比以前较少量的抗风雨合成物涂渍的基本无弹性的,抗拉力的织物。
于所附的权利要求中给出了本发明的主要特征。
依照本发明一防水,抗风雨和基本无弹性的纺织品是由玻璃纤维织物组成,它已用廉价的聚亚胺酯或聚丙烯酸酯浸渍过,形成了连续的,作为实际经得起极端条件的抗风雨合成物质的涂层基底,这些合成物质为一聚酰亚胺或卤化聚亚胺酯,最好是浸渍剂的卤化表层。
所采用的基本无弹性,抗拉力织物为具有抗张强度约300KP/5Cm和极低的延伸率,少于5%的玻璃纤维织物。除了它的高强度,这样的玻璃纤维是非常轻的,它的重量为400g/m2左右。某些粘合改善剂例如有机硅烷,最好缩水甘油丙氧基三甲氧基硅烷(glyc-idoxypropyltrimethoxy silane),可加至聚合物的混合物以使聚合物良好的粘附在玻璃纤维织物上。
齐本发明的一个推荐的实例中,一以聚亚胺酯水分散体浸渍过的玻璃纤维织物在其表面仍然潮湿时使之与氟气接触,于是聚亚胺酯的表面层卤化从而生成一极薄的抗风雨和耐化学的表面层,其厚度范围为一个氟化聚亚胺酯分子,另外此层对溶剂和气体是一有效的屏障。
此外,因为用以浸渍和涂布织物的聚合物形成弹性薄膜,其拉伸性在100-300%左右,例如200%,故获得的纺织品可以轧制。
织物最好用一混合物浸渍,其中基本的聚合物为脂族聚亚胺酯的分散体,它已用一阴离子脂族聚亚胺酯乳化液改良过以软化基本聚合物,因此能同时调节产品的弹性,可且可进一步改良此聚合物使其与一脂族聚亚胺酯乳化液交联以调节其强度和坚韧性。在此混合物中阴离子脂族聚亚胺酯乳化液和脂族聚亚胺酯乳化液的合量以重量计可高至50%,如果这样则后一组分的量以重量计最多约为20%。
依照本发明,将用一廉价的聚合物浸渍过的基本无弹性,抗拉力的玻璃纤维织物涂渍以能经受极严唆条件的卤化聚亚胺酯或芳族聚酰亚胺。依照本发明用以涂渍纺织品的芳族聚酰亚胺可以藉,例如,一芳族二胺与一芳族多元酸,它的酰基卤或酸酐反应制取。例如苯甲酸-4.3′-二氨基苯及1,2,4,5-苯回酸酐用作此聚酰亚胺的起始物质是有利的,所获得的芳族聚酰亚胺在约450℃以下不会开始热分解。
依照本发明,这样的聚酰亚胺物料能以极薄的膜分布于纺织品的表面,其厚度最好为约2-180μm,例如2-10mμ。虽然抗风雨的涂层较贵,但在此实例总的价格不会上升至过高的水平。
依照本发明将聚亚胺酯浸渍的玻璃纤维织物在其表面干燥以前导经氟的气氛以卤化其表面层,生成作为纺织品抗风雨涂层的卤化聚亚胺酯。
依照本发明所用的玻璃纤维织物作为基本无弹性,抗拉力纺织品的织物可如任何涂渍基底一样用轧辊涂渍。于工业规模涂渍是在油漆工业通常使用的涂渍生产线进行的,例如采用砑光技术,浸渍槽技术,或幕涂机技术,或幕涂机技术。亦可用塑料工业所熟知的纸张涂渍技术,或热熔技术。或者也可采用纺织品涂渍技术已熟知的直接或间接涂渍法,等等。适当尺寸的纺织品构件,最好具有长度约25m和宽度1.2m可由防水,抗风雨和基本无弹性的纺织品依照本发明制造。这些构件可用例如缝纫,胶合,或拉链连接在一起形成较大的实体,其中例如具有聚乙酸酯齿的拉链是用双针机将其带固定于织物上;带可以是聚酯的。此外,拉链连接可有利地以胶布或自粘带覆盖,因此拉链接口留在下面的纺织品构件的边缘。如是这样连接可在现场进行以形成使用所需的实体,以及当需要更改或结束时,纺织品房屋可以拆卸成它的构件。
依照本发明纺织品构件可用于制造纺织品房屋或结构物,比之以前其中构架上较大部分的荷载可转移至纺织品构件上,这样构架可以做得较轻,因而同时花费较少。
用途包括专门的纺织品,例如水力或地面结构、临时房屋、棚、存储场所和遮篷以及各种轻工兵装备例如桥梁、无滑道雪橇、小艇、帐篷、伪装、障碍物和围栏。依照本发明的纺织品亦可用在农业中以建造畜舍、牛棚、生产屋宇、仓库和筒仓。依照本发明的纺织品特别合用于极圈地带和热带的建筑,以及它们甚至可用于严峻如外层空间那样的条件下。
藉助于例子十分详细地说明本发明于下。
例 1
