CN85100580B - 耐蚀、光亮、可发色压铸铝合金 - Google Patents

耐蚀、光亮、可发色压铸铝合金 Download PDF

Info

Publication number
CN85100580B
CN85100580B CN85100580A CN85100580A CN85100580B CN 85100580 B CN85100580 B CN 85100580B CN 85100580 A CN85100580 A CN 85100580A CN 85100580 A CN85100580 A CN 85100580A CN 85100580 B CN85100580 B CN 85100580B
Authority
CN
China
Prior art keywords
alloy
aluminium alloy
aluminium
silicon
casting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
CN85100580A
Other languages
English (en)
Other versions
CN85100580A (zh
Inventor
周国桢
杨汉国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Institute of Technology
Original Assignee
Nanjing Institute of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Institute of Technology filed Critical Nanjing Institute of Technology
Priority to CN85100580A priority Critical patent/CN85100580B/zh
Publication of CN85100580A publication Critical patent/CN85100580A/zh
Publication of CN85100580B publication Critical patent/CN85100580B/zh
Expired legal-status Critical Current

Abstract

一种压铸铝合金，在含有镁、锰、锌、铜、铁、锆、硅的铝合金中添加含量为０．１５～０．８％（重量）的稀土金属元素，其各元素的成份比为（重量，％）。镁－３．５～５．５，锌－０．１～４．５，锰－０．１～０．６，铜－０．０５～０．１，铁－０．２～１．０，硅－０．２～１．０，锆－０．０１～０．３，其余为铝。该压铸铝合金的铸造性能良好，经机械抛光可获得镜面亮度，并能进行化学抛光和阳极氧化、染色、电介发色处理。

Description

耐蚀、光亮、可发色压铸铝合金
本发明是一种压铸铝合金，该铝合金含镁、锌、锰、铜、铁、锆、硅，添加稀土金属元素，适用于制作自行车和摩托车零件，建筑装璜、装修零件和水暖器材零件等，并可代替镀铬件、不锈钢和黄铜、青铜制品。
现有的压铸（铸造）铝合金中，铝-硅类合金占多数。这类合金的压铸性能优良，但不能获得光亮和各种具有金属光泽的发色压铸件（铸件）。铝硅类合金压铸件（铸件），一经化学处理表面即发灰、发黑，机械性能也较低，脆性较大。而铝镁系合金虽然表面处理性能比铝硅系合金优良，但压铸性能不好，容易形成粘模、热裂、浇不足和冷隔、疏松等缺陷，机械性能和表面硬度也不高。
日本专利昭53-56114提供的铝镁系压铸合金，虽然可提高合金的脱模性能和机械性能，但增加了热裂倾向，降低了耐蚀性能，恶化了加工工艺，使融液容易变稠，表面化学性能变差，容易发黑、发灰。
本发明的目的在于提供一种压铸铝合金，使其既有优良的表面处理性能，又具有良好的压铸性能。
本发明所提供的压铸铝合金，是一种含有镁、锌、锰、铜、铁、锆（或者钛和硼）、硅的铝合金，其区别是在下列成份重量百分比的条件下，添加含量可为0.15～0.8%（重量）的混合稀土金属Xt（铈、镧、钇）或纯稀土金属（铈或镧或钇）。
镁-3.5～5.5，锌-0.1～4.5，
锰-0.1～0.6，铜-0.05～0.1
铁-0.2～1.0，硅-0.2～1.0，
锆-0.01～0.3（或者
钛-0.03～0.5，硼-0.01～0.05）
其余为铝。
本发明所提供的压铸铝合金，提高了铝合金的流动性、充填性和抗热裂性能，并有良好的脱模性，能压铸2毫米左右的薄壁零件。经机械抛光可获得镜面亮度，反射率超过镀铬件;并能进行化学抛光和阳极氧化、染色、电介发色处理，获得均一的具有金属光泽的各种色彩。
下面是本发明的一个实施例。
用本发明的铝合金和波兰AC5合金、苏联B92合金、日本昭53-56114专利合金和我国ZL302合金、日本ADC6合金作了对比试验。其性能列入表1和表2，熔炼和铸造工艺均采用公知的常规方法。
作为实施例之试件，为薄壁、空心之轴状零件（见附图），两法兰边直径为60毫米，边厚2毫米，轴管壁厚为2毫米，长80毫米，轴管内孔直径10毫米。
轴状零件经表面去毛刺、飞边、浇口、冒气口后，在布抛光轮上抛光，可获镜面亮度;零件经70%磷酸+5%硝酸的水溶液中，加温到7℃，浸渍1分钟经硝酸30%的水溶液出光，可获银白的具有金属光泽的表面，经化学抛光后的零件，在15%H2SO4溶液中，通直流电，V＝15伏，30分钟，18℃，可获银白色5～10微米的阳极氧化膜，此膜可通过染色，二次电介发色，获得红、绿、金黄、古铜、青铜、茶褐、黑色等具有金属光泽的色彩。
合金 （金型） 性能
铸造　　性能 阳极氧化性能
流动性 螺旋长度 (mm) 热裂倾向 （轴状零件） 15%H2SO4 D·C='15'V 30分
B92 （苏联） 495 裂 灰白色 膜厚3μ-5μ
AC5 （波兰） 487 裂 暗灰色 膜厚2μ-3μ
昭53-56114 （日本） 490 裂 暗灰色 膜厚2μ-3μ
ADC6 （日本） 492 微裂 灰白色 膜厚3μ-4μ
ZL302 （中国） 512 微裂 灰白色 膜厚2μ-3μ
本发明合金 （中国） 536 不裂 银白色 膜厚3μ-7μ 可染色及二次电介发色
合金 （金型） 性 能
机 械 性 能
状态 σb MPa σ MPa δ % HB MPa
B92 （苏联） 铸态 T6 200-240 280-320 160-200 220-240 4-6 3-4 700-800 1000-1100
AC5 （波兰 铸态 T6 250-280 320-380 200-240 280-340 2-4 1-3 800-900 1000-1100
昭53-56114 （日本） 铸态 T6 180-200 240-260 120-160 200-220 4-6 3-4 600-800 800-950
ADC6 （日本） 铸态 T6 150-170 200-220 100-140 160-180 3-4 2-3 600-700 750-900
ZL302 （中国） 铸态 T6 150-170 － － － 1-2 － 550-600 －
本发明合金 （中国） 铸态 T6 240-260 300-360 200-220 240-280 4-6 3-4 800-900 1050-1200

Claims (1)

1、一种压铸铝合金，其特征是含有（重量%）。Mg3.5～5.5 Zn0.1～4.5 Mn0.1～0.6 Cu0.05～0.1 Fe0.2～1.0 Si0.2～1.0 Zr0.01～0.3（或Ti0.03～0.5、B0.01～0.05）混合Xt（Ce、La、Y）或Xt（Ce或La或Y）0.15～0.8、Al余量。
CN85100580A 1985-04-01 1985-04-01 耐蚀、光亮、可发色压铸铝合金 Expired CN85100580B (zh)