CN1948525B - 羰基法提取镍铜一次合金中钴的方法 - Google Patents
羰基法提取镍铜一次合金中钴的方法 Download PDFInfo
- Publication number
- CN1948525B CN1948525B CN200610145350A CN200610145350A CN1948525B CN 1948525 B CN1948525 B CN 1948525B CN 200610145350 A CN200610145350 A CN 200610145350A CN 200610145350 A CN200610145350 A CN 200610145350A CN 1948525 B CN1948525 B CN 1948525B
- Authority
- CN
- China
- Prior art keywords
- cobalt
- carbonyl
- copper alloy
- gas
- nickel copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
羰基法提取镍铜一次合金中钴的方法，涉及一种镍铜一次合金生产羰基钴的方法。其特征在于其提取过程是将镍铜一次合金在20.0-25.0MPa压力、150-250℃温度条件下，连续通入含有催化剂的CO气体进行羰化反应。本发明的羰基法提取镍铜一次合金中钴的方法，合成羰基钴的反应温度低且温度适用范围宽，效果理想。合成羰基钴的收率比较高，反应时间短，反应压力处于高压状态，对反应原料的要求不苛刻，使用范围广；反应工艺简单且原料比较充沛，适宜于大规模进行生产。
Description
技术领域
羰基法提取镍铜一次合金中钴的方法，涉及一种镍铜一次合金生产羰基钴的方法。
背景技术
羰基法提取金属的技术在国外已经发展了100多年的历史，其中以羰基镍和羰基铁为主。人们也利用羰基法提取了原料中的钴，制取钴粉、催化剂等；在高温、高压条件下，以碳酸钴、钴的卤化物为原料制备了羰基钴。这种方法存在流程复杂、所需试剂多、回收率低、能源消耗大的缺点。在铜镍生产过程中，如何回收铜镍一次合金中的钴，特别是将合金中的钴生成羰基钴，对原料中的钴进行提取，在减少了能源消耗同时，生产产品性能优异的羰基钴意义重大。
发明内容
本发明的目的就是针对上述已有技术存在的不足，提供一种能有效简化流程、提高回收率、降低能源消耗的对原料中的钴进行选择性提取羰基钴的生产方法。
本发明的目的是通过以下技术方案实现的。
羰基法提取镍铜一次合金中钴的方法，其提取过程是将镍铜一次合金在20.0-25.0MPa压力、150-250℃温度条件下，连续通入含有催化剂的CO气体进行羰化反应；其特征在于所述的CO气体是含有的催化剂是硫化氢气体，且含有催化剂硫化氢的CO气体中，催化剂硫化氢的体积百分比含量为0.1％-0.5％。
本发明的羰基法提取镍铜一次合金中钴的方法，合成羰基钴的反应温度低且温度适用范围宽，效果理想。合成羰基钴的收率比较高，反应时间短，反应压力处于高压状态，对反应原料的要求不苛刻，使用范围广；反应工艺简单且原料比较充沛，适宜于大规模进行生产。
本发明方法，用于镍铜一次合金羰化提取钴的过程，由于压力和温度比较适中，对设备及原料的要求不严格；同时对原料独特的活化处理，又可在反应器内实现钴的高效羰化，工程造价大为降低。
具体实施方式
羰基法提取镍铜一次合金中钴的方法，其生产过程是将镍铜一次合金在20.0-25.0MPa压力、150-250℃温度条件下，连续通入含有催化剂的CO气体进行羰化反应。CO气体含有的催化剂是硫化氢气体，且含有催化剂的CO气体中，催化剂的体积百分含量为0.1％-0.5％。
实施例1
在反应器内加入50g镍铜一次合金，反应器经过CO置换空气后，连续通入含体积百分含量为0.1％的催化剂硫化氢CO气体，在压力20.0MPa，温度185℃条件下反应进行45小时，含有羰基钴的反应混合气导入冷凝气液分离器，收集羰基钴，尾气循环利用，钴收率为30.1％.
实施例2
在反应器内加入50g镍铜一次合金，反应器经过CO置换空气后，连续通入含体积百分含量为0.5％的催化剂硫化氢CO气体，在压力20.5MPa MPa，温度190℃条件下反应进行45小时，含有羰基钴的反应混合气导入冷凝气液分离器，收集羰基钴，尾气循环利用，钴收率为32.0％。
实施例3
在反应器内加入50g镍铜一次合金，反应器经过CO置换空气后，连续通入含体积百分含量为0.3％的催化剂硫化氢CO气体，在压力21.0MPa MPa，温度195℃条件下反应进行45小时，含有羰基钴的反应混合气导入冷凝气液分离器，收集羰基钴，尾气循环利用，钴收率为33.4％。
实施例4
在反应器内加入50g镍铜一次合金，反应器经过CO置换空气后，连续通入含体积百分含量为0.2％的催化剂硫化氢CO气体，在压力23.0MPa MPa，温度210℃条件下反应进行45小时，含有羰基钴的反应混合气导入冷凝气液分离器，收集羰基钴，尾气循环利用，钴收率为32.9％。
实施例5
在反应器内加入50g镍铜一次合金，反应器经过CO置换空气后连续通入含体积百分含量为0.4％的催化剂硫化氢CO气体，在压力25MPa，温度150℃条件下反应进行48小时，含有羰基钴的反应混合气导入冷凝气液分离器，收集羰基钴，尾气循环利用。钴收率为34.1％。
实施例6
在反应器内加入50g镍铜一次合金，反应器经过CO置换空气后，连续通入含体积百分含量为0.5％的催化剂硫化氢CO气体，在压力20.0MPa，温度250℃条件下反应进行45小时，含有羰基钴的反应混合气导入冷凝气液分离器，收集羰基钴，尾气循环利用。钴收率为30.8％。
Claims (1)
1.羰基法提取镍铜一次合金中钴的方法，其提取过程是将镍铜一次合金在20.0-25.0MPa压力、150-250℃温度条件下，连续通入含有催化剂的CO气体进行羰化反应；其特征在于所述的CO气体是含有的催化剂是硫化氢气体，且含有催化剂硫化氢的CO气体中，催化剂硫化氢的体积百分比含量为0.1％-0.5％。