CN1816640A - 两相不锈钢 - Google Patents
两相不锈钢 Download PDFInfo
- Publication number
- CN1816640A CN1816640A CNA2004800188034A CN200480018803A CN1816640A CN 1816640 A CN1816640 A CN 1816640A CN A2004800188034 A CNA2004800188034 A CN A2004800188034A CN 200480018803 A CN200480018803 A CN 200480018803A CN 1816640 A CN1816640 A CN 1816640A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- duplex stainless
- inclusion
- phase
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
编号 | C | Si | Mn | P | S | Ni | Cr | Mo | W | N | sol.Al | PREW | 第1群元素 | 第2群元素 |
A1 | 0.020 | 0.30 | 0.51 | 0.016 | 0.001 | 7.02 | 25.20 | 2.97 | 2.16 | 0.30 | 0.005 | 43.365 | ||
A2 | 0.020 | 0.31 | 0.49 | 0.016 | 0.001 | 6.32 | 25.47 | 2.92 | 2.17 | 0.26 | 0.006 | 42.8305 | ||
A3 | 0.021 | 0.31 | 0.51 | 0.015 | 0.001 | 7.12 | 24.20 | 3.64 | 2.10 | 0.31 | 0.005 | 44.669 | ||
A4 | 0.020 | 0.31 | 0.50 | 0.016 | 0.001 | 6.99 | 26.10 | 2.21 | 2.19 | 0.26 | 0.007 | 41.2305 | ||
A5 | 0.019 | 0.12 | 0.49 | 0.016 | 0.001 | 7.06 | 25.26 | 2.34 | 3.15 | 0.27 | 0.006 | 42.5315 | Cu=0.56 | |
A6 | 0.021 | 0.28 | 0.50 | 0.022 | 0.001 | 7.35 | 24.98 | 3.12 | 2.15 | 0.31 | 0.007 | 43.7995 | V=0.65 | |
A7 | 0.021 | 0.45 | 0.50 | 0.016 | 0.001 | 6.85 | 24.98 | 2.87 | 2.32 | 0.31 | 0.008 | 43.255 | B=0.006 | |
A8 | 0.019 | 0.35 | 0.47 | 0.015 | 0.001 | 7.12 | 25.26 | 2.98 | 2.24 | 0.27 | 0.005 | 43.142 | REM=0.01 | |
A9 | 0.019 | 0.37 | 0.49 | 0.016 | 0.001 | 8.15 | 24.87 | 3.25 | 2.26 | 0.27 | 0.006 | 43.676 | ||
A10 | 0.021 | 0.30 | 0.58 | 0.017 | 0.001 | 6.95 | 25.98 | 2.95 | 2.15 | 0.31 | 0.005 | 44.2385 | ||
A11 | 0.021 | 0.30 | 0.50 | 0.016 | 0.001 | 7.23 | 24.98 | 3.12 | 2.64 | 0.31 | 0.007 | 44.608 | Cu=0.46 | B=0.006 |
A12 | 0.022 | 0.30 | 0.49 | 0.017 | 0.001 | 7.74 | 24.78 | 3.14 | 2.17 | 0.28 | 0.005 | 43.1865 | Cu=1.25 V=0.87 | |
A13 | 0.021 | 0.30 | 0.50 | 0.016 | 0.001 | 6.58 | 25.12 | 3.30 | 2.37 | 0.27 | 0.006 | 44.2085 | Cu=1.31 V=0.77 | B=0.007 |
A14 | 0.021 | 0.32 | 0.50 | 0.014 | 0.001 | 7.11 | 25.17 | 2.99 | 3.16 | 0.26 | 0.005 | 44.411 | Cu=1.31 V=0.77 | REM=0.01 |
A15 | 0.021 | 0.29 | 0.10 | 0.015 | 0.001 | 7.00 | 25.25 | 2.98 | 2.18 | 0.27 | 0.005 | 43.049 | Cu=1.31 V=0.77 | |
