CN1821328A - 一种聚氨酯改性不饱和聚酯清面漆 - Google Patents

一种聚氨酯改性不饱和聚酯清面漆 Download PDF

Info

Publication number
CN1821328A
CN1821328A CN 200610034563 CN200610034563A CN1821328A CN 1821328 A CN1821328 A CN 1821328A CN 200610034563 CN200610034563 CN 200610034563 CN 200610034563 A CN200610034563 A CN 200610034563A CN 1821328 A CN1821328 A CN 1821328A
Authority
CN
China
Prior art keywords
unsaturated polyester
lacquer
master
polyurethane
ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610034563
Other languages
English (en)
Other versions
CN100344718C (zh
Inventor
肖亚亮
叶义英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN WANZHENG PAINT Co Ltd
Original Assignee
FOSHAN WANZHENG PAINT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN WANZHENG PAINT Co Ltd filed Critical FOSHAN WANZHENG PAINT Co Ltd
Priority to CNB2006100345638A priority Critical patent/CN100344718C/zh
Publication of CN1821328A publication Critical patent/CN1821328A/zh
Application granted granted Critical
Publication of CN100344718C publication Critical patent/CN100344718C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚氨酯改性不饱和聚酯清面漆，该漆由聚氨酯(PU)和不饱和聚酯(PE)通过配油按配比混合组成，其配比范围为PU∶PE＝1∶(0.3－5)；所述PU的组分配比为：PU主漆∶固化剂∶PU稀释剂＝1∶1∶(0.6－1)；所述PU主漆由如下组分构成，含醇酸树脂80％－93％、二甲苯5％－10％、流平剂0.3％－0.5％、消泡剂0.1％0.3％；所述PE的组分配比为：PE主漆∶促进剂∶引发剂＝100∶0.8－1.2∶1－1.5；所述PE主漆由如下组分构成，不饱和聚酯树脂80％－90％、苯乙烯9％－18％、流平剂0.3％－0.5％、消泡剂0.2％－0.3％。本发明具有硬度高、丰满度好、附着力强、柔韧性好、易抛光、成本更低等优点。

