CN1792943A - 烧制白砖的生产方法 - Google Patents

烧制白砖的生产方法 Download PDF

Info

Publication number
CN1792943A
CN1792943A CN 200510120622 CN200510120622A CN1792943A CN 1792943 A CN1792943 A CN 1792943A CN 200510120622 CN200510120622 CN 200510120622 CN 200510120622 A CN200510120622 A CN 200510120622A CN 1792943 A CN1792943 A CN 1792943A
Authority
CN
China
Prior art keywords
white
brick
adobe
starting material
white clay
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510120622
Other languages
English (en)
Other versions
CN100556841C (zh
Inventor
王健阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2005101206229A priority Critical patent/CN100556841C/zh
Publication of CN1792943A publication Critical patent/CN1792943A/zh
Application granted granted Critical
Publication of CN100556841C publication Critical patent/CN100556841C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种烧制白砖的生产方法，采用以往烧红砖的生产设备，生产出可替代白水泥熟料，包括白粘土砖和白熟料砖的白砖，烧制白粘土砖用90％～95％的白粘土，5％～10％的标煤，加上0.5％～1.0％的添加剂；烧制白熟料砖，用20％～60％的白粘土，30％～65％的白石灰石，5％～10％标煤及0.5％～1.0％的添加剂，分别在600℃～1000℃和1000℃～1400℃的温度下，在砖窑里锻烧，所得白砖粉碎后可替代30％～70％的白水泥熟料，掺入白水泥中。该方法能耗低，产品活性强，白度较高，生产成本低。

Description

烧制白砖的生产方法
所属技术领域
本发明涉及一种建筑材料的生产方法，特别是烧制一种用作白水泥熟料，包括白粘土砖和白熟料砖的白砖的生产方法。
背景技术
目前国内白水泥生产水平，标准煤耗达300Kgs标准煤/吨白水泥，占了白水泥生产成本一半以上。寻找白水泥熟料的替代品，以降低煤耗，成为硅酸盐工业技术进步方面的一个课题。另一方面，根据我国的技术政策，已全面禁止粘土红砖的生产和使用，以保护耕地和生态环境。这样一来，在广大农村废弃了许多以往用于烧制红砖的砖窑，即那些简易的隧道窑。利用以往烧制红砖的设备和技术原理，烧制一种可替代白水泥熟料的白砖，成为需急切解决的技术问题。而有关烧制白砖的技术，尚未见报导。
发明内容
本发明的目的在于避免上述现有技术的不足，而提供一种用砖窑烧制出活性强，白度高，能替代白水泥熟料，包括白粘土砖和白熟料砖的白砖的生产方法。
本发明的目的可通过如下的措施来达到：
一种烧制白砖的生产方法，是一种烧制白粘土砖和白熟料砖的生产方法，该方法包括
1.配料：将下列原材料粉碎至300目，按配比用适量水调和均匀，至能填模；
A.对于白粘土砖，使用原材料：
白粘土                           90％～95％
煤粉                                     10％～5％
盐类添加剂                               0.5％～1.0％
总量                                     100％
B.对于白熟料砖，使用原材料：
白粘土                                   20％～60％
白石灰石                                 65％～30％
煤粉                                     10％～5％
盐类添加剂                               0.5％～1.0％
总量                                     100％
2.制成砖坯：将由上述原材料混和而成的浆团，置入砖模中，用制砖机制成砖坯，并晒干；
3.烧制：将砖坯移入砖窑中锻烧4小时～5小时，白粘土砖坯的锻烧温度在600℃～1000℃；白熟料砖坯的锻烧温度在1000℃～1400℃；
4.粉碎：砖坯烧熟冷却后得到白粘土砖和白熟料砖；经粉碎作为活性混合材掺入白水泥熟料中。
上述的原材料中，白粘土含Fe2O3＜0.8％；白石灰石含CaO＞54％；煤的热值≥6000千卡/千克。
本发明的生产方法，具有如下优点：
1.能耗低：使用本发明的生产方法，烧制白粘土砖的标准煤耗约为50Kgs/T，约为传统白水泥熟料的标准煤耗的1/3；而电耗仅为1/6。
2.产品活性强，白度较高：锻烧时白粘土中SiO2，Al2O3的结晶水挥发，破坏了其晶体结构，使活性大幅增强。而SiO2，Al2O3与石灰石中的CaO反应生成硅酸钙和铝酸钙，使白熟料砖具有较高的强度。另一方面，Fe2O3被还原成着色力较弱的FeO，而与盐类添加剂在适宜温度下，又生成可挥发的铁盐，随烟气排走，也进一步提高白熟料砖的白度。
3.节省劳力，生产成本降低，节省设备投资。白熟料砖的生产成本200元/吨，较用小回转窑生产的传统白水泥熟料350元/吨的成本低150元。
4.温室气体排放量少，CO2的排放量是传统白水泥熟料的1/3，
下面结合附图和实施例对本发明的生产方法作进一步叙述
附图说明
图1是本发明生产方法的生产流程示意图。
具体实施方式
在一条包括砖窑和制砖机的制砖生产线上，按日产50吨砖的生产规模，准备足够的白粘土、白石灰石、石粉、煤粉，以及盐类添加剂、所有原材料过粗的，粉碎至300目。其中，白粘土含Fe2O3＜0.8％，白石灰石含CaO＞54％，煤的热值≥6000千卡/千克。按以下配比将原材料混和：烧制白粘土砖时，用白粘土94.5％，煤5％，盐类添加剂0.5％；烧制白熟料砖时，用白粘土39.5％，白石灰石50％，煤10％，盐类添加剂0.5％。配料混和均匀后进入制砖机成型，砖坯晒干后，送入砖窑里锻烧，白粘土砖坯的锻烧温度控制在600℃～1000℃；白熟料砖坯控制在1000℃～1400℃。砖坯烧熟冷却后，粉碎用作活性混合材，掺入到白水泥熟料里。可以替代30％～70％的传统白水泥熟料。

Claims (2)

1.一种烧制白砖的生产方法，是一种烧制白粘土砖和白熟料砖的生产方法，其特征在于，该方法包括
(1)配料：将下列原材料粉碎，按配比用适量水调和均匀，至能填模；
A.对于白粘土砖，使用原材料：
白粘土          90％～95％
煤粉            10％～5％
盐类添加剂      0.5％～1.0％
总量            100％
B.对于白熟料砖，使用原材料：
白粘土          20％～60％
白石灰石        65％～30％
煤粉            10％～5％
盐类添加剂      0.5％～1.0％
总量            100％
(2)制成砖坯：将由上述原材料混和而成的浆团，置入砖模中，用制砖机制成砖坯，并晒干；
(3)烧制：将砖坯移入砖窑中锻烧4小时～5小时，白粘土砖坯的锻烧温度在600℃～1000℃；白熟料砖坯的锻烧温度在1000℃～1400℃；
(4)粉碎：砖坯烧熟冷却后得到白粘土砖和白熟料砖；经粉碎作为活性混合材，掺入白水泥熟料中。
2.根据权利要求1所述的烧制白砖的生产方法，其特征在于，所述的原材料白粘土含Fe2O3＜0.8％；白石灰石含CaO＞54％；煤的热值≥6000千卡/千克。
CNB2005101206229A 2005-12-20 2005-12-20 烧制白砖的生产方法 Expired - Fee Related CN100556841C (zh)