CN1861738A - 一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法 - Google Patents

一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法 Download PDF

Info

Publication number
CN1861738A
CN1861738A CN 200610019318 CN200610019318A CN1861738A CN 1861738 A CN1861738 A CN 1861738A CN 200610019318 CN200610019318 CN 200610019318 CN 200610019318 A CN200610019318 A CN 200610019318A CN 1861738 A CN1861738 A CN 1861738A
Authority
CN
China
Prior art keywords
luminescent powder
alkaline earth
ethylene glycol
compact film
earth aluminate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200610019318
Other languages
English (en)
Inventor
吕兴栋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi University of Finance and Economics
Original Assignee
Jiangxi University of Finance and Economics
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi University of Finance and Economics filed Critical Jiangxi University of Finance and Economics
Priority to CN 200610019318 priority Critical patent/CN1861738A/zh
Publication of CN1861738A publication Critical patent/CN1861738A/zh
Pending legal-status Critical Current

Abstract

一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法，它以乙二醇为分散介质，Al2 (SO4) 3为包膜剂，通过液相沉淀在碱土铝酸盐长余辉发光材料表面包覆氧化铝致密膜层。本发明的有益效果是：工艺简单，成本低，适合于工业化生产。氧化铝包覆量超过5％后，发光粉已具有很好的耐水性能，在水中长时间放置后不发生水解，同时抗高温氧化性能也得到显著改善，而且包覆后依然保持较好的长余辉发光特性。