具有抗张强度300KP/5Cm,延伸率少于5%,及重量为400g/m2的玻璃纤维织物以一用水稀释的脂族一阴离子乳化液一分散体混合物浸渍,改变混合物的组成如下面的表1所示。
表1
混合物 自由薄膜的性质
1 2 3 抗张强度N/mm2延伸%
100% - - 20
80% 15% 5% 227
60% 20% 20% 16.5 197
50% 25% 25% 16 150
50% 10% 40% 24 35
50% 40% 10% 16 295
混合物1、2和3的组成如下:
含量%
涂 料 清 漆
辅助液剂 丙二醇 20 -
水 100 -
消泡剂 消泡剂388K 2 -
分散剂 Dispex GA 10 -
“缶中毒” Proxel GLX 0.8 -
颜料 Finntitan RR 230 -
粘合剂 1 Witcobond W 234a)485 770
〃 2 〃 W 290Hb)61 100
〃 3 〃 W 240c)60 100
增稠剂 Borchigel L 75 10 10
表面活性剂 Surfynol 104 E 10 10
消泡剂 消泡剂 388K 5 5
〃 〃 5 5
a)脂族聚氨酯橡胶的胶态分散体,固体含量30%。
b)一阴离子,低粘度聚氨酯橡浆,固体含量60%。
c)自身交联的,含水的聚亚胺酯分散体,固体含量30%。
浸渍了这些混合物的玻璃纤维织物最后涂以一有机聚酰亚胺,它是由苯甲酸4,3′二氨基苯和1,2,4,5一苯回酸酐反应制取的,结果获得的纺织品在严峻和迅速变化的极端条件下是非常坚牢,防水和抗风雨的。
例 2
将例1所用的玻璃纤维织物用下列组成的丙烯酸酯清漆浸渍:
数量,%
Primal AC-388 68
水 10
丙二醇 5 辅助溶剂
Texanol 1 辅助溶剂
Nopco NXZ 0.2消泡剂
Primal ASE 60(50%) 10增稠剂
氨(25%) 0.2
水 4.1
Nopcoside N54D 1.5毒素
100
Primal AC-388是Rohm & Haas公司出售的100%丙烯酸酯乳化液,其固体含量为49.5-50.5%。测得此丙烯酸酯混合物制得的薄膜的延伸率为300%,和它的抗张强度为5N/mm2。当浸渍了此混合物的玻璃纤维织物最后依照例1涂以有机聚酰亚胺便得到一防水和基本无弹性纺织品它具有广阔范围的耐热性和热稳定性。
勘误表
Claims (9)
1、一防水,抗风雨和基本无弹性的纺织品,它是涂渍了抗风雨合成物质的基本无弹性,抗拉力织物,其特征为一玻璃纤维织物涂渍以聚丙烯酸酯或聚亚胺酯,它形成一连续的,作为抗风雨的芳族聚酰亚胺或卤化聚亚胺酯的涂层基底。
2、一依照权利要求1的纺织品,其特征为聚亚胺酯的卤化层厚度约为一个卤化聚亚胺酯分子的大小。
3、一依照权利要求1的纺织品,其特征为聚酰亚胺层若厚度约为2-180μm。
4、用抗风雨的合成物质涂渍一基本无弹性,抗拉力的织物以生产防水,抗风雨和基本无弹性纺织品的方法,其特征为一玻璃纤维织物先用聚亚胺酯或聚丙烯酸酯浸渍以便在织物上形成一连续的涂层基底,在其上涂敷抗风雨的芳族聚酰亚胺或生成一抗风雨的卤化聚亚胺酯薄层。
5、依照权利要求4的方法,其特征为玻璃纤维织物用聚亚胺酯或聚丙烯酸酯的水分散体浸渍,干燥后涂以一芳族聚酰亚胺。
6、依照权利要求4的方法,其特征为玻璃纤维织物用聚亚胺酯的水分散体浸渍并在聚亚胺酯分散体的表面干燥以前,将其暴露于氟的气氛中以便卤化此表面层。
7、一防水,抗风雨和基本无弹性的纺织品构件,预定用作房屋或结构物中承受荷载的部分,此构件为一用抗风雨的合成物质涂渍的基本无弹性,抗拉力的织物,其特征为此织物为玻璃纤维织物它已用比玻璃纤维弹性大得多的聚亚胺酯或聚丙烯酸酯浸渍,聚亚胺酯或聚丙烯酸酯形成一连续的作为抗风雨的聚酰亚胺或卤化聚亚胺酯的涂层基底。
8、依照权利要求7的纺织品构件,其特征为至少它的一面涂以氟化聚亚胺酯。
9、依照权利要求7或8的纺织品构件,其特征为预定用固定在它边上或靠近边缘的拉链使其与邻近的纺织品构件相连接。