CN85100875A - 新型阳图预涂感光平印版 - Google Patents
新型阳图预涂感光平印版 Download PDFInfo
- Publication number
- CN85100875A CN85100875A CN 85100875 CN85100875A CN85100875A CN 85100875 A CN85100875 A CN 85100875A CN 85100875 CN85100875 CN 85100875 CN 85100875 A CN85100875 A CN 85100875A CN 85100875 A CN85100875 A CN 85100875A
- Authority
- CN
- China
- Prior art keywords
- milliliters
- condensate
- ethylene glycol
- glycol monomethyl
- potassium thiocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
一种由经过表面粗化及阳极氧化处理的铝板基和涂布在其表面上的感光层组成的供平印印刷用的新型阳图预涂感光版。感光层用的感光溶液采用重氮树脂(对甲氧基二苯胺重氮盐酸盐与多聚甲醛缩合物)与硫氰酸钾缩合物、对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物、4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物、线性间甲酚醛树脂、以及溶剂、染料组成。这种版感光速度快、吸墨性能好，稳定性、抗磨损性和可保存性均优于或不次于已有的重氮萘醌型阳图预涂感光平印版，且价格低廉。适用于彩色图片或书刊的印刷，耐印力为10-20万印。
Description
预涂感光平印版材，一般用于印刷复制图案和文字。其使用的基本原理是：将接受图像的感光层涂布在感光层的支承体（铝、锌、纸基）上，然后覆上待印图案或文字的底片，经过含紫外线的光源曝光和用适当的显影液进行显影、干燥等工艺过程后，得到相应于底片图案或文字的正像或负像的印版，即可上印刷机印刷。在本发明作出之前，有关平印用的阳图预涂感光版已经发表了很多专利，但是，几乎所有的阳图预涂感光版的感光层均使用萘醌重氮磺酸酯的衍生物作为感光剂，粘合剂为碱溶性高分子化合物，如线性酚醛树脂或含丙烯酸及其酯的共聚物等。这种感光层具有本身稳定性好，感光性能好，有利于保存等优点。然而该感光剂合成步骤多，涉及的原材料多，成本较高。
美国专利4093465，曾记述了用对重氮二苯胺与多聚甲醛的缩合产物-重氮树脂同硫氰酸钾缩合，所得缩合产物作为感光剂，以环氧树脂作为粘合剂，溶于乙二醇独甲醚、二氯乙烷、甲醇和二甲基甲酰胺组成的混合溶剂中，涂布于经过电解研磨和阳极氧化处理的铝版表面上，制备成平印用预涂感光版。但是该种印版是阴图型的。即经过原稿曝光、显影处理后，所得图像与原稿图像相反。与本发明的阳图印版属截然不同的两种类型。
本发明的目的在于提供一种新型阳图预涂感光平印版。使用了与美国专利4093465中所述同一类型的感光剂，改变了作为粘合剂的高分子化合物的类型，经与适当的染料混合，溶于有机溶剂中制成感光溶液，涂布于经过表面处理的铝板基上，制备成新型阳图预涂感光平印版。该版经原稿曝光，显影处理后，所得图像与原稿图像相同。这里采用的感光剂具有合成路线短，工艺步骤少，原料易得，制造成本低的优点。而且这种阳图型预涂感光平印版的稳定性、感光性、抗磨损性、亲墨性和可保存性都优于或不次于已有的阳图型预涂感光平印版。
本发明中所述的感光层支承体是0.3毫米厚的铝板，其幅面大小可根据待印原稿或印刷机型的需要裁切制作。在一般情况下，感光层的支承体也可使用锌板。
铝板表面粗化处理可以用机械方法研磨，最好采用电化学方法研磨，制备出适于印刷用的砂目，然后在硫酸溶液中经阳极氧化处理，形成坚硬的、亲水性能好的三氧化二铝氧化层。此时，就可以在其表面上涂布感光溶液制造印版。
本发明的要点是：涂布在铝板基上的感光层用的感光溶液由重氮树脂（对甲氧基二苯胺重氮盐酸盐与多聚甲醛缩合物）与硫氰酸钾缩合物（Ⅰ）、对甲氧基二苯胺重氮盐酸盐或其衍生物与硫氰酸钾缩合物（Ⅱ）、4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物（Ⅲ）中的任何一种或相互混合构成感光剂，用线性间甲酚醛树脂作为粘合剂，乙二醇独乙醚、甲醇、二甲基甲酰胺作为溶剂，5%碱性艳兰乙二醇独乙醚溶液作为染料组成。其配方分别为：
例一
重氮树脂与硫氰酸钾缩合物 15克
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 4.5克
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 7.5克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
例二
重氮树脂与硫氰酸钾缩合物 30克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
例三
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 26.7克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
例四