Description

一种聚氨酯改性不饱和聚酯清面漆
技术领域
本发明涉及木制品油漆的技术领域，更具体地说是涉及一种具有装饰效果好的新型木制品抛光面漆。
背景技术
目前，木制品抛光面漆，主要有聚氨酯漆和不饱和聚酯漆等，其具有附着力强、柔韧性好、易抛光等优点，广泛应用在木制品表面抛光上，但用于高档出口家具或乐器等方面，要求各项技术指标优异的产品仍需进口，成本较高；如申请号为99101988，申请日为1999年4月3日，发明名称为一种聚氨酯漆的发明专利申请，其特征是其为甲乙双组份漆，涂装时甲乙组分的重量配比为1∶2.5～4；甲组分重量百分比为：改性聚酯50～60％混合溶剂40～50％按常规还需加入甲组分总量的0.2％的流平剂CAB-35-1；乙组分重量百分比为：改性聚酯27.2～29.4％甲苯二异氰酸酯20.6～22.8％混合溶剂47.8～52.2％乙组分的制法是将甲苯二异氰酸酯用混合溶剂稀释成50％的溶液，升温至70℃，开始加入改性聚酯的混合溶剂的溶液，并保温在70～80℃，1～2小时内连续加入完毕，然后在90～120℃下搅拌反应1～2小时，测得NCO含量为6～8.5％时，过滤出料。上述专利采用聚酯废料等合成的聚氨酯漆，其工艺复杂，成本高，其有些技术指标仍有待提高。
发明内容
本发明的目的在于克服现有技术之不足，而提供一种技术指标优异，达到外国同类产品的，具有硬度高、丰满度好、附着力强、柔韧性好、易抛光等优点的一种聚氨酯改性不饱和聚酯清面漆。
本发明为了解决上述技术问题而采用的技术解决方案如下：
一种聚氨酯改性不饱和聚酯清面漆，其特征在于：该漆由聚氨酯(PU)和不饱和聚酯(PE)通过配油按规定配比混合组成，其配比范围为PU∶PE＝1∶(0.3-5)；
所述PU的组分配比为：PU主漆∶固化剂∶PU稀释剂＝1∶1∶(0.6-1)；所述PU主漆由如下组分构成，含醇酸树脂80％-93％、二甲苯5％-10％、流平剂0.3％-0.5％、消泡剂0.1％-0.3％；
所述PE的组分配比为：PE主漆∶促进剂∶引发剂＝100∶0.8-1.2∶1-1.5；所述PE主漆由如下组分构成，不饱和聚酯树脂80％-90％、苯乙烯9％-18％、流平剂0.3％-0.5％、消泡剂0.2％-0.3％；
所述固化剂为40％固含甲苯二异氰酸酯(TDI)-三羟甲基丙烷加成物；所述PU稀释剂由如下组分构成，二甲苯50％-55％、醋酸丁酯25％-40％、环己酮10％-15％；所述促进剂为金属钴含量6％的异辛酸钴；所述引发剂为氧含量10％的过氧化甲乙酮。
本发明采用上述技术解决方案所能达到的有益效果是：本发明产品用于高档出口家具和乐器等，装饰效果好，具有硬度高、硬度可达到3H，丰满度好、附着力强、柔韧性好、不易开裂、易施工、不易起针孔或其它表面缺陷、抛光性优等优点，技术指标优异，同时可替代国外同类产品，而且成本更低，使用本发明产品可使涂饰的木器具备优异的抗刮、高丰满度及良好的耐温变和耐化学品性、大大提高产品的装饰效果，提高产品的市场竞争力。
具体实施方式
实施例1：
一种聚氨酯改性不饱和聚酯清面漆，包括聚氨酯(PU)和不饱和聚酯(PE)，根据实际漆膜要求，通过配油按1∶1配比混合组成，混合后施工待干燥后可打磨抛光。所述PU油的组分配比为：PU主漆∶固化剂∶PU稀释剂＝1∶1∶1；所述PU主漆由如下组分构成，含醇酸树脂90％、二甲苯9.2％、流平剂0.5％、消泡剂0.3％；所述固化剂为40％固含固含甲苯二异氰酸酯(TDI)-三羟甲基丙烷合成物；所述PU稀释剂由如下组分构成，二甲苯50％、醋酸丁酯40％、环己酮10％。
所述PE油的组分配比为：PE主漆∶促进剂∶引发剂＝100∶1∶1；所述PE主漆由如下组分构成，不饱和聚酯树脂85％、苯乙烯14.2％、流平剂0.5％、消泡剂0.3％；所述促进剂为金属钴含量6％异辛酸钴；所述引发剂为氧含量10％过氧化甲乙酮。
经实际测试数据表明：按上述1∶1配油的漆，主要性能为：硬度≥3H，柔韧性≤1mm，附着力100％，光泽(60°角)105～115，丰满度、抗刮性及抛光性均为优等，可施工时间(在25℃)为3小时，达到国外进口同类产品的技术指标。
实施例2：
一种聚氨酯改性不饱和聚酯清面漆，由聚氨酯(PU)和不饱和聚酯(PE)通过配油按配比混合组成，其配比范围为PU∶PE＝1∶2。
所述PU油的组分配比为：PU主漆∶固化剂∶PU稀释剂＝1∶1∶0.6；所述PU主漆由如下组分构成，含醇酸树脂89.5％、二甲苯10％、流平剂0.3％、消泡剂0.2％；所述固化剂为40％固含固含甲苯二异氰酸酯(TDI)-三羟甲基丙烷合成物；所述PU稀释剂由如下组分构成，二甲苯55％、醋酸丁酯35％、环己酮10％。
所述PE油的组分配比为：PE主漆∶促进剂∶引发剂＝100∶1.2∶1.5；所述PE主漆由如下组分构成，不饱和聚酯树脂83.5％、苯乙烯16％、流平剂0.3％、消泡剂0.2％；所述促进剂为金属钴含量6％异辛酸钴；所述引发剂为氧含量10％过氧化甲乙酮。
采用本配方制作的抛光面漆，其综合了聚氨酯漆和不饱和聚酯漆的优点，具有硬度高、丰满度好、附着力强、柔韧性好、易抛光等优点，技术指标优异，可替代国外同类产品，而且成本更低，产业化生产，具有较好的经济效益和社会效益。

Claims (2)

1、一种聚氨酯改性不饱和聚酯清面漆，其特征在于：该漆由聚氨酯(PU)和不饱和聚酯(PE)通过配油按配比混合组成，其配比范围为PU∶PE＝1∶(0.3-5)；
所述PU的组分配比为：PU主漆∶固化剂∶PU稀释剂＝1∶1∶(0.6-1)；所述PU主漆由如下组分构成，含醇酸树脂80％-93％、二甲苯5％-10％、流平剂0.3％-0.5％、消泡剂0.1％-0.3％；
所述PE的组分配比为：PE主漆∶促进剂∶引发剂＝100∶0.8-1.2∶1-1.5；所述PE主漆由如下组分构成，不饱和聚酯树脂80％-90％、苯乙烯9％-18％、流平剂0.3％-0.5％、消泡剂0.2％-0.3％。
2、根据权利要求1所述的聚氨酯改性不饱和聚酯清面漆，其特征在于：所述固化剂为40％固含甲苯二异氰酸酯(TDI)-三羟甲基丙烷合成物；所述PU稀释剂由如下组分构成，二甲苯50％-55％、醋酸丁酯25％-40％、环己酮10％-15％；所述促进剂为金属钴含量6％异辛酸钴；所述引发剂为氧含量10％过氧化甲乙酮。
CNB2006100345638A 2006-03-27 2006-03-27 一种聚氨酯改性不饱和聚酯清面漆 Expired - Fee Related CN100344718C (zh)