CN1944013A - 蓖麻秆碎料板的制作方法 - Google Patents

蓖麻秆碎料板的制作方法 Download PDF

Info

Publication number
CN1944013A
CN1944013A CN 200610096823 CN200610096823A CN1944013A CN 1944013 A CN1944013 A CN 1944013A CN 200610096823 CN200610096823 CN 200610096823 CN 200610096823 A CN200610096823 A CN 200610096823A CN 1944013 A CN1944013 A CN 1944013A
Authority
CN
China
Prior art keywords
castor
stalk
oil plant
mat formation
chipboard
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610096823
Other languages
English (en)
Other versions
CN100381263C (zh
Inventor
周定国
徐咏兰
张洋
梅长彤
周哓燕
潘明珠
徐信武
华毓坤
李晓平
易常经
吕增瑞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Forestry University
Original Assignee
Nanjing Forestry University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Forestry University filed Critical Nanjing Forestry University
Priority to CNB2006100968234A priority Critical patent/CN100381263C/zh
Publication of CN1944013A publication Critical patent/CN1944013A/zh
Application granted granted Critical
Publication of CN100381263C publication Critical patent/CN100381263C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是蓖麻秆碎料板的制作方法，其特征是(一)原料处理工艺：粉碎、筛选、干燥；(二)拌胶工艺：采用异氰酸酯胶粘剂或异氰酸酯胶粘剂；(三)铺装和脱模工艺：采用机械式铺装机铺装，使用异氰酸酯胶粘剂铺装后用脱模剂或隔离层脱模，进行板坯预压；(四)热压工艺：采用单层或多层形式压机；(五)后期处理工艺：常温下冷却、裁边、堆垛和砂光。本发明的优点：制造成本低，可实行工业化生产。蓖麻秆碎料板的性能可以达到木质刨花板的国家标准要求。其中使用尿醛树脂胶粘剂的蓖麻秆碎料板主要性能：密度0.75－0.80g/cm3；静曲强度15－17MPa；平面抗拉强度0.40－0.50MPa；吸水厚度膨胀率6.5－7.5％。