A16 | - | 0.32 | 0.49 | 0.015 | 0.001 | 7.01 | 25.1 | 2.97 | 2.17 | 0.37 | 0.004 | 44.4015 | ||
A17 | 0.021 | - | 0.48 | 0.018 | 0.001 | 7.04 | 25.17 | 3.01 | 2.37 | 0.31 | 0.003 | 43.9735 | ||
A18 | 0.022 | 0.3 | - | 0.017 | 0.001 | 6.89 | 24.87 | 3.11 | 2.26 | 0.28 | 0.005 | 43.342 | ||
A19 | 0.022 | 0.32 | 0.49 | 0.018 | 0.001 | 7.1 | 24.89 | 3.08 | 2.26 | 0.26 | - | 42.943 | ||
B1 | 0.021 | 0.30 | 0.30 | 0.016 | 0.001 | 8.56 | 24.88 | 3.61 | 2.16 | 0.28 | 0.005 | 44.805 | ||
B2 | 0.021 | 0.30 | 0.50 | 0.015 | 0.001 | 6.12 | 24.95 | 3.52 | 2.15 | 0.28 | 0.006 | 44.5615 | ||
B3 | 0.020 | 0.30 | 0.51 | 0.016 | 0.001 | 7.02 | 25.20 | 2.97 | 2.16 | 0.30 | 0.008 | 43.365 | ||
B4 | 0.020 | 0.31 | 0.49 | 0.016 | 0.001 | 6.32 | 25.47 | 2.92 | 2.17 | 0.26 | 0.007 | 42.8305 | ||
B5 | 0.021 | 0.31 | 0.51 | 0.015 | 0.001 | 7.12 | 24.20 | 3.64 | 2.10 | 0.31 | 0.007 | 44.669 | ||
B6 | 0.020 | 0.30 | 0.51 | 0.016 | 0.001 | 7.02 | 25.20 | 2.97 | 2.16 | 0.30 | 0.005 | 43.365 |
编号 | 有害夹杂物密度 | Mo+1.1Ni-12.5 | Mo-0.8Ni+1.6 | 焊接条件1 | 焊接条件2 | 备考 | ||
微量σ相 | 点蚀的有无 | 微量σ相 | 点蚀的有无 | |||||
A1 | 5 | -1.808 | -1.046 | ○ | ○ | ○ | 无 | 本发明例 |
A2 | 7 | -2.628 | -0.536 | ○ | ○ | ○ | 无 | |
A3 | 4 | -1.028 | -0.456 | ○ | ○ | ○ | 无 | |
A4 | 8 | -2.601 | -1.782 | ○ | ○ | ○ | 无 | |
A5 | 4 | -2.394 | -1.708 | ○ | ○ | ○ | 无 | |
A6 | 6 | -1.295 | -1.16 | ○ | ○ | ○ | 无 | |
A7 | 7 | -2.095 | -1.01 | ○ | ○ | ○ | 无 | |
A8 | 6 | -1.688 | -1.116 | ○ | ○ | ○ | 无 | |
A9 | 5 | -0.285 | -1.67 | ○ | ○ | ○ | 无 | |
A10 | 5 | -1.905 | -1.01 | ○ | ○ | ○ | 无 | |
A11 | 3 | -1.427 | -1.064 | ○ | ○ | ○ | 无 | |
A12 | 6 | -0.846 | -1.452 | ○ | ○ | ○ | 无 | |
A13 | 6 | -1.962 | -0.364 | ○ | ○ | ○ | 无 | |
A14 | 5 | -1.689 | -1.098 | ○ | ○ | ○ | 无 | |
A15 | 3 | -1.82 | -1.02 | ○ | ○ | ○ | 无 | |
A16 | 4 | -1.819 | -1.038 | ○ | ○ | ○ | 无 | |
A17 | 5 | -1.746 | -1.022 | ○ | ○ | ○ | 无 | |
A18 | 5 | -1.811 | -0.802 | ○ | ○ | ○ | 无 | |
A19 | 3 | -1.61 | -1 | ○ | ○ | ○ | 无 | |
B1 | 6 | 0.526 | -1.638 | ○ | ○ | × | 有 | 比较例 |
B2 | 7 | -2.248 | 0.224 | ○ | ○ | × | 有 | |
B3 | 13 | -1.808 | -1.046 | ○ | ○ | × | 有 | |
B4 | 12 | -2.628 | -0.536 | ○ | ○ | × | 有 | |
B5 | 15 | -1.028 | -0.456 | ○ | ○ | × | 有 | |
B6 | 30 | -1.808 | -1.046 | ○ | ○ | × | *有 |
Claims (4)