Description

一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法
                        技术领域
本发明涉及一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法。
                        背景技术
碱土铝酸盐长余辉发光材料一般采用高温固相法合成，经球磨工序研磨成微细粉末，因而具有较高的比表面积，在与水接触时，会缓慢发生水解反应，使体系pH值升高，同时生成氢氧化铝沉淀。这样不仅坏了材料的晶体结构，降低粉体的长余辉发光性能，又影响体系的酸碱平衡，因而极大地限制了发光材料在水性体系中的应用。另外，由于Eu2+，Dy3+共掺杂碱土铝酸盐发光材料是在弱还原性气氛下合成，在氧化气氛(如空气)下高温处理时会失去蓄光性能，限制了发光材料在发光玻璃、发光陶瓷以及发光釉等领域的应用。为了改善材料的耐水性能和抗高温氧化性能，对材料进行表面包膜处理，可保护材料免受水或化学品的侵蚀，改善发光粉的抗高温氧化性能。目前，对碱土铝酸盐长余辉发光粉表面的无机包覆改性主要是二氧化硅包覆改性(采用溶胶—凝胶法)。
                        发明内容
本发明的目的是提供一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法，它采用液相沉淀法在碱土铝酸盐长余辉发光材料表面包覆氧化铝致密膜层。
本发明是这样来实现的，它以乙二醇为分散介质，Al2(SO4)3为包膜剂，通过液相沉淀在碱土铝酸盐长余辉发光材料表面包覆氧化铝致密膜层。在进行氧化铝包覆时，预先称取发光粉，加入到乙二醇溶液中，发光粉∶乙二醇＝1～5∶20，用超声波分散10～30分钟，然后转移至恒温水浴槽中。在保持匀速搅拌条件下，用滴管滴加浓度为0.1mol/l的Al2(SO4)3溶液，保持Al2(SO4)3的重量占发光粉重量的10～25％，然后逐滴滴加10％的氢氧化钠溶液调节pH值至4～6。将水浴锅温度设定为60～80℃，恒温加热2～4小时。反应结束后将上述悬浮液冷却至常温，抽滤除去乙二醇和少量的水分，用去离子水漂洗2遍，再用无水乙醇洗涤2次，放入30～60℃烘箱中干燥1～4小时后，即可得到经氧化铝包覆改性的发光粉产品。
本发明的有益效果是：工艺简单，成本低，适合于工业化生产。氧化铝包覆量超过5％后，发光粉已具有很好的耐水性能，在水中长时间放置后不发生水解，同时抗高温氧化性能也得到显著改善，而且包覆后依然保持较好的长余辉发光特性。
                        具体实施方式
实施例一、以乙二醇为分散介质，Al2(SO4)3为包膜剂，通过液相沉淀在碱土铝酸盐长余辉发光材料表面包覆氧化铝致密膜层。在进行氧化铝包覆时，预先称取发光粉3g，加入到20g乙二醇溶液中，用超声波分散20分钟，然后转移至水浴锅中。在保持匀速搅拌条件下，用滴管滴加浓度为0.1mol/l的Al2(SO4)3溶液，保持Al2(SO4)3的重量占发光粉重量的20％，然后逐滴滴加10％的氢氧化钠溶液调节pH值至6。将水浴槽温度设定为80℃，恒温加热3小时。反应结束后将上述悬浮液冷却至常温，抽滤除去乙二醇和少量的水分，用去离子水漂洗2遍，再用无水乙醇洗涤2次，放入60℃烘箱中干燥3小时后，即可得到经氧化铝包覆改性的发光粉产品。
实施例二、以乙取二醇为分散介质，Al2(SO4)3为包膜剂，通过液相沉淀在碱土铝酸盐长余辉发光材料表面包覆氧化铝致密膜层。在进行氧化铝包覆时，预先称取发光粉1g，加入到20g乙二醇溶液中，用超声波分散10分钟，然后转移至恒温水浴槽中。在保持匀速搅拌条件下，用滴管滴加浓度为0.1mol/l的Al2(SO4)3溶液，保持Al2(SO4)3的重量占发光粉重量的10％，然后逐滴滴加10％的氢氧化钠溶液调节pH值至4。将水浴槽温度设定为60℃，恒温加热2小时。反应结束后将上述悬浮液冷却至常温，抽滤除去乙二醇和少量的水分，用去离子水漂洗2遍，再用无水乙醇洗涤2次，放入30℃烘箱中干燥4小时后，即可得到经氧化铝包覆改性的发光粉产品。
实施例三、以乙取二醇为分散介质，Al2(SO4)3为包膜剂，通过液相沉淀在碱土铝酸盐长余辉发光材料表面包覆氧化铝致密膜层。在进行氧化铝包覆时，预先称取发光粉5g，加入到20g乙二醇溶液中，用超声波分散30分钟，然后转移至恒温水浴槽中。在保持匀速搅拌条件下，用滴管滴加浓度为0.1mol/l的Al2(SO4)3溶液，保持Al2(SO4)3的重量占发光粉重量的10～25％，然后逐滴滴加10％的氢氧化钠溶液调节pH值至6。将水浴槽温度设定为80℃，恒温加热4小时。反应结束后将上述悬浮液冷却至常温，抽滤除去乙二醇和少量的水分，用去离子水漂洗2遍，再用无水乙醇洗涤2次，放入30～60℃烘箱中干燥1小时后，即可得到经氧化铝包覆改性的发光粉产品。

Claims (1)

1、一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法，其特征在于方法步骤为：预先称取发光粉，加入到乙二醇溶液中，发光粉∶乙二醇＝1～5∶20，用超声波分散10～30分钟，然后转移至恒温水浴槽中，在保持匀速搅拌条件下，用滴管滴加浓度为0.1mol/l的Al2(SO4)3溶液，保持Al2(SO4)3的重量占发光粉重量的10～25％，然后逐滴滴加10％的氢氧化钠溶液调节pH值至4～6，将水浴槽温度设定为60～80℃，恒温加热2～4小时，反应结束后将上述悬浮液冷却至常温，抽滤除去乙二醇和水分，用去离子水漂洗2遍，再用无水乙醇洗涤2次，放入30～60℃烘箱中干燥1～4小时后，即可得到经氧化铝包覆改性的发光粉产品。
CN 200610019318 2006-06-09 2006-06-09 一种碱土铝酸盐长余辉发光粉表面氧化铝致密膜层包覆方法 Pending CN1861738A (zh)