Description

蓖麻秆碎料板的制作方法
技术领域
本发明涉及的是一种蓖麻秆碎料板的制作方法，属于人造板制造技术领域。
背景技术
目前，一方面各国对环境及森林资源的保护力度加大，另一方面社会对人造板的需求却在不断加大，人造板企业逐年增加，造成人造板所用的木材原料缺乏，各国均加大对采用农作物秸杆制造人造板的研究，蓖麻秆也属于农作物秸杆的范围，我国内蒙古一些地区具有丰富的蓖麻秆资源，研究蓖麻秆碎料板的制作方法将有助于扩大农作物秸杆人造板原料的范围，解决部分人造板厂所用木材原料缺乏的问题。
发明内容
本发明的目的是提供一种成本低、可工业化生产的蓖麻秆碎料板制作方法。
本发明的技术解决方案：蓖麻秆碎料板制作方法，其工艺步骤分为(一)原料处理、(二)拌胶、(三)铺装和脱模、(四)热压、(五)后期处理；
所述的原料处理工艺步骤(一)包括a.用粉碎机破碎蓖麻秆，用筛选机筛选去除碎料中的粉尘，并将大于？mm的粗碎料送去再碎；b.将蓖麻秆碎料送入干燥机干燥，干燥温度80-120℃，干燥后含水率6％-12％；所述的拌胶工艺步骤(二)包括：采用异氰酸酯胶粘剂或尿醛树脂胶粘剂，使用异氰酸酯胶粘剂，其施胶量占绝干蓖麻秆碎料重量的5-7％，使用尿醛树脂胶粘剂，其施胶量占绝干蓖麻秆碎料重量的12-16％；所述的铺装和脱模工艺步骤(三)包括：采用机械式铺装机铺装，使用异氰酸酯胶粘剂铺装后用脱模剂或隔离层脱模，进行板坯预压，预压在常温下进行，最大线压力180-260kg/cm；
所述的热压工艺步骤(四)包括：采用单层或多层形式压机，热压温度160-180℃，热压时间为0.5-0.8min/mm，热压压力为2.5-3.5Mpa；
所述的后期处理工艺步骤(五)包括：冷却、裁边和砂光，冷却在翻板冷却装置中进行，时间20-50min，裁边是用裁边机对产品的幅面尺寸裁为1220mm×2440mm，堆垛48小时，用砂光机砂光。
本发明的优点：制造成本低，可实行工业化生产。蓖麻秆碎料板的性能可以达到木质刨花板的国家标准要求。其中使用尿醛树脂胶粘剂的蓖麻秆碎料板主要性能如下：
密度0.75-0.80g/cm3
静曲强度15-17MPa
平面抗拉强度0.40-0.50MPa
吸水厚度膨胀率6.5-7.5％
使用异氰酸酯胶粘剂的蓖麻秆碎料板主要性能如下：
密度0.70-0.80g/cm3
静曲强度18-23MPa
平面抗拉强度1.0-1.5MPa
吸水厚度膨胀率4-6％
具体实施方式
实施例1  取蓖麻秆为原材料制作蓖麻秆碎料板，
(一)对原材料处理工，其工艺步骤：a.用粉碎机破碎蓖麻秆，用筛选机筛选去除碎料中的粉尘，并将大于50mm的粗碎料送去再碎；b.将蓖麻秆碎料送入干燥机干燥，干燥温度80℃，干燥后含水率6％；
(二)拌胶，其工艺步骤：用异氰酸酯胶粘剂或尿醛树脂胶粘剂，用异氰酸酯胶粘剂，其施胶量占绝干蓖麻秆碎料重量的5％；用尿醛树脂胶粘剂，其施胶量占绝干蓖麻秆碎料重量的12％；
(三)铺装和脱模，其工艺步骤：采用机械式铺装机铺装，用异氰酸酯胶粘剂铺装后用脱模剂或隔离层脱模，进行板坯预压，预压在常温下进行，最大线压力180kg/cm；
(四)热压，其工艺步骤：采用单层或多层形式压机，热压温度160℃，热压时间为0.5min/mm，热压压力为2.5Mpa；
(五)后期处理，其工艺步骤：在常温下冷却、裁边和砂光，冷却在翻板冷却装置中进行，时间20min，裁边是用裁边机对产品的幅面尺寸裁为1220mm×2440mm，堆垛48小时，用砂光机砂光。实施例2取蓖麻秆为原材料制作蓖麻秆碎料板，
(一)对原材料处理工，其工艺步骤：a.用粉碎机破碎蓖麻秆，用筛选机筛选去除碎料中的粉尘，并将大于50mm的粗碎料送去再碎；b.将蓖麻秆碎料送入干燥机干燥，干燥温度100℃，干燥后含水率8％；
(二)拌胶，其工艺步骤：用异氰酸酯胶粘剂或尿醛树脂胶粘剂，用异氰酸酯胶粘剂，其施胶量占绝干蓖麻秆碎料重量的6％；用尿醛树脂胶粘剂，其施胶量占绝干蓖麻秆碎料重量的14％；
(三)铺装和脱模，其工艺步骤：采用机械式铺装机铺装，用异氰酸酯胶粘剂铺装后用脱模剂或隔离层脱模，进行板坯预压，预压在常温下进行，最大线压力220kg/cm；
(四)热压，其工艺步骤：采用单层或多层形式压机，热压温度170℃，热压时间为0.65min/mm，热压压力为3Mpa；
(五)后期处理，其工艺步骤：在常温下冷却、裁边和砂光，冷却在翻板冷却装置中进行，时间35min，裁边是用裁边机对产品的幅面尺寸裁为1220mm×2440mm，堆垛48小时，用砂光机砂光。
实施例3  取蓖麻秆为原材料制作蓖麻秆碎料板，
(一)对原材料处理工，其工艺步骤：a.用粉碎机破碎蓖麻秆，用筛选机筛选去除碎料中的粉尘，并将大于50mm的粗碎料送去再碎；b.将蓖麻秆碎料送入干燥机干燥，干燥温度120℃，干燥后含水率12％；
(二)拌胶，其工艺步骤：用异氰酸酯胶粘剂或尿醛树脂胶粘剂，用异氰酸酯胶粘剂，其施胶量占绝干蓖麻秆碎料重量的7％；用尿醛树脂胶粘剂，其施胶量占绝干蓖麻秆碎料重量的16％；
(三)铺装和脱模，其工艺步骤：采用机械式铺装机铺装，用异氰酸酯胶粘剂铺装后用脱模剂或隔离层脱模，进行板坯预压，预压在常温下进行，最大线压力260kg/cm；
(四)热压，其工艺步骤：采用单层或多层形式压机，热压温度180℃，热压时间为0.8min/mm，热压压力为3.5Mpa；
(五)后期处理，其工艺步骤：在常温下冷却、裁边和砂光，冷却在翻板冷却装置中进行，时间50min，裁边是用裁边机对产品的幅面尺寸裁为1220mm×2440mm，堆垛48小时，用砂光机砂光。

Claims (3)

1、蓖麻秆碎料板的制作方法，其特征是(一)原料处理工艺：a.用粉碎机破碎蓖麻秆，用筛选机筛选去除碎料中的粉尘，并将大于？mm的粗碎料送去再碎；b.将蓖麻秆碎料送入干燥机干燥，干燥温度80-120℃，干燥后含水率6％-12％；(二)拌胶工艺：采用异氰酸酯胶粘剂使用异氰酸酯胶粘剂，其施胶量占绝干蓖麻秆碎料重量的5-7％；(三)铺装和脱模工艺：采用机械式铺装机铺装，使用异氰酸酯胶粘剂铺装后用脱模剂或隔离层脱模，进行板坯预压，预压在常温下进行，线压力180-260kg/cm；(四)热压工艺：采用单层或多层形式压机，热压温度160-180℃，热压时间为0.5-0.8min/mm，热压压力为2.5-3.5Mpa；(五)后期处理工艺：常温下冷却、裁边、堆垛和砂光。
2、根据权利要求1所述的蓖麻秆碎料板的制作方法，其特征是(二)拌胶工艺：用尿醛树脂胶粘剂，其施胶量占绝干蓖麻秆碎料重量的12-16％。
3、根据权利要求1所述的蓖麻秆碎料板的制作方法，其特征是(三)铺装和脱模工艺：采用机械式铺装机铺装。
CNB2006100968234A 2006-10-19 2006-10-19 蓖麻秆碎料板的制作方法 Expired - Fee Related CN100381263C (zh)