重氮树脂与硫氰酸钾缩合物 15克
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 13.4克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
例五
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 13.4克
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 13.4克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
例六
重氮树脂与硫氰酸钾缩合物 15克
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 13.4克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
例七
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 26.7克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
将按上述配方配制成的感光溶液，在经过除尘处理的工作间内，用离心涂布方法、挤压涂布方法或辊涂等涂布方法涂布到经过表面粗化和阳极氧化处理的铝板表面上，涂布量在铝板干燥后为每平方米1.8-2.5克，即得到所需要的新型阳图预涂感光平印版。
按照上述方法制造的阳图预涂感光平印版，经阳图原稿在紫外光源下曝光，用硅酸钠和苯甲醇水溶液的显影处理之后，水洗，干燥，即制成适于上印刷机印刷的平印印版。
本发明的阳图预涂感光平印版，感光速度快，显影加工后的非图像空白部分无底色，不易上脏，吸墨性能好，可保存一年左右无任何变化，版面清洁，文字、线条或网点清晰，层次分明。可用于彩色图片和书刊印刷，也可用于打样。最高耐印率达二十万印以上，一般为十万-二十万印，感光溶液也可用于印刷车间作即涂版使用，最佳实施例为例一。
Claims (8)
1、一种由经过表面粗化和阳极氧化处理的铝板基以及涂布在其表面上的含有重氮树脂(对一甲氧基二苯胺重氮盐酸盐和多聚甲醛的缩合物)与硫氰酸钾的缩合产物的感光层组成的供平印印刷用的预涂感光版材，其特征在于感光层用的感光溶液的成份还包括有：对甲氧基二苯胺重氮盐酸盐与硫氰酸钾的缩合产物、4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物、线性间甲酚醛树脂、乙二醇独乙醚、甲醇、二甲基甲酰胺和染料碱性艳兰。由于上述材料的组成，从而使该预涂感光平印版材成为阳图型。
2、如权利要求1所述的阳图预涂感光平印版，其特征在于感光层用的感光溶液的组成为：
重氮树脂与硫氰酸钾缩合物 5-20克
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 1.5-6克
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 2.5-10克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
3、如权利要求1所述的阳图型预涂感光平印版，其特征在于感光层用的感光溶液的组成为：
重氮树脂与硫氰酸钾缩合物 9-36克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
4、如权利要求1所述的阳图预涂感光平印版，其特征在于感光层用的感光溶液的组成为：
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 13.3-53克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
5、如权利要求1所述的阳图型预涂感光平印版，其特征在于感光层用的感光溶液的组成为：
重氮树脂与硫氰酸钾缩合物 5-20克
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 4-16克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
6、如权利要求1所述的阳图型预涂感光平印版，其特征在于感光层用的感光溶液的组成为：
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 5-20克
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 24-16克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
7、如权利要求1所述的阳图型预涂感光平印版，其特征在于感光层用的感光溶液的组成为：
重氮树脂与硫氰酸钾缩合物 5-20克
对甲氧基二苯胺重氮盐酸盐与硫氰酸钾缩合物 1.5-6克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升
8、如权利要求1所述的阳图型预涂感光平印版，其特征在于感光层用的感光溶液的组成为：
4-吗啉基重氮苯氯化锌复盐与硫氰酸钾缩合物 13.3-53克
线性间甲酚醛树脂 200克
乙二醇独乙醚 810毫升
甲醇 1080毫升
二甲基甲酰胺 270毫升
5%碱性艳兰乙二醇独乙醚溶液 47.5